CN103219296A - 用于半导体封装的多功能膜及其制造方法 - Google Patents
用于半导体封装的多功能膜及其制造方法 Download PDFInfo
- Publication number
- CN103219296A CN103219296A CN2013101086931A CN201310108693A CN103219296A CN 103219296 A CN103219296 A CN 103219296A CN 2013101086931 A CN2013101086931 A CN 2013101086931A CN 201310108693 A CN201310108693 A CN 201310108693A CN 103219296 A CN103219296 A CN 103219296A
- Authority
- CN
- China
- Prior art keywords
- daf
- film
- modulus
- elasticity
- psa
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种多功能膜及其制造方法,所述多功能膜包括:PO膜;PSA,形成在PO膜上;第一DAF,形成在PSA上;第二DAF,形成在第一DAF上,其中,第二DAF的弹性模量大于第一DAF的弹性模量。
Description
技术领域
本发明涉及一种用于半导体封装的多功能膜,更具体地说,涉及一种能够防止芯片在切割的过程中的翘曲的用于半导体封装的多功能膜。
背景技术
在半导体封装件的制备过程中,通常包括将形成有预定图案的晶圆切割开以形成单个半导体芯片的步骤。
图1A至图1C示出了现有的芯片切割过程的示意图。图1A示出了现有技术中使用的膜的结构;图1B示出了晶圆和膜在切割过程中的状态;图1C示出了切割后的半导体芯片。
如图1A至图1C所示,现有技术中使用的膜由DAF、PSA和PO膜顺序地堆叠而成。在半导体芯片的制造过程中,将晶圆附着到DAF上。然后,在晶圆上形成预定的图案,在将晶圆切割为单独的半导体芯片。然而,如图1B所示,在切割过程中,由于晶圆的厚度较小,因此在切割过程中,DAF与PSA分离,使得晶圆和DAF产生翘曲,因此会影响切割的精确度,从而得到有缺陷的半导体芯片(如图1C所示)。因此,会降低产品良率,从而增大了制造成本。
发明内容
本发明的一方面提供一种多功能膜,所述多功能膜包括:PO膜;PSA,形成在PO膜上;第一DAF,形成在PSA上;第二DAF,形成在第一DAF上,其中,第二DAF的弹性模量大于第一DAF的弹性模量。
第一DAF和第二DAF之间还可设置有粘合层。
第二DAF的弹性模量可为1Gpa至9999Gpa,第一DAF的弹性模量可为1Mpa至4999Mpa。
在芯片切割过程中,晶圆可设置在第二DAF上。
第一DAF可包括10%-30%的丙烯酸共聚物、20%-30%的环氧树脂、10%-20%的硬化剂和30%-40%的无定形硅,第二DAF可包括10%-20%的丙烯酸共聚物、10%-20%的环氧树脂、10%-20%的硬化剂和50%-60%的无定形硅。
本发明的另一方面提供一种多功能膜的制造方法,该方法包括下述步骤:设置PO膜;在PO膜上设置PSA;在PSA上设置第一DAF;在第一DAF上设置第二DAF,其中,第二DAF的弹性模量大于第一DAF的弹性模量。
附图说明
通过下面结合附图进行的对实施例的描述,本发明的上述和/或其他目的和优点将会变得更加清楚,其中:
图1A示出了现有技术中使用的膜的结构;
图1B示出了晶圆和膜在切割过程中的状态;
图1C示出了切割后的半导体芯片;
图2A示出了根据本发明示例性实施例的多功能膜的结构;
图2B示出了根据本发明示例性实施例的晶圆和多功能膜在切割过程中的状态;
图2C示出了根据本发明示例性实施例的切割后的半导体芯片。
具体实施方式
下面将参照附图更详细地描述本发明,在附图中示出了本发明的示例性实施例,然而本领域技术人员应当理解,仅以说明性的意义来提供这些实施例,而不是出于限制性的目的。相反,提供这些实施例使得本公开将是彻底的和完整的,并将把本发明的范围充分地传达给本领域技术人员。
图2A示出了根据本发明示例性实施例的多功能膜的结构;图2B示出了根据本发明示例性实施例的晶圆和多功能膜在切割过程中的状态;图2C示出了根据本发明示例性实施例的切割后的半导体芯片。
参照图2A,根据本发明示例性实施例的多功能膜包括:PO膜100;PSA200,形成在PO膜100上;第一DAF(即,芯片粘结膜die attach film)310,形成在PSA200上;第二DAF320,形成在第一DAF310上。其中,第二DAF320的弹性模量大于第一DAF310的弹性模量。
根据本发明的一个实施例,PO膜100主要起到支撑上层材料的作用,其中,PO膜可由聚烯烃(polyolefin)形成。
