CN103752287A - Building finishing pollutant treating agent and preparation method thereof - Google Patents
Building finishing pollutant treating agent and preparation method thereof Download PDFInfo
- Publication number
- CN103752287A CN103752287A CN201410034740.7A CN201410034740A CN103752287A CN 103752287 A CN103752287 A CN 103752287A CN 201410034740 A CN201410034740 A CN 201410034740A CN 103752287 A CN103752287 A CN 103752287A
- Authority
- CN
- China
- Prior art keywords
- parts
- decoration
- construction
- pollutant
- inorganic agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention belongs to the technical field of a chemical preparation and particularly relates to a building finishing pollutant treating agent and a preparation method thereof. The building finishing pollutant treating agent comprises the following raw materials in parts by weight: 10-20 parts of amino acid, 10-20 parts of polyacrylamide, 5-10 parts of casein, 10-20 parts of isoamyl alcohol, 5-10 parts of activated carbon carboxymethylcellulose, 10-20 parts of starch, 8-16 parts of sorbic acid, 8-15 parts of sodium sorbate, 30-50 parts of extractives of plant flowers, 5-12 parts of a penetrant, 16-25 parts of sepiolite powder, 1-3 parts of a manganese-cerium composite oxide catalyst, 5-15 parts of cross-linking rectorite, 10-20 parts of chitosan and 120-200 parts of deionized water. The building finishing pollutant treating agent provided by the invention has the advantages of good adsorbability and long service life, so that the pollution caused by the building finishing pollutant in indoor finishing can be solved.
Description
Technical field
The present invention relates to chemical industry preparation technique field, relate in particular to a kind of construction and decoration pollutant inorganic agent and preparation method thereof.
Background technology
In recent years, along with the develop rapidly of China's economy, having occurred fitting up high-grade office building and luxurious room, there is great variety in indoor environment.The closed finishing in many rooms and indoor ornament materials used have caused serious air pollution problem inside rooms.Common indoor pollutant has: escaping gas pollutant, biological pollutant and the particles etc. such as formaldehyde, benzene homologues, ammonia.Formaldehyde has another name called formaldehyde, is a kind of colourless, gas of having intense stimulus, soluble in water, alcohol and ether.Its aqueous solution is volatile, at room temperature can emit gas formaldehyde, and during heating, rate of release is faster.Formaldehyde easily aggregates into many aldehyde, and its polymer is heated depolymerization easily occurs.Indoor formaldehyde is mainly derived from urea formaldehyde resin adhesive, and the decoration on the various artificial boards that finishing uses, new-type furniture, metope ground is laid all will use adhesive, and the place of every use adhesive all can have formaldehyde to discharge.Benzene homologues (BTEX) is a class VOC (VOC), mainly comprises benzene, toluene, ethylbenzene, neighbour,, the compounds such as paraxylene, isopropylbenzene, styrene.Indoor Air Benzene is that thing is mainly derived from paint, glue and interior wall coating, contains this type of a large amount of materials in finishing in the various adhesive solvents that use, and in paint thinner banana oil, benzene or toluene level are up to 50-55%.Ammonia is mainly as antifreezing agent, swelling agent and early strength agent, to be present in the middle of the construction material such as concrete one class; In addition the ammoniacal liquor that, contains ammonia is also taken as additive, brightening agent and for the covering with paint of furniture.Radon gas is radgas unique in indoor environmental pollution thing, and its main source is to produce owing to containing too much radioactive source in ground, construction material; Radon gas can not volatilize voluntarily and but exist for a long time, is mainly to take measures to reduce the exit dose in source at present to the countermeasure of radon excessive concentration, still there is no radical-ability way thoroughly.Conventionally the house containing the higher construction material building of radioactive element for office building, hotel and use radioactive element that house, air-conditioned room, the closure of basement, next-door neighbour's basement are stronger, easily occurs that indoor radon concentration is higher.
