CN103541120A - Method for weaving glass fiber screen cloth with density of 16 strands every 25 millimeters - Google Patents

Method for weaving glass fiber screen cloth with density of 16 strands every 25 millimeters Download PDF

Info

Publication number
CN103541120A
CN103541120A CN201310410807.8A CN201310410807A CN103541120A CN 103541120 A CN103541120 A CN 103541120A CN 201310410807 A CN201310410807 A CN 201310410807A CN 103541120 A CN103541120 A CN 103541120A
Authority
CN
China
Prior art keywords
warp
density
fell
doup
glass fiber
Prior art date
Application number
CN201310410807.8A
Other languages
Chinese (zh)
Inventor
刘源
李世英
房金旭
Original Assignee
陕西华特新材料股份有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 陕西华特新材料股份有限公司 filed Critical 陕西华特新材料股份有限公司
Priority to CN201310410807.8A priority Critical patent/CN103541120A/en
Publication of CN103541120A publication Critical patent/CN103541120A/en

Abstract

The invention discloses a method for weaving glass fiber screen cloth with the density of 16 stands every 25 millimeters. The high-density glass fiber screen cloth is woven by crossing warps and ground warps. According to a GA747 rapier loom opening device, auxiliary components such as a tension spring, a lease rod, a yarn guiding rod and a yarn distributing rod are used for enabling nylon heald to be vertically stirred, so that the weaving process of the crossing warps and the ground warps is accomplished. Through lifting of a warp stopping pattern rail, the warp position lines are changed, and therefore the loom-feeding technology satisfies the requirement for screen cloth production. Through the adjustment conducted on a rapier conveying box, the problem of hand-over time of weft rapier sending and weft rapier receiving conducted by a rapier head is solved. Starting from take-up of a GA747 rapier loom, the problem of weft density of the cloth face is solved through a multi-head worm and gear. According to the method for weaving the glass fiber screen cloth with the density of 16 strands every 25 millimeters, the weaving requirements for producing the high-density screen cloth are satisfied and the appearance quality of the product is improved to a large extent. Under the normal illuminance, visual inspection and straight steel ruler inspection are conducted, the defects of cracked ends and broken picks are avoided, the defects of loose warp and tight warp are avoided, the defects of broken holes are avoided, the defect of skipping are avoided, and warps and wefts deviate from the prior positions by smaller than 5mm.

Description

A kind of density is the weaving method of the glass fiber mesh of 16/25mm

Technical field

The present invention relates to fiberglass weaving field, specifically a kind of density is the weaving method of the glass fiber mesh of 16/25mm.

Background technology

At present glass fiber mesh weaving process all adopts the method for shaping after first plain weave, and it is larger that fabric construction stability is twisted woven fabric gap, be generally≤13/25mm of the density of woven glass fiber mesh.But have partial density≤13 piece/25mm glass fiber mesh to be weaved by traditional 1511 looms, this loom production efficiency is low, inconvenient operation, change yarn often, need a large amount of labours, fault rate high, fabric quality is poor.

Continuous expansion along with new material Application Areas, in many post processings and manufacture field, the requirement of the density of the requirement of the stability of screen cloth institutional framework and glass fiber mesh is improved, the plain weave screen cloth of prior art can not meet the high density screen cloth fabric technology requirement for industry of development.

Existing strand is knitted technology and mainly in Power-line technology field, textile industry, is generally applied.

A kind of high-density gridding gauze and production method thereof are disclosed in the innovation and creation that are CN101209545 at publication number.These innovation and creation are high-density griddings that silk weaving is made about terylene, with diamond dust or silicon carbide sand cementation surface, the high-density gridding gauze of formation.The method essence is the process of deep processing that the finished product of screen cloth is carried out, and does not describe the concrete weaving method of glass fiber mesh.

A kind of glass fibre knitted net is disclosed in the innovation and creation that are CN2272899 at publication number.It is stacked that these innovation and creation are mainly that every glass fibre in described warp thigh and every glass fibre in parallel thigh intermesh, and at the infall of warp thigh and parallel thigh, forms fabric structure, online coated with resins material.Glass fibre knitted net in this invention is intersecting to form by warp thigh and parallel thigh.And the woven high-density glass fiber mesh cloth of the present invention is to be casted off into through strand with ground by doup end, compares and there is no common ground with the present invention.

