CN103255124A - 一种聚丙烯腈固定化酶的制备方法 - Google Patents

一种聚丙烯腈固定化酶的制备方法 Download PDF

Info

Publication number
CN103255124A
CN103255124A CN2013101825651A CN201310182565A CN103255124A CN 103255124 A CN103255124 A CN 103255124A CN 2013101825651 A CN2013101825651 A CN 2013101825651A CN 201310182565 A CN201310182565 A CN 201310182565A CN 103255124 A CN103255124 A CN 103255124A
Authority
CN
China
Prior art keywords
enzyme
polyacrylonitrile
tunica fibrosa
preparation
solution
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013101825651A
Other languages
English (en)
Inventor
徐冉
李风亭
迟成龙
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tongji University
Original Assignee
Tongji University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tongji University filed Critical Tongji University
Priority to CN2013101825651A priority Critical patent/CN103255124A/zh
Publication of CN103255124A publication Critical patent/CN103255124A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种聚丙烯腈纳米纤维膜固定化酶的制备方法。将聚丙烯腈聚合物溶于N,N-二甲基甲酰胺，通过静电纺丝法制成聚丙烯腈纳米纤维膜。然后，将其浸入纯乙醇溶液中，通入氯化氢气体10~30分钟，通过化学键合的方法将酶固定到纳米纤维膜上。本发明利用聚丙烯腈纳米纤维膜的高空隙率和高机械强度，可以得到具有载酶量高、易于从反应体系中回收、可反复多次使用纳米纤维膜固定化酶。该固定化酶载体能够提高酶的利用率和降低生产成本，并且具有制备过程简单等优点。