People more and more pay attention to construction and decoration now, at complicated finishing, inevitably can produce various pollutants simultaneously, have very many potential safety hazards.And current most of indoorly all install an air-conditioner, in summer and winter, depend on air-conditioning especially more, like this, airtight longer in room, the time of ventilation is just fewer, and indoor pernicious gas is just difficult to be discharged away.
Therefore, need badly a kind of inorganic agent of removing construction and decoration pollutant is provided.
Summary of the invention
The object of the invention is provides a kind of effective, the long service life of construction and decoration pollutant, construction and decoration pollutant inorganic agent of non-secondary pollution removed for the deficiencies in the prior art.
Another object of the present invention is for the deficiencies in the prior art, to provide a kind of to remove effective, the long service life of construction and decoration pollutant, the preparation method of the construction and decoration pollutant inorganic agent of non-secondary pollution.
A construction and decoration pollutant inorganic agent, it comprises the raw material of following weight portion: 0 ~ 20 part of amino acid/11,10 ~ 20 parts of polyacrylamides, 5 ~ 10 parts of caseins, 10 ~ 20 parts of isoamyl alcohol, 5 ~ 10 parts of active carbon carboxymethyl celluloses, 10 ~ 20 parts of starch, 8 ~ 16 parts of sorbic acids, 8 ~ 15 parts of sodium sorbates, 30 ~ 50 parts of plants and flowers extracts, 5 ~ 12 parts of bleeding agents, 16 ~ 25 parts of sepiolite powders, 1 ~ 3 part of manganese-cerium composite oxide catalyst, 5 ~ 15 parts of cross-linked rectorites, 10 ~ 20 parts of shitosans, 120 ~ 200 parts of deionized waters.
Preferably, it comprises the raw material of following weight portion: 0 ~ 15 part of amino acid/11,15 ~ 20 parts of polyacrylamides, 5 ~ 8 parts of caseins, 15 ~ 20 parts of isoamyl alcohol, 5 ~ 8 parts of active carbon carboxymethyl celluloses, 15 ~ 20 parts of starch, 8 ~ 12 parts of sorbic acids, 12 ~ 15 parts of sodium sorbates, 30 ~ 40 parts of plants and flowers extracts, 5 ~ 10 parts of bleeding agents, 20 ~ 25 parts of sepiolite powders, 1 ~ 2 part of manganese-cerium composite oxide catalyst, 10 ~ 15 parts of cross-linked rectorites, 15 ~ 20 parts of shitosans, 120 ~ 150 parts of deionized waters.
Preferably, it comprises the raw material of following weight portion: 5 ~ 20 parts of amino acid/11s, 10 ~ 15 parts of polyacrylamides, 8 ~ 10 parts of caseins, 10 ~ 15 parts of isoamyl alcohol, 8 ~ 10 parts of active carbon carboxymethyl celluloses, 10 ~ 15 parts of starch, 12 ~ 16 parts of sorbic acids, 8 ~ 12 parts of sodium sorbates, 40 ~ 50 parts of plants and flowers extracts, 10 ~ 12 parts of bleeding agents, 16 ~ 20 parts of sepiolite powders, 2 ~ 3 parts of manganese-cerium composite oxide catalysts, 5 ~ 10 parts of cross-linked rectorites, 10 ~ 15 parts of shitosans, 150 ~ 200 parts of deionized waters.
More preferably, it comprises the raw material of following weight portion: 0 ~ 15 part of amino acid/11,12 ~ 18 parts of polyacrylamides, 6 ~ 8 parts of caseins, 13 ~ 17 parts of isoamyl alcohol, 6 ~ 9 parts of active carbon carboxymethyl celluloses, 12 ~ 16 parts of starch, 10 ~ 12 parts of sorbic acids, 10 ~ 13 parts of sodium sorbates, 35 ~ 45 parts of plants and flowers extracts, 8 ~ 10 parts of bleeding agents, 18 ~ 22 parts of sepiolite powders, 2 ~ 3 parts of manganese-cerium composite oxide catalysts, 8 ~ 12 parts of cross-linked rectorites, 14 ~ 18 parts of shitosans, 140 ~ 160 parts of deionized waters.
