CN103537695A - 一种粉末冶金气门座圈及其制备方法 - Google Patents

一种粉末冶金气门座圈及其制备方法 Download PDF

Info

Publication number
CN103537695A
CN103537695A CN201310472218.2A CN201310472218A CN103537695A CN 103537695 A CN103537695 A CN 103537695A CN 201310472218 A CN201310472218 A CN 201310472218A CN 103537695 A CN103537695 A CN 103537695A
Authority
CN
China
Prior art keywords
powder
valve seat
sintering
under
hour
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310472218.2A
Other languages
English (en)
Inventor
黄浩
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuhu Hongkun Auto Parts Co Ltd
Original Assignee
Wuhu Hongkun Auto Parts Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuhu Hongkun Auto Parts Co Ltd filed Critical Wuhu Hongkun Auto Parts Co Ltd
Priority to CN201310472218.2A priority Critical patent/CN103537695A/zh
Publication of CN103537695A publication Critical patent/CN103537695A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种粉末冶金气门座圈，其特征在于，由下列重量份的原料制成：镍14.0-14.5、铬12.0-12.5、钼1.0-1.5、石墨0.3-0.5、钴3.2-3.5、铁粉74.5-75.5、Mn3.3-3.5、Mg6.4-6.8、Zn2.0-2.3、助剂2-3；本发明针对传统的气门座圈耐高温性能差、很容易发生氧化、其产品使用时磨损大而且价格高的问题，采用了镍、铬、钼、钴等金属材料制作，该产品合金扩散充分，抗氧化程度高，提高了强度与硬度，改善其耐磨性，有效提高了耐高温性。

Description

一种粉末冶金气门座圈及其制备方法
技术领域
本发明涉及粉末冶金领域，特别是一种粉末冶金气门座圈及其制备方法。
背景技术
粉末冶金是制取金属粉末或用金属粉末(或金属粉末与非金属粉末的混合物)作为原料，经过成形和烧结，制取金属材料、复合材料以及各种类型制品的工业技术。目前，粉末冶金技术已被广泛应用于交通、机械、电子、航空航天、兵器、生物、新能源、信息和核工业等领域，成为新材料科学中最具发展活力的分支之一。粉末冶金技术具备显著节能、省材、性能优异、产品精度高且稳定性好等一系列优点，非常适合于大批量生产。另外，部分用传统铸造方法和机械加工方法无法制备的材料和复杂零件也可用粉末冶金技术制造，因而备受工业界的重视。粉末冶金结构件制品材料成分不受熔炼限制，既可以加入合金成分，也可以加入其它结构组分，并且在相当大的范围内根据要求进行调整，进而在力学性能上能达到与钢件匹配的效果。
粉末冶金机械化程度高，既能减少人员，又能提高效率，进而节约成本。粉末冶金技术能取代传统的制造工艺，为广大传统企业节约成本。
所以研究各种机械零部件的粉末冶金的配方，适应不同的需要，具有重要的意义。
发明内容
本发明的目的是提供一种粉末冶金气门座圈及其制备方法。
为了实现本发明的目的，本发明通过以下方案实施：
一种粉末冶金气门座圈，由下列重量份的原料制成：镍14.0-14.5、铬12.0-12.5、钼1.0-1.5、石墨0.3-0.5、钴3.2-3.5、铁粉74.5-75.5、Mn3.3-3.5、Mg 6.4-6.8、Zn 2.0-2.3、助剂2-3；
所述的助剂由下列重量份的原料制成：铁粉30-34、氢氧化铝2-3、硫酸锌1-2、麦饭石1-2、纳米碳1-2、玉石2-3、聚异丁烯2-3、铝酸酯偶联剂DL-411 1-2、碳化硅粉2-3；制备方法是将铁粉、氢氧化铝、硫酸锌、麦饭石混合，研磨成200-300目粉末，然后加入铝酸酯偶联剂DL-411混合均匀，在10-15Mpa下压制成坯料，然后，送入920-950℃下煅烧3-4小时，冷却后，粉碎成300-400目粉末，与其它剩余成分混合，加热至60-70℃，在1200-1500转/分下搅拌1-2小时，即得。
本发明所述粉末冶金气门座圈，由以下具体步骤制成：
（1）将镍、铬、钼、钴、Mn、Mg、Zn铁粉混合，加入适量水中，送入球磨机中球磨，得到250-400目粉末，然后，喷雾干燥、烘干，在8-10Mpa压力下压制成块状，然后在氮气保护气氛下600-650℃进行烧结8-10小时，将烧结后的物料粉碎后过200-400目筛；
（2）将其它剩余成分混合均匀；
（3）将步骤（1）、（2）物料在55-65℃下混合搅拌均匀65-85分钟后，装入模具，压制成坯；
（4）将压坯放在烧结炉中，以6-8℃/分钟速率升温至800-850℃条件下烧结1.5-2小时;然后以5-7℃/分钟速率升温至1100-1150℃条件下烧结2-3小时；再以8-12℃/分钟速率降温至450-550℃条件下烧结1-2小时，最后空气中冷却至室温即可。
本发明针对传统的气门座圈耐高温性能差、很容易发生氧化、其产品使用时磨损大而且价格高的问题，采用了镍、铬、钼、钴等金属材料制作，该产品合金扩散充分，抗氧化程度高，提高了强度与硬度，改善其耐磨性，有效提高了耐高温性。
具体实施方案
下面通过具体实例对本发明进行详细说明。
一种粉末冶金气门座圈，由下列重量份(公斤)的原料制成：镍14.0、铬12.0、钼1.0、石墨0.3、钴3.2、铁粉74.5、Mn3.3、Mg 6.4、Zn 2.0、助剂2；
所述的助剂由下列重量份（公斤）的原料制成：铁粉30、氢氧化铝2、硫酸锌1、麦饭石1、纳米碳1、玉石2、聚异丁烯2、铝酸酯偶联剂DL-411 1、碳化硅粉2；制备方法是将铁粉、氢氧化铝、硫酸锌、麦饭石混合，研磨成200-300目粉末，然后加入铝酸酯偶联剂DL-411混合均匀，在10-15Mpa下压制成坯料，然后，送入920-950℃下煅烧3-4小时，冷却后，粉碎成300-400目粉末，与其它剩余成分混合，加热至60-70℃，在1200-1500转/分下搅拌1-2小时，即得。
本发明所述粉末冶金气门座圈，由以下具体步骤制成：
（1）将镍、铬、钼、钴、Mn、Mg、Zn铁粉混合，加入适量水中，送入球磨机中球磨，得到250-400目粉末，然后，喷雾干燥、烘干，在8-10Mpa压力下压制成块状，然后在氮气保护气氛下600-650℃进行烧结8-10小时，将烧结后的物料粉碎后过200-400目筛；
（2）将其它剩余成分混合均匀；
（3）将步骤（1）、（2）物料在55-65℃下混合搅拌均匀65-85分钟后，装入模具，压制成坯；
（4）将压坯放在烧结炉中，以6-8℃/分钟速率升温至800-850℃条件下烧结1.5-2小时;然后以5-7℃/分钟速率升温至1100-1150℃条件下烧结2-3小时；再以8-12℃/分钟速率降温至450-550℃条件下烧结1-2小时，最后空气中冷却至室温即可。
经过检测，本发明的硬度：HRC68；抗拉强度：860MPa 。