Description

一种聚丙烯腈固定化酶的制备方法
技术领域
 本发明涉及一种使用聚丙烯腈纳米纤维膜固定化酶的制备方法。
背景技术
  固定化酶与游离酶相比，在保持其高效、专一及温和的酶催化反应特性的同时，还呈现贮存稳定性高、分离回收容易、多次重复使用、操作连续可控、工艺简便等特点。当酶以游离的状态存在时，一些缺陷如稳定性差、使用寿命短等未得到改善，将酶固定在分离膜上可以有效地避免上述的不足。另外，当酶以游离态存在时，由于酶膜表面的不利吸附而造成酶的空间结构改变或活性位点遮蔽，而降低了酶的活性。
固定化酶的材料和方法有很多种，其中纳米材料固定化酶因其高载酶量受到了研究者的青睐，尤其是一些具有多孔结构、大比表面积的载体材料有利于提高固定化酶的载酶量，并有利于底物向酶活性中心和产物向反应区域以外扩散以提高固定化酶的生物活性和催化效率。具有空间连续性的纳米纤维膜作为固定化酶的载体具有较大的比表面积和高空隙率，并且可以通过纺丝条件进行调控等优点，近年来越来越引起人们的重视。[1] Mincheva R, Manolova N, Paneva D, Roshkov I. Preparation of polyelectrolyte-containing nanofibers by electrospinning in the presence of a non-ionogenic water-soluble polymer.  J Bioactive Compat Polym  2005, 20: 419-435. CN100371372C通过电纺丙烯腈/磷脂共聚物，得到磷脂改性的丙烯腈纳米纤维，并通过物理吸附的方法将酶固定化在纳米纤维膜上。美国专利US20070077567A1提供了一种首先将酶单分子层共价键固定化在聚（苯乙烯-马来酸酐）纳米纤维上，然后再利用戊二醛将更多的酶分子与第一层固定化好的酶分子进行交联，在纳米纤维表面形成酶聚集体。但上述固定化酶的方法存在固定化过程操作繁琐、固定化酶催化稳定性较低和固定化载体机械强度较低等缺点。
因此有必要研制一种固定化酶过程操作简单且具有稳定结构、比表面积高和固定化酶材料机械强度高的纳米纤维膜用于酶的固定化，以有效的提高固定化酶的载酶量、提高固定化酶的催化效率，同时易于从反应体系中回收且重复使用，极大地提高酶的利用率和降低生产成本。
发明内容
  针对一些用于固定化酶的载体容易导致酶催化稳定性降低、固定化酶过程操作繁琐、固定化材料机械强度低和难以回收等问题，本发明的目的在于提供一种具有高比表面积、高空隙率、固定化酶过程操作简单和固定化材料机械强度高的一种聚丙烯腈纳米纤维膜固定化酶的制备方法。
本发明提出的聚丙烯腈纳米纤维膜固定化酶的制备方法，具体步骤如下：
将聚丙烯腈纳米纤维膜浸入纯乙醇溶液中，通入氯化氢气体10~30分钟，进行活化处理取出聚丙烯腈纳米纤维膜并用pH为7.0的磷酸盐缓冲溶液充分冲洗，以除去聚丙烯腈纳米纤维膜上残余的乙醇；然后，将活化之后的纳米纤维膜浸入浓度为0.1~2毫克/毫升的酶磷酸盐缓冲溶液中，密封后于10~30℃、转速为30~120转/分钟条件下，震荡1~5小时；从溶液中取出处理后的聚丙烯腈纳米纤维膜，用去离子水反复冲洗3~5次，即可得到聚丙烯腈纳米纤维膜固定化酶；将固定化酶的纳米纤维膜浸入pH为5.0的磷酸缓冲溶液中，于4℃下储存备用。
本发明中，所述酶磷酸盐缓冲溶液上的酶为酚氧化酶、过氧化物酶、蛋白酶、淀粉酶或脂肪酶中任一种。
本发明中，聚丙烯腈纳米纤维膜的制备方法为：将聚丙烯腈溶于N,N-二甲基甲酰胺溶剂中，配成重量百分比为5%~10%的溶液。然后，将配好的溶液注入静电纺丝装置中，在电压为12~20千伏、喷丝头溶液流量为0.8~1.5毫升/小时、接受距离为10~20厘米的条件下进行静电纺丝得到纤维直径在100~600纳米的纤维膜。将得到的纤维膜放置于真空干燥箱中在30℃~50℃的条件下干燥5小时~12小时。
本发明中，所述聚丙烯腈的相对分子量为12~18万。
本发明的有益效果在于：
（1）聚丙烯腈纳米纤维膜的制备及其酶固定化操作过程简单。
（2）聚丙烯腈纳米纤维膜具有高比表面积和高空隙率，有利于提高固定化酶的载酶量和提高固定化酶的催化稳定性。
（3）聚丙烯腈纳米纤维膜作为酶的固定化载体，易于从反应体系中回收，可以重复使用，极大地提高酶的利用率和降低生产成本。
（4）聚丙烯腈纳米纤维膜的机械强度高，能够反复用于反应体系中，为酶的工业化应用提供了基础。
附图说明
图1为实施例1所得到的聚丙烯腈纳米纤维膜固定化漆酶的扫描电镜图；
图2为实施例3所得到的聚丙烯腈纳米纤维膜固定化辣根过氧化物酶扫描电镜图。
具体实施方式
以下实施实例对本发明做更详细的描述，但所述例不构成对本发明的限制。
实施例1
聚丙烯腈纳米纤维膜的制备方法为：将聚丙烯腈溶于N,N-二甲基甲酰胺溶剂中，配成重量百分比为5%~10%的溶液。然后，将配好的溶液注入静电纺丝装置中，在电压为12~20千伏、喷丝头溶液流量为0.8~1.5毫升/小时、接受距离为10~20厘米的条件下进行静电纺丝得到纤维直径在100~600纳米的纤维膜。将得到的纤维膜放置于真空干燥箱中在30℃~50℃的条件下干燥5小时~12小时。
将1克聚丙烯腈纳米纤维膜浸入纯乙醇溶液中，通入氯化氢气体10分钟。取出纳米纤维膜并用pH为7.0的磷酸盐缓冲溶液充分冲洗，以除去膜上残余乙醇。然后，将活化之后的纳米纤维膜浸入浓度为0.5毫克/毫升的漆酶磷酸盐缓冲溶液中，密封后于15℃、转速为50转/分钟条件下，震荡2小时。从溶液中取出膜，用去离子水反复冲洗3次，即可得到聚丙烯腈纳米纤维膜固定化漆酶。将固定化漆酶的纳米纤维膜浸入pH为5.0的磷酸缓冲溶液中，于4℃下储存备用。
 从图1中扫描电镜的结果可以看出，上述得到的聚丙烯腈纳米纤维膜固定化漆酶形貌和结构较好，纤维直径也比较的均匀。
实施例2
将1克聚丙烯腈纳米纤维膜浸入纯乙醇溶液中，通入氯化氢气体20分钟。取出纳米纤维膜并用pH为7.0的磷酸盐缓冲溶液充分冲洗，以除去膜上残余乙醇。然后，将活化之后的纳米纤维膜浸入浓度为1.0毫克/毫升的漆酶磷酸盐缓冲溶液中，密封后于30℃、转速为80转/分钟条件下，震荡3小时。从溶液中取出膜，用去离子水反复冲洗5次，即可得到聚丙烯腈纳米纤维膜固定化漆酶。将固定化漆酶的纳米纤维膜浸入pH为5.0的磷酸缓冲溶液中，于4℃下储存备用。
实施例3
将1克聚丙烯腈纳米纤维膜浸入纯乙醇溶液中，通入氯化氢气体15分钟。取出纳米纤维膜并用pH为7.0的磷酸盐缓冲溶液充分冲洗，以除去膜上残余乙醇。然后，将活化之后的纳米纤维膜浸入浓度为1.0毫克/毫升的辣根过氧化物酶磷酸盐缓冲溶液中，密封后于20℃、转速为60转/分钟条件下，震荡1.5小时。从溶液中取出膜，用去离子水反复冲洗3次，即可得到聚丙烯腈纳米纤维膜固定化辣根过氧化物酶、。将固定化辣根过氧化物酶的纳米纤维膜浸入pH为5.0的磷酸缓冲溶液中，于4℃下储存备用。
 从图2中扫描电镜的结果可以看出，上述得到的聚丙烯腈纳米纤维膜固定化辣根过氧化物酶的形貌和结构较好，纤维直径也比较的均匀。
实施例4
将1克聚丙烯腈纳米纤维膜浸入纯乙醇溶液中，通入氯化氢气体25分钟。取出纳米纤维膜并用pH为7.0的磷酸盐缓冲溶液充分冲洗，以除去膜上残余乙醇。然后，将将活化之后的纳米纤维膜浸入浓度为1.5毫克/毫升的辣根过氧化物酶磷酸盐缓冲溶液中，密封后于30℃、转速为120转/分钟条件下，震荡3小时。从溶液中取出膜，用去离子水反复冲洗5次，即可得到聚丙烯腈纳米纤维膜固定化辣根过氧化物酶。将固定化辣根过氧化物酶的纳米纤维膜浸入pH为5.0的磷酸缓冲溶液中，于4℃下储存备用。
 实施例5
将1克聚丙烯腈纳米纤维膜浸入纯乙醇溶液中，通入氯化氢气体15分钟。取出纳米纤维膜并用pH为7.0的磷酸盐缓冲溶液充分冲洗，以除去膜上残余乙醇。然后，将活化之后的纳米纤维膜浸入浓度为0.5毫克/毫升的过氧化氢酶磷酸盐缓冲溶液中，密封后于10℃、转速为40转/分钟条件下，震荡1小时。从溶液中取出膜，用去离子水反复冲洗3次，即可得到聚丙烯腈纳米纤维膜固定化辣根过氧化物酶。将固定化辣根过氧化物酶的纳米纤维膜浸入pH为5.0的磷酸缓冲溶液中，于4℃下储存备用。
  实施例6
将1克聚丙烯腈纳米纤维膜浸入纯乙醇溶液中，通入氯化氢气体30分钟。取出纳米纤维膜并用pH为7.0的磷酸盐缓冲溶液充分冲洗，以除去膜上残余乙醇。然后，将活化之后的纳米纤维膜浸入浓度为1.5毫克/毫升的过氧化氢酶磷酸盐缓冲溶液中，密封后于25℃、转速为80转/分钟条件下，震荡3小时。从溶液中取出膜，用去离子水反复冲洗4次，即可得到聚丙烯腈纳米纤维膜固定化辣根过氧化物酶。将固定化辣根过氧化物酶的纳米纤维膜浸入pH为5.0的磷酸缓冲溶液中，于4℃下储存备用。

