CN103334340A - 一种阻燃型滤清器滤纸及其制备方法 - Google Patents

一种阻燃型滤清器滤纸及其制备方法 Download PDF

Info

Publication number
CN103334340A
CN103334340A CN2013102081719A CN201310208171A CN103334340A CN 103334340 A CN103334340 A CN 103334340A CN 2013102081719 A CN2013102081719 A CN 2013102081719A CN 201310208171 A CN201310208171 A CN 201310208171A CN 103334340 A CN103334340 A CN 103334340A
Authority
CN
China
Prior art keywords
parts
filter paper
filter
paper
add
Prior art date
Application number
CN2013102081719A
Other languages
English (en)
Inventor
金鑫
胡辉
Original Assignee
蚌埠首创滤清器有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 蚌埠首创滤清器有限公司 filed Critical 蚌埠首创滤清器有限公司
Priority to CN2013102081719A priority Critical patent/CN103334340A/zh
Publication of CN103334340A publication Critical patent/CN103334340A/zh

Abstract

本发明公开了一种阻燃型滤清器滤纸,它是由下述重量份的原料组成的:竹浆70-80、氢氧化铝粉30-40、纯丙乳液5-6、聚苯并咪唑纤维15-20、钨酸钠1-2、磷酸二氢铵1-2、水滑石粉1-2、聚乙二醇4002-4、三甘醇二异辛酸酯1-2、1,2-双(三乙氧基硅基)乙烷0.6-1、月桂醇硫酸钠0.2-0.3、二乙醇酰胺0.4-0.5、VAE乳液DA10113-20、丙烯酸3-4、柠檬酸三丁酯1-2、二甲基亚砜3-5、过氧化二苯甲酰0.1-0.2、十二烷基三甲基氯化铵0.6-1、水适量;本发明生产的滤纸过滤性能高、使用寿命长、环保、质量稳定,使用的浸渍液具有很强的粘结性和成膜性,浸渍后能够增强滤纸的干湿强度,韧性,提高了滤清器滤清效率。

Description

一种阻燃型滤清器滤纸及其制备方法
技术领域
[0001] 本发明主要涉及一种滤纸,尤其涉及一种阻燃型滤清器滤纸及其制备方法。
背景技术
[0002] 滤清器是发动机的重要零部件,其作用为滤除进入发动机的空气、柴油、机油中的尘埃和机械杂质等微粒,以减少发动机缸套活塞环、曲轴连杆运动副和高压油泵柱塞偶件的磨损,优化发动机的燃烧过程,降低一氧化碳等有机污染物的排放。传统生产滤清器滤纸存在过滤性能低、使用寿命短、滤纸质量不稳定等问题,很大程度的限制了滤清器滤清效率的提高,也影响了发动机性能的提升,难以满足目前人们对于高性能、高品质产品的追求。
发明内容
[0003] 本发明目的就是提供一种阻燃型滤清器滤纸。
[0004] 本发明是通过以下技术方案实现的:
一种阻燃型滤清器滤纸,它是由下述重量份的原料组成的:
竹浆70-80、氢氧化铝粉30-40、纯丙乳液5-6、聚苯并咪唑纤维15-20、钨酸钠1_2、磷酸二氢铵1-2、水滑石粉1-2、聚乙二醇400 2-4、三甘醇二异辛酸酯1-2、1,2-双(三乙氧基硅基)乙烷0.6-1、月桂醇硫酸钠0.2-0.3、二乙醇酰胺0.4-0.5,VAE乳液DAlOl 13-20、丙烯酸3-4、柠檬酸三丁酯1-2、二甲基亚砜3-5、过氧化二苯甲酰0.1-0.2、十二烷基三甲基氯化按0.6-1、水适量。
[0005] 一种阻燃型滤清器滤纸的制备方法,包括以下步骤:
在上述竹浆、氢氧化铝粉中加入相当于竹浆重量1-2%的二乙醇胺、1,2-双(三乙氧基硅基)乙烷与适量水,在温度为80-90°C下搅拌反应10-20分钟,再加入纯丙乳液,低速200-300转/分分散3-5分钟,得分散液;将得到的分散液与聚苯并咪唑纤维混合加入到打浆机中,打浆,再加入磷酸二氢铵、水滑石粉,800-1000转/分分散1-2分钟,加入除了 VAE乳液DA101、丙烯酸、柠檬酸三丁酯、二甲基亚砜、过氧化二苯甲酰、十二烷基三甲基氯化铵以外的剩余各原料,搅拌均匀后在60-70°C下保温20-30分钟,疏解、磨浆,加水至固含量为4-6%,由造纸机抄造成型,脱水;将上述VAE乳液DAlOl与十二烷基三甲基氯化铵混合,加4-5倍水,加热至85-90°C,加入丙烯酸、二甲基亚砜,低速300-400转/分分散10-12分钟,加入柠檬酸三丁酯、过氧化二苯甲酰,在温度为70-80°C下搅拌反应1-2小时,过滤出料,得浸溃液;将脱水后的纸浸于上述浸溃液中浸溃2-3h,再用压力辊除去过量的浸溃液;160-20(TC下烘干至干度95-98%,压光整理,即得阻燃型滤清器滤纸。
[0006] 本发明的优点是:
本发明生产的滤纸中大大提高氢氧化铝用量,提高了其阻燃性能。滤纸过滤性能高、使用寿命长、环保、防腐、质量稳定,将主浆料加入助剂进行分散处理后再与纤维混合,使得各物料间的相容性更好,增强了成型后的滤纸的综合品质,使用的浸溃液具有很强的粘结性和成膜性,浸溃后能够增强滤纸的干湿强度,韧性,进一步提高了滤清器滤清效率。具体实施方式
[0007] 实施例1
一种阻燃型滤清器滤纸,它是由下述重量份(公斤)的原料组成的:
竹浆80、氢氧化铝粉40、纯丙乳液5、聚苯并咪唑纤维20、钨酸钠2、磷酸二氢铵2、水滑石粉2、聚乙二醇400 2-4、三甘醇二异辛酸酯2、1,2-双(三乙氧基硅基)乙烷1、月桂醇硫酸钠0.3、二乙醇酰胺0.5、VAE乳液DAlO 120、丙烯酸3、柠檬酸三丁酯1、二甲基亚砜5、过氧化二苯甲酰0.2、十二烷基三甲基氯化铵0.6、水适量。
[0008] 一种阻燃型滤清器滤纸的制备方法,包括以下步骤:
在上述竹浆、氢氧化铝粉中加入相当于竹浆重量1-2%的二乙醇胺、1,2-双(三乙氧基硅基)乙烷与适量水,在温度为90°C下搅拌反应20分钟,再加入纯丙乳液,低速300转/分分散3-5分钟,得分散液;将得到的分散液与聚苯并咪唑纤维混合加入到打浆机中,打浆,再加入磷酸二氢铵、水滑石粉,1000转/分分散2分钟,加入除了 VAE乳液DA101、丙烯酸、柠檬酸三丁酯、二甲基亚砜、过氧化二苯甲酰、十二烷基三甲基氯化铵以外的剩余各原料,搅拌均匀后在70°C下保温30分钟,疏解、磨浆,加水至固含量为5%,由造纸机抄造成型,脱水;将上述VAE乳液DAlOl与十二烷基三甲基氯化铵混合,加5倍水,加热至90°C,加入丙烯酸、二甲基亚砜,低速400转/分分散12分钟,加入柠檬酸三丁酯、过氧化二苯甲酰,在温度为80°C下搅拌反应2小时,过滤出料,得浸溃液;将脱水后的纸浸于上述浸溃液中浸溃3h,再用压力辊除去过量的浸溃液;200°C下烘干至干度98%,压光整理,即得阻燃型滤清器滤纸。

