CN103437241B - 人造皮革用离型纸及其制作方法 - Google Patents

人造皮革用离型纸及其制作方法 Download PDF

Info

Publication number
CN103437241B
CN103437241B CN201310382329.4A CN201310382329A CN103437241B CN 103437241 B CN103437241 B CN 103437241B CN 201310382329 A CN201310382329 A CN 201310382329A CN 103437241 B CN103437241 B CN 103437241B
Authority
CN
China
Prior art keywords
paper
release
release paper
preparation
layer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310382329.4A
Other languages
English (en)
Other versions
CN103437241A (zh
Inventor
杨汉东
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Fujian Mingxing Laser Science & Technology Co Ltd
Original Assignee
Fujian Mingxing Laser Science & Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Fujian Mingxing Laser Science & Technology Co Ltd filed Critical Fujian Mingxing Laser Science & Technology Co Ltd
Priority to CN201510532999.9A priority Critical patent/CN105239454B/zh
Priority to CN201310382329.4A priority patent/CN103437241B/zh
Publication of CN103437241A publication Critical patent/CN103437241A/zh
Application granted granted Critical
Publication of CN103437241B publication Critical patent/CN103437241B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及离型纸制作技术领域，具体涉及一种人造皮革用离型纸，其包括长纤底纸层、有机硅离型层以及设置于所述长纤底纸层与所述有机硅离型层之间的带有纹路的聚氨酯涂层；制作上述人造皮革用离型纸的方法包括通过UV光固化将纹路辊压于透明PET膜表面上，将聚氨酯树脂涂覆于长纤底纸表面，并将透明PET膜上的纹路通过压辊并合及UV光固化转移至长纤底纸表面，再将长纤底纸表面涂上有机硅离型层，得到人造皮革用离型纸成品。本发明所述人造皮革用离型纸的制作方法，制作出来的纹路清晰、仿真度可达到99%以上；光固化速度快，生产效率高；对底纸的要求不高，节省生产成本。

