CN103103706A - Production process of copper ammonia blend fabric - Google Patents
Production process of copper ammonia blend fabric Download PDFInfo
- Publication number
- CN103103706A CN103103706A CN2012104460467A CN201210446046A CN103103706A CN 103103706 A CN103103706 A CN 103103706A CN 2012104460467 A CN2012104460467 A CN 2012104460467A CN 201210446046 A CN201210446046 A CN 201210446046A CN 103103706 A CN103103706 A CN 103103706A
- Authority
- CN
- China
- Prior art keywords
- copper ammonia
- cuprammonium
- fabric
- blending
- grey cloth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a production process of copper ammonia blend fabric. The production method of copper ammonia blend fabric includes the following craft steps: (1) blending copper ammonia blending grey fabric, carbon fibers and cotton fibers to obtain copper ammonia blend fabric; (2) washing the copper ammonia blending grey fabric in a water washer with a bath ratio of 1 to 30-50 and adding neutral cleaning agents and the temperature is 60 to 65 DEG C; (3) sinking the copper ammonia blend raw fabric which is washed by water in the water with a bate rate of 1 to 10-15, adding neutral refining agent solution with a addition of 5 to 10 grams per liter water, and processing 0.5 to 1 hour with a refining temperature of 65 to 70 DEG C; (4) placing the copper ammonia blend raw fabric which is refined into a dyeing machine and adding softener and levelling agent; (5) rinsing, drying and obtaining the copper ammonia blend fabric. The production method of copper ammonia blend fabric is manufactured by copper ammonia fibers, carbon fibers and cotton fibers does not damage antibiosis performance and meanwhile possesses good comfort.
Description
Technical field
The present invention relates to a kind of fabric, especially a kind of production technology of cuprammonium blended yarn woven fabric belongs to the textile garment technical field.
Background technology
Copper ammonia fibre is a kind of regenerated celulose fibre, it is that the natural cellulosic feedstocks such as cotton linter are dissolved in the liquor ammoniae fortis of Kocide SD or alkaline cupric salt, be made into spinning solution, copper ammonia fibre element molecular compound disintegrating and regeneration goes out cellulose in coagulating bath, the hydrate cellulose of generation through after process and namely obtain copper ammonia fibre.The cross section of copper ammonia fibre is rounded, and without skin-core structure, fiber can bear highly to carry to be stretched, and the monofilament that makes is thinner, so fabric is soft, gloss is soft, and silky touch is arranged.Because copper ammonia fibre is poor to the resistivity of the oxidants such as chlorine bleaches, hydrogen peroxide, so there is certain difficulty in the fabric of copper ammonia fibre and other fiber blends in follow-up pre-treatment, dyeing and rear arrangement process.
Summary of the invention
The objective of the invention is to overcome the deficiencies in the prior art, a kind of production technology of cuprammonium blended yarn woven fabric is provided, this cuprammonium blended yarn woven fabric is obtained by copper ammonia fibre, carbon fiber and cotton fiber blending, can not destroy the anti-microbial property of copper ammonia fibre, has good wearability.
According to technical scheme provided by the invention, the production technology of described cuprammonium blended yarn woven fabric is characterized in that, comprises following processing step:
(1) copper ammonia fibre, carbon fiber and cotton fiber blending are obtained cuprammonium blending grey cloth, the mass ratio of copper ammonia fibre, carbon fiber and cotton fiber is 40 ~ 60:1.5 ~ 3:37 ~ 58.5;
(2) washing: cuprammonium blending grey cloth is cleaned in rinsing machine, and bath raio is 1:30 ~ 50, and adds mild detergent, and the consumption of cleaning agent is every premium on currency 3 ~ 5g, and water temperature is 60 ~ 65 ℃, and washing time is 0.5 ~ 1 hour;
(3) concise: the cuprammonium blending grey cloth after washing is immersed in water, and bath raio is 1:10 ~ 15, and to add mass percentage concentration be 30 ~ 35% neutral scouring agent solution, and addition is every premium on currency 5 ~ 10g, processes 0.5 ~ 1 hour, and concise temperature is 65 ~ 70 ℃;
(4) dyeing: the cuprammonium blending grey cloth after concise is put into dyeing machine, and bath of dye liquor is than being 1:10 ~ 13, and every premium on currency adds 1 ~ 2g softener and 1 ~ 3g levelling agent, is warming up to 70 ~ 90 ℃, is incubated 10 ~ 15 minutes; Be warming up to again 110 ~ 120 ℃, be incubated 10 ~ 15 minutes; Be warming up to again 120 ~ 130 ℃, be incubated 30 ~ 45 minutes; Cool to room temperature, discharge dye liquor;
(5) rinsing, oven dry obtain described cuprammonium blended yarn woven fabric.
Programming rate in step (4) is 1 ~ 2 ℃/minute.
The production technology of cuprammonium blended yarn woven fabric of the present invention adopts copper ammonia fibre, carbon fiber and cotton fiber blending to obtain, and can not destroy the anti-microbial property of copper ammonia fibre, has simultaneously snugness of fit preferably.
The specific embodiment
The invention will be further described below in conjunction with specific embodiment.
Neutral scouring agent used in the present invention is neutral nonionic scouring agent, can be used for the pre-treatment of cotton and synthetic fabrics; The scouring agent QTQ-105 that the neutral scouring agent that adopts in the embodiment of the present invention can adopt Guangzhou universe Thailand chemical industry Co., Ltd to produce.
Embodiment one: a kind of production technology of cuprammonium blended yarn woven fabric comprises following processing step:
(1) copper ammonia fibre, carbon fiber and cotton fiber blending obtain cuprammonium blending grey cloth, and the mass ratio of copper ammonia fibre, carbon fiber and cotton fiber is 40:1.5:58.5
(2) washing: cuprammonium blending grey cloth is cleaned in rinsing machine, and bath raio is 1:30, and adds mild detergent, and the consumption of cleaning agent is every premium on currency 3g, and water temperature is 60 ℃, and washing time is 1 hour;
(3) concise: the cuprammonium blending grey cloth after washing is immersed in water, and bath raio is 1:10, and to add mass percentage concentration be 30% neutral scouring agent solution, and addition is every premium on currency 5g, processes 0.5 hour, and concise temperature is 65 ℃;
(4) dyeing: the cuprammonium blending grey cloth after concise is put into dyeing machine, and bath of dye liquor is than being 1:10, and every premium on currency adds 1g softener and 1g levelling agent, is warming up to 70 ℃, is incubated 10 minutes; Be warming up to again 110 ℃, be incubated 10 minutes; Be warming up to again 120 ℃, be incubated 30 minutes; Cool to room temperature, discharge dye liquor; Described programming rate is 1 ℃/minute; (5) rinsing, oven dry obtain described cuprammonium blended yarn woven fabric.
Embodiment two: a kind of production technology of cuprammonium blended yarn woven fabric comprises following processing step:
(1) copper ammonia fibre, carbon fiber and cotton fiber blending are obtained cuprammonium blending grey cloth, the mass ratio of copper ammonia fibre, carbon fiber and cotton fiber is 60:3:58.5;
(2) washing: cuprammonium blending grey cloth is cleaned in rinsing machine, and bath raio is 1:50, and adds mild detergent, and the consumption of cleaning agent is every premium on currency 5g, and water temperature is 65 ℃, and washing time is 0.5 hour;
(3) concise: the cuprammonