CN103689844A - Manufacture method of multicolored double-layered fabric - Google Patents

Manufacture method of multicolored double-layered fabric Download PDF

Info

Publication number
CN103689844A
CN103689844A CN201310734711.7A CN201310734711A CN103689844A CN 103689844 A CN103689844 A CN 103689844A CN 201310734711 A CN201310734711 A CN 201310734711A CN 103689844 A CN103689844 A CN 103689844A
Authority
CN
China
Prior art keywords
yarns
fabric
double
broadwise
yarn
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310734711.7A
Other languages
Chinese (zh)
Inventor
孙德荣
邱成
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
XUZHOU SILK FIBER TECHNOLOGY Co Ltd
Original Assignee
XUZHOU SILK FIBER TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by XUZHOU SILK FIBER TECHNOLOGY Co Ltd filed Critical XUZHOU SILK FIBER TECHNOLOGY Co Ltd
Priority to CN201310734711.7A priority Critical patent/CN103689844A/en
Publication of CN103689844A publication Critical patent/CN103689844A/en
Pending legal-status Critical Current

Abstract

The invention provides a manufacture method of multicolored double-layered fabric. The method includes the steps of 1, selecting raw materials, namely making warp yarns out of polyester yarns, using colored composite yarns as weft-wise yarns A, using black yarns as weft-wise yarns B, compositing cationic polyester chip spun yarns and conventional chip polyester spun yarns into the colored composite yarns, continuously rotating and winding the cationic colored composite yarns to core spandex yarns drawn at uniform speed, with spandex yarns as core yarns; 2, performing double-layer weaving, namely weaving by a double-layer weaving method; 3, dyeing, namely, dyeing woven grey cloth at two different temperatures. The fabric manufactured by the manufacture method has the advantages that the fabric is multiply colored, a lining frame of the fabric is stiff, and the fabric is well drapeable and easy to treat.

Description

A kind of preparation method of colour mixture double-layer fabric
Technical field
The present invention relates to a kind of fabric preparation method, especially relate to a kind of preparation method of colour mixture double-layer fabric.
Background technology
Clothes of fine quality is as very fastidious to fabric in jacket, wind coat, but practical function is often not fully up to expectations, especially on durable and barely satisfactory especially on the gorgeous degree of color; Even if or by polyester-cotton blend be composited thickness true to nature and face matter feel, several times after washing because colloidal property weakens, cause in fabric table separatedly, function is lost to the greatest extent.
Summary of the invention
For addressing the above problem, the preparation method that the double-deck super imitative cotton face fabric of a kind of colour mixture is provided of the present invention, skeleton is hale and hearty inside to make the fabric that weaves, drapability is good, easily arrange, add many colour mixtures of spending ash, be applied in the high-grade garment markets such as jacket and wind coat hyperchromic much.
Concrete technical scheme of the present invention is as follows:
A preparation method for colour mixture double-layer fabric, comprises the steps:
Step 1: select raw material
Warp thread adopts terylene silk, broadwise A yarn adopts extraordinary splendor composite filament, broadwise B yarn adopts black silk, described extraordinary splendor composite filament is to be composited by cationic polyester slice spinning and conventional section Direct-spinning of PET Fiber, described coated referring to be take spandex thread as core silk, cation extraordinary splendor composite filament constantly rotated and be wrapped in by the core silk spandex of at the uniform velocity drawing-off;
Step 2: carry out bilayer and weave cotton cloth
Adopt the bilayer method of weaving cotton cloth to weave cotton cloth;
Step 3: dye
To the grey cloth weaving, adopt two-bath process to dye, described two-bath process refers in two kinds of different temperatures environment and dyes.
The preparation method of foregoing colour mixture double-layer fabric, described warp thread specification is 60D-125D, and broadwise A yarn specification is 40D-80D, and broadwise B yarn specification is 75D-150D.
The invention has the advantages that:
1, there is color blending effect.
2, skeleton is hale and hearty inside for fabric, and drapability is good, easily arranges.
The specific embodiment
Below in conjunction with example, be described further:
Embodiment 1:
Material set-up procedure:
Warp thread selects 88D/50F to imitate cotton fiber, and broadwise A yarn is selected 44D/30F extraordinary splendor composite filament, and broadwise B yarn adopts the black silk of 75D/36F, adopts the institutional framework of latitude bilayer, 153/CM of warp-wise density (upper machine), 178/CM of latitudinal density.
Dyeing engineering:
In the temperature environment of 95 ℃ and 180 ℃, dye.
It is as follows that gained fabric detects evaluation result: 4 grades of color fastness, water pressure resistance 250MM, the powerful 12.8N of warp-wise, the powerful 11.4N of broadwise.
Embodiment 2:
Material set-up procedure:
Warp thread selects 138D/120F to imitate cotton fiber, and broadwise is selected the black silk of the imitative cotton fiber of 88D/50F and 120D/72F.Adopt the institutional framework of latitude bilayer: 150/CM of warp-wise density (upper machine), 163/CM of latitudinal density.
Dyeing engineering:
In the temperature environment of 95 ℃ and 180 ℃, dye.
It is as follows that gained fabric detects evaluation result: 4 grades of color fastness, water pressure resistance 300MM, the powerful 15.6N of warp-wise, the powerful 13.4N of broadwise.

Claims (2)

1. a preparation method for colour mixture double-layer fabric, is characterized in that:
Step 1: select raw material
Warp thread adopts terylene silk, broadwise A yarn adopts extraordinary splendor composite filament, broadwise B yarn adopts black silk, described extraordinary splendor composite filament is to be composited by cationic polyester slice spinning and conventional section Direct-spinning of PET Fiber, described coated referring to be take spandex thread as core silk, cation extraordinary splendor composite filament constantly rotated and be wrapped in by the core silk spandex of at the uniform velocity drawing-off;
Step 2: carry out bilayer and weave cotton cloth
Adopt the bilayer method of weaving cotton cloth to weave cotton cloth;
Step 3: dye
To the grey cloth weaving, adopt two-bath process to dye, described two-bath process refers in two kinds of different temperatures environment and dyes.
2. the preparation method of colour mixture double-layer fabric according to claim 1, is characterized in that: described warp thread specification is 60D-125D, and broadwise A yarn specification is 40D-80D, and broadwise B yarn specification is 75D-150D.
CN201310734711.7A 2013-12-27 2013-12-27 Manufacture method of multicolored double-layered fabric Pending CN103689844A (en)