CN103465337B - A kind of production technology with the high light melamine decorative veneer of wood effect - Google Patents
A kind of production technology with the high light melamine decorative veneer of wood effect Download PDFInfo
- Publication number
- CN103465337B CN103465337B CN201210185875.4A CN201210185875A CN103465337B CN 103465337 B CN103465337 B CN 103465337B CN 201210185875 A CN201210185875 A CN 201210185875A CN 103465337 B CN103465337 B CN 103465337B
- Authority
- CN
- China
- Prior art keywords
- spread
- modified cyanurotriamide
- decorative veneer
- high light
- production technology
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to decorative panel processing technique field, particularly a kind of production technology with the high light melamine decorative veneer of wood effect.Its technique introduces part silane coupler in modified cyanurotriamide methylal resin, adds the binding ability of the inorganic matter such as resin glue and fibrage, adds the binding ability with Lacquer finish finish paint simultaneously.It not only solves texture vivid effect, also solves the problem that poor adhesive force easily ftractures after melamine decorative veneer spray paint.
Description
Technical field
The present invention relates to decorative panel processing technique field, particularly a kind of production technology with the high light melamine decorative veneer of wood effect.
Background technology
At present, melamine decorative veneer is that different colours and texture printing paper are immersed melamine resin adehsive, then through partially cured, then is posted hot pressing in particieboard, density board and forms, can be made into composite floor board, the ornament materials such as household sheet material.Melamine decorative veneer can copy various pattern arbitrarily, color is beautiful, hardness, anti-wear performance excellence after impregnation, but due to printing grammes per square metre compatibility corresponding spread must be considered during impregnation, so traditional printing paper infiltration melamine resin adehsive ratio is not high, cause decoration panel texture vivid effect, plumpness and solid wood still by certain gap.Although some technology introduction crosses the melamine decorative veneer produced by the method for cyanurotriamide modified or simple interpolation brightener, still can not reach real high glaze or high emulation effect through Market Feedback, and Lacquer finish spraying paint easily ftractures to melamine decorative veneer poor adhesive force.
Summary of the invention
In order to solve the problem of prior art, embodiments provide a kind of production technology with the high light melamine decorative veneer of wood effect.
Described technical scheme is as follows:
There is a production technology for the high light melamine decorative veneer of wood effect, comprise following operation:
A, by melamine, formaldehyde, diethylene glycol, methyl-silicone oil, polyethers, silane coupler react make modified cyanurotriamide methylal resin;
B, printing paper flood above-mentioned modified cyanurotriamide methylal resin, the total spread of modified cyanurotriamide methylal resin to printing paper controls at 145%-155%, impregnation one soaks and controls the 55%-60% that spread is total spread, and impregnation two soaks and controls the 40%-45% that spread is total spread; Impregnation speeds control, at 20 ms/min, by nine joint oven for drying after the modified cyanurotriamide methylal resin described in printing paper dipping, then obtains modified cyanurotriamide methylal resin layer through the cooling of chill roll and conveyer belt;
C, carry out hot pressing with particieboard and modified cyanurotriamide methylal resin layer, be cooled to normal temperature, health 15 days, carries out grinding process;
D, on the modified cyanurotriamide methylal resin layer after polishing, spray silane coupler, then to dry in 50 degree of baking ovens, spray paint, dry.
In step B, the total spread of modified cyanurotriamide methylal resin to printing paper controls 145%, 150% or 155%.
In step B, it is 55%, 58% or 60% of total spread that impregnation one soaks control spread.
In step B, it is 40%, 42% or 45% of total spread that impregnation two soaks control spread.
In step D, the finish paint of spraying is solid content is the polyurethane finish of 46%, the acrylic acid top-coat of solid content 47% or solid content are 40%UV UV-curable finish coat.
The present invention introduces part silane coupler in modified cyanurotriamide methylal resin, adds the binding ability of the inorganic matter such as resin glue and fibrage, adds the binding ability with Lacquer finish finish paint simultaneously.In immersing glue process, increase nozzle quantity and gas output in baking oven by extending baking oven length, adjustment nozzle angle, breach traditional handicraft cannot improve merely spread, cannot the problems such as drying and forming-film.Before spray Lacquer finish finish paint, bridging agent spray treatment is carried out to modified cyanurotriamide methylal resin layer, add the finish paints such as polyurethane polyureas acrylic acid to the adhesive force of modified cyanurotriamide methylal resin layer, ensure that product high glaze shortly, high richness solves the disadvantages such as paint film cracking comes off simultaneously.
Detailed description of the invention
For making the object, technical solutions and advantages of the present invention clearly, below in conjunction with accompanying drawing, embodiment of the present invention is described further in detail.
Embodiment one
A kind of production method and technique with the high light melamine decorative veneer of wood effect:
1. reacted made modified cyanurotriamide methylal resin by melamine, formaldehyde, diethylene glycol, methyl-silicone oil, polyethers, silane coupler.
