CN103406534A - 一种粉末冶金法兰及其制备方法 - Google Patents

一种粉末冶金法兰及其制备方法 Download PDF

Info

Publication number
CN103406534A
CN103406534A CN2013102726013A CN201310272601A CN103406534A CN 103406534 A CN103406534 A CN 103406534A CN 2013102726013 A CN2013102726013 A CN 2013102726013A CN 201310272601 A CN201310272601 A CN 201310272601A CN 103406534 A CN103406534 A CN 103406534A
Authority
CN
China
Prior art keywords
powder
sintering
condition
minute
parts
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2013102726013A
Other languages
English (en)
Other versions
CN103406534B (zh
Inventor
张李华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Ruitai Auto Parts Co Ltd
Original Assignee
Anhui Ruitai Auto Parts Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Ruitai Auto Parts Co Ltd filed Critical Anhui Ruitai Auto Parts Co Ltd
Priority to CN201310272601.3A priority Critical patent/CN103406534B/zh
Publication of CN103406534A publication Critical patent/CN103406534A/zh
Application granted granted Critical
Publication of CN103406534B publication Critical patent/CN103406534B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种粉末冶金法兰及其制备方法，其特征在于由下列重量份的原料制成：铜粉1.1-1.3、铬粉0.2-0.4、硅粉0.4-0.5、石墨粉0.2-0.3、铁粉93-94、硬酸酸锌2-3、铝粉2.2-2.4、二硫化钼粉0.3-0.5、二硼化钛0.2-0.3、硼化铌0.5-0.6、V2O50.3-0.4、Fe3O40.8-0.9、TaC0.2-0.3、分散剂2-3。本发明制造的法兰组织致密，微观结构良好，孔隙很少，结构刚度、硬度、耐疲劳性能、抗拉强度性能优良。而且由于采用了模压，使设备简化，降低了生产成本。

Description

一种粉末冶金法兰及其制备方法
技术领域
本发明涉及粉末冶金领域，尤其涉及一种粉末冶金法兰及其制备方法。
背景技术
粉末冶金技术是将材料科学和金属成形技术完善的结合起来一种新型技术，因为高效、无切削加工、节材、节能、环保而被广泛使用于各种行业。
粉末冶金结构件制品材料成分不受熔炼限制，既可以加入合金成分，也可以加入其它结构组分，并且在相当大的范围内根据要求进行调整，进而在力学性能上能达到与钢件匹配的效果。
粉末冶金机械化程度高，既能减少人员，又能提高效率，进而节约成本。粉末冶金技术能取代传统的制造工艺，为广大传统企业节约成本。
所以研究各种机械零部件的粉末冶金的配方，适应不同的需要，具有重要的意义。
发明内容
本发明的目的是提供一种粉末冶金法兰及其制备方法。
本发明的技术方案如下：
一种粉末冶金法兰，其特征在于由下列重量份的原料制成：
铜粉1.1-1.3、铬粉0.2-0.4、硅粉0.4-0.5、石墨粉0.2-0.3、铁粉93-94、硬酸酸锌2-3、铝粉2.2-2.4、二硫化钼粉0.3-0.5、二硼化钛0.2-0.3、硼化铌0.5-0.6、V2O5 0.3-0.4、 Fe3O40.8-0.9、TaC0.2-0.3、分散剂2-3。 
所述的分散剂由下列重量份的原料制成：聚乙二醇2-3、Bi2O3 0.2-0.3、氨丙基三乙氧基硅烷0.5-0.8、氮化铝1-1.3、Nb2O5 0.3-0.5、硫酸钡1-2、硬脂酸锌4-5、硬酯酸单甘油酯2-3。
制备方法是：将各物料混合，研磨分散均匀即可。
所述的粉末冶金法兰的制备方法，其特征在于包括以下步骤：
  （1）将铜粉、铬粉、硅粉、铝粉、二硫化钼粉、石墨粉混合均匀；
（2）将其它剩余成分混合，均匀；
（3）将步骤（1）、（2）物料在48-52℃下混合搅拌均匀60-80分钟后，装入模具，压制成坯；
（4）将压坯放在烧结炉中，以4-6℃/分钟速率升温至420-450℃条件下烧结1-2小时;再以6-8℃/分钟速率升温至720-750℃条件下烧结1-2小时;然后以10-12℃/分钟速率升温至1070-1120℃条件下烧结2-3小时；取出空冷；
（5）将压坯在520-550℃条件下烧结1-2小时；
（6）将压坯送入蒸汽处理炉中，在炉中温度420-450℃的条件下通入蒸汽60-90分钟；
（7）将压坯送入100-120℃溶剂油中冷却1-2小时，取出空冷即得。
本发明的有益效果在于：
本发明制造的法兰组织致密，微观结构良好，孔隙很少，结构刚度、硬度、耐疲劳性能、抗拉强度性能优良。而且由于采用了模压，使设备简化，降低了生产成本。
具体实施方式
一种粉末冶金法兰，由下列重量份的原料（公斤）制成：
铜粉1.1、铬粉0.4、硅粉0.5、石墨粉0.2、铁粉94、硬酸酸锌2、铝粉2.4、二硫化钼粉0.3、二硼化钛0.3、硼化铌0.6、V2O5 0.4、 Fe3O4 0.9、TaC0.3、分散剂3。
所述的分散剂由下列重量份的原料制成：聚乙二醇3、Bi2O 30.3、氨丙基三乙氧基硅烷0.8、氮化铝1.3、Nb2O5 0.5、硫酸钡2、硬脂酸锌5、硬酯酸单甘油酯3。
制备方法是：将各物料混合，研磨分散均匀即可。
粉末冶金法兰的制备方法，包括以下步骤：
   （1）将铜粉、铬粉、硅粉、铝粉、二硫化钼粉、石墨粉混合均匀；
（2）将其它剩余成分混合，均匀；
（3）将步骤（1）、（2）物料在48-52℃下混合搅拌均匀60-80分钟后，装入模具，压制成坯；
（4）将压坯放在烧结炉中，以4-6℃/分钟速率升温至420-450℃条件下烧结1-2小时;再以6-8℃/分钟速率升温至720-750℃条件下烧结1-2小时;然后以10-12℃/分钟速率升温至1070-1120℃条件下烧结2-3小时；取出空冷；
（5）将压坯在520-550℃条件下烧结1-2小时；
（6）将压坯送入蒸汽处理炉中，在炉中温度420-450℃的条件下通入蒸汽60-90分钟；
（7）将压坯送入100-120℃溶剂油中冷却1-2小时，取出空冷即得。
经过检测，本发明法兰的热处理硬度：HRC55 ；抗拉强度：1080MPa 。

