CN103242626A - 新型生物可分解材料 - Google Patents
新型生物可分解材料 Download PDFInfo
- Publication number
- CN103242626A CN103242626A CN2012100310121A CN201210031012A CN103242626A CN 103242626 A CN103242626 A CN 103242626A CN 2012100310121 A CN2012100310121 A CN 2012100310121A CN 201210031012 A CN201210031012 A CN 201210031012A CN 103242626 A CN103242626 A CN 103242626A
- Authority
- CN
- China
- Prior art keywords
- starch
- weight percent
- poly
- decomposing material
- group
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种生物可分解材料,包含有:可生物分解型聚酯,其重量百分比为50%-70%。淀粉,其重量百分比为25%-50%,L-赖氨酸二异氰酸酯LDI(L-Lysine Diisocyanate),其重量百分比为0.5%-2%。
Description
技术领域
本发明与减碳环保的材料有关,特别是涉及一种生物可分解材料。
背景技术
目前市面上有许多的生物可分解材料,这些材料虽都有着可分解的特质,可是在材料本身的特性上却或多或少都有一些缺点。例如有些材料虽然可分解但是可分解的百分比并不高,又有些虽然可分解的百分比很高但是材料本身的结构强度却不佳,这会使得材料本身在被应用时的领域或是应用范围无形中受到了许多限制。因此有必要研发一种较理想的生物可分解材料供产业广泛运用。
发明内容
本发明的目的在于提供一种可分解百分比高且材料本身结构强度强的生物可分解材料。
为实现上述目的,本发明提供的生物可分解材料,包含有:
可生物分解型聚酯,其重量百分比为50%-70%;
淀粉,其重量百分比为25%-50%;
L-赖氨酸二异氰酸酯LDI(L-Lysine Diisocyanate),其重量百分比为0.5%-2%。
所述的生物可分解材料,其中,该可生物分解型聚酯是聚丁二酸丁二醇酯PBS(Poly Butylenes Succinate)、聚己内酯PCL(Poly Capro Lactone)、聚乳酸PLA(Poly Lactic Acid)、聚丁二酸己二酸丁二醇共聚酯PB SA(PolyButylene Succinate-co-Adipate)、聚对苯二甲酸丁二酸丁二酯PBAT(PolyButylene Adipate-co-Terephthalate)、聚甘醇酸PGA(Poly Glycolic Acid)、聚乙烯醇PVA(Poly Vinyl Alcohol)的族群所选择。
所述的生物可分解材料,其中,淀粉为α淀粉、玉米淀粉、马铃薯淀粉、树薯淀粉、米淀粉或小麦淀粉等谷类淀粉的族群所选择。
所述的生物可分解材料,其中,可生物分解型聚酯,其重量百分比为60%-70%;淀粉,其重量百分比为29%-39%;L-赖氨酸二异氰酸酯LDI(L-Lysine Diisocyanate),其重量百分比为0.5%-1%。
所述的生物可分解材料,其中,拉力强度以ASTM D638方法检测时在290kgf/cm2以上。
本发明提供生物可分解材料,具有一定的结构强度并且能够被生物分解,是一种良好的复合材料。
具体实施方式
本发明生物可分解材料包含有:可生物分解型聚酯,其重量百分比为50%-70%;淀粉,其重量百分比为25%-50%;L-赖氨酸二异氰酸酯LDI(L-Lysine Diisocyanate)其重量百分比为0.5%-2%。
为能详细说明本发明的特征及功效,以下列测试数据表进行说明。
本发明生物可分解材料包含有:
可生物分解型聚酯例如聚丁二酸丁二醇酯PBS(Poly ButylenesSuccinate)、聚己内酯PCL(Poly Capro Lactone)、聚乳酸PLA(Poly LacticAcid)、聚丁二酸己二酸丁二醇共聚酯PBSA(Poly ButyleneSuccinate-co-Adipate)、聚对苯二甲酸丁二酸丁二酯PBAT(Poly ButyleneAdipate-co-Terephthalate)、聚甘醇酸PGA(Poly Glycolic Acid)、聚乙烯醇PVA(Poly Vinyl Alcohol)族群所选择者,其重量百分比为50%-70%。
