CN103233236A - 一种用于消除银器表面黑斑或黄斑的药剂及其方法 - Google Patents
一种用于消除银器表面黑斑或黄斑的药剂及其方法 Download PDFInfo
- Publication number
- CN103233236A CN103233236A CN2013101338561A CN201310133856A CN103233236A CN 103233236 A CN103233236 A CN 103233236A CN 2013101338561 A CN2013101338561 A CN 2013101338561A CN 201310133856 A CN201310133856 A CN 201310133856A CN 103233236 A CN103233236 A CN 103233236A
- Authority
- CN
- China
- Prior art keywords
- silverware
- medicament
- magnesium
- liquid medicine
- pending
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种用于消除银器表面黑斑或黄斑的药剂,包括按重量份数计的以下组分:碳酸氢钠50~80、氢氧化钠8~12、磷酸二氢钾40~44和纯铜粉0~5及其方法,包括步骤:将待处理的银器表面冲洗干净;将镁条或者镁片与待处理的银器表面紧密接触;将所述的药剂溶解于10℃~60℃的水中,使银器完全没入药剂溶液中;将药剂溶液的温度保持在20℃~45℃,银器浸泡时间0.5~2小时后用清水冲洗干净。本发明通过控制电解质浓度控制反应的速度,修复了银器表面的光洁度,增强了修复效果。
Description
技术领域
本发明属于化工技术领域,具体涉及一种用于消除银器表面黑斑或黄斑的药剂及其方法。
背景技术
随着人民生活水平的提高和收藏热的兴起,银器和镀银器物已经日益普及。但长期暴露在空气中的银其,表面容易产生黑色的或黄色的斑点,逐渐覆盖银器的整个表面,影响器物的美观性和观赏性,并大大降低其收藏价值。
银器表面黑色或黄色斑点的主要成分是硫化银,同时含有少量的氯化银、氧化银等成分。
除去清洁银器表面黑斑或者黄斑通常采用的方法有物理抛光法、化学腐蚀法、化学还原法等。但是目前没有一种简单有效且不损伤银器表面的方法去除银器表面的黑斑或者黄斑。更没有一种适合日常家庭使用的,不损伤银器表面的方法,
物理抛光法系采用各类打磨材料例如硅藻土、丝绸、毛绒等,打磨发黑银器的表面。该方法的主要缺点是,打磨会导致银器表面银质的损失,且无法处理表面花纹较复杂的银器;操作需要一定的工艺技巧,普通家庭难于掌握和使用该方法。
化学腐蚀法系采用化学药剂,与银器表面的硫化银反应,达到除去硫化银的目的。该方法的主要缺点是,会导致银器表面银质的损失,尤其不适用于镀银器物或具有纪念意义的银器。所采用的化学药剂有一定的腐蚀性,普通家庭使用该方法须高度注意安全。同时该方法对于去除氧化银没有效果。
化学还原法系将银器放入含电解质的水溶液中,保持银器与铝箔等活泼金属的直接接触,利用电化学反应将硫化银还原成银。此方法可以彻底还原银器表面的硫化银、氯化银、氧化银,且银器表面银质不会损失。缺点是反应后银器表面光洁度有所降低,影响器物的美观性,还原反应导致银表面活性提高,会导致银器表面再次发黑发黄的速度加快。这是由于传统的还原反应中,无法保持还原反应的速度缓慢且均匀,当反应速度过快时,银分子在银器表面重新排列,降低了光洁度和增加了表面积,导致银器容易被再次硫化。同时由于铜的性质比银活泼,当镀银铜器的铜质暴露在表面时,即无法采用化学还原法进行修复。
目前尚没有复原发黑银器的万全之策。尤其对于博物馆,由于无法将变黑的银器完美修复,对于具有历史意义或者纪念价值的银器只能展出其复制品或者仿制品。
发明内容
本发明的目的在于克服上述现有技术的不足,提供一种还原银器表面黑斑黄斑的药剂及其方法,不损伤银器表面光洁性,同时可以清理任何形状的银器,包括表面有损伤的镀银铜器。该方法操作简单,危险性极低,无论是博物馆等专业机构还是普通家庭都可以放心使用。
本发明的技术解决方案如下:
一种用于消除银器表面黑斑或黄斑的药剂,其特点在于,该药剂包括按重量份数计的以下组分:
碳酸氢钠 50~80
氢氧化钠 8~12
磷酸二氢钾 40~44
纯铜粉 0~5。
优选的,该药剂包括按重量份数计的以下组分:
碳酸氢钠 65
氢氧化钠 10
磷酸二氢钾 42
纯铜粉 0。
本发明还涉及一种利用上述药剂消除银器表面黑斑或黄斑的方法,该方法包括如下步骤:
1)将待处理的银器表面冲洗干净,确保没有油污、灰尘或者泥土污垢;