By retrieving patent documentation both domestic and external and paper database, not yet retrieve the weaving method of the glass fibre high density screen cloth identical with the present invention.Prior art cannot meet user the needs of the high product of density requirements are asked.

Summary of the invention

In order to overcome, the production efficiency existing in prior art is low, inconvenient operation, change yarn often, need a large amount of labours, fault rate high, the deficiency that fabric quality is poor, the present invention proposes the weaving method that a kind of density is the glass fiber mesh of 16/25mm.

Detailed process of the present invention is:

Step 1: spinning.Glass strand, through moving back solution, also twisting with the fingers, is spun into glass fiber yarn.

Step 2: warping.The glass fiber yarn obtaining is reeled in warp beam.

Step 3: pass.The glass fiber yarn being wound up in warp beam is through on reed.

Step 4: weave; According to the requirement of fabric, on GA747 Rapier looms, warp thread and weft yarn are interweaved, make the high density screen cloth fabric of desired structure.Woven process is:

When strand is knitted, first by a ground warp, form fell with a doup end, then form Yi Ge cellular organization with a weft yarn.When forming described fell, ground warp and doup end be with being through in a dent, and doup end, under the traction of flake, successively at the both-side opening of ground warp, and is bringd weft yarn into fell in.Flexing, twisting mutually between doup end and ground warp, thereby the Yi Ge cellular organization of formation high density screen cloth fabric.Constantly repeat described on ground through the process of both-side opening, until complete strand, knit.

When weft yarn is included fell in, by the latitude sword that send of Weaving-machine, a weft yarn is sent into fell, by the latitude sword that connects of Weaving-machine, the weft yarn of sending into fell is drawn to fell, complete a wefting insertion process.

In weaving, by GA747 Rapier looms, control the tension force of doup end and ground warp.Specifically, the upper tension roller in GA747 Rapier looms and the vertical range between lower tension roller are 150~200mm, and lower tension roller and back rest distance are 720~920mm, and lower tension roller and shed stick distance are 220~250mm.Lease rods, between the first heald frame and the second heald frame, and is fixed respectively a spring and a heald twine at the two ends of described lease rods, by described spring, realize the pulling force that this lease rods makes progress, and by described heald twine, is equilibrated at the pulling force that strand produces this lease rods in knitting.

Described fell be the wefting insertion passage between warp and doup end, the generation type of this fell is, when the second heald frame declines, flake is moved doup end to form second fell through the below of a side to through lease rods, drops into a weft yarn, after strand is knitted, the second heald frame rises, the first heald frame declines, and flake passes through again lease rods, by doup end move to through the below of opposite side, same second fell that forms, and drop into a weft yarn, and so continuous reciprocation cycle, doup end forms high density screen cloth fabric around ground through twisting to knit.

During described wefting insertion, send latitude sword and connect latitude sword and start simultaneously, described in to send the sword time of entering of latitude sword be 330 °~350 °, described in connect latitude sword the sword time of entering be 330 °~350 °.

The object of the invention is in order to solve the high requirement of user to high density screen cloth institutional framework stability aspect, by the adaptability reform of the global design of production technology and relevant device being reached to production high density strand knitmesh cloth, meet the active demand of market user to this product, fill up domestic high density screen cloth and produce blank.

The present invention utilizes GA747 rapier loom shedding motion, by installing the auxiliaries such as extension spring, lease rods, thread-carrier rod, yarn-distributing rod additional, nylon is to sum up stirred down, and the strand that completes doup end and ground warp is knitted process.By raising stop over flower hurdle, change through the position line, knitting technology is reached and meet the requirement that screen cloth is produced.For making to produce smoothly, by the adjusting to rapier transmission box, solved sword head and sent latitude sword and connect latitude sword handover time problem.From GA747 rapier loom, batch and start with, utilize bull worm and gear to solve cloth cover filling density problem.Above-mentioned technique, GA747 loom is transformed, made it meet the requirements of weaving process of production high density screen cloth.