Description

人造皮革用离型纸及其制作方法
技术领域
本发明涉及离型纸制作技术领域，尤其涉及一种人造皮革用离型纸及其制作
方法。
背景技术
传统的人造皮革离型纸是在纸上压纹之后涂布有机硅离型涂层，再通过热固化得到成品，这种方式作出来的离型纸纹路不清晰、不逼真，达不到皮纹的逼真效果；另外，涂布后再热固化涂层，生产工艺复杂，且要通过长时间的加热，生产效率大大降低；其对底纸的平整度要求也很高，否则难以制作出精细的纹路，这样无形中增加了成本。
发明内容
本发明要解决的问题是现有的人造皮革用离型纸不逼真、生产工艺复杂、生产效率低、成本高的缺陷，提供一种人造皮革用离型纸，其纹路逼真、仿真效果好。
本发明还提供一种人造皮革用离型纸的制作方法，其工艺简便、成本低。
本发明实施例提供一种人造皮革用离型纸，其包括长纤底纸层、有机硅离型层以及设置于所述长纤底纸层与所述有机硅离型层之间的带有纹路的聚氨酯涂层。
制作上述人造皮革用离型纸的方法，包括如下步骤：
一、在透明PET膜上涂布增粘剂后再涂布聚氨酯树脂，然后包覆于花纹辊表面，滚压并经UV光固化成型，得到带有纹路的透明PET膜。
二、在带有纹路的透明PET膜上涂覆有机硅涂层，形成一层离型层。
三、在长纤底纸表面涂布聚氨酯树脂，将步骤（二）所得带有纹路的透明PET膜有纹路的一面与长纤底纸涂布聚氨酯的一面通过压辊并合及UV光照射透过PET透明膜固化，纹路成型于长纤底纸上，分离后各自收卷，得到成型纹路纸。
四、将步骤（三）所得成型纹路纸的聚氨酯涂层进行电晕处理，再在其表面涂覆有机硅并固化后形成有机硅离型层，收卷，得到人造皮革用离型纸成品。
优选地，所述步骤（一）中花纹辊对压的压力为3千克/平方厘米，滚压速度是10-20米/分钟。
优选地，所述步骤（四）中有形成机硅离型层的方法为：涂覆95%~99.5%
的有机硅以及0.5%-5%固化剂后，100~120摄氏度下加热2~5分钟。
优选地，所述步骤（四）中形成机硅离型层的方法为：涂覆90%有机硅以及10%光敏剂，在1000-1400MT/平方米的UV光强度下固化。
优选地，所述步骤（一）或（三）中聚氨酯树脂包括90%聚氨酯以及10%光敏剂。
所述步骤（四）中有机硅离型层的厚度为0.5um~1um。
本发明所述人造皮革用离型纸的制作方法，有益效果是：
通过聚氨酯合成涂层直接用光固化的原理，将纹辊上的纹路直接转移到离型纸面上，然后涂上有机硅层，制作出来的纹路清晰、逼真，仿真度可达到99%以上；光固化只需要几秒钟，速度快，生产效率高；这种制作方法对底纸的要求不高，一般的底纸都可以使用，从而节省了生产成本。
附图说明
附图1为本发明实施例人造皮革用离型纸结构示意图；
附图2为本发明实施例人造皮革用离型纸制作步骤一示意图；
附图3为本发明实施例人造皮革用离型纸制作步骤三示意图；
附图4为本发明实施例人造皮革用离型纸制作步骤四示意图；
其中：
1、长纤底纸层         2、聚氨酯涂层            3、有机硅离型层。
具体实施方式
为使本发明的目的、技术方案和优点更加清楚，下面将结合附图对本发明作进一步地详细描述。
实施例1：
本发明所述人造皮革用离型纸，其包括长纤底纸层1，长纤底纸层1一表面设置有聚氨酯涂层2，所述聚氨酯涂层2的表面设置有机硅离型层3。
制作上述人造皮革用离型纸的方法，包括如下步骤：
一、参照图2，在透明PET膜上涂布增粘剂，接着再涂布聚氨酯树脂，聚氨酯树脂包括90%聚氨酯以及10%光敏剂，然后包覆于花纹辊表面，在压力为3千克/平方厘米，滚压速度是10米/分钟下滚压并经1000MT/平方米的UV光强度下UV光固化成型，得到带有纹路的透明PET膜。
二、在带有纹路的透明PET膜上涂覆有机硅涂层，形成一层离型层。
三、在长纤底纸表面涂布聚氨酯树脂，聚氨酯树脂包括90%聚氨酯以及10%光敏剂，将步骤（二）所得带有纹路的透明PET膜有纹路的一面与长纤底纸涂布聚氨酯的一面通过压辊并合及UV光照射透过PET透明膜固化，纹路成型于长纤底纸上，分离后各自收卷，得到成型纹路纸。
四、将步骤（三）所得成型纹路纸的聚氨酯涂层进行电晕处理，再在其表
面涂覆95%~99.5%的有机硅以及0.5%-5%固化剂后，经100~120摄氏度下加热2~5分钟固化或者涂覆90%有机硅以及10%光敏剂，在1000MT/平方米的UV光强度下固化，形成厚度0.5um~1um的有机硅离型层，电晕处理使有机硅更好的附着在成型纹路纸表面，收卷，得到人造皮革用离型纸成品。
实施例2：
本发明所述人造皮革用离型纸，其包括长纤底纸层1，长纤底纸层1一表面设置有聚氨酯涂层2，所述聚氨酯涂层2的表面设置有机硅离型层3。
制作上述人造皮革用离型纸的方法，包括如下步骤：
一、参照图2，在透明PET膜上涂布增粘剂，接着再涂布聚氨酯树脂，聚氨酯树脂包括90%聚氨酯以及10%光敏剂，然后包覆于花纹辊表面，在压力为3千克/平方厘米，滚压速度是20米/分钟下滚压并经1400MT/平方米的UV光强度下UV光固化成型，得到带有纹路的透明PET膜。
二、在带有纹路的透明PET膜上涂覆有机硅涂层，形成一层离型层。
三、在长纤底纸表面涂布聚氨酯树脂，聚氨酯树脂包括90%聚氨酯以及10%光敏剂，将步骤（二）所得带有纹路的透明PET膜有纹路的一面与长纤底纸涂布聚氨酯的一面通过压辊并合及UV光照射透过PET透明膜固化，纹路成型于长纤底纸上，分离后各自收卷，得到成型纹路纸。
四、将步骤（三）所得成型纹路纸的聚氨酯涂层进行电晕处理，再在其表
面涂覆95%~99.5%的有机硅以及0.5%-5%固化剂后，经100~120摄氏度下加热2~5分钟固化或者涂覆90%有机硅以及10%光敏剂，在1400MT/平方米的UV光强度下固化，形成厚度0.5um~1um的有机硅离型层，电晕处理使有机硅更好的附着在成型纹路纸表面，收卷，得到人造皮革用离型纸成品。
本发明是通过聚氨酯合成涂层直接用光固化的原理，将花纹辊上的纹路直接转移到离型纸面上，然后涂上有机硅层，制作出来的纹路清晰，仿真度可达到99%以上。
以上所述是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也视为本发明的保护范围。