Wherein, described plants and flowers extract is the one or more kinds of mixtures in African Chrysanthemum extract, ivy extract, bracketplant extract, Monstera deliciosa leaf extract.
Wherein, described bleeding agent is any one or the two or more mixture in laruyl alcohol, menthol, oleic acid.
Amino acid can be eliminated free formaldehyde, benzene homologues, ammonia, the radon gas producing in application, and the free formaldehyde reducing in urea-formaldehyde resin adhesive is had to positive effect.
Starch, casein, plants and flowers extract are all natural formaldehyde, benzene homologues, ammonia, radon gas capturing agents, can reduce the content of pollutants in air, and to the well improvement effect of indoor-outdoor air environment.
Polyacrylamide is a kind of high polymer coagulant, and outward appearance is water white transparency colloid, is white random powder after dehydration, water-soluble, has good suction-operated.
Adopt food grade materials sorbic acid, sodium sorbate as chemical absorbent, have absorption fast and thorough, the advantage that is difficult to be reversed, can not cause secondary pollution chemical absorbing.
Sepiolite powder be pure natural, nontoxic, tasteless, without a kind of hydrous magnesium silicate clay mineral of asbestos, "dead" element, there is in nonmetallic mineral maximum specific area and (reach as high as 900m
2/ g) and unique content pore passage structure, be the clay mineral that adsorption capacity is the strongest.
Bleeding agent can remove rapidly artificial board surface and artificial board inside is not discharged into surperficial free formaldehyde and finishing paint, glue and interior wall coating etc. are not discharged into surperficial benzene homologues etc.
Manganese-cerium composite oxide catalyst is applied to O3 catalytic oxidation benzene homologues, its catalytic activity and stability are significantly improved, can realize ozone self decomposes simultaneously, be solve construction and decoration pollutant and prevent the effective way that ozone is poisoned, in the complete oxidation of gas phase medium/low concentration benzene series matter, have good application prospect.
Cross-linked rectorite Stability Analysis of Structures, do not expand, have larger specific area, ion exchange capacity and micropore size and have the features such as Heat stability is good, surface acidity be strong, adsorption capacity increases more than 70%, having larger layer thickness, is a kind of catalyst and adsorbent of excellent performance.
Shitosan wide material sources, non-secondary pollution, the feature such as tasteless, alkaline-resisting, heat-resisting, corrosion-resistant, and on shitosan linear molecule chain, contain a plurality of hydroxyls and amino, as adsorbent, have that removal efficiency is high, the feature of non-secondary pollution.
Further, it also comprises graphene nano layer (GNS)/MnO
2compound 5 ~ 8 weight portions.Graphene nano layer (GNS)/MnO
2compound (GNS/MnO
2) be the significant adsorbent of effect, greatly improve the effect of absorption formaldehyde, benzene homologues, ammonia, radon gas; GNS, as carrier, has increased the specific area of adsorbent, MnO
2play main suction-operated, after reusing for 5 times, GNS/MnO
2adsorption capacity can also return to 91%, have good power of regeneration.
Further, it also comprises sodium bentonite 10 ~ 20 weight portions.Sodium bentonite will catch formaldehyde, benzene homologues, ammonia, radon gas, by ion-exchange or suction type, be placed between interlayer or space, can fully contact with formaldehyde, benzene homologues, ammonia, radon gas, thereby performance catches the effect of formaldehyde, benzene homologues, ammonia, radon gas.
