CN103481696A - 一种抗刮高韧性pvc热转印膜及其制备方法 - Google Patents

一种抗刮高韧性pvc热转印膜及其制备方法 Download PDF

Info

Publication number
CN103481696A
CN103481696A CN201310455111.7A CN201310455111A CN103481696A CN 103481696 A CN103481696 A CN 103481696A CN 201310455111 A CN201310455111 A CN 201310455111A CN 103481696 A CN103481696 A CN 103481696A
Authority
CN
China
Prior art keywords
heat transfer
transfer film
parts
scratch
mould release
Prior art date
Application number
CN201310455111.7A
Other languages
English (en)
Inventor
王向东
Original Assignee
太仓市鸿运包装材料有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 太仓市鸿运包装材料有限公司 filed Critical 太仓市鸿运包装材料有限公司
Priority to CN201310455111.7A priority Critical patent/CN103481696A/zh
Publication of CN103481696A publication Critical patent/CN103481696A/zh

Abstract

本发明公开了一种抗刮高韧性PVC热转印膜,包括基底层、离型层、印刷层、胶黏层构成,所述离型层采用复合离型剂涂布而成,所述复合离型剂按重量份数主要由以下原料制成:丙烯酸树脂30~60份、A-603液体增韧剂10~30份、抗刮助剂5~10份、乙酸乙基苷酯醇3~5份、甲苯50~100份。本发明还公开了该热转印膜的制备方法。本发明的一种抗刮高韧性PVC热转印,采用复合离型剂涂布得到离型剂层,其中通过加入加入抗刮助剂为微晶蜡或Nano-R 1003而获得更好的抗刮性能,得到的离型剂用于热转印膜的制备工艺中,使得热热转印膜具备防刮高韧性的功能,可以用于热转印、光学、广告制图等领域。

