CN103525081A - Material used for steel lining instead of PVC (polyvinyl chloride) profile - Google Patents
Material used for steel lining instead of PVC (polyvinyl chloride) profile Download PDFInfo
- Publication number
- CN103525081A CN103525081A CN201310478231.9A CN201310478231A CN103525081A CN 103525081 A CN103525081 A CN 103525081A CN 201310478231 A CN201310478231 A CN 201310478231A CN 103525081 A CN103525081 A CN 103525081A
- Authority
- CN
- China
- Prior art keywords
- pvc
- parts
- steel lining
- profile
- present
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a material used for a steel lining instead of a PVC (polyvinyl chloride) profile. The material comprises the following components in parts by weight: 50-60 parts of nylon, 40-50 parts of glass fibers, 1-5 parts of chlorinated polyethylene and 1-5 parts of polyethylene wax. A preparation process of the material comprises the steps of mixing the prepared components, stirring the components uniformly and carrying out granulating and packaging. The material is novel in conception, standard in process, high in cost performance and simple and convenient to operate. Compared with the existing PVC standard samples, the steel lining material has tensile strength 4.65 times that of the PVC standard samples and notch impact strength 3.78 times that of the PVC standard samples through detection, which shows that the material has better reinforcing and toughening effects than those of the PVC profile. The material disclosed by the invention can be industrially produced in batches and can be widely used in the field of processing of plastic materials.
Description
Technical field
The present invention relates to a kind ofly for plastic material, particularly relate to the material that a kind of alternative PVC section bar steel lining is used.
Background technology
Up to now, the PVC(polyvinyl chloride circulating on existing market) physicals of section bar is poor, and tensile strength is lower, shock strength a little less than, cost performance is not high, is difficult to meet consumer demand, how to improve the Performance and quality of section bar product, this is the problem that the present invention will study.
Summary of the invention
The object of the invention is, in order to overcome the defect of above-mentioned background technology, through contriver, to concentrate on studies, repetition test, in order to improve cost performance and the quality of polychloroethylene section bar, and the material that provides a kind of alternative PVC section bar steel lining to use.
The technical scheme of the material that to achieve these goals, alternative PVC section bar steel lining of the present invention is used is such:
Material of the present invention comprises following component and weight part: nylon (PA) 50～60; Glass fibre (MTF) 40～50; Chlorinatedpolyethylene (CPE) 1～5; Polyethylene wax 1～5.
Material of the present invention comprises following component and weight part: nylon (PA) 55～60; Glass fibre (MTF) 45～50; Chlorinatedpolyethylene (CPE) 2～4; Polyethylene wax 2～4.
Material of the present invention comprises following component and weight part: nylon (PA) 52; Glass fibre (MTF) 42; Chlorinatedpolyethylene (CPE) 3; Polyethylene wax 3.
The material that alternative PVC section bar steel lining of the present invention is used has following beneficial effect: novel, technological specification, easy and simple to handle, cost performance is high; Detect contrast with existing PVC standard: steel lining material tensile strength is that 148Mpa, PVC standard are 31.85Mpa, and steel lining material tensile strength is 4.65 times of PVC standard; Notched Izod impact strength steel lining material is 12.3KT/m
2, PVC standard is 3.25KT/m
2, steel lining material notched Izod impact strength is 3.78 times of PVC standard, this shows that material of the present invention has the toughness reinforcing effect of better enhancing than PVC section bar.The present invention can be widely used in the fields such as chemical industry, plastics and building materials.
Embodiment
Below in conjunction with embodiment, the present invention is described in further detail, but this embodiment should not be construed as limitation of the present invention.
Embodiment 1
The material that alternative PVC section bar steel lining of the present invention is used is prepared by following processing sequence:
1, get nylon (PA) 50; Glass fibre (MTF) 48; Chlorinatedpolyethylene (CPE) 1; Polyethylene wax 1, standby.
2, batch mixing: above-mentioned each ingredients weight parts preparing is mixed, drop into together stirrer for mixing and stir, stir at normal temperatures and shut down standby in 15 minutes.
2, granulation packing: the above-mentioned batch mixing processing is dropped in tablets press, starts shooting and within 5 minutes, shut down discharging, granular material, packing.
Embodiment 2
The present embodiment is substantially the same manner as Example 1, and its difference is:
1, get nylon (PA) 52; Glass fibre (MTF) 44; Chlorinatedpolyethylene (CPE) 2; Polyethylene wax 2, standby.
Embodiment 3
The present embodiment is substantially the same manner as Example 1, and its difference is:
1, get nylon (PA) 52; Glass fibre (MTF) 42; Chlorinatedpolyethylene (CPE) 3; Polyethylene wax 3, standby.
Embodiment 4
The present embodiment is substantially the same manner as Example 1, and its difference is:
1, get nylon (PA) 52; Glass fibre (MTF) 40; Chlorinatedpolyethylene (CPE) 4; Polyethylene wax 4, standby.
Embodiment 5
The present embodiment is substantially the same manner as Example 1, and its difference is:
1, get nylon (PA) 50; Glass fibre (MTF) 40; Chlorinatedpolyethylene (CPE) 5; Polyethylene wax 5, standby.
Obviously, those skilled in the art can carry out various changes and variation and not depart from the spirit and scope of the present invention the present invention.Like this, if within these modifications and variations of the present invention belong to the scope of the claims in the present invention and equivalent technologies thereof, the present invention is also intended to comprise these changes and change interior.
The content not being described in detail in this specification sheets belongs to the known prior art of professional and technical personnel in the field.
Claims (3)
1. the material that alternative PVC section bar steel lining is used, is characterized in that: described material comprises following component and weight part:
Nylon 50～60; Glass fibre 40～50; Chlorinatedpolyethylene 1～5; Polyethylene wax 1～5.
2. the material that alternative PVC section bar steel lining according to claim 1 is used, is characterized in that: described material comprises following component and weight part:
Nylon 55～60; Glass fibre 45～50; Chlorinatedpolyethylene 2～4; Polyethylene wax 2～4.
3. the material that alternative PVC section bar steel lining according to claim 2 is used, is characterized in that: described material comprises following component and weight part:
Nylon 52; Glass fibre 42; Chlorinatedpolyethylene 3; Polyethylene wax 3.