A preparation method for construction and decoration pollutant inorganic agent, described preparation process is as follows:
(1) will be by weight, by deionized water, starch and polyacrylamide, join in agitator, under 60-70 degree Celsius, stir 3-5 hour, obtain reactant liquor;
(2) reactant liquor obtaining in previous step is cooled to 20～30 degrees Celsius, then adds successively cross-linked rectorite, shitosan by weight in reactant liquor, be stirred to material and all dissolve;
(3) in the reactant liquor obtaining in previous step, add remaining raw material, vibration of ultrasonic wave 30 ~ 40 minutes, then stirs 1～2 hour;
(4) reactant liquor obtaining in previous step is cooled to 0～5 degree Celsius, after standing 5～8 hours, reactant liquor is filtered, gained liquid is construction and decoration pollutant inorganic agent.
compared with prior art, the present invention has following beneficial effect:
(1) construction and decoration pollutant inorganic agent uniform component distribution of the present invention, very easily water-soluble, corrosion-free effect, the pollutants such as PARA FORMALDEHYDE PRILLS(91,95), benzene homologues, ammonia, radon gas have good absorption or reaction to generate the effect of stable material, thereby reach the object of removing fast construction and decoration pollutant, can not produce infringement to finishing product, reaction condition is gentle, good stability, has higher practical value.
(2) construction and decoration pollutant inorganic agent long service life of the present invention, thereby the benzene homologues after solution interior decoration pollutes, can also, to effectively suppressing or kill such as flu class, enteron aisle class, some germ of skin class, virus, be conducive to the healthy of people.
(3) construction and decoration pollutant inorganic agent of the present invention is non-toxic, uses in a large number, also can not produce secondary pollution to environment.
(4) cost of raw material of construction and decoration pollutant inorganic agent of the present invention is low, and preparation method is simple, easy to use, is applicable to large-scale production.
The specific embodiment
Below in conjunction with the specific embodiment, the present invention is described in detail.
embodiment 1.
A construction and decoration pollutant inorganic agent, it comprises the raw material of following weight portion: 0 part of amino acid/11,20 parts of polyacrylamides, 5 parts of caseins, 20 parts of isoamyl alcohol, 5 parts of active carbon carboxymethyl celluloses, 20 parts of starch, 8 parts of sorbic acids, 15 parts of sodium sorbates, 30 parts of plants and flowers extracts, 12 parts of bleeding agents, 16 parts of sepiolite powders, 3 parts of manganese-cerium composite oxide catalysts, 5 parts of cross-linked rectorites, 20 parts of shitosans, 120 parts of deionized waters.Plants and flowers extract is ivy extract; Bleeding agent is laruyl alcohol.
A preparation method for construction and decoration pollutant inorganic agent, described preparation process is as follows:
(1) will be by weight, by deionized water, starch and polyacrylamide, join in agitator, under 60 degrees Celsius, stir 5 hours, obtain reactant liquor;
(2) reactant liquor obtaining in previous step is cooled to 20 degrees Celsius, then adds successively cross-linked rectorite, shitosan by weight in reactant liquor, be stirred to material and all dissolve;
(3) in the reactant liquor obtaining in previous step, add remaining raw material, vibration of ultrasonic wave 40 minutes, then stirs 2 hours; Described ultrasonic frequency is 2000W;
(4) reactant liquor obtaining in previous step is cooled to 0 degree Celsius, after standing 5 hours, reactant liquor is filtered, gained liquid is construction and decoration pollutant inorganic agent.
embodiment 2.
A construction and decoration pollutant inorganic agent, it comprises the raw material of following weight portion: 5 parts of amino acid/11s, 15 parts of polyacrylamides, 8 parts of caseins, 15 parts of isoamyl alcohol, 8 parts of active carbon carboxymethyl celluloses, 15 parts of starch, 12 parts of sorbic acids, 12 parts of sodium sorbates, 40 parts of plants and flowers extracts, 5 parts of bleeding agents, 25 parts of sepiolite powders, 1 part of manganese-cerium composite oxide catalyst, 15 parts of cross-linked rectorites, 15 parts of shitosans, 150 parts of deionized waters.Plants and flowers extract is the mixture of 13 parts of African Chrysanthemum extracts, 17 parts of bracketplant extracts, 20 parts of Monstera deliciosa leaf extracts; Bleeding agent is the mixture of 4 parts of laruyl alcohols, 1 part of menthol.