Description

—种抗刮高韧性PVC热转印膜及其制备方法
技术领域
[0001] 本发明属于高分子材料技术领域,具体涉及一种抗刮高韧性PVC热转印膜及其制备方法。
背景技术
[0002] 热转印膜是耐湿、不透气、柔软、强度大、耐酸碱油脂和溶剂、对高低温均不怕的极性材料。目前市面上生产的热转移膜由于添加的离型剂容易产生膜间的粘连,而且不能重复使用。
[0003] 离型剂是一种具有离型性、成膜性和粘合性的低粘度的透明树脂,因为离型剂中溶剂挥发速度较快,所以在涂布过程中,要注意控制粘度,即控制离型剂的固含量,固含量一般控制在23%左右,若固含量低于19%,涂布离型剂后的热转印膜转印效果不理想。同时注意离型剂的透明性,不然会影响印刷层的效果。目前的热转印膜由于没有抗紫外线功能,因此容易老化,使用寿命短。PVC薄膜耐腐蚀、绝缘性好。当目前用pvc薄膜制备的热转印膜因为韧性差,极易撕裂,而且抗刮效果差。
发明内容
[0004] 发明目的:针对上述问题,本发明的第一个目的是提供一种抗刮高韧性PVC热转印膜。本发明的第二个目的是提供该热转印膜的制备方法。
[0005] 技术方案:为了解决上述技术问题,本发明提供一种抗刮高韧性PVC热转印膜,包括基底层、离型层、印刷层、胶黏层构成,所述离型层采用复合离型剂涂布而成,所述复合离型剂按重量份数主要由以下原料制成:丙烯酸树脂30飞0份、A-603液体增韧剂10-30份、抗刮助剂5~10份、乙酸乙基苷酯醇3飞份、甲苯50-100份。
[0006] 抗刮助剂为微晶蜡或Nano-R 1003。Nano-R 1003购买于昆山卡斯特高分子材料
有限公司。
[0007] 上述复合离型剂的制备方法,包括以下步骤:
1)称取上述重量份数的原料;
2)将丙烯酸树脂溶解于有机溶剂中,同时加入增韧剂、抗刮助剂、乙酸乙基苷酯醇,以520"600rpm/min 转速搅拌 3(T60min,并在 12(Tl30°C下加热;
3)停止加热,继续搅拌2(T30min直至温度降低至常温出料即得到复合离型剂。
[0008] 一种抗刮高韧性PVC热转印膜的制备方法,包括以下步骤:将所述复合离型剂涂布在15μ以上的PVC薄膜上,印刷图文得到印刷层,待印刷层完全干燥后,涂布胶黏层,涂布后进行烘干即得到热转印膜。
[0009] 所述复合离型剂中固含量为15~17%,网纹辊160-200目,涂布干量为O. 8~1· Og/
m2o
[0010] 有益效果:本发明的一种抗刮高韧性PVC热转印,采用复合离型剂涂布得到离型剂层,其中通过加入加入抗刮助剂为微晶蜡或Nano-R 1003而获得更好的抗刮性能,得到的离型剂用于热转印膜的制备工艺中,使得热热转印膜具备防刮高韧性的功能,可以用于热转印、光学、广告制图等领域。
具体实施方式
[0011] 根据下述实施例,可以更好地理解本发明。然而,本领域的技术人员容易理解,实施例所描述的具体的物料配比仅用于说明本发明,而不应当也不会限制权利要求书中所详细描述的本发明。
[0012] 实施例I
一种抗刮高韧性PVC热转印膜,包括基底层、离型层、印刷层、胶黏层构成,所述离型层采用复合离型剂涂布而成,所述复合离型剂按重量份数主要由以下原料制成:丙烯酸树脂30份、A-603液体增韧剂10份、微晶蜡5份、乙酸乙基苷酯醇3份、甲苯50份。
[0013] 上述复合离型剂的制备方法,包括以下步骤:
1)称取上述重量份数的原料;
2)将丙烯酸树脂溶解于有机溶剂中,同时加入A-603液体增韧剂、微晶蜡、乙酸乙基苷酯醇,以520rpm/min转速搅拌30min,并在120°C下加热;
3)停止加热,继续搅拌2(T30min直至温度降低至常温出料即得到复合离型剂。
[0014] 抗刮高韧性PVC热转印膜的制备方法,包括以下步骤:将所述复合离型剂涂布在15 μ以上的PVC薄膜上,印刷图文得到印刷层,待印刷层完全干燥后,涂布胶黏层,涂布后进行烘干即得到热转印膜。所述复合离型剂中固含量为15%,网纹辊160目,涂布干量为O. 8g/m2。
[0015] 将上述离型剂用于制备PVC热转印膜,测得的性能参数结果:其中1~4项为离型剂的性能参数,其中5飞为PVC热转印膜具备的性能参数
Figure CN103481696AD00041
实施例2
一种抗刮高韧性PVC热转印膜,包括基底层、离型层、印刷层、胶黏层构成,所述离型层采用复合离型剂涂布而成,所述复合离型剂按重量份数主要由以下原料制成:丙烯酸树脂60份、A-603液体增韧剂30份、Nano-R 1003 10份、乙酸乙基苷酯醇5份、甲苯100份。
[0016] 复合离型剂的制备方法,包括以下步骤:
1)称取上述重量份数的原料;
2)将丙烯酸树脂溶解于有机溶剂中,同时加入A-603液体增韧剂、Nano-R 1003、乙酸乙基苷酯醇,以600rpm/min转速搅拌60min,并在130°C下加热;
3)停止加热,继续搅拌30min直至温度降低至常温出料即得到复合离型剂。
[0017] 一种抗刮高韧性PVC热转印膜的制备方法,包括以下步骤:将复合离型剂涂布在15 μ以上的PVC薄膜上,印刷图文得到印刷层,待印刷层完全干燥后,涂布胶黏层,涂布后进行烘干即得到热转印膜。复合离型剂中固含量为17%,网纹辊200目,涂布干量为1.0g/m2o
[0018] 将离型剂用于制备PVC热转印膜,测得的性能参数结果:其中1-4项为离型剂的性
能参数,其中5飞为PVC热转印膜具备的性能参数:
Figure CN103481696AD00051
实施例3
一种抗刮高韧性PVC热转印膜,包括基底层、离型层、印刷层、胶黏层构成,所述离型层采用复合离型剂涂布而成,所述复合离型剂按重量份数主要由以下原料制成:丙烯酸树脂45份、A-603液体增韧剂20份、Nano-R 1003 7份、乙酸乙基苷酯醇4份、甲苯75份。
[0019] 上述复合离型剂的制备方法,包括以下步骤:
1)称取上述重量份数的原料;
2)将丙烯酸树脂溶解于有机溶剂中,同时加入A-603液体增韧剂、微晶蜡或Nano-R1003、乙酸乙基苷酯醇,以560rpm/min转速搅拌45min,并在125°C下加热;
3)停止加热,继续搅拌25min直至温度降低至常温出料即得到复合离型剂。
[0020] 一种抗刮高韧性PVC热转印膜的制备方法,包括以下步骤:将所述复合离型剂涂
布在15μ以上的PVC薄膜上,印刷图文得到印刷层,待印刷层完全干燥后,涂布胶黏层,涂
布后进行烘干即得到热转印膜。所述复合离型剂中固含量为16%,网纹辊180目,涂布干量
为O. 9g/m2。将上述离型剂用于制备PVC热转印膜,测得的性能参数结果:其中f 4项为离
型剂的性能参数,其中5飞为PVC热转印膜具备的性能参数
Figure CN103481696AD00052

Claims (4)

1. 一种抗刮高韧性PVC热转印膜,包括基底层、离型层、印刷层、胶黏层构成,其特征在于,所述离型层采用复合离型剂涂布而成,所述复合离型剂按重量份数主要由以下原料制成:丙烯酸树脂30-60份、Α-603液体增韧剂10-30份、抗刮助剂5~10份、乙酸乙基苷酯醇3~5份、甲苯50~100份。
2.根据权利要求1所述的一种抗刮高韧性PVC热转印膜,抗刮助剂为微晶蜡或Nano-R1003。
3.权利要求1或2任一项所述的一种抗刮高韧性PVC热转印膜的制备方法,其特征在于,包括以下步骤:将所述复合离型剂涂布在15μ以上的PVC薄膜上,印刷图文得到印刷层,待印刷层完全干燥后,涂布胶黏层,涂布后进行烘干即得到热转印膜。
4.根据权利要求4所述的一种抗刮高韧性PVC热转印膜的制备方法,其特征在于,所述复合离型剂中固含量为15~17%,网纹辊160-200目,涂布干量为O. 8^1. Og/m2。
CN201310455111.7A 2013-09-29 2013-09-29 一种抗刮高韧性pvc热转印膜及其制备方法 CN103481696A (zh)