Claims (2)

1.一种粉末冶金气门座圈，其特征在于，由下列重量份的原料制成：镍14.0-14.5、铬12.0-12.5、钼1.0-1.5、石墨0.3-0.5、钴3.2-3.5、铁粉74.5-75.5、Mn3.3-3.5、Mg 6.4-6.8、Zn 2.0-2.3、助剂2-3；
所述的助剂由下列重量份的原料制成：铁粉30-34、氢氧化铝2-3、硫酸锌1-2、麦饭石1-2、纳米碳1-2、玉石2-3、聚异丁烯2-3、铝酸酯偶联剂DL-411 1-2、碳化硅粉2-3；制备方法是将铁粉、氢氧化铝、硫酸锌、麦饭石混合，研磨成200-300目粉末，然后加入铝酸酯偶联剂DL-411混合均匀，在10-15Mpa下压制成坯料，然后，送入920-950℃下煅烧3-4小时，冷却后，粉碎成300-400目粉末，与其它剩余成分混合，加热至60-70℃，在1200-1500转/分下搅拌1-2小时，即得。
2.根据权利要求1所述粉末冶金气门座圈，其特征在于，由以下具体步骤制成：
（1）将镍、铬、钼、钴、Mn、Mg、Zn铁粉混合，加入适量水中，送入球磨机中球磨，得到250-400目粉末，然后，喷雾干燥、烘干，在8-10Mpa压力下压制成块状，然后在氮气保护气氛下600-650℃进行烧结8-10小时，将烧结后的物料粉碎后过200-400目筛；
（2）将其它剩余成分混合均匀；
（3）将步骤（1）、（2）物料在55-65℃下混合搅拌均匀65-85分钟后，装入模具，压制成坯；
（4）将压坯放在烧结炉中，以6-8℃/分钟速率升温至800-850℃条件下烧结1.5-2小时;然后以5-7℃/分钟速率升温至1100-1150℃条件下烧结2-3小时；再以8-12℃/分钟速率降温至450-550℃条件下烧结1-2小时，最后空气中冷却至室温即可。
CN201310472218.2A 2013-10-11 2013-10-11 一种粉末冶金气门座圈及其制备方法 Pending CN103537695A (zh)