CN103467008A - Aerated concrete block added with bamboo carbon powder - Google Patents
Aerated concrete block added with bamboo carbon powder Download PDFInfo
- Publication number
- CN103467008A CN103467008A CN2013103359505A CN201310335950A CN103467008A CN 103467008 A CN103467008 A CN 103467008A CN 2013103359505 A CN2013103359505 A CN 2013103359505A CN 201310335950 A CN201310335950 A CN 201310335950A CN 103467008 A CN103467008 A CN 103467008A
- Authority
- CN
- China
- Prior art keywords
- parts
- bamboo carbon
- carbon powder
- building block
- calcium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to an aerated concrete block added with bamboo carbon powder. The aerated concrete block added with the bamboo carbon powder is prepared by the following raw materials by weight: 5-7 parts of the bamboo carbon powder, ash 10-15 parts of fly ash, 16-22 parts of cement, 8-10 parts of gypsum, 2-4 parts of rice husk carbon, 0.2-0.4 part of acrylic fibers, 0.4-0.6 part of organosilicone emulsion, 3-5 parts of a sugar-calcium water reducing agent, 3-5 parts of aluminum magnesium metasilicate, 0.001-0.003 part of polyisobutylene succinimide, 0.002-0.004 part of tripolyglycerol diisopstearate, 0.002-0.003 part of isomeric alcohol polyoxyethylene ether, 0.002-0.004 part of coconut oil fatty acid diethanolamide, 1-2 parts of polyester fibers, 8-12 parts of modified attapulgite, 0.001-0.003 part of sugar calcium, 0.002-0.003 part of calcium formate, 0.02-0.06 part of aluminum powder and 0.01-0.03 part of oxidized paraffin soap.
Description
Technical field
The present invention relates to the aerated bricks field, is exactly a kind of air-entrained concrete building block that adds bamboo carbon powder.
Background technology
Aerated bricks is the air-entrained concrete building block of producing by the autoclave at high temperature apparatus and process." aerated bricks " can be understood as a simplification or a general title.Its product scope contained should more greatly, adopt the brick product of other various explained hereafter that comprise steam pressure.
Construction market materials for wall used was mainly common brick in the past, and present many advanced areas have been completely forbidden common brick and used.
Existing aerated bricks Development Technology is slow, can't meet the market requirement of diversification.
Summary of the invention
The object of the present invention is to provide a kind of air-entrained concrete building block that adds bamboo carbon powder.
Above-mentioned purpose realizes by following scheme:
A kind of air-entrained concrete building block that adds bamboo carbon powder, it is characterized in that: it is that raw material by following weight parts makes: bamboo carbon powder 5-7, flyash 10-15, cement 16-22, gypsum 8-10, rice hull carbon 2-4, acrylic fiber 0.2-0.4, organic silicon emulsion 0.4-0.6, sugar calcium water reducer 3-5, metasilicic acid magnalium 0.3-0.5, polyisobutenyl succimide 0.001-0.003, three Polyglycerine diisopstearate 0.002-0.004, isomery polyoxyethylenated alcohol 0.002-0.003, cocoanut fatty acid diethanolamide 0.002-0.004, trevira 1-2, attapulgite modified 8-12, sugar calcium 0.001-0.003, calcium formiate 0.002-0.003, aluminium powder 0.02-0.06, oxidized paraffin wax soap 0.01-0.03,
Described attapulgite modified preparation method is: attapulgite is calcined under 900-1000 ℃ to 1-2 hour, cool to 700-800 ℃ of insulation 1-2 hour, grind, cross the 100-200 mesh sieve, then add the ethoxylated dodecyl alcohol that is equivalent to its weight 0.5-1.2%, the triethanolamine oleate of 0.1-0.5%, the aluminium nitride of 0.1-0.2% and appropriate water, under 40-42 ℃, stir after 10-15 minute, take out, dry, obtain.
Described a kind of air-entrained concrete building block that adds bamboo carbon powder is characterized in that:
The preparation method is:
(1) get by weight bamboo carbon powder, then soak 10-15 hour in the hydrochloric acid soln that is 10-15% in concentration, take out,
Deionized water wash, dry, and crosses the 100-200 mesh sieve, obtains the modified bamboo powdered carbon standby;
(2) modified bamboo carbon dust, flyash, cement, gypsum, organic silicon emulsion, sugared calcium water reducer, metasilicic acid magnalium are mixed by weight, stir 15-18 minute under 70-80 rev/min, take out, after mixing with the whole raw materials of residue and suitable quantity of water again, join in the double-shaft horizontal stirring tank, 200-300 rev/min is at the uniform velocity stirred 20-30 minute, again by the moulding that pours into the mold for material be stirred, after at 40-50 ℃ of lower precuring 3-5 hour, the demoulding, handling to cutting part cuts, and obtains the building block base;
(3) the building block base is put into to the reactor steam press maintenance, put finished product in storage and get final product.