Claims (6)

1.一种人造皮革用离型纸的制作方法，所述离型纸包括长纤底纸层（1）、有机硅离型层
（3）以及设置于所述长纤底纸层（1）与所述有机硅离型层（3）之间的带有纹路的聚氨酯涂
层（2），其特征在于，包括如下步骤：
    一、在透明PET 膜上涂布增粘剂后再涂布聚氨酯树脂，然后包覆于花纹辊表面，滚压并
经UV 光固化成型，得到带有纹路的透明PET 膜；
    二、在带有纹路的透明PET 膜上涂覆有机硅涂层，形成一层离型层；
    三、在长纤底纸表面涂布聚氨酯树脂，将步骤（二）所得带有纹路的透明PET膜有纹路的
一面与长纤底纸涂布聚氨酯的一面通过压辊并合及UV光照射透过PET透明膜固化，纹路成
型于长纤底纸上，分离后各自收卷，得到成型纹路纸；
    四、将步骤（三）所得成型纹路纸的聚氨酯涂层进行电晕处理，再在其表面涂覆有机硅
并固化后形成有机硅离型层，收卷，得到人造皮革用离型纸成品。
2.根据权利要求1 所述人造皮革用离型纸的制作方法，其特征在于：所述步骤（一）中
花纹辊滚压的压力为3千克/平方厘米，滚压速度是10-20米/分钟。
3.根据权利要求1所述人造皮革用离型纸的制作方法，其特征在于：所述步骤（四）中
形成有机硅离型层的方法为：涂覆95%~99.5%的有机硅以及0.5%-5%固化剂后，100~120摄
氏度下加热2~5分钟。
4.根据权利要求1所述人造皮革用离型纸的制作方法，其特征在于：所述步骤（四）中
形成有机硅离型层的方法为：涂覆90%有机硅以及10%光敏剂，在1000-1400MT/平方米的UV
光强度下固化。
5.根据权利要求1所述人造皮革用离型纸的制作方法，其特征在于：所述步骤（一）或
（三）中聚氨酯树脂包括90%聚氨酯以及10%光敏剂。
6.根据权利要求1所述人造皮革用离型纸的制作方法，其特征在于：所述步骤（四）
中有机硅离型层的厚度为0.5μm~1μm。
CN201310382329.4A 2013-05-25 2013-08-29 人造皮革用离型纸及其制作方法 Active CN103437241B (zh)