CN103522605B - Novel composite template, manufacturing method and board manufactured through composite template - Google Patents
Novel composite template, manufacturing method and board manufactured through composite template Download PDFInfo
- Publication number
- CN103522605B CN103522605B CN201310535522.7A CN201310535522A CN103522605B CN 103522605 B CN103522605 B CN 103522605B CN 201310535522 A CN201310535522 A CN 201310535522A CN 103522605 B CN103522605 B CN 103522605B
- Authority
- CN
- China
- Prior art keywords
- rubber
- plastic
- board
- substrate
- base plate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a novel composite template, a board manufactured through the template and a production method of the board. The novel composite template comprises a base plate and rubber and plastic cladding layers, and further comprises rubber and plastic connecting columns and/or rubber and plastic connecting pieces. Through holes are formed in the base plate and/or oblique grooves which form a certain angle with the horizontal face of the base plate are formed in the base plate. The rubber and plastic connecting columns are arranged in the through holes of the base plate in a penetrating mode and/or the rubber and plastic connecting pieces are filled into the oblique grooves. The rubber and plastic cladding layers are tightly attached to the upper surface of the base plate and the lower surface of the base plate and form an integrated structure with the rubber and plastic connecting columns in the through holes and/or the rubber and plastic connecting pieces in the oblique grooves. According to the novel composite template, through a new processing measure and method, a surface rubber and plastic material is made to be attached to the surface layer of the base plate firmly so as to prevent the base plate from being invaded by moisture and humidity, the phenomena of delaminating and stripping are overcome, the strength, the rigidity and the friction resistance are enhanced, the service life is prolonged and the decoration effect is improved.
Description
Technical field
The present invention relates to building, furniture, car and boat field, the sheet material that is specifically related to a kind of Novel composite mouldboard, manufacture method and makes.Be applicable to the fields such as compartment board, dividing plate, clamping plate, kitchen guarding's furniture-plates, decorative panel, floor such as building template, door and window auxiliary frame plate, light wall board, automobile, motor-car, steamer.
Background technology
At present, in building industry, furniture manufacturing industry, car and boat industry and advertising field, organic board comparatively conventional on market is: solid wood board, bamboo matter, wooden plywood, wood particle board, wound card and in high fiberboard and foamed board.These sheet materials are mostly used as the substrate of composite board above, and plate surface needs film, the sheet top layer of compound one deck and even multilayer unlike material, play protection and decoration function.Yet because substrate is not identical with Surface sheet matter physical property, especially thermal linear expansion coefficient difference causes delamination and peels off, and greatly reduces its weatherability and service life.And current existing artificial board exists mostly, and bending resistance and tensile strength are not enough, rigidity not, cannot be waterproof and dampproof, the series of problems such as preponderance, this is current problem demanding prompt solution.
The present invention is intended to by new manufacturing process and method, make top layer rubber-plastics material very firmly to prevent substrate, be subject to the invasion of moisture and moisture in adhesive substrates top layer, overcome delamination and peeling, gain in strength, rigidity and wearability, improve service life, decorative effect.
Summary of the invention
One of object of the present invention is in order to overcome people's mold board or sheet material the deficiencies in the prior art, provides a kind of when improving intensity, rigidity and solving wood-based plate waterproof, moistureproof problem, reduces the composite shuttering of integrated cost.
A kind of Novel composite mouldboard of the present invention, it comprises substrate, rubber and plastic coating layer, it is characterized in that: it also comprises that rubber and plastic connects post and/or rubber and plastic in flakes;
Described substrate is provided with through hole and/or has the skewed slot of certain angle with substrate horizontal plane;
Described rubber and plastic connects post in the through hole of described substrate; And/or
Rubber and plastic is filled in skewed slot in flakes;
Described rubber and plastic coating layer respectively close adhesion the upper and lower surface of described substrate and with described through hole in rubber and plastic connect post and/or skewed slot in rubber and plastic form in flakes integrative-structure.
A kind of Novel composite mouldboard of the present invention, rubber and plastic coating layer is connected post and/or is had the rubber and plastic of certain angle tightly bonding with substrate in flakes with substrate horizontal plane by a plurality of rubber and plastics that are integrated with it, substrate provides the basic bearing capacity of composite board, and the rubber and plastic coating layer on surface and the rubber and plastic of the One's name is legion that is connected connects post and rubber and plastic has been strengthened its intensity and rigidity in flakes greatly, rivet and clamping plate have been played, substrate is not easy to crack, significant prolongation its service life.In addition, in the occasion for building template, select hydrophobicity rubber and plastic as template surface layer, without using releasing agent to get final product the demoulding, both can reduce costs, solved again the pollution problem of releasing agent to environment.