A preparation method for construction and decoration pollutant inorganic agent, described preparation process is as follows:
(1) will be by weight, by deionized water, starch and polyacrylamide, join in agitator, under 63 degrees Celsius, stir 4 hours, obtain reactant liquor;
(2) reactant liquor obtaining in previous step is cooled to 22 degrees Celsius, then adds successively cross-linked rectorite, shitosan by weight in reactant liquor, be stirred to material and all dissolve;
(3) in the reactant liquor obtaining in previous step, add remaining raw material, vibration of ultrasonic wave 38 minutes, then stirs 1.5 hours; Described ultrasonic frequency is 1800W;
(4) reactant liquor obtaining in previous step is cooled to 2 degrees Celsius, after standing 6 hours, reactant liquor is filtered, gained liquid is construction and decoration pollutant inorganic agent.
embodiment 3.
A construction and decoration pollutant inorganic agent, it comprises the raw material of following weight portion: 20 parts, amino acid, 10 parts of polyacrylamides, 10 parts of caseins, 10 parts of isoamyl alcohol, 10 parts of active carbon carboxymethyl celluloses, 10 parts of starch, 16 parts of sorbic acids, 8 parts of sodium sorbates, 50 parts of plants and flowers extracts, 12 parts of bleeding agents, 20 parts of sepiolite powders, 2 parts of manganese-cerium composite oxide catalysts, 5 parts of cross-linked rectorites, 10 parts of shitosans, 200 parts of deionized waters.Plants and flowers extract is the mixture of 20 parts of ivy extracts, 20 parts of bracketplant extracts, 10 parts of Monstera deliciosa leaf extracts.Bleeding agent is the mixture in 4 parts of 5 parts of laruyl alcohols, 3 parts of menthols, oleic acid.
A preparation method for construction and decoration pollutant inorganic agent, described preparation process is as follows:
(1) will be by weight, by deionized water, starch and polyacrylamide, join in agitator, under 65 degrees Celsius, stir 4 hours, obtain reactant liquor;
(2) reactant liquor obtaining in previous step is cooled to 25 degrees Celsius, then adds successively cross-linked rectorite, shitosan by weight in reactant liquor, be stirred to material and all dissolve;
(3) in the reactant liquor obtaining in previous step, add remaining raw material, vibration of ultrasonic wave 5 minutes, then stirs 2 hours; Ultrasonic frequency is 1600W;
(4) reactant liquor obtaining in previous step is cooled to 5 degrees Celsius, after standing 7 hours, reactant liquor is filtered, gained liquid is construction and decoration pollutant inorganic agent.
embodiment 4.
A construction and decoration pollutant inorganic agent, it comprises the raw material of following weight portion: 5 parts of amino acid/11s, 18 parts of polyacrylamides, 6 parts of caseins, 17 parts of isoamyl alcohol, 6 parts of active carbon carboxymethyl celluloses, 16 parts of starch, 10 parts of sorbic acids, 13 parts of sodium sorbates, 35 parts of plants and flowers extracts, 10 parts of bleeding agents, 18 parts of sepiolite powders, 3 parts of manganese-cerium composite oxide catalysts, 8 parts of cross-linked rectorites, 18 parts of shitosans, 140 parts of deionized waters, graphene nano layer (GNS)/MnO
25 parts of compounds.Plants and flowers extract is the mixture of 20 parts of bracketplant extracts, 15 parts of Monstera deliciosa leaf extracts.Bleeding agent is the mixture of 6 parts of laruyl alcohols, 4 parts of oleic acid.
