CN103757914A - Preparation method of wearproof and antibacterial blended fabric - Google Patents

Preparation method of wearproof and antibacterial blended fabric Download PDF

Info

Publication number
CN103757914A
CN103757914A CN201310749266.1A CN201310749266A CN103757914A CN 103757914 A CN103757914 A CN 103757914A CN 201310749266 A CN201310749266 A CN 201310749266A CN 103757914 A CN103757914 A CN 103757914A
Authority
CN
China
Prior art keywords
parts
woven fabric
blended yarn
yarn woven
wear
Prior art date
Application number
CN201310749266.1A
Other languages
Chinese (zh)
Other versions
CN103757914B (en
Inventor
张德轩
Original Assignee
苏州市轩德纺织科技有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 苏州市轩德纺织科技有限公司 filed Critical 苏州市轩德纺织科技有限公司
Priority to CN201310749266.1A priority Critical patent/CN103757914B/en
Publication of CN103757914A publication Critical patent/CN103757914A/en
Application granted granted Critical
Publication of CN103757914B publication Critical patent/CN103757914B/en

Abstract

The invention provides a preparation method of a wearproof and antibacterial blended fabric. The preparation method comprises the following steps: (1) preparing fabric coating liquid from 5-9 parts of polyvinyl alcohol tert-butyraldehyde, 3-5 parts of dibutyl sebacate, 7-10 parts of dammar, 5-7 parts of ethyl acetate, 4-6 parts of magnesium oxide, 3-4 parts of zinc oxide and 15-19 parts of ethanol; (2) heating and then dissolving the components in the step (1), stirring the components uniformly after dissolving, and sealing and insulating the components at 80 DEG C after uniform stirring; (3) taking a cotton and polyvinyl chloride blended fabric; (4) blade-coating the coating liquid at the outer layer of the blended fabric with a scraper blade; (5) ventilating and drying the blended fabric, thus preparing the wearproof and antibacterial blended fabric.

Description

A kind of preparation method of blended yarn woven fabric of wear-resistant antibacterial
Technical field
The present invention relates to a kind of preparation method of blended yarn woven fabric, particularly relate to a kind of preparation method with the cotton of good scuff resistance and anti-microbial property and the blended yarn woven fabric of polyvinyl chloride fibre.
Background technology
While applying textiles out of doors, need to consider the wear-resisting and antibacterial effect of textiles.Conventional textiles does not have antibacterial performance.After arranging, some textiless have possessed antibacterial performance.It is by having thereon some antibacterial compositions that common fabric has anti-microbial property, these compositions are some antibacterial materials of inorganic compound or natural extraction normally, these compounds mix after use with some wear-resisting material compositions again, its antibacterial effect can significantly decline, and has affected the anti-microbial property of textiles.Therefore we need to effectively arrange in pairs or groups wear-resisting composition and antimicrobial component, could allow blended yarn woven fabric possess wear-resisting and antibacterial effect simultaneously.
Summary of the invention
The technical problem solving: the scuff resistance of conventional cotton and the blended yarn woven fabric of polyvinyl chloride fibre is also poor problem of lower, anti-microbial property conventionally.
Technical scheme: the preparation method who the invention discloses a kind of blended yarn woven fabric of wear-resistant antibacterial, comprise the following steps: (1) preparation fabric coatings liquid, getting the tertiary butyraldehyde of polyvinyl alcohol and be 5~9 parts, dibutyl sebacate and be 3~5 parts, gum dammar and be 7~10 parts, ethyl acetate and be 5~7 parts, magnesia and be 4~6 parts, zinc oxide and be 3~4 parts, ethanol is 15~19 parts; (2) by dissolving after each composition heating in step (1), after dissolving, stir, after stirring, sealing thermal insulation is 80 ℃; (3) get the blended yarn woven fabric of cotton and polyvinyl chloride fibre, 65wt%~75wt% that cotton content is gross weight, 25wt%~35wt% that polyvinyl chloride fibre content is gross weight; (4) use scraper blade coating at the skin of blended yarn woven fabric coating solution, coating solution thickness is 1.5mm~2.5mm; (5) blended yarn woven fabric is ventilated and dried up, be prepared into the blended yarn woven fabric of wear-resistant antibacterial.
During preparation, in coating solution, the tertiary butyraldehyde of polyvinyl alcohol is preferably 7~9 parts.During preparation, in coating solution, gum dammar is preferably 10 parts.During preparation, in coating solution, zinc oxide is preferably 4 parts.During preparation, in coating solution, zinc oxide order number is preferably 500 orders.
Beneficial effect: anti-wear performance and the anti-microbial property of blended yarn woven fabric that the present invention obtains cotton and polyvinyl chloride fibre is all higher, use fabric plain grinding instrument to measure the anti-wear performance of blended yarn woven fabric, its rubbed 400 turn after, rate of weight loss only has 0.37% to 0.49%, and its inhibiting rate to staphylococcus aureus has reached 77% to 84%.
The specific embodiment
Embodiment 1
(1) preparation fabric coatings liquid, getting the tertiary butyraldehyde of polyvinyl alcohol is that 5kg, dibutyl sebacate are that 5kg, gum dammar are that 10kg, ethyl acetate are that 6kg, magnesia are that 5kg, zinc oxide are that 4kg, ethanol are 15kg; (2) by dissolving after each composition heating in step (1), after dissolving, stir, after stirring, sealing thermal insulation is 80 ℃; (3) get the blended yarn woven fabric of cotton and polyvinyl chloride fibre, the 75wt% that cotton content is gross weight, the 25wt% that polyvinyl chloride fibre content is gross weight; (4) use scraper blade coating at the skin of blended yarn woven fabric coating solution, coating solution thickness is 2.5mm; (5) blended yarn woven fabric is ventilated and dried up, be prepared into the blended yarn woven fabric of wear-resistant antibacterial.
Embodiment 2
(1) preparation fabric coatings liquid, getting the tertiary butyraldehyde of polyvinyl alcohol is that 7kg, dibutyl sebacate are that 3kg, gum dammar are that 7kg, ethyl acetate are that 5kg, magnesia are that 6kg, zinc oxide are that 3kg, ethanol are 17kg; (2) by dissolving after each composition heating in step (1), after dissolving, stir, after stirring, sealing thermal insulation is 80 ℃; (3) get the blended yarn woven fabric of cotton and polyvinyl chloride fibre, the 70wt% that cotton content is gross weight, the 30wt% that polyvinyl chloride fibre content is gross weight; (4) use scraper blade coating at the skin of blended yarn woven fabric coating solution, coating solution thickness is 2mm; (5) blended yarn woven fabric is ventilated and dried up, be prepared into the blended yarn woven fabric of wear-resistant antibacterial.
Embodiment 3
(1) preparation fabric coatings liquid, getting the tertiary butyraldehyde of polyvinyl alcohol is that 9kg, dibutyl sebacate are that 4kg, gum dammar are that 8kg, ethyl acetate are that 7kg, magnesia are that 4kg, zinc oxide are that 4kg, ethanol are 19kg; (2) by dissolving after each composition heating in step (1), after dissolving, stir, after stirring, sealing thermal insulation is 80 ℃; (3) get the blended yarn woven fabric of cotton and polyvinyl chloride fibre, the 65wt% that cotton content is gross weight, the 35wt% that polyvinyl chloride fibre content is gross weight; (4) use scraper blade coating at the skin of blended yarn woven fabric coating solution, coating solution thickness is 1.5mm; (5) blended yarn woven fabric is ventilated and dried up, be prepared into the blended yarn woven fabric of wear-resistant antibacterial.
Get the blended yarn woven fabric of embodiment 1, embodiment 2, embodiment 3, with fabric plain grinding instrument, measure its scuff resistance, diameter is 120cm, weight quality is 300g, measure the rate of weight loss after its friction 400 turns, the inhibiting rate of the blended yarn woven fabric of having measured embodiment 1, embodiment 2, embodiment 3 to staphylococcus aureus, bioassay standard is FZ/T 73023-2006, wear-resisting and antibacterial effect is as follows.
? Embodiment 1 Embodiment 2 Embodiment 3
Friction loss rate 0.41% 0.37% 0.49%
Staphylococcus aureus inhibiting rate 77% 84% 82%
Its friction loss rate of the blended yarn woven fabric preparing is lower, and the inhibiting rate of staphylococcus aureus is also higher, has effectively promoted the serviceability of blended yarn woven fabric.

Claims (5)

1. the preparation method of the blended yarn woven fabric of a wear-resistant antibacterial, it is characterized in that comprising the following steps: (1) preparation fabric coatings liquid, getting the tertiary butyraldehyde of polyvinyl alcohol and be 5~9 parts, dibutyl sebacate and be 3~5 parts, gum dammar and be 7~10 parts, ethyl acetate and be 5~7 parts, magnesia and be 4~6 parts, zinc oxide and be 3~4 parts, ethanol is 15~19 parts; (2) by dissolving after each composition heating in step (1), after dissolving, stir, after stirring, sealing thermal insulation is 80 ℃; (3) get the blended yarn woven fabric of cotton and polyvinyl chloride fibre, 65wt%~75wt% that cotton content is gross weight, 25wt%~35wt% that polyvinyl chloride fibre content is gross weight; (4) use scraper blade coating at the skin of blended yarn woven fabric coating solution, coating solution thickness is 1.5mm~2.5mm; (5) blended yarn woven fabric is ventilated and dried up, be prepared into the blended yarn woven fabric of wear-resistant antibacterial.
2. the preparation method of the blended yarn woven fabric of a kind of wear-resistant antibacterial according to claim 1, while it is characterized in that preparing, in coating solution, the tertiary butyraldehyde of polyvinyl alcohol is 7~9 parts.
3. the preparation method of the blended yarn woven fabric of a kind of wear-resistant antibacterial according to claim 1, while it is characterized in that preparing, in coating solution, gum dammar is 10 parts.
4. the preparation method of the blended yarn woven fabric of a kind of wear-resistant antibacterial according to claim 1, while it is characterized in that preparing, in coating solution, zinc oxide is 4 parts.
5. the preparation method of the blended yarn woven fabric of a kind of wear-resistant antibacterial according to claim 1, while it is characterized in that preparing, in coating solution, zinc oxide order number is 500 orders.
CN201310749266.1A 2013-12-31 2013-12-31 A kind of preparation method of blended yarn woven fabric of wear-resistant antibacterial CN103757914B (en)