The present invention is with substrate surface the skewed slot of certain angle, and described skewed slot is monomer groove and/or dovetail groove.When hot melt or thermosets being bonded in to substrate surface by the form of the pressurization of heating, penetrate in the skewed slot of substrate certain depth.In top layer and groove, material is identical and be connected.The angle of preferred skewed slot and substrate horizontal plane is 45～135 °, and the width of skewed slot is: 1～5mm, the degree of depth is: 2～20mm.Every adjacent two each self-reversals of incline direction of this skewed slot, become upper and lower splayed configuration.According to mechanics principle, cause top layer to be pulled on substrate firmly.Can not peel off and delamination.The peeling force of composite board while having digested variations in temperature, the service life of greatly improving sheet material.Optimized its cost performance.There is far-reaching Social benefit and economic benefit.
Preferably, described through hole is one or more in cylindrical hole, cylindroid hole, tetragonal prism sky, rectangular post sky, cruciform vent, L shaped hole, described through hole is one or more (as shown in Figure 3) in the above-mentioned shape of array arrangement, illustrated through hole has further increased the sectional area that rubber and plastic connects post, improved its rivet force, the size of its concrete size and sectional area, depending on engineering design to composite board specification requirement; When described through hole is cylindrical hole, the diameter that described rubber and plastic connects post is preferably 5～15mm.
Preferably, the distance that adjacent two described rubber and plastics connect post is 10～100mm, size and the layout density in substrate that rubber and plastic reasonable in design connects post can guarantee that composite board has reliable intensity and rigidity, guarantee excellent bearing capacity, if rubber and plastic connects post, excessive, too intensive increasing made man-hour and material cost; If rubber and plastic connects too small, the too sparse insufficient strength that causes composite board of post, frangibility or press-bending, riveted effect reduces simultaneously, and can not be guaranteed service life.
Preferably, the thickness of described rubber and plastic composite bed is 1～6mm, not wear-resisting if thickness is crossed the thin top layer as composite board, and blocked up weight is excessive, simultaneously high cost; The thickness of described composite shuttering is 10～100mm, causes the increase of cost and weight if blocked up, and preponderance is used inconvenience, if cross the thin bearing capacity that whole composite board provides, cannot meet quality requirement.Be applied to, in the situation of energy-conservation, heat insulation, heat-insulation wall plate, cross thin heat insulation effect not good.
Preferably, described substrate be wood wool board, bamboo filament plate, glued board, finger circuit board, wood fibre board, wood particle board, particieboard, stalk board, fireproof heat insulating foamed board and paper honeycomb board,, plastic honeycomb central layer or aluminium matter honeycomb core plate, the substrate of above-mentioned material has basic bearing capacity, and cost is relatively cheap, market ample supply and prompt delivery.
The present invention, according to Novel composite mouldboard described above, also provides the composite board being made by above-mentioned Novel composite mouldboard.Template of the present invention comprises building template wood wool board, bamboo filament plate, glued board, finger circuit board, wood fibre board, wood particle board, particieboard, stalk board, fireproof heat insulating foamed board, paper honeycomb board, plastic honeycomb central layer or aluminium matter honeycomb core plate.Composite board of the present invention also comprises building template wood wool board, bamboo filament plate, glued board, finger circuit board, wood fibre board, wood particle board, particieboard, stalk board, fireproof heat insulating foamed board, paper honeycomb board, plastic honeycomb central layer or aluminium matter honeycomb core plate.Deng above all kinds of sheet material, be the finished product sheet material that substrate adopts novel processing 2 techniques to make.
The manufacture method that the invention provides a kind of above-mentioned Novel composite mouldboard, comprises the following steps:
(1) on substrate, bore the through hole being completely arranged in array, the upper and lower surface of substrate is carried out to the processing of sanding plucking, to increase substrate surface roughness, to be combined thereafter close and firm more with rubber and plastic coating layer; ;
(2) rubber slurry in container is heated to 120-280 ℃;
(3) in the slurries that substrate immersion melted in heat, flood, until rubber and plastic melts through hole and/or skewed slot that body is fully filled substrate, and the upper and lower surface of wrapping up substrate completely;
(4) sheet material is sent from rubber slurry, through tank, given cooling 2-5min, make the sclerosis of rubber and plastic coating layer surface skining;
(5) by conveyer belt, send sheet material to surge suppressor cold moudling; Surge suppressor can be used the cold press of 50～100t, makes rubber and plastic coating layer and rubber and plastic connect post and fully condenses, and be closely integrated into integral body with substrate;
(6) by the plate cutting after moulding, and finished product is put to obtain in check in storage.