2. in printing paper dipping modified cyanurotriamide methylal resin layer, the total spread of modified cyanurotriamide methylal resin to simulated grain paper controls 145%, it is 55% of total spread that impregnation one soaks control spread, and it is 45% of total spread that impregnation two soaks control spread.Impregnation speeds control is at 20 ms/min, and printing paper, also will through the property melamine formaldehyde resin layer of lowering the temperature to obtain of chill roll and conveyer belt after dipping modified cyanurotriamide methylal resin is by nine joint oven for drying.
3. carry out hot pressing with particieboard and modified cyanurotriamide methylal resin layer, be cooled to normal temperature, health 15 days, carries out grinding process.
4. on the modified cyanurotriamide methylal resin layer after polishing, spray silane coupler, then dry in 50 degree of baking ovens, spraying solid content is 46% polyurethane finish, carries out drying both obtaining product of the present invention.
Embodiment two
It is characterized in that: a kind of production method and technique with the high light melamine decorative veneer of wood effect:
1. reacted made modified cyanurotriamide methylal resin by melamine, formaldehyde, diethylene glycol, methyl-silicone oil, polyethers, silane coupler.
2. in printing paper dipping modified cyanurotriamide methylal resin layer, the total spread of modified cyanurotriamide methylal resin to simulated grain paper controls 150%, it is 58% of total spread that impregnation one soaks control spread, and it is 42% of total spread that impregnation two soaks control spread.Impregnation speeds control is at 20 ms/min, and printing paper, also will through the property melamine formaldehyde resin layer of lowering the temperature to obtain of chill roll and conveyer belt after impregnated melamine methylal resin is by nine joint oven for drying.
3. carry out hot pressing with particieboard and modified cyanurotriamide methylal resin layer, be cooled to normal temperature, health 15 days, carries out grinding process.
4. on the modified cyanurotriamide methylal resin layer after polishing, spray silane coupler, then dry in 50 degree of baking ovens, spraying solid content is 47% acrylic acid top-coat, carries out drying both obtaining product of the present invention.
Embodiment three
A kind of production method and technique with the high light melamine decorative veneer of wood effect:
1. reacted made modified cyanurotriamide methylal resin by melamine, formaldehyde, diethylene glycol, methyl-silicone oil, polyethers, silane coupler.
2. in printing paper dipping modified cyanurotriamide methylal resin layer, the total spread of modified cyanurotriamide methylal resin to simulated grain paper controls 155%, it is 60% of total spread that impregnation one soaks control spread, and it is 40% of total spread that impregnation two soaks control spread.Impregnation speeds control is at 20 ms/min, and printing paper, also will through the property melamine formaldehyde resin layer of lowering the temperature to obtain of chill roll and conveyer belt after impregnated melamine methylal resin is by nine joint oven for drying.
3. carry out hot pressing with particieboard and modified cyanurotriamide methylal resin layer, be cooled to normal temperature, health 15 days, carries out grinding process.
4. on the modified cyanurotriamide methylal resin layer after polishing, spray silane coupler, then dry in 50 degree of baking ovens, spraying solid content is 40%UV UV-curable finish coat, carries out drying both obtaining product of the present invention.
The foregoing is only preferred embodiment of the present invention, not in order to limit the present invention, within the spirit and principles in the present invention all, any amendment done, equivalent replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (5)
1. there is a production technology for the high light melamine decorative veneer of wood effect, comprise following operation:
A, by melamine, formaldehyde, diethylene glycol, methyl-silicone oil, polyethers, silane coupler react make modified cyanurotriamide methylal resin;
B, printing paper flood above-mentioned modified cyanurotriamide methylal resin, the total spread of modified cyanurotriamide methylal resin to printing paper controls at 145%-155%, impregnation one soaks and controls the 55%-60% that spread is total spread, and impregnation two soaks and controls the 40%-45% that spread is total spread; Impregnation speeds control, at 20 ms/min, by nine joint oven for drying after the modified cyanurotriamide methylal resin described in printing paper dipping, then obtains modified cyanurotriamide methylal resin layer through the cooling of chill roll and conveyer belt;
C, carry out hot pressing with particieboard and modified cyanurotriamide methylal resin layer, be cooled to normal temperature, health 15 days, carries out grinding process;
D, on the modified cyanurotriamide methylal resin layer after polishing, spray silane coupler, then to dry in 50 degree of baking ovens, spray paint, dry.
2. a kind of production technology with the high light melamine decorative veneer of wood effect according to claim 1, is characterized in that, in step B, the total spread of modified cyanurotriamide methylal resin to printing paper controls 145%, 150% or 155%.
3. a kind of production technology with the high light melamine decorative veneer of wood effect according to claim 1, is characterized in that, in step B, it is 55%, 58% or 60% of total spread that impregnation one soaks control spread.
4. a kind of production technology with the high light melamine decorative veneer of wood effect according to claim 1, is characterized in that, in step B, it is 40%, 42% or 45% of total spread that impregnation two soaks control spread.
5. a kind of production technology with the high light melamine decorative veneer of wood effect according to claim 1, it is characterized in that, in step D, the finish paint of spraying is solid content is the polyurethane finish of 46%, the acrylic acid top-coat of solid content 47% or solid content are 40%UV UV-curable finish coat.