淀粉例如α淀粉、玉米淀粉、马铃薯淀粉、树薯淀粉、米淀粉或小麦淀粉等谷类淀粉之族群所选择者,其重量百分比为25%-50%。
L-赖氨酸二异氰酸酯LDI(L-Lysine Diisocyanate)其重量百分比为0.5%-2%。
以本发明所提供的成分组合可以作为母料或以适当比例与其他塑料材料混合,以提供一可生物分解并且具有良好材料结构强度的生物可分解塑料制品。
以本发明的组成成分进行材料强度检测,其检测结果如表1及表2所示,为本发明的A组测试数据,表1中的百分比为重量百分比,在A组的测试中生物可分解型聚酯重量百分比为60%。
经由上列的检测数据可以得知,在材料组成成分加以调整后所得的测试数字仍保有相当的材料强度特性。
如表3及表4所示则为本发明以不同成分比例所进行的材料强度检测。在B组的测试中生物可分解型聚酯重量百分比为50%
如表5及表6所示则为本发明另一组不同成分比例所进行材料强度检测的数字。在C组的测试中生物可分解型聚酯重量百分比为70%。
由上列多组检测结果表明,本发明的生物可分解材料具有良好的结构强度,特别是在其最佳的成分比:可生物分解型聚酯,其重量百分比为50%。淀粉,其重量百分比为49%。L-赖氨酸二异氰酸酯LDI(L-LysineDiisocyanste)其重量百分比为1%时可以具有最佳的拉力强度。而其最佳的成分比是:可生物分解型聚酯,其重量百分比为70%。淀粉,其重量百分比为29%。L-赖氨酸二异氰酸酯LDI(L-Lysine Diisocyanste)其重量百分比为1%时可以具有最佳的耐冲击强度。
另外,以本发明的材料可生物分解型聚酯,其重量百分比为50%。淀粉,其重量百分比为49%。L-赖氨酸二异氰酸酯LDI(L-Lysine Diisocyanste)其重量百分比为1%送交塑料工业技术发展中心进行拉力测试及耐冲击测试的结果则如附件1所示。
并且由塑料工业技术发展中心以ISO14855-1试验方法进行生物分解测试,其结果如附件1所示,在该测试中可以看到在59天时分解率已达50%,而在第113天时分解率超过99%,如附件2所示。经由上述的测试结果证明,本发明的生物可分解材料可以提供一定的结构强度并且能够被生物分解,是一种良好的复合材料。
以上实施例仅为本发明的实施说明,并非作为限定本发明的范围,其他依据实施例的改良变化实质仍属于本发明的范围。
表1
A-1组 | A-2组 | A-3组 | A-4组 | A-5组 | |
PBS(Poly Butylene Succinate)60% | 100% | 60% | 60% | 60% | 60% |
α淀粉 40% | --- | 40% | 39.5% | 39% | 38% |
LDI(L-Lysine Diisocyanate) 0.5%~2% | --- | --- | 0.5% | 1% | 2% |
表2
表3
B-1组 | B-2组 | B-3组 | |
PBS(Poly Butylene Succinate)50% | 50% | 50% | 50% |
α淀粉 50% | 49.5% | 49% | 48% |
LDI(L-Lysine Diisocyanste) 0.5%~2% | 0.5% | 1% | 2% |
表4
表5
C-1组 | C-2组 | C-3组 | |
PBS(Poly Butylene Succinate)70% | 70% | 70% | 70% |
A淀粉 30% | 29.5% | 29% | 28% |
LDI(L-Lysine Diisocyanste) 0.5%~2% | 0.5% | 1% | 2% |
表6
Claims (5)
1.一种生物可分解材料,包含有:
可生物分解型聚酯,其重量百分比为50%-70%;
淀粉,其重量百分比为25%-50%;
L-赖氨酸二异氰酸酯,其重量百分比为0.5%-2%。
2.根据权利要求1所述的生物可分解材料,其中,该可生物分解型聚酯是聚丁二酸丁二醇酯、聚己内酯、聚乳酸、聚丁二酸己二酸丁二醇共聚酯、聚对苯二甲酸丁二酸丁二酯、聚甘醇酸、聚乙烯醇族群所选择。
3.根据权利要求1所述的生物可分解材料,其中,淀粉为α淀粉、玉米淀粉、马铃薯淀粉、树薯淀粉、米淀粉或小麦淀粉谷类淀粉族群所选择。
4.根据权利要求2所述的生物可分解材料,其中,可生物分解型聚酯,其重量百分比为60%-70%;淀粉,其重量百分比为29%-39%;L-赖氨酸二异氰酸酯,其重量百分比为0.5%-1%。
5.根据权利要求1所述的生物可分解材料,其中,拉力强度以ASTMD638方法检测时在290kgf/cm2以上。