With in the publication number innovation and creation that are CN2272899 disclosed by warp thigh and parallel thigh intersect to form glass fibre knitted net comparison, the woven high-density glass fiber mesh cloth of the present invention is through strand, to be casted off into ground by doup end.Testing identity, the woven high density screen cloth of the present invention fabric appearance quality has significantly lifting.Under normal light illumination, range estimation and straight steel ruler check, product of the present invention, without cracked ends, staplings fault, without loosening, tighten through fault, without broken hole fault, without skips fault, departs from below original position 5mm through weft yarn.

Table 1 is physical testing result of the present invention:

Table 1

After having weaved, according to Shaanxi Ward new material limited company company standard-alkali-free glass fibre filter net cloth, after being tested, this experiment finished fabric obtains sample specification and performance indications:

Table 2

Accompanying drawing explanation

Fig. 1 high density screen cloth process flow diagram

Fig. 2 is flow chart of the present invention.

Wherein:

1. the first heald frame 2. second heald frame 3 lease rods 4 shed stick 5 upper tension roller 6 lower tension rollers

The specific embodiment

Embodiment mono-

The present embodiment is the weaving method of EN16X16-92L high-density glass fiber mesh cloth.Adopt GA747 Rapier looms to weave, warp is through warp-feeding mechanism, tension mechanism, warp stop motion, leasing mechanism, shedding mechanism, then through wefting insertion, the formation fabric that beats up, then process spooler, rolling-up mechanism are rolled onto cloth on cloth beam, form cloth.After waste selvage yarn, by slitter edge mechanism, be sent to slitter edge storage bin.

The detailed process of the present embodiment is:

Step 1: spinning.Adopt conventional method, by glass strand, through moving back solution, also twisting with the fingers, being spun into warp thread is EC9.0-33 * 2S120, the glass fiber yarn that weft yarn is EC9.0-33 * 2 * 2S120.

Step 2: warping.Adopt conventional method, by EC9.0-33 * 2S120 glass fiber yarn, what be parallel to each other is wound up in warp beam.

Step 3: pass.Adopt conventional method, the EC9.0-33 * 2S120 glass fiber yarn being wound up in warp beam is through on reed according to the denting mode of technological requirement.

Step 4: weave; According to the requirement of fabric, on GA747 Rapier looms, warp thread and weft yarn are interweaved, make the high density screen cloth fabric of desired structure.Woven process is:

When strand is knitted, first by a ground warp, form fell with a doup end, then form Yi Ge cellular organization with a weft yarn.When forming described fell, ground warp and doup end be with being through in a dent, and doup end, under the traction of flake, successively at the both-side opening of ground warp, and is bringd weft yarn into fell in.Flexing, twisting mutually between doup end and ground warp, thereby the Yi Ge cellular organization of formation high density screen cloth fabric.Constantly repeat described on ground through the process of both-side opening, until complete strand, knit.

Described fell be the wefting insertion passage between warp and doup end, the generation type of this fell is, when the second heald frame declines, flake is moved doup end to form second fell through the below of a side to through lease rods, drops into a weft yarn, after strand is knitted, the second heald frame rises, the first heald frame declines, and flake passes through again lease rods, by doup end move to through the below of opposite side, same second fell that forms, and drop into a weft yarn, and so continuous reciprocation cycle, doup end forms high density screen cloth fabric around ground through twisting to knit.

During wefting insertion, by regulating rapier transmission box to determine the Filling Insertion Time that send latitude sword and connect latitude sword.Send latitude sword and connect latitude sword and start simultaneously, described in to send the sword time of entering of latitude sword be 330 °~350 °, described in connect latitude sword the sword time of entering be 330 °~350 °.In the present embodiment, sending the sword time of entering of latitude sword is 330 °, meets entering 330 ° of sword times of latitude sword.

