CN103570240B - A kind of devices and methods therefor reducing bushing place, centrifugal cotton molten bath glass melt viscosity - Google Patents
A kind of devices and methods therefor reducing bushing place, centrifugal cotton molten bath glass melt viscosity Download PDFInfo
- Publication number
- CN103570240B CN103570240B CN201210263831.9A CN201210263831A CN103570240B CN 103570240 B CN103570240 B CN 103570240B CN 201210263831 A CN201210263831 A CN 201210263831A CN 103570240 B CN103570240 B CN 103570240B
- Authority
- CN
- China
- Prior art keywords
- glass melt
- bushing
- molten bath
- glass
- source device
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention provides a kind of devices and methods therefor reducing bushing place, centrifugal cotton molten bath glass melt viscosity, comprise molten bath, glass melt, bushing, platinum electrode slice, alternating source device, it is characterized in that placing two platinum electrode slices above bushing, electrode slice is by the external alternating source device of wire.Alternating source is utilized to produce alternating electric field between two platinum electrodes; Polymer-based group [SiO in glass fluxed melt
3]
n 2n-issue solution estranged or ionization at action of alternative electric field, change the microtexture of glass melt, reduce the reduction of glass melt viscosity.By the present invention, the temperature without the need to improving glass melt just can reduce the viscosity of glass melt, save energy, improves centrifugal pan work-ing life, obtains the centrifugally glass-wool that Fibre diameter is tiny; By changing output voltage and output frequency, the viscosity of glass melt can be regulated, obtains the centrifugally glass-wool of different Fibre diameter simultaneously.
Description
Technical field
The present invention relates to a kind of devices and methods therefor reducing glass melt viscosity, especially relate to a kind of devices and methods therefor reducing bushing place, centrifugal cotton molten bath glass melt viscosity.
Background technology
Centrifugally glass-wool take glass cullet as main raw material, through fusing, homogenizing and clarifying treatment in high temperature melting furnaces, then glass melt is flowed out by the bushing place in molten bath, enters the centrifugal pan of high speed rotating, by centrifugal action, glass melt is thrown away and makes centrifugally glass-wool.
The diameter of current domestic centrifugally glass-wool is generally more than 7-8 micron, and the heat preservation and insulation of glass wool product is poor.Research shows, Fibre diameter often reduces 1 micron, and thermal conductivity value can reduce by 9.2%.And glass melt viscosity is the most important factor affecting centrifugally glass-wool Fibre diameter, the viscosity of glass melt is lower, and Fibre diameter is more tiny.
The conventional art of current centrifugally glass-wool is the temperature by raising glass melt, reduce the viscosity of glass melt, thus obtain the tiny centrifugal cotton of Fibre diameter, but this method can cause the reduction in centrifugal pan life-span, the increase of production energy consumption, does not meet the policy that national energy-saving reduces discharging.
Summary of the invention
For the deficiencies in the prior art, the invention provides a kind of device reducing bushing place, centrifugal cotton molten bath glass melt viscosity, comprise molten bath, glass melt, bushing, platinum electrode slice, alternating source device, it is characterized in that placing two platinum electrode slices above bushing, electrode slice is by the external alternating source device of wire.
Another technical problem to be solved by this invention is to provide a kind of method reducing bushing place, centrifugal cotton molten bath glass melt viscosity, is realized by following steps:
(1) fixed placement two platinum electrode slices above bushing, electrode slice is by the external alternating source device of wire;
(2) relation bushing, waits for that the glass melt of front end high temperature melting, homogenizing and clarifying treatment is full of molten bath;
(3) open alternating source device, setting output voltage and output frequency, produce alternating electric field between two electrode slices;
(3) after certain hour, open bushing, glass melt is flowed out from bushing, enters the centrifugal pan of high speed rotating.
Method described above, it is characterized in that output voltage is 220-380V, output frequency is 50-5000Hz, and certain hour is 5-10 minute.
The invention has the beneficial effects as follows and a kind of devices and methods therefor reducing glass melt viscosity is provided, utilize alternating source to produce alternating electric field between two platinum electrodes; Polymer-based group [SiO in glass fluxed melt
3]
n 2n-issue solution estranged or ionization at action of alternative electric field, change the microtexture of glass melt, reduce the reduction of glass melt viscosity.By the present invention, the temperature without the need to improving glass melt just can reduce the viscosity of glass melt, save energy, improves centrifugal pan work-ing life, obtains the centrifugally glass-wool that Fibre diameter is tiny; By changing output voltage and output frequency, the viscosity of glass melt can be regulated, obtains the centrifugally glass-wool of different Fibre diameter simultaneously.
Accompanying drawing explanation
Fig. 1 is structural representation of the present invention:
10 is molten bath;
20 is glass melt;
30 is bushing;
40 is platinum electrode slice;
50 is alternating source device;
60 is wire.
Embodiment
Below in conjunction with accompanying drawing, technical solution of the present invention is described in detail, but protection scope of the present invention is not limited to described embodiment.
Embodiment 1: a kind of device reducing bushing place, centrifugal cotton molten bath glass melt viscosity:
Device of the present invention, comprise molten bath 10, glass melt 20, bushing 30, platinum electrode slice 40, alternating source device 50, is characterized in that fixed placement two platinum electrode slices 40 above bushing, and electrode slice is by the external alternating source device of wire 60:
(1) molten bath is built into by electric fused zirconium corundum refractory brick;
(2) glass melt is from high temperature molten bath, front end, through fusing, homogenizing, clarifying treatment;
(3) bushing is by the platinum plate of central aperture, and opening diameter size is 2-5 centimetre;
(4) platinum electrode slice fixed placement is above bushing, by the external alternating source device of wire;
(5) alternating source device can regulation output voltage and output frequency, thus between two battery lead plates, form the alternating electric field of varying strength.
Embodiment 2: a kind of method reducing bushing place, centrifugal cotton molten bath glass melt viscosity, comprises the following steps:
(1) fixed placement two platinum electrode slices 40 above bushing 30, electrode slice is by the external alternating source device 50 of wire 60;
(2) close bushing 30, wait for that the glass melt 10 of front end high temperature melting, homogenizing and clarifying treatment is full of molten bath 20;
(3) open alternating source device 50, setting output voltage is 300V, and output frequency 1000Hz produces alternating electric field between two electrode slices;
After (4) five minutes, open bushing, glass melt is flowed out from bushing, enters the centrifugal pan of high speed rotating.
Claims (4)
1. one kind is reduced the method for bushing place, centrifugal cotton molten bath glass melt viscosity, comprise molten bath, glass melt, bushing, platinum electrode slice, alternating source device, it is characterized in that placing two platinum electrode slices above bushing, electrode slice, by the external alternating source device of wire, is realized by following steps:
(1) fixed placement two platinum electrode slices above bushing, electrode slice is by the external alternating source device of wire;
(2) close bushing, wait for that the glass melt of front end high temperature melting, homogenizing and clarifying treatment is full of molten bath;
(3) open alternating source device, setting output voltage and output frequency, produce alternating electric field between two electrode slices;
(4) after certain hour, open bushing, glass melt is flowed out from bushing, enters the centrifugal pan of high speed rotating.
2., according to method according to claim 1, it is characterized in that output voltage is 220-380V.
3., according to method according to claim 1, it is characterized in that output frequency is 50-5000Hz.
4., according to method according to claim 1, it is characterized in that certain hour is 5-10 minute.