CN103320804A - 一种锆材酸洗液及酸洗工艺 - Google Patents

一种锆材酸洗液及酸洗工艺 Download PDF

Info

Publication number
CN103320804A
CN103320804A CN201310243057XA CN201310243057A CN103320804A CN 103320804 A CN103320804 A CN 103320804A CN 201310243057X A CN201310243057X A CN 201310243057XA CN 201310243057 A CN201310243057 A CN 201310243057A CN 103320804 A CN103320804 A CN 103320804A
Authority
CN
China
Prior art keywords
zirconium
water
pickling
pickle solution
solution
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201310243057XA
Other languages
English (en)
Other versions
CN103320804B (zh
Inventor
吴厚金
邱守光
宋四兵
韦德明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nanjing Duble Metal Equipment Engineering Co Ltd
Original Assignee
Nanjing Duble Metal Equipment Engineering Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nanjing Duble Metal Equipment Engineering Co Ltd filed Critical Nanjing Duble Metal Equipment Engineering Co Ltd
Priority to CN201310243057.XA priority Critical patent/CN103320804B/zh
Publication of CN103320804A publication Critical patent/CN103320804A/zh
Application granted granted Critical
Publication of CN103320804B publication Critical patent/CN103320804B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种锆材酸洗液,按重量份计,由氢氟酸5-12份,硝酸60-75份,水15-25份,缓蚀剂0.1-1份混合而成。本发明还公开了锆材酸洗液的酸洗方法,在10-20℃下,将锆材酸洗液在10分钟内喷涂到锆材表面,喷涂酸洗液的量为每平方分米2-5毫升,待锆材表面产生黄色烟雾并逐渐消失时对锆材表面用水进行冲洗,直至表面烟雾完全消失。本发明工艺简单,成本较低,且工人操作方便、灵活,随用随配,酸洗的效率高,尤其是从根本上解决了锆材及其焊缝表面的氧化膜问题,尤其是保证焊缝,大大提高了设备的耐蚀性能和设备的使用寿命。