In weaving, by GA747 Rapier looms, control the tension force of doup end and ground warp.Specifically, the upper tension roller in GA747 Rapier looms and the vertical range between lower tension roller are 150~200mm, and lower tension roller and back rest distance are 720~920mm, and lower tension roller and shed stick distance are 220~250mm.In the present embodiment, the upper tension roller in GA747 Rapier looms and the vertical range between lower tension roller are 150mm, and lower tension roller and back rest distance are 720mm, and lower tension roller and shed stick distance are 220mm.Lease rods, between the first heald frame and the second heald frame, and is fixed respectively a spring and a heald twine at the two ends of described lease rods, by described spring, realize the pulling force that this lease rods makes progress, and by described heald twine, is equilibrated at the pulling force that strand produces this lease rods in knitting.

Described spring is coiled into Ф 1.3mm steel wire.The diameter of this spring is 12mm, length 100mm, and density is 7.7 circles/10mm.

During strand is knitted, shed stick is coaxial with upper tension roller and lease rods.

The high-density glass fiber mesh cloth that the present embodiment is obtained carries out physical testing, and it is as shown in the table for its physical property.

Subordinate list:

High density screen cloth physical property

Project Unit Measured value Density Root/25mm 16 Width cm 92.5 Mass area ratio g/m 2 172 Combustible content % 1.1

Embodiment bis-

The present embodiment is the weaving method of EN16X16-92L high-density glass fiber mesh cloth.Adopt GA747 Rapier looms to weave, warp is through warp-feeding mechanism, tension mechanism, warp stop motion, leasing mechanism, shedding mechanism, then through wefting insertion, the formation fabric that beats up, then process spooler, rolling-up mechanism are rolled onto cloth on cloth beam, form cloth.After waste selvage yarn, by slitter edge mechanism, be sent to slitter edge storage bin.

The detailed process of the present embodiment is:

Step 1: spinning.Adopt conventional method, by glass strand, through moving back solution, also twisting with the fingers, being spun into warp thread is EC9.0-33 * 2S120, the glass fiber yarn that weft yarn is EC9.0-33 * 2 * 2S120.

Step 2: warping.Adopt conventional method, by EC9.0-33 * 2S120 glass fiber yarn, what be parallel to each other is wound up in warp beam.

Step 3: pass.Adopt conventional method, the EC9.0-33 * 2S120 glass fiber yarn being wound up in warp beam is through on reed according to the denting mode of technological requirement.

Step 4: weave; According to the requirement of fabric, on GA747 Rapier looms, warp thread and weft yarn are interweaved, make the high density screen cloth fabric of desired structure.Woven process is:

When strand is knitted, first by a ground warp, form fell with a doup end, then form Yi Ge cellular organization with a weft yarn.When forming described fell, ground warp and doup end be with being through in a dent, and doup end, under the traction of flake, successively at the both-side opening of ground warp, and is bringd weft yarn into fell in.Flexing, twisting mutually between doup end and ground warp, thereby the Yi Ge cellular organization of formation high density screen cloth fabric.Constantly repeat described on ground through the process of both-side opening, until complete strand, knit.

Described fell be the wefting insertion passage between warp and doup end, the generation type of this fell is, when the second heald frame declines, flake is moved doup end to form second fell through the below of a side to through lease rods, drops into a weft yarn, after strand is knitted, the second heald frame rises, the first heald frame declines, and flake passes through again lease rods, by doup end move to through the below of opposite side, same second fell that forms, and drop into a weft yarn, and so continuous reciprocation cycle, doup end forms high density screen cloth fabric around ground through twisting to knit.

During wefting insertion, by regulating rapier transmission box to determine the Filling Insertion Time that send latitude sword and connect latitude sword.Send latitude sword and connect latitude sword and start simultaneously, described in to send the sword time of entering of latitude sword be 330 °~350 °, described in connect latitude sword the sword time of entering be 330 °~350 °.In the present embodiment, sending the sword time of entering of latitude sword is 340 °, meets entering 340 ° of sword times of latitude sword.