2)将镁条或者镁片与待处理的银器表面紧密接触;
3)将所述的药剂溶解于10℃~60℃的水中,药剂与水的重量比例为1∶5~1∶20;
4)将所述待处理的银器放入容器中,加入步骤3)得到药剂溶液,使银器完全没入溶液中;
5)将溶液温度保持在20℃~45℃,银器浸泡时间0.5~2小时后用清水冲洗干净。
优选的,步骤2)中采用去除保护层,将金属镁完全露出的镁条或镁片,并且将镁条或镁片紧密缠绕在银器表面,以确保镁条与银器表面的接触。
与现有技术相比,本发明的有益效果包括:利用镁和银器的接触,以获得更高的接触电势差,而较高的电势差,将有利于通过控制电解质浓度控制反应的速度;采用碳酸氢钠、氢氧化钠、磷酸二氢钾和水,组成药剂溶液有效控制碳酸氢钠的电离程度,保持电解反应速度均匀可控,同时克服了传统的碱性或者酸性药剂导致金属镁被直接腐蚀的可能性;同时,磷酸二氢根的存在能起到类似电解抛光的作用,保持器物表面的光洁度;同时金属镁在弱碱性环境下可以直接与被还原出的硫和氯发生反应,进一步增强了修复效果。
具体实施方式
下面结合实施例对本发明作进一步说明,但不应以此限制本发明的保护范围。
实施例1
首先,称取碳酸氢钠50克、氢氧化钠10克、磷酸二氢钾44克和纯铜粉5克制备药剂,并将药剂溶解于10℃的水中,药剂与水的重量比例为1∶8得到药剂溶液;
然后,将待处理的银器表面冲洗干净,确保没有油污、灰尘或者泥土污垢;
接着,将镁条缠绕在待处理银器表面,使其与银器表面紧密接触;
其次,将待处理的银器放入容器中,并加入药剂溶液,使银器完全没入药剂溶液中,将该药剂溶液的温度保持在20℃~45℃,银器浸泡时间0.5小时;
最后,用清水冲洗干净,得到表面光洁如新的银器。
实施例2
首先,称取碳酸氢钠65克、氢氧化钠10克和磷酸二氢钾42克制备药剂,并将药剂溶解于30℃的水中,药剂与水的重量比例为1∶14得到药剂溶液;
然后,将待处理的银器表面冲洗干净,确保没有油污、灰尘或者泥土污垢;
接着,将镁条缠绕在待处理银器表面,使其与银器表面紧密接触;
其次,将待处理的银器放入容器中,并加入药剂溶液,使银器完全没入药剂溶液中,将该药剂溶液的温度保持在20℃~45℃,银器浸泡时间0.5小时;
最后,用清水冲洗干净,得到表面光洁如新的银器。
实施例3
首先,称取碳酸氢钠70克、氢氧化钠8克、磷酸二氢钾42克和纯铜粉2克制备药剂,并将药剂溶解于50℃的水中,药剂与水的重量比例为1∶20得到药剂溶液;
然后,将待处理的银器表面冲洗干净,确保没有油污、灰尘或者泥土污垢;
接着,将镁片缠绕在待处理银器表面,使其与银器表面紧密接触;
其次,将待处理的银器放入容器中,并加入药剂溶液,使银器完全没入药剂溶液中,将该药剂溶液的温度保持在20℃~45℃,银器浸泡时间0.5小时;
最后,用清水冲洗干净,得到表面光洁如新的银器。
实施例4
首先,称取碳酸氢钠80克、氢氧化钠60克和磷酸二氢钾41克制备药剂,并将药剂溶解于60℃的水中,药剂与水的重量比例为1∶20得到药剂溶液;
然后,将待处理的银器表面冲洗干净,确保没有油污、灰尘或者泥土污垢;
接着,将镁条缠绕在待处理银器表面,使其与银器表面紧密接触;
其次,将待处理的银器放入容器中,并加入药剂溶液,使银器完全没入药剂溶液中,将该药剂溶液的温度保持在20℃~45℃,银器浸泡时间0.5小时;
最后,用清水冲洗干净,得到表面光洁如新的银器。
虽然本发明已将较佳实施例揭示如上,然其并非用以限定本发明的内容,任何熟悉此技艺者,在不脱离本发明的主要精神和内容范围内,当可作各种更动与润饰,因此发明的保护范围应以申请专利的实际权利要求范围为准。
Claims (4)
1.一种用于消除银器表面黑斑或黄斑的药剂,其特征在于,该药剂包括按重量份数计的以下组分:
碳酸氢钠 50~80
氢氧化钠 8~12
磷酸二氢钾 40~44
纯铜粉 0~5。
2.根据权利要求1去除银器表面硫化银的药剂,其特征在于,该药剂包括按重量份数计的以下组分:
碳酸氢钠 65
氢氧化钠 10
磷酸二氢钾 42
纯铜粉 0。
3.一种利用权利要求1或2所述的药剂消除银器表面黑斑或黄斑的方法,其特征在于,该方法包括如下步骤:
1)将待处理的银器表面冲洗干净,确保没有油污、灰尘或者泥土污垢;
2)将镁条或者镁片与待处理的银器表面紧密接触;
3)将所述的药剂溶解于10℃~60℃的水中,药剂与水的重量比例为1∶8~20得到药剂溶液;
4)将所述待处理的银器放入容器中,加入步骤3)得到药剂溶液,使银器完全没入药剂溶液中;
5)将药剂溶液的温度保持在20℃~45℃,银器浸泡时间0.5~2小时后用清水冲洗干净。
4.根据权利要求3所述的方法,其特征在于,步骤2)中所采用的是去除保护层,将金属镁完全露出的镁条或镁片,该镁条或镁片缠绕在待处理银器表面。