The manufacturing process that the invention provides the above-mentioned Novel composite mouldboard of the second, comprises the following steps:
(1) on substrate, output many skewed slots, the incline direction of every adjacent two skewed slots is reverse between two, becomes positive and negative Eight characters shape, and the upper and lower surface of substrate is carried out to the processing of sanding plucking;
(2) by conveyer belt, template is carried out to the coated extrusion molding of surperficial coating and injection moulding moulding or surface;
(3) by the plate cutting after moulding, and finished product is put to obtain in check in storage.
The sheet material being made by above-mentioned template also prepares with reference to said method.
Further, described rubber slurry comprises that described rubber slurry comprises one or more in PP plastics, PE plastics, PET plastics, PS plastics, ABS plastic, PVC plastics, EVA elastomer, nitrile rubber, butadiene-styrene rubber, pitch.Described rubber slurry can also contain colloid, the resin of wear-resistant materials such as being added with alundum (Al2O3) and/or melamine and/or hyaline-quartz powder.Particularly PP, PE, PET plastics are non-polar material, embody extremely strong hydrophobic character, be applied to building template, after theing cement solidifies, this rubber and plastic surface layer can not stick with xoncrete structure, therefore can make building template and building element separate easily without releasing agent when the demoulding.Building template top layer rubber and plastic also can be by the fire-retardant 1 grade standard design of GB, to eliminate building-site disaster hidden-trouble.
Further, when step (3) concora crush, remain that the upper and lower surface of sheet material has water, play effect cooling, lubricated and that be not stained with machine; In order to keep plate surface to have all the time water, the water flowing of cold press pressing plate is cooling, can reduce the temperature of substrate surface rubber and plastic, to improve work efficiency, guarantees composite board surface smoothness and fineness.
Further, according to the specification requirement of different product, step (2) can select to adopt foaming or without the rubber slurry of foaming; In the situation that cellular board is substrate, adopt the rubber slurry not foaming, to guarantee rigidity and the intensity of whole sheet material as far as possible; In the situation that selecting the solid substrate such as glued board, wood wool board, select micro-foamed rubber-plastic slurries as far as possible, after cooling skinning, use, make substrate top layer there is certain elasticity, increase service life.
Preferably, when described substrate is paper honeycomb board or aluminium matter honeycomb core plate, in step (1), do not carry out plucking processing, because honeycomb core plate is hollow, cannot plucking, so in step (1), do not carry out plucking processing.
The present invention compared with prior art, has following technical advantage:
1, the oblique sheet of rubber and plastic that the rubber and plastic coating layer of substrate upper and lower surface of the present invention connects in post or skewed slot by the rubber and plastic in substrate through-hole is pressed on intermediate layer by substrate, a plurality of rubber and plastics that are structure as a whole with rubber and plastic coating layer connect post and can produce the powerful rivet force just as rivet, and substrate is riveted tightly and between rubber and plastic surface layer, formed the whole robust construction of composite board; In skewed slot, the oblique sheet of rubber and plastic is connected and meets mechanics principle with top layer.
2, the invention solves composite board and be applied to need the problem easily occurring when waterproof and dampproof, substrate is coated by rubber and plastic material, and isolated substrate and extraneous contacting are not perishable, can not be out of shape, and lightweight, intensity is reliable, good processability.Particularly the present invention is applied to the occasion of building template, and be the more than 10 times of common bamboo wood building formwork service life, and the life cycle of common building template is 1～3 time, and building template of the present invention can reach more than 30 times;
3, need be to building template nail in when construction, nail can directly be beaten on the wooden structures of substrate through rubber and plastic coating layer, has solved that metal, plastics and Bamboo Formwork are difficultly constructed, the problem of nailing difficulty;
4, demolding performace is splendid, without apply releasing agent on template surface, can easily template be taken out from building structure, greatly improve efficiency of construction, save time, material and construction cost, guarantee that surface of concrete structure is smooth bright and clean, cost performance is high, has wide market prospects; Also solved the problem of environmental pollution of conventional template use releasing agent.