In weaving, by GA747 Rapier looms, control the tension force of doup end and ground warp.Specifically, the upper tension roller in GA747 Rapier looms and the vertical range between lower tension roller are 150~200mm, and lower tension roller and back rest distance are 720~920mm, and lower tension roller and shed stick distance are 220~250mm.In the present embodiment, the upper tension roller in GA747 Rapier looms and the vertical range between lower tension roller are 175mm, and lower tension roller and back rest distance are 820mm, and lower tension roller and shed stick distance are 235mm.Lease rods, between the first heald frame and the second heald frame, and is fixed respectively a spring and a heald twine at the two ends of described lease rods, by described spring, realize the pulling force that this lease rods makes progress, and by described heald twine, is equilibrated at the pulling force that strand produces this lease rods in knitting.

Described spring is coiled into Ф 1.3mm steel wire.The diameter of this spring is 12mm, length 100mm, and density is 7.7 circles/10mm.

During strand is knitted, shed stick is coaxial with upper tension roller and lease rods.

The high-density glass fiber mesh cloth that the present embodiment is obtained carries out physical testing, and it is as shown in the table for its physical property.

Subordinate list:

High density screen cloth physical property

Project Unit Measured value Density Root/25mm 16 Width cm 100.5 Mass area ratio g/m 2 168 Combustible content % 1.1

Embodiment tri-

The present embodiment is the weaving method of EN16X16-102L high-density glass fiber mesh cloth.Adopt GA747 Rapier looms to weave, warp is through warp-feeding mechanism, tension mechanism, warp stop motion, leasing mechanism, shedding mechanism, then through wefting insertion, the formation fabric that beats up, then process spooler, rolling-up mechanism are rolled onto cloth on cloth beam, form cloth.After waste selvage yarn, by slitter edge mechanism, be sent to slitter edge storage bin.

The detailed process of the present embodiment is:

Step 1: spinning.Adopt conventional method, by glass strand, through moving back solution, also twisting with the fingers, being spun into warp thread is EC9.0-33 * 2S120, the glass fiber yarn that weft yarn is EC9.0-33 * 2 * 2S120.

Step 2: warping.Adopt conventional method, by EC9.0-33 * 2S120 glass fiber yarn, what be parallel to each other is wound up in warp beam.

Step 3: pass.Adopt conventional method, the EC9.0-33 * 2S120 glass fiber yarn being wound up in warp beam is through on reed according to the denting mode of technological requirement.

Step 4: weave; According to the requirement of fabric, on GA747 Rapier looms, warp thread and weft yarn are interweaved, make the high density screen cloth fabric of desired structure.Woven process is:

When strand is knitted, first by a ground warp, form fell with a doup end, then form Yi Ge cellular organization with a weft yarn.When forming described fell, ground warp and doup end be with being through in a dent, and doup end, under the traction of flake, successively at the both-side opening of ground warp, and is bringd weft yarn into fell in.Flexing, twisting mutually between doup end and ground warp, thereby the Yi Ge cellular organization of formation high density screen cloth fabric.Constantly repeat described on ground through the process of both-side opening, until complete strand, knit.

Described fell be the wefting insertion passage between warp and doup end, the generation type of this fell is, when the second heald frame declines, flake is moved doup end to form second fell through the below of a side to through lease rods, drops into a weft yarn, after strand is knitted, the second heald frame rises, the first heald frame declines, and flake passes through again lease rods, by doup end move to through the below of opposite side, same second fell that forms, and drop into a weft yarn, and so continuous reciprocation cycle, doup end forms high density screen cloth fabric around ground through twisting to knit.

During wefting insertion, by regulating rapier transmission box to determine the Filling Insertion Time that send latitude sword and connect latitude sword.Send latitude sword and connect latitude sword and start simultaneously, described in to send the sword time of entering of latitude sword be 330 °~350 °, described in connect latitude sword the sword time of entering be 330 °~350 °.In the present embodiment, sending the sword time of entering of latitude sword is 350 °, meets entering 350 ° of sword times of latitude sword.