Claims (2)

1.一种粉末冶金法兰，其特征在于由下列重量份的原料制成：
铜粉1.1-1.3、铬粉0.2-0.4、硅粉0.4-0.5、石墨粉0.2-0.3、铁粉93-94、硬酸酸锌2-3、铝粉2.2-2.4、二硫化钼粉0.3-0.5、二硼化钛0.2-0.3、硼化铌0.5-0.6、V2O5 0.3-0.4、 Fe3O40.8-0.9、TaC0.2-0.3、分散剂2-3；
所述的分散剂由下列重量份的原料制成：聚乙二醇2-3、Bi2O 30.2-0.3、氨丙基三乙氧基硅烷0.5-0.8、氮化铝1-1.3、Nb2O5 0.3-0.5、硫酸钡1-2、硬脂酸锌4-5、硬酯酸单甘油酯2-3；
制备方法是：将各物料混合，研磨分散均匀即可。
2.根据权利要求1所述的粉末冶金法兰的制备方法，其特征在于包括以下步骤：
（1）将铜粉、铬粉、硅粉、铝粉、二硫化钼粉、石墨粉混合均匀；
（2）将其它剩余成分混合，均匀；
（3）将步骤（1）、（2）物料在48-52℃下混合搅拌均匀60-80分钟后，装入模具，压制成坯；
（4）将压坯放在烧结炉中，以4-6℃/分钟速率升温至420-450℃条件下烧结1-2小时；再以6-8℃/分钟速率升温至720-750℃条件下烧结1-2小时；然后以10-12℃/分钟速率升温至1070-1120℃条件下烧结2-3小时；取出空冷；
（5）将压坯在520-550℃条件下烧结1-2小时；
（6）将压坯送入蒸汽处理炉中，在炉中温度420-450℃的条件下通入蒸汽60-90分钟；
（7）将压坯送入100-120℃溶剂油中冷却1-2小时，取出空冷即得。
CN201310272601.3A 2013-07-02 2013-07-02 一种粉末冶金法兰及其制备方法 Active CN103406534B (zh)