5, this building template is after finishing its service life, due to the surface cement that do not bond, its material itself is to consist of rubber and plastic, wood fibre or aluminium foil simultaneously, can equally with other composite boards carry out after fragmentation be wood mould with plastic-aluminum in first-class raw material, can all reclaim, not producing any building waste discarded object, is typical low-carbon (LC), environmental protection, economic item capable of circulation.Reclaiming raw material, cost-effective while, can reduce a certain proportion of sale price.Also be the marketing bright spot opening up a market.
Accompanying drawing explanation
The overall structure schematic diagram that Fig. 1, Fig. 5, Fig. 8 are one embodiment of the present of invention;
Fig. 2, Fig. 6 are the structural representation of substrate of the present invention;
Fig. 3 is the substrate shape schematic diagram that the present invention is provided with through hole;
Fig. 4 is the flow chart of a kind of manufacturing method of plate thereof of the present invention;
Fig. 7 is the generalized section of embodiment 4 novel composite floors;
Fig. 9 is the flow chart of the another kind of manufacturing method of plate thereof of the present invention.
The specific embodiment
Below technical solution of the present invention is elaborated, but protection scope of the present invention is not limited to described embodiment.
Embodiment 1: a kind of NEW TYPE OF COMPOSITE building template
A kind of NEW TYPE OF COMPOSITE building template, as shown in Figure 1, 2, comprise that substrate 1, rubber and plastic connect post 2 and rubber and plastic coating layer 3, on substrate 1, have cylindrical hole 4, rubber and plastic connects post 2 in the through hole 4 of substrate 1, rubber and plastic coating layer 3 is coated on upper and lower surface and substrate 1 close adhesion of substrate 1, and connects post 2 formation integrative-structures with rubber and plastic; The diameter that rubber and plastic connects post 2 is 6mm, and the distance that adjacent two rubber and plastics connect post 2 is 50mm, and the thickness of rubber and plastic coating layer 3 is 1mm, and building template gross thickness is 10mm.In the present embodiment, substrate 1 is selected wooden plywood.
By the manufacture method of above-mentioned NEW TYPE OF COMPOSITE building template, as shown in Figure 3, comprise the following steps:
(1) on substrate 1, drill through hole 4, with thick abrasive-belt sand-light machine by wooden plywood's upper and lower surface sanding plucking;
(2) the rubber slurry formula batch mixing that carries out as shown in table 1, is increased to the temperature of rubber slurry in 235～280 ℃ of PP that do not foam, PE rubber slurry that substrate 1 are immersed in to melting;
Table 1 formula 1 (according to the mass fraction)
(3) substrate 1 is immersed in the rubber slurry of melting and floods, until wrap up respectively and be filled with rubber and plastic in the surface of substrate 1 and through hole 4, melt body;
(4) sheet material is sent from rubber slurry, through tank, given cooling 5min, reach surface skining;
(5) by conveyer belt, send sheet material the cold moudling of to 100t spreader bar, remain that the upper and lower surface of sheet material has water while colding pressing, cooling down makes template sizing, guarantees not to be stained with machine simultaneously;
(6) cut into required size, detect and put to obtain finished product in storage.
The bearing capacity of the building template being obtained by the present embodiment can reach 1.96N/mm
2(higher than rower [JGJ162-2008]), template quality is light, be only 680kg/m3, maximum deformation value is only 1/1200 of template span, visible, this building template has enough bearing capacitys, rigidity and stability, can carry reliably the dynamic load producing in concrete weight and pressure and work progress, and resistance to capsizing is strong; Can not adhere to building element, without realizing effective demoulding by mechanical external force, dismounting speed is fast, effectively the reduction of erection time; Meanwhile, simple and reasonable, easy accessibility, reusable 40 times.
If substrate 1 selects particieboard, wood fibre board, wood wool board, bamboo filament plate etc. can reach basic similar technology effect.
