CN103522610A - High-strength composite material and preparation method thereof - Google Patents
High-strength composite material and preparation method thereof Download PDFInfo
- Publication number
- CN103522610A CN103522610A CN201210227006.3A CN201210227006A CN103522610A CN 103522610 A CN103522610 A CN 103522610A CN 201210227006 A CN201210227006 A CN 201210227006A CN 103522610 A CN103522610 A CN 103522610A
- Authority
- CN
- China
- Prior art keywords
- layer
- strength composite
- oxford
- high strength
- vmpet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a high-strength composite material which is sequentially composed of an oxford fabric, a VMPET (vacuum metalized polyethylene terephthalate) layer and an EPE (expand aple poly ephylene) layer from outside to inside. Compared with the prior art, the high-strength composite material has the advantages of high strength, long service life, favorable sealability, low price and wide application range, can be used for carrying and packaging larger objects without damage, and can be used for manufacturing shopping bags, insulating bags, packaging bags, shopping baskets and the like. The preparation method is simple and can implement industrial production.
Description
Technical field
The present invention relates to a kind of material, specifically relate to a kind of high strength composite.
Background technology
Along with growth in the living standard, people require also more and more higher to the material of daily necessities, common material can not meet people's demand, for example, people in supermarket, food market is while buying food, be generally to use common shopping bag (material is nonwoven) or polybag, its function only limits to carrying and packs a small amount of article.If the thing of buying is heavier or have harder corner angle, common shopping bag or polybag are easily bad in the process of transporting, and cannot continue to use.In addition, when buying frozen foods, be generally to use common shopping bag, its function only limits to loading and packing, transports in process and easily makes frozen food dissolve, and impact is edible.
Summary of the invention
Goal of the invention: in order to solve the deficiencies in the prior art, the invention provides a kind of long service life, the high strength composite that sealing is strong.
The present invention also provides the method for preparing above-mentioned high strength composite.
Technical scheme: in order to realize above object, high strength composite of the present invention, this composite ecto-entad is comprised of oxford, VMPET layer and EPE layer successively.
Preferably, described oxford top layer is printed with pattern.
Preferably, the thickness of described oxford is that the thickness of 0.3～0.6mm, VMPET layer is 10～20um, and the thickness of EPE layer is 0.6～2mm.
A method of preparing high strength composite, comprises the steps:
1, by VMPET layer and EPE layer, in temperature, be to carry out pressing under 150～250 ℃ of conditions;
2, oxford is sutured in to the surface of VMPET layer, makes high strength composite.
Wherein, as preferably, the oxford described in step 2, before stitching, is printed on it pattern.
Beneficial effect: the present invention compared with prior art has the following advantages: intensity is high, can be used for carrying and packs relatively large article and can not damage long service life, good airproof performance, cheap, the scope of application is extensive, can be used for making shopping bag, insulated bag, packaging bag, shopping basket etc.Preparation method of the present invention is simple, can realize suitability for industrialized production.
The specific embodiment
Below in conjunction with specific embodiment, further illustrate the present invention, should understand these embodiment is only not used in and limits the scope of the invention for the present invention is described, after having read the present invention, those skilled in the art all fall within the application's claims limited range to various equivalents of the present invention or modification.
Embodiment 1:
, this composite ecto-entad is comprised of oxford, VMPET layer and EPE layer successively, on described oxford top layer, is printed with pattern.The thickness of described oxford is that the thickness of 0.4mm, VMPET layer is 15um, and the thickness of EPE layer is 1.3mm.
The preparation method of above-mentioned high strength composite, comprises the steps:
1, by VMPET layer and EPE layer, in temperature, be to carry out pressing under 150～250 ℃ of conditions;
2, pattern is printed on to oxford surface, then the bottom surface of oxford is sutured in to the surface of VMPET layer, make high strength composite.
Embodiment 2:
, this composite ecto-entad is comprised of oxford, VMPET layer and EPE layer successively.The thickness of described oxford is that the thickness of 0.3mm, VMPET layer is 10um, and the thickness of EPE layer is 0.6mm.
The preparation method of above-mentioned high strength composite, comprises the steps:
1, by VMPET layer and EPE layer, in temperature, be to carry out pressing under 150～250 ℃ of conditions;
2, the bottom surface of oxford is sutured in to the surface of VMPET layer, makes high strength composite.
Embodiment 3:
, this composite ecto-entad is comprised of oxford, VMPET layer and EPE layer successively, on described oxford top layer, is printed with pattern.The thickness of described oxford is that the thickness of 0.6mm, VMPET layer is 20um, and the thickness of EPE layer is 2mm.
The preparation method of above-mentioned high strength composite, comprises the steps:
1, by VMPET layer and EPE layer, in temperature, be to carry out pressing under 150～250 ℃ of conditions;
2, pattern is printed on to oxford surface, then the bottom surface of oxford is sutured in to the surface of VMPET layer, make high strength composite.
Claims (5)
1. a high strength composite, is characterized in that: this composite ecto-entad is comprised of oxford, VMPET layer and EPE layer successively.
2. high strength composite according to claim 1, is characterized in that: described oxford top layer is printed with pattern.
3. high strength composite according to claim 1 and 2, is characterized in that: the thickness of described oxford is that the thickness of 0.3～0.6mm, VMPET layer is 10～20um, and the thickness of EPE layer is 0.6～2mm.
4. a method of preparing high strength composite claimed in claim 1, is characterized in that: comprise the steps:
(1) by VMPET layer and EPE layer, in temperature, be to carry out pressing under 150～250 ℃ of conditions;
(2) oxford is sutured in to the surface of VMPET layer, makes high strength composite.
5. the preparation method of high strength composite according to claim 4, is characterized in that: the oxford described in step (2), before stitching, is printed on it pattern.