Description

一种锆材酸洗液及酸洗エ艺
技术领域
[0001] 本发明属于化工技术领域,具体涉及ー种锆材酸洗液及酸洗エ艺。
背景技术
[0002] 锆是ー种稀有金属,具有惊人的抗腐蚀性能、极高的熔点、超高的硬度和強度等特性,被广泛用在航空航天、军エ、核反应、原子能和化工领域。随着国内经济的快速发展,尤其是核电、化工行业的技术改造升级的加快,锆材在国内化工行业的应用也越来越广泛,同时对核电、化工行业的加工设备的质量也提出了越来越高的要求。在化工设备中选用锆材,主要是因为锆材表面有一层钝化的氧化膜,该氧化膜具有极强的耐蚀性,但通常因为锆材在设备加工成型过程中该氧化膜极易损坏,且锆制化工设备通常为焊接设备,故在使用过程中易在焊缝处及氧化膜损坏处产生腐蚀,大大降低了设备的使用寿命。
发明内容
[0003] 本发明目的是提出一种锆材酸洗液及酸洗エ艺,为解决锆材制品在焊缝处及氧化膜损坏处产生腐蚀,从而使锆材制品真正发挥耐蚀的作用。
[0004] 本发明采用以下技术方案:
[0005] 一种锆材酸洗液,由以下组分混合而成,按重量份计:
[0006] 氢氟酸:5-12份;
[0007]硝酸:60-75 份;
[0008]水:15-25 份;
[0009]缓蚀剂:0.1-1 份。
[0010] 进ー步地,在低于32°C的条件下配制锆材酸洗液。
[0011] 进ー步地,所述缓蚀剂为Lan-826酸洗缓蚀剂。
[0012] 上述锆材酸洗液的酸洗方法,在10_20°C下,将锆材酸洗液在10分钟内喷涂到锆材表面,喷涂酸洗液的量为每平方分米2-5毫升,待锆材表面产生黄色烟雾并逐渐消失时对锆材表面用水进行冲洗,直至表面烟雾完全消失。
[0013] 进ー步地,采用0.2-0.5Mpa压カ的水雾喷淋的方法冲洗,水雾喷淋的水量是锆材酸洗液使用量的6-10倍,最后将锆材表面整体用水再次冲洗。
[0014] 进ー步地,所述的锆材为纯锆材或锆占30%以上的合金。
[0015] 本发明的有益效果:本发明エ艺简单,成本较低,且工人操作方便、灵活,随用随配,酸洗的效率高,尤其是从根本上解决了锆材及其焊缝表面的氧化膜问题,尤其是保证焊縫,大大提高了设备的耐蚀性能和设备的使用寿命。
具体实施方式
[0016] 下面结合实施例对本发明做更进一歩的解释。下列实施例仅用于说明本发明,但并不用来限定本发明的实施 范围。[0017] 实施例1
[0018] 1、将锆材制品表面清洁,如将表面的灰尘用抹布擦除干净,保持锆材制品处于通风厂房内。
[0019] 2、按10份的氢氟酸+70份的硝酸+20份的水+0.5份Lan-826酸洗缓蚀剂的比例(均为重量份)配制酸洗溶液,并将溶液搅拌均匀,保持随用随配。室温条件,尤其是低于32°C的条件下配制。硝酸浓度会有10%的偏移并不影响到使用,反应速度与使用时温度(环境温度等)有关系。
[0020] 3、将溶液均匀的喷涂到设备表面。喷涂酸洗溶液的量为每平方分米4毫升;溶液在15°C的条件下10分钟内施用。喷涂酸洗溶液在风罩内进行,风罩的出风进行吸附处理。
[0021] 4、待锆材表面产生黄色烟雾并逐渐消失时用水对锆材表面进行冲洗,直至表面烟雾完全消失。为节约后处理费用,采用0.3Mpa压カ的水雾喷淋的方法,水雾喷淋的水量是酸洗溶液的8倍。
[0022] 5、将设备表面整体用水再次冲洗。
[0023] 实施例2
[0024] 本实施例与实施例1的区别在于,步骤2中按5份的氢氟酸+60份的硝酸+15份的水+0.1份Lan-826酸洗缓蚀 剂的比例(均为重量份)配制酸洗溶液;步骤3中喷涂酸洗溶液的量为姆平方分米2晕升,溶液在10°C的条件下10分钟内施用;步骤4中,米用0.2Mpa压カ的水雾喷淋的方法,水雾喷淋的水量是酸洗溶液的6倍。
[0025] 实施例3
[0026] 本实施例与实施例1的区别在于,步骤2中按12份的氢氟酸+75份的硝酸+25份的水+1份Lan-826酸洗缓蚀剂的比例(均为重量份)配制酸洗溶液;步骤3中喷涂酸洗溶液的量为姆平方分米5晕升,溶液在20°C的条件下10分钟内施用;步骤4中,米用0.5Mpa压カ的水雾喷淋的方法,水雾喷淋的水量是酸洗溶液的10倍。
[0027] 本发明所述的锆材是纯锆材或锆重量占30%以上的合金。Lan-826酸洗缓蚀剂为
市售产品。

Claims (6)

1.一种锆材酸洗液,其特征在于,由以下组分混合而成,按重量份计: 氢氟酸:5-12份; 硝酸:60-75份; 水:15-25 份; 缓蚀剂:0.1-1份。
2.根据权利要求1所述的锆材酸洗液,其特征在于,在低于32°C的条件下配制锆材酸洗液。
3.根据权利要求1所述的锆材酸洗液,其特征在于,所述缓蚀剂为Lan-826酸洗缓蚀齐U。
4.权利要求1所述的锆材酸洗液的酸洗方法,其特征在于,在10-20°C下,将锆材酸洗液在10分钟内喷涂到锆材表面,喷涂酸洗液的量为每平方分米2-5毫升,待锆材表面产生黄色烟雾并逐渐消失时对锆材表面用水进行冲洗,直至表面烟雾完全消失。
5.根据权利要求4所述的酸洗方法,其特征在于,采用0.2-0.5Mpa压カ的水雾喷淋的方法冲洗,水雾喷淋的水量是锆材酸洗液使用量的6-10倍,最后将锆材表面整体用水再次冲洗。
6.根据权利要求 4所述的酸洗方法,其特征在于,所述的锆材为纯锆材或锆占30%以上的合金。
CN201310243057.XA 2013-06-18 2013-06-18 一种锆材酸洗液的酸洗工艺 Active CN103320804B (zh)