Embodiment 2: the fire-retardant ash wall body plate of a kind of energy-saving heat preserving
As shown in Figure 1, 2, comprise that substrate 1, rubber and plastic connect post 2 and rubber and plastic coating layer 3, have cylindroid through hole 4 on substrate 1, rubber and plastic connects post 2 in the through hole 4 of substrate 1, upper and lower surface and substrate 1 that rubber and plastic coating layer 3 is coated on substrate 1 fit tightly, and form integrative-structure with rubber and plastic post 2; Concrete, substrate 1 is selected phenolic foam warming plate.Through hole is the cross through hole of width 8mm.The distance of adjacent two rubber and plastic posts 2 is 100mm.The thickness of rubber and plastic coating layer 3 is 6mm.The thickness of composite board is 100mm.Rubber slurry selects the CPVC plastics of micro-foaming to make.Rubber slurry formula is as shown in table 2, the present embodiment preparation method is with reference to embodiment 1, but the temperature of step in manufacture method (1) rubber slurry is increased to 120～160 ℃, the maximum temperature of PVC plastics can not be for a long time over 160 ℃, otherwise can be burnt, step (4) is through the cooling 3min of tank.The plastics that the present embodiment is used are PVC.Belong to macromolecule polar material.This composite board can be used for doing the fire-retardant ash wall body plate of energy-saving heat preserving, heat-insulating roof board.Surface printing, the color fastness of spraying is fabulous.Range of application is wide, and market prospects are considerable.
Table 2 formula 2 (according to the mass fraction)
Embodiment 3: a kind of NEW TYPE OF COMPOSITE lightweight bulkhead
As shown in Figure 1, 2, comprise that substrate 1, rubber and plastic connect post 2 and rubber and plastic coating layer 3, have cylindrical hole 4 on substrate 1, rubber and plastic connects post 2 in the through hole 4 of substrate 1, upper and lower surface and substrate 1 that rubber and plastic coating layer 3 is coated on substrate 1 fit tightly, and form integrative-structure with rubber and plastic post 2; Concrete, the diameter that rubber and plastic connects post 2 is 8mm, and the distance between the oval center of circle is that the lateral separation of adjacent two the rubber and plastic posts 2 of 10mm is 10mm, and fore-and-aft distance is 10mm, and the thickness of rubber and plastic coating layer 3 is 6mm, composite board gross thickness is 26mm.In the present embodiment, substrate 1 is selected moistureproof paper honeycombed sheet, the brown paper that honeycomb paper core is 350g, and aperture is 6mm.
The manufacture method of above-mentioned NEW TYPE OF COMPOSITE lightweight bulkhead, as shown in Figure 3, comprises the following steps:
(1) on substrate 1, bore array through hole 4,
(2) the rubber slurry formula batch mixing that carries out as shown in table 2, is immersed in substrate 1 in the PE rubber slurry of micro-foaming of melting, and the temperature of rubber slurry is increased to 150～180 ℃;
Table 3 formula 3 (according to the mass fraction)
(3) substrate 1 is immersed in the rubber slurry of melting and floods, until wrap up respectively and be filled with plastics melt in the surface of substrate 1 and through hole 4;
(4) sheet material is sent from rubber slurry, through tank, given cooling 3min, reach surface skining;
(5) by conveyer belt, send sheet material the cold moudling of to 60t spreader bar, remain that the upper and lower surface of sheet material has water while colding pressing, cooling down makes template sizing, guarantees not to be stained with machine, surface smoothing simultaneously;
(6) cut into required size, detect warehouse-in.
The bearing capacity of the composite board being obtained by the present embodiment can reach 1.26N/mm
2, board quality is 360kg/m
3, visible, under the condition fully meeting the demands at rigidity, intensity and bearing capacity, weight only has 1/2nd of common solid wood board.And cost is lower.Cost performance is very superior.Because the Intermediate substrate of this composite board is hollow sheeting.Can be widely used in furniture-plates, kitchen tools plate and ash wall body plate, roof boarding and dividing plate, ceiling for car and boat.
If substrate 1 aluminium matter cellular board can reach similar technology effect, its bearing capacity is stronger, longer service life.
Embodiment 4: a kind of novel composite floor
As shown in Fig. 6,7,8, comprise substrate 1, the upper and lower oblique sheet 5 of rubber and plastic and rubber and plastic coating layer 3.On substrate 1, have skewed slot 6.The oblique sheet 5 of rubber and plastic is in each skewed slot 6 of substrate 1.Upper and lower surface and substrate 1 that plastics coating layer 3 is coated on substrate 1 fit tightly, and form integrative-structure with the oblique sheet 5 of rubber and plastic; Concrete, the thickness of the oblique sheet 5 of rubber and plastic is 2mm, the distance between adjacent two skewed slots is 12mm; The degree of depth of rubber and plastic skewed slot 6 is 3mm, 60 ° and 120 ° of the angles of skewed slot 6 and floor.The thickness of rubber and plastic coating layer 3 is 1.5mm, and composite floor board gross thickness is 15mm.In the present embodiment, substrate 1 is selected MDF, and density is chosen to be 780KG/m3
The manufacture method of above-mentioned novel composite floor, as shown in Figure 9, comprises the following steps:
First, on substrate, output many skewed slots on 1, the incline direction of every adjacent two skewed slots 6 is reverse between two, becomes positive and negative Eight characters shape.Angle angle is: 60 ° and 120 °.