In weaving, by GA747 Rapier looms, control the tension force of doup end and ground warp.Specifically, the upper tension roller in GA747 Rapier looms and the vertical range between lower tension roller are 150~200mm, and lower tension roller and back rest distance are 720~920mm, and lower tension roller and shed stick distance are 220~250mm.In the present embodiment, the upper tension roller in GA747 Rapier looms and the vertical range between lower tension roller are 200mm, and lower tension roller and back rest distance are 920mm, and lower tension roller and shed stick distance are 2500mm.Lease rods, between the first heald frame and the second heald frame, and is fixed respectively a spring and a heald twine at the two ends of described lease rods, by described spring, realize the pulling force that this lease rods makes progress, and by described heald twine, is equilibrated at the pulling force that strand produces this lease rods in knitting.

Described spring is coiled into Ф 1.3mm steel wire.The diameter of this spring is 12mm, length 100mm, and density is 7.7 circles/10mm.

During strand is knitted, shed stick is coaxial with upper tension roller and lease rods.

The high-density glass fiber mesh cloth that the present embodiment is obtained carries out physical testing, and it is as shown in the table for its physical property.

Subordinate list:

High density screen cloth physical property

Project Unit Measured value Density Root/25mm 16 Width cm 102.5 Mass area ratio g/m 2 179 Combustible content % 1.1

Claims (3)

1. a weaving method for high-density glass fiber mesh cloth, is characterized in that, detailed process is:
Step 1: spinning; Glass strand, through moving back solution, also twisting with the fingers, is spun into glass fiber yarn;
Step 2: warping; The glass fiber yarn obtaining is reeled in warp beam;
Step 3: pass; The glass fiber yarn being wound up in warp beam is through on reed;
Step 4: weave; According to the requirement of fabric, on GA747 Rapier looms, warp thread and weft yarn are interweaved, make the high density screen cloth fabric of desired structure; Woven process is:
When strand is knitted, first by a ground warp, form fell with a doup end, then form Yi Ge cellular organization with a weft yarn;
When forming described fell, ground warp and doup end be with being through in a dent, and doup end, under the traction of flake, successively at the both-side opening of ground warp, and is bringd weft yarn into fell in; Flexing, twisting mutually between doup end and ground warp, thereby the Yi Ge cellular organization of formation high density screen cloth fabric; Constantly repeat described on ground through the process of both-side opening, until complete strand, knit;
When weft yarn is included fell in, by the latitude sword that send of Weaving-machine, a weft yarn is sent into fell, by the latitude sword that connects of Weaving-machine, the weft yarn of sending into fell is drawn to fell, complete a wefting insertion process;
In weaving, by GA747 Rapier looms, control the tension force of doup end and ground warp; Specifically, the upper tension roller in GA747 Rapier looms and the vertical range between lower tension roller are 150~200mm, and ground is 720~920mm through lower tension roller and back rest distance, and ground is 220~250mm through lower tension roller and shed stick distance; Lease rods, between the first heald frame and the second heald frame, and is fixed respectively a spring and a heald twine at the two ends of described lease rods, by described spring, realize the pulling force that this lease rods makes progress, and by described heald twine, is equilibrated at the pulling force that strand produces this lease rods in knitting.
2. the weaving method of high-density glass fiber mesh cloth as claimed in claim 1, it is characterized in that, described fell be the wefting insertion passage between warp and doup end, the generation type of this fell is, when the second heald frame declines, flake is moved doup end to form second fell through the below of a side to through lease rods, drop into a weft yarn, after strand is knitted, the second heald frame rises, the first heald frame declines, flake passes through again lease rods, by doup end move to through the below of opposite side, same second fell that forms, and drop into a weft yarn, so continuous reciprocation cycle, doup end forms high density screen cloth fabric around ground through twisting to knit.
3. the weaving method of high-density glass fiber mesh cloth as claimed in claim 1, it is characterized in that, during described wefting insertion, send latitude sword and connect latitude sword to start simultaneously, it is described that to send the sword time of entering of latitude sword be 330 °~350 °, described in connect latitude sword the sword time of entering be 330 °~350 °.
CN201310410807.8A 2013-09-10 2013-09-10 Method for weaving glass fiber screen cloth with density of 16 strands every 25 millimeters CN103541120A (en)