Beneficial effect of the present invention is: the present invention has added bamboo carbon powder, has increased porosity of the present invention, has good water-reduction when reducing unit weight.
Embodiment
A kind of air-entrained concrete building block that adds bamboo carbon powder, it is that raw material by following weight parts (kg) makes: bamboo carbon powder 7, flyash 15, cement 17, gypsum 8, rice hull carbon 3, acrylic fiber 0.4, organic silicon emulsion 0.5, sugar calcium water reducer 5, metasilicic acid magnalium 0.3, polyisobutenyl succimide 0.003, three Polyglycerine diisopstearates 0.004, isomery polyoxyethylenated alcohol 0.003, cocoanut fatty acid diethanolamide 0.004, trevira 2, attapulgite modified 12, sugared calcium 0.003, calcium formiate 0.003, aluminium powder 0.04, oxidized paraffin wax soap 0.03;
Described attapulgite modified preparation method is: attapulgite is calcined 2 hours under 900 ℃, cool to 800 ℃ of insulations 1 hour, grind, cross 100 mesh sieves, then add the ethoxylated dodecyl alcohol that is equivalent to its weight 0.8%, 0.5% triethanolamine oleate, 0.2% aluminium nitride and appropriate water, under 42 ℃, stir after 15 minutes, take out, dry, obtain.
Described a kind of air-entrained concrete building block that adds bamboo carbon powder, the preparation method is:
(1) get by weight bamboo carbon powder, then soak 12 hours in the hydrochloric acid soln that is 12% in concentration, take out,
Deionized water wash, dry, and crosses 100 mesh sieves, obtains the modified bamboo powdered carbon standby;
(2) modified bamboo carbon dust, flyash, cement, gypsum, organic silicon emulsion, sugared calcium water reducer, metasilicic acid magnalium are mixed by weight, under 70 rev/mins, stir 15 minutes, take out, then, after mixing with the whole raw materials of residue and suitable quantity of water, join in the double-shaft horizontal stirring tank, 300 rev/mins are at the uniform velocity stirred 30 minutes, again by the moulding that pours into the mold for material be stirred, after in 47 ℃ of lower precuring 5 hours, the demoulding, handling to cutting part cuts, and obtains the building block base;
(3) the building block base is put into to the reactor steam press maintenance, put finished product in storage and get final product.
The average unit weight of this building block is 600-650kg/m
3, good heat insulating, have a large amount of pores and micropore in building block inside, thereby good thermal and insulating performance, mean value ultimate compression strength are arranged is 8.7MPa.
Claims (2)
1. an air-entrained concrete building block that adds bamboo carbon powder, it is characterized in that: it is that raw material by following weight parts makes: bamboo carbon powder 5-7, flyash 10-15, cement 16-22, gypsum 8-10, rice hull carbon 2-4, acrylic fiber 0.2-0.4, organic silicon emulsion 0.4-0.6, sugar calcium water reducer 3-5, metasilicic acid magnalium 0.3-0.5, polyisobutenyl succimide 0.001-0.003, three Polyglycerine diisopstearate 0.002-0.004, isomery polyoxyethylenated alcohol 0.002-0.003, cocoanut fatty acid diethanolamide 0.002-0.004, trevira 1-2, attapulgite modified 8-12, sugar calcium 0.001-0.003, calcium formiate 0.002-0.003, aluminium powder 0.02-0.06, oxidized paraffin wax soap 0.01-0.03,
Described attapulgite modified preparation method is: attapulgite is calcined under 900-1000 ℃ to 1-2 hour, cool to 700-800 ℃ of insulation 1-2 hour, grind, cross the 100-200 mesh sieve, then add the ethoxylated dodecyl alcohol that is equivalent to its weight 0.5-1.2%, the triethanolamine oleate of 0.1-0.5%, the aluminium nitride of 0.1-0.2% and appropriate water, under 40-42 ℃, stir after 10-15 minute, take out, dry, obtain.
2. a kind of air-entrained concrete building block that adds bamboo carbon powder according to claim 1 is characterized in that:
The preparation method is:
(1) get by weight bamboo carbon powder, then soak 10-15 hour in the hydrochloric acid soln that is 10-15% in concentration, take out, deionized water wash, dry, and crosses the 100-200 mesh sieve, obtains the modified bamboo powdered carbon standby;
(2) modified bamboo carbon dust, flyash, cement, gypsum, organic silicon emulsion, sugared calcium water reducer, metasilicic acid magnalium are mixed by weight, stir 15-18 minute under 70-80 rev/min, take out, after mixing with the whole raw materials of residue and suitable quantity of water again, join in the double-shaft horizontal stirring tank, 200-300 rev/min is at the uniform velocity stirred 20-30 minute, again by the moulding that pours into the mold for material be stirred, after at 40-50 ℃ of lower precuring 3-5 hour, the demoulding, handling to cutting part cuts, and obtains the building block base;
(3) the building block base is put into to the reactor steam press maintenance, put finished product in storage and get final product.