Secondly, the upper and lower surface of substrate 1 is carried out to the processing of sanding plucking;
Finally, by conveyer belt, send sheet material to extrusion molding production line mould and carry out the coated extrusion molding in surface; Or carry out surperficial coating and injection moulding moulding.(referring to Fig. 9) production equipment is: the plastic extrusion production line or the injection moulding production line that dispose coated plank mould.
Table 4 formula 4 (according to the mass fraction)
The composite floor board being obtained by the present embodiment has solved the difficult problem that the macromolecular material such as PVC, PP, PE is up to now unfit to do indoor floor.Its main cause is that the linear temperature coefficient of expansion of above macromolecular material is excessive.Can play drum summer, can ftracture winter.And expanding with heat and contract with cold of the wood-based plates such as MDF, glued board is little.Substantially there is not this problem.But non-watertight, non-moistureproof, easily delamination, Yi Mei is rotten.By this invention technology.The outer surface of these substrates is by moulding rubber and plastic coating.Securely together with base plate bonding.Effectively protected substrate.Without putrefaction is indeformable.Visible, not only solved the problem that material expands with heat and contract with cold.And aspect rigidity, intensity and bearing capacity, playing the effect of reinforcement, and product longer service life, cost is lower, and cost performance is very superior.
As mentioned above, although represented and explained the present invention with reference to specific preferred embodiment, it shall not be construed as the restriction to the present invention self.Not departing under the spirit and scope of the present invention prerequisite of claims definition, can make in the form and details various variations to it.Such as embodiment 1 (or embodiment 2, embodiment 3) adopts the structure of embodiment 4 and method, make composite shuttering or sheet material, also belong to protection scope of the present invention; Such as embodiment 4 adopt embodiment 1 structure and method make composite board, also should be understood to belong to protection scope of the present invention.
Claims (4)
1. a composite shuttering, it comprises substrate and rubber and plastic coating layer, wherein, described composite shuttering also comprises rubber and plastic in flakes;
Described substrate is provided with many skewed slots that have certain angle with substrate horizontal plane, and wherein, described skewed slot is monomer groove, described angle is 60 ° and 120 °, and the incline direction of every adjacent two skewed slots is reverse between two, becomes positive and negative Eight characters shape, the width of described skewed slot is 1～5mm, and the degree of depth is 2～20mm;
Described rubber and plastic is filled in skewed slot in flakes;
Described rubber and plastic coating layer respectively close adhesion the upper and lower surface of described substrate and with described skewed slot in rubber and plastic form in flakes integrative-structure,
Wherein, the thickness of described rubber and plastic coating layer is 1～6mm, and the thickness of described composite shuttering is 10～100mm;
Described substrate is one or more in wood wool board, bamboo filament plate, glued board, finger circuit board, wood fibre board, wood particle board, particieboard, stalk board, foamed board, fireproof heated board, paper honeycomb board, plastic honeycomb central layer and aluminium matter honeycomb core plate.
2. the composite board that composite shuttering according to claim 1 makes.
3. a manufacture method for composite shuttering claimed in claim 1, the method comprises the following steps:
(1) on substrate, output many skewed slots, the incline direction of every adjacent two skewed slots is reverse between two, becomes positive and negative Eight characters shape, and the upper and lower surface of substrate is carried out to the processing of sanding plucking;
(2) template by conveyer belt and after using rubber slurry to above-mentioned plucking processing is carried out the coated extrusion molding of surperficial coating and injection moulding moulding or surface;
(3) by the plate cutting after moulding, and finished product is put to obtain in check in storage.
4. the manufacture method of composite board according to claim 3, wherein, described rubber slurry comprises one or more in PP plastics, PE plastics, PET plastics, PS plastics, ABS plastic, PVC plastics, EVA elastomer, nitrile rubber, butadiene-styrene rubber and pitch.