Claims (2)

1.一种阻燃型滤清器滤纸,其特征在于它是由下述重量份的原料组成的: 竹浆70-80、氢氧化铝粉30-40、纯丙乳液5-6、聚苯并咪唑纤维15-20、钨酸钠1_2、磷酸二氢铵1-2、水滑石粉1-2、聚乙二醇400 2-4、三甘醇二异辛酸酯1-2、1,2-双(三乙氧基硅基)乙烷0.6-1、月桂醇硫酸钠0.2-0.3、二乙醇酰胺0.4-0.5,VAE乳液DAlOl 13-20、丙烯酸3-4、柠檬酸三丁酯1-2、二甲基亚砜3-5、过氧化二苯甲酰0.1-0.2、十二烷基三甲基氯化按0.6-1、水适量。
2.一种如权利要求1所述的阻燃型滤清器滤纸的制备方法,其特征在于包括以下步骤: 在上述竹浆、氢氧化铝粉中加入相当于竹浆重量1-2%的二乙醇胺、1,2-双(三乙氧基硅基)乙烷与适量水,在温度为80-90°C下搅拌反应10-20分钟,再加入纯丙乳液,低速200-300转/分分散3-5分钟,得分散液;将得到的分散液与聚苯并咪唑纤维混合加入到打浆机中,打浆,再加入磷酸二氢铵、水滑石粉,800-1000转/分分散1-2分钟,加入除了 VAE乳液DA101、丙烯酸、柠檬酸三丁酯、二甲基亚砜、过氧化二苯甲酰、十二烷基三甲基氯化铵以外的剩余各原料,搅拌均匀后在60-70°C下保温20-30分钟,疏解、磨浆,加水至固含量为4-6%,由造纸机抄造成型,脱水;将上述VAE乳液DAlOl与十二烷基三甲基氯化铵混合,加4-5倍水,加热至85-90°C,加入丙烯酸、二甲基亚砜,低速300-400转/分分散10-12分钟,加入柠檬酸三丁酯、过氧化二苯甲酰,在温度为70-80°C下搅拌反应1-2小时,过滤出料,得浸溃液;将脱水后的纸浸于上述浸溃液中浸溃2-3h,再用压力辊除去过量的浸溃液;160-20(TC下烘干至干度95-98%,压光整理,即得阻燃型滤清器滤纸。
CN2013102081719A 2013-05-30 2013-05-30 一种阻燃型滤清器滤纸及其制备方法 CN103334340A (zh)