Claims (4)

1.一种聚丙烯腈纳米纤维膜固定化酶的制备方法，其特征在于具体步骤如下：
将聚丙烯腈纳米纤维膜浸入纯乙醇溶液中，通入氯化氢气体10~30分钟，进行活化处理取出聚丙烯腈纳米纤维膜并用pH为7.0的磷酸盐缓冲溶液充分冲洗，以除去聚丙烯腈纳米纤维膜上残余的乙醇；然后，将活化之后的纳米纤维膜浸入浓度为0.1~2毫克/毫升的酶磷酸盐缓冲溶液中，密封后于10~30℃、转速为30~120转/分钟条件下，震荡1~5小时；从溶液中取出处理后的聚丙烯腈纳米纤维膜，用去离子水反复冲洗3~5次，即可得到聚丙烯腈纳米纤维膜固定化酶；将固定化酶的纳米纤维膜浸入pH为5.0的磷酸缓冲溶液中，于4℃下储存备用。
2.根据权利要求1所述的制备方法，其特征在于所述酶磷酸盐缓冲溶液上的酶为酚氧化酶、过氧化物酶、蛋白酶、淀粉酶或脂肪酶中任一种。
3.根据权利要求1所述的制备方法，其特征在于聚丙烯腈纳米纤维膜的制备方法为：将聚丙烯腈溶于N,N-二甲基甲酰胺溶剂中，配成重量百分比为5%~10%的溶液；然后，将配好的溶液注入静电纺丝装置中，在电压为12~20千伏、喷丝头溶液流量为0.8~1.5毫升/小时、接受距离为10~20厘米的条件下进行静电纺丝得到纤维直径在100~600纳米的纤维膜；将得到的纤维膜放置于真空干燥箱中在30℃~50℃的条件下干燥5小时~12小时。
4.根据权利要求3所述的制备方法，其特征在于所述聚丙烯腈的相对分子量为12~18万。
CN2013101825651A 2013-05-17 2013-05-17 一种聚丙烯腈固定化酶的制备方法 Pending CN103255124A (zh)