CN103653276B - A kind of solar heat protection fabric and preparation method thereof - Google Patents

A kind of solar heat protection fabric and preparation method thereof Download PDF

Info

Publication number
CN103653276B
CN103653276B CN201310610489.XA CN201310610489A CN103653276B CN 103653276 B CN103653276 B CN 103653276B CN 201310610489 A CN201310610489 A CN 201310610489A CN 103653276 B CN103653276 B CN 103653276B
Authority
CN
China
Prior art keywords
solar heat
heat protection
protection fabric
fabric
surfactant
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310610489.XA
Other languages
Chinese (zh)
Other versions
CN103653276A (en
Inventor
吴园园
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nantong Haiyu Chemical Fiber Co.,Ltd.
Original Assignee
吴园园
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 吴园园 filed Critical 吴园园
Priority to CN201310610489.XA priority Critical patent/CN103653276B/en
Publication of CN103653276A publication Critical patent/CN103653276A/en
Application granted granted Critical
Publication of CN103653276B publication Critical patent/CN103653276B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses a kind of solar heat protection fabric and preparation method thereof, solar heat protection fabric is made up of the raw material of following parts by weight: polyvinyl chloride 40-60 part, hydroquinones 10-20 part, trimethylbenzene ammonio methacrylate 20-30 part, polyamide 40-60 part, acrylonitrile-butadiene rubber 50-55 part, surfactant 20-30 part; Preparation method is by polyvinyl chloride, hydroquinones, trimethylbenzene ammonio methacrylate, polyamide, acrylonitrile-butadiene rubber mixing, is heated into molten condition, adds surfactant mixing, extrude from spinneret, form fiber, fibrage is become fabric.The present invention to solar thermal energy through with reflection higher, transmitance 10-16%, reflectivity 20-25%, absorb heat energy lower, illustrate that the present invention has good thermal protective performance.

Description

A kind of solar heat protection fabric and preparation method thereof
Technical field
The present invention relates to fabric field, particularly relate to a kind of solar heat protection fabric and preparation method thereof.
Background technology
The color of fabric is different, its effect absorbing solar thermal energy and release heat energy is also different, white is than being easier to through light, absorption heat energy is low, and more nice and cool when summer wears, black then the most easily absorbs heat energy, sunlight is warmmer relative to white when irradiating, but people like different colors, some people likes dark, but can be hotter when summer wears.
" summer wears the clothes and is very learned ", Yi Kai, " township enterprise of Chinatown industry health ", 03 interim record in 1987: fixed according to side, time summer, noon was the hottest, the heat of earth surface solar radiation often will reach every square centimeter 1.9 card per minute.The color of clothes is absorbed with much relations with hot.As the absorptivity with white is decided to be 100%, then yellow is 165%, and redness is 207%, and black is 250%.Perceived color is darker, and heat absorption rate is higher.
Summary of the invention
The present invention is directed to the deficiencies in the prior art, provide a kind of solar heat protection fabric, there is good thermal protective performance.
Solar heat protection fabric, is made up of the raw material of following parts by weight: polyvinyl chloride 40-60 part, hydroquinones 10-20 part, trimethylbenzene ammonio methacrylate 20-30 part, polyamide 40-60 part, acrylonitrile-butadiene rubber 50-55 part, surfactant 20-30 part.
As preferably, surfactant is the one in glycerol caprylate, glycerol tristearate or glycerine certain herbaceous plants with big flowers acid esters.
Present invention also offers a kind of preparation method of solar heat protection fabric, technique is simple, comprise the following steps: by polyvinyl chloride, hydroquinones, trimethylbenzene ammonio methacrylate, polyamide, acrylonitrile-butadiene rubber mixing, be heated into molten condition, add surfactant mixing, extrude from spinneret, form fiber, fibrage is become fabric.
As preferably, the orifice diameter of spinneret is 0.01-0.12mm.
As preferably, the warp density of solar heat protection fabric is 80-100 root/cm, and weft density is 60-90 root/cm.
The present invention to solar thermal energy through with reflection higher, transmitance 10-16%, reflectivity 20-25%, absorb heat energy lower, illustrate that the present invention has good thermal protective performance.
Detailed description of the invention
Below by specific embodiment 1-3, the present invention is described in further detail:
Embodiment 1-3 adopts following raw material (unit is Kg):
Embodiment 1
Preparation method of the present invention, comprise the following steps: by polyvinyl chloride, hydroquinones, trimethylbenzene ammonio methacrylate, polyamide, acrylonitrile-butadiene rubber mixing, be heated into molten condition, add the mixing of surfactant glycerol caprylate, extrude from spinneret (orifice diameter is 0.01mm), form fiber, according to warp density 80/cm, weft density 60/cm, becomes fabric by fibrage.
Embodiment 2
Preparation method of the present invention, comprise the following steps: by polyvinyl chloride, hydroquinones, trimethylbenzene ammonio methacrylate, polyamide, acrylonitrile-butadiene rubber mixing, be heated into molten condition, add the mixing of surfactant glycerol tristearate, extrude from spinneret (orifice diameter is 0.12mm), form fiber, according to warp density 100/cm, weft density 90/cm, becomes fabric by fibrage.
Embodiment 3
Preparation method of the present invention, comprise the following steps: by polyvinyl chloride, hydroquinones, trimethylbenzene ammonio methacrylate, polyamide, acrylonitrile-butadiene rubber mixing, be heated into molten condition, add surfactant glycerine certain herbaceous plants with big flowers acid esters) mixing, extrude from spinneret (orifice diameter is 0.08mm), form fiber, according to warp density 90/cm, weft density 70/cm, becomes fabric by fibrage.
Test:
Test the performance parameter of fabric of the present invention:
As from the foregoing, the present invention to solar thermal energy through with reflection higher, transmitance 10-16%, reflectivity 20-25%, absorb heat energy lower, illustrate that the present invention has good thermal protective performance.

Claims (5)

1. a solar heat protection fabric, it is characterized in that, be made up of the raw material of following parts by weight: polyvinyl chloride 40-60 part, hydroquinones 10-20 part, trimethylbenzene ammonio methacrylate 20-30 part, polyamide 40-60 part, acrylonitrile-butadiene rubber 50-55 part, surfactant 20-30 part.
2. solar heat protection fabric according to claim 1, is characterized in that, surfactant is the one in glycerol caprylate, glycerol tristearate or glycerine certain herbaceous plants with big flowers acid esters.
3. the preparation method of solar heat protection fabric according to claim 1, it is characterized in that, comprise the following steps: by polyvinyl chloride, hydroquinones, trimethylbenzene ammonio methacrylate, polyamide, acrylonitrile-butadiene rubber mixing, be heated into molten condition, add surfactant mixing, extrude from spinneret, form fiber, fibrage is become fabric.
4. the preparation method of solar heat protection fabric according to claim 3, is characterized in that, the orifice diameter of spinneret is 0.01-0.12mm.
5. the preparation method of solar heat protection fabric according to claim 3, is characterized in that, the warp density of solar heat protection fabric is 80-100 root/cm, and weft density is 60-90 root/cm.
CN201310610489.XA 2013-11-27 2013-11-27 A kind of solar heat protection fabric and preparation method thereof Active CN103653276B (en)