根据本发明的一个实施例,PSA200的主要作用是在PO层与DAF层之间起粘结作用,并且对于两种材质具有选择性的粘结力,其中,PSA200可由聚砜酰胺(polysulfone amide)形成。
根据本发明的一个实施例,第二DAF320(高模量DAF)的弹性模量为1Gpa至9999Gpa,第一DAF310(低模量DAF)的弹性模量为1Mpa至4999Mpa。第一DAF310的主要作用是实现芯片与基板的粘结,第一DAF310可以包括丙烯酸共聚物(Acrylic Copolymer)、环氧树脂(Epoxy resin)、硬化剂(Hardner)、无定形硅(Amorphous Silica)。第二DAF320的主要作用是直接与芯片粘结降低切割过程的翘曲,第二DAF320可以包括丙烯酸共聚物(Acrylic Copolymer)、环氧树脂(Epoxy resin)、硬化剂(Hardner)、无定形硅(Amorphous Silica)。第一DAF310与第二DAF320的不同主要在于硬度(弹性模量)的差异,通过调节不同高分子树脂的配比实现。例如,第一DAF包括10%-30%的丙烯酸共聚物、20%-30%的环氧树脂、10%-20%的硬化剂和30%-40%的无定形硅,第二DAF包括10%-20%的丙烯酸共聚物、10%-20%的环氧树脂、10%-20%的硬化剂和50%-60%的无定形硅。
参照图2B,在半导体芯片的制造过程中,首先将晶圆400附着在第二DAF320上,然后在晶圆上形成用于制造半导体芯片的图案,然后,对图案化之后的晶圆400执行切割工艺。如图2中所示,在切割过程中,由于第二DAF320具有较高的弹性模量,所以在切割的过程中不会发生翘曲,另一方面,由于第一DAF310具有较低的弹性模量,所以在后续的工艺中,不会影响芯片与基板的结合力。
参照图2C,利用根据本发明示例性实施例的多功能膜制造的芯片500可具有完整的外观,不会发生翘曲等缺陷,因此能够提高产品良率,降低制造成本。
根据本发明的另一实施例,还可在第一DAF310与第二DAF320之间形成粘合层(未示出),从而可以确保第一DAF310与第二DAF320能够紧密结合。因此,能够在切割过程中更好地防止发生翘曲或其它问题。
下面将参照本发明的另一示例性实施例描述根据本发明的多功能膜的制造方法。在本实施例中,制造多功能膜的方法可包括下述步骤:设置PO膜;在PO膜上设置PSA;在PSA上设置第一DAF;在第一DAF上设置第二DAF。根据本实施例的方法中的PO膜、PSA、第一DAF以及第二DAF可以与根据前述实施例描述的PO膜、PSA、第一DAF以及第二DAF相同,因此在这里将省略对它们的详细描述。根据本发明的另一实施例,在形成第一DAF之后且在形成第二DAF之前,可在第一DAF上形成粘合层。
虽然已经结合附图具体描述了本发明的示例性实施例,但是本领域技术人员应当理解,在不脱离本发明的精神和范围的情况下,可以对这些实施例进行各种修改和改变,本发明的范围由权利要求书及其等同物限定。
Claims (10)
1.一种多功能膜,所述多功能膜包括:
PO膜;
PSA,形成在PO膜上;
第一DAF,形成在PSA上;
第二DAF,形成在第一DAF上,
其中,第二DAF的弹性模量大于第一DAF的弹性模量。
2.如权利要求1所述的多功能膜,其中,第一DAF和第二DAF之间设置有粘合层。
3.如权利要求1所述的多功能膜,其中,第二DAF的弹性模量为1Gpa至9999Gpa,第一DAF的弹性模量为1Mpa至4999Mpa。
4.如权利要求1所述的多功能膜,其中,在芯片切割过程中,晶圆设置在第二DAF上。
5.如权利要求1所述的多功能膜,其中,第一DAF包括10%-30%的丙烯酸共聚物、20%-30%的环氧树脂、10%-20%的硬化剂和30%-40%的无定形硅,第二DAF包括10%-20%的丙烯酸共聚物、10%-20%的环氧树脂、10%-20%的硬化剂和50%-60%的无定形硅。
6.一种多功能膜的制造方法,该方法包括下述步骤:
设置PO膜;
在PO膜上设置PSA;
在PSA上设置第一DAF;
在第一DAF上设置第二DAF,
其中,第二DAF的弹性模量大于第一DAF的弹性模量。
7.如权利要求6所述的方法,其中,在形成第一DAF之后且在形成第二DAF之前,在第一DAF上形成粘合层。
8.如权利要求6所述的方法,其中,第二DAF的弹性模量为1Gpa至9999Gpa,第一DAF的弹性模量为1Mpa至4999Mpa。
9.如权利要求6所述的方法,其中,在芯片切割过程中,晶圆设置在第二DAF上。
10.如权利要求6所述的方法,其中,第一DAF包括10%-30%的丙烯酸共聚物、20%-30%的环氧树脂、10%-20%的硬化剂和30%-40%的无定形硅,第二DAF包括10%-20%的丙烯酸共聚物、10%-20%的环氧树脂、10%-20%的硬化剂和50%-60%的无定形硅。