A preparation method for construction and decoration pollutant inorganic agent, described preparation process is as follows:
(1) will be by weight, by deionized water, starch and polyacrylamide, join in agitator, under 68 degrees Celsius, stir 4 hours, obtain reactant liquor;
(2) reactant liquor obtaining in previous step is cooled to 30 degrees Celsius, then adds successively cross-linked rectorite, shitosan by weight in reactant liquor, be stirred to material and all dissolve;
(3) in the reactant liquor obtaining in previous step, add remaining raw material, vibration of ultrasonic wave 38 minutes, then stirs 1 hour; Described ultrasonic frequency is 1500W;
(4) reactant liquor obtaining in previous step is cooled to 4 degrees Celsius, after standing 7 hours, reactant liquor is filtered, gained liquid is construction and decoration pollutant inorganic agent.
embodiment 5.
A construction and decoration pollutant inorganic agent, it comprises the raw material of following weight portion: 6 parts of amino acid/11s, 12 parts of polyacrylamides, 8 parts of caseins, 13 parts of isoamyl alcohol, 9 parts of active carbon carboxymethyl celluloses, 12 parts of starch, 12 parts of sorbic acids, 10 parts of sodium sorbates, 45 parts of plants and flowers extracts, 8 parts of bleeding agents, 22 parts of sepiolite powders, 2 parts of manganese-cerium composite oxide catalysts, 12 parts of cross-linked rectorites, 14 parts of shitosans, 160 parts of deionized waters, graphene nano layer (GNS)/MnO
28 parts of compounds, 15 parts of sodium bentonites.Plants and flowers extract is Monstera deliciosa leaf extract; Bleeding agent is oleic acid.
A preparation method for construction and decoration pollutant inorganic agent, described preparation process is as follows:
(1) will be by weight, by deionized water, starch and polyacrylamide, join in agitator, under 70 degrees Celsius, stir 3 hours, obtain reactant liquor;
(2) reactant liquor obtaining in previous step is cooled to 25 degrees Celsius, then adds successively cross-linked rectorite, shitosan by weight in reactant liquor, be stirred to material and all dissolve;
(3) in the reactant liquor obtaining in previous step, add remaining raw material, vibration of ultrasonic wave 40 minutes, then stirs 2 hours; Described ultrasonic frequency is 1000W;
(4) reactant liquor obtaining in previous step is cooled to 5 degrees Celsius, after standing 8 hours, reactant liquor is filtered, gained liquid is construction and decoration pollutant inorganic agent.
The construction and decoration pollutant inorganic agent of Application Example 1 ~ 5 preparation carries out spray application, acts on after 24 hours and detecting, and effect is as follows:
Finally should be noted that; above embodiment is only in order to illustrate technical scheme of the present invention; but not limiting the scope of the invention; although the present invention has been done to explain with reference to preferred embodiment; those of ordinary skill in the art is to be understood that; can modify or be equal to replacement technical scheme of the present invention, and not depart from essence and the scope of technical solution of the present invention.
Claims (9)
1. a construction and decoration pollutant inorganic agent, it is characterized in that, it comprises the raw material of following weight portion: 0 ~ 20 part of amino acid/11,10 ~ 20 parts of polyacrylamides, 5 ~ 10 parts of caseins, 10 ~ 20 parts of isoamyl alcohol, 5 ~ 10 parts of active carbon carboxymethyl celluloses, 10 ~ 20 parts of starch, 8 ~ 16 parts of sorbic acids, 8 ~ 15 parts of sodium sorbates, 30 ~ 50 parts of plants and flowers extracts, 5 ~ 12 parts of bleeding agents, 16 ~ 25 parts of sepiolite powders, 1 ~ 3 part of manganese-cerium composite oxide catalyst, 5 ~ 15 parts of cross-linked rectorites, 10 ~ 20 parts of shitosans, 120 ~ 200 parts of deionized waters.
2. construction and decoration pollutant inorganic agent according to claim 1, it is characterized in that, it comprises the raw material of following weight portion: 0 ~ 15 part of amino acid/11,15 ~ 20 parts of polyacrylamides, 5 ~ 8 parts of caseins, 15 ~ 20 parts of isoamyl alcohol, 5 ~ 8 parts of active carbon carboxymethyl celluloses, 15 ~ 20 parts of starch, 8 ~ 12 parts of sorbic acids, 12 ~ 15 parts of sodium sorbates, 30 ~ 40 parts of plants and flowers extracts, 5 ~ 10 parts of bleeding agents, 20 ~ 25 parts of sepiolite powders, 1 ~ 2 part of manganese-cerium composite oxide catalyst, 10 ~ 15 parts of cross-linked rectorites, 15 ~ 20 parts of shitosans, 120 ~ 150 parts of deionized waters.
3. construction and decoration pollutant inorganic agent according to claim 1, it is characterized in that, it comprises the raw material of following weight portion: 5 ~ 20 parts of amino acid/11s, 10 ~ 15 parts of polyacrylamides, 8 ~ 10 parts of caseins, 10 ~ 15 parts of isoamyl alcohol, 8 ~ 10 parts of active carbon carboxymethyl celluloses, 10 ~ 15 parts of starch, 12 ~ 16 parts of sorbic acids, 8 ~ 12 parts of sodium sorbates, 40 ~ 50 parts of plants and flowers extracts, 10 ~ 12 parts of bleeding agents, 16 ~ 20 parts of sepiolite powders, 2 ~ 3 parts of manganese-cerium composite oxide catalysts, 5 ~ 10 parts of cross-linked rectorites, 10 ~ 15 parts of shitosans, 150 ~ 200 parts of deionized waters.
4. construction and decoration pollutant inorganic agent according to claim 1, it is characterized in that, it comprises the raw material of following weight portion: 0 ~ 15 part of amino acid/11,12 ~ 18 parts of polyacrylamides, 6 ~ 8 parts of caseins, 13 ~ 17 parts of isoamyl alcohol, 6 ~ 9 parts of active carbon carboxymethyl celluloses, 12 ~ 16 parts of starch, 10 ~ 12 parts of sorbic acids, 10 ~ 13 parts of sodium sorbates, 35 ~ 45 parts of plants and flowers extracts, 8 ~ 10 parts of bleeding agents, 18 ~ 22 parts of sepiolite powders, 2 ~ 3 parts of manganese-cerium composite oxide catalysts, 8 ~ 12 parts of cross-linked rectorites, 14 ~ 18 parts of shitosans, 140 ~ 160 parts of deionized waters.
5. construction and decoration pollutant inorganic agent according to claim 1, is characterized in that, described plants and flowers extract is the one or more kinds of mixtures in African Chrysanthemum extract, ivy extract, bracketplant extract, Monstera deliciosa leaf extract.
6. construction and decoration pollutant inorganic agent according to claim 1, is characterized in that, described bleeding agent is any one or the two or more mixture in laruyl alcohol, menthol, oleic acid.
7. according to the construction and decoration pollutant inorganic agent described in claim 1 ~ 6 any one, it is characterized in that, it also comprises graphene nano layer (GNS)/MnO
2compound 5 ~ 8 weight portions.
8. construction and decoration pollutant inorganic agent according to claim 7, is characterized in that, it also comprises sodium bentonite 10 ~ 20 weight portions.
9. a preparation method for the construction and decoration pollutant inorganic agent described in claim 1 to 8 any one, is characterized in that, described preparation process is as follows:
(1) will be by weight, by deionized water, starch and polyacrylamide, join in agitator, under 60-70 degree Celsius, stir 3-5 hour, obtain reactant liquor;
(2) reactant liquor obtaining in previous step is cooled to 20～30 degrees Celsius, then adds successively cross-linked rectorite, shitosan by weight in reactant liquor, be stirred to material and all dissolve;
(3) in the reactant liquor obtaining in previous step, add remaining raw material, vibration of ultrasonic wave 30 ~ 40 minutes, then stirs 1～2 hour;
(4) reactant liquor obtaining in previous step is cooled to 0～5 degree Celsius, after standing 5～8 hours, reactant liquor is filtered, gained liquid is construction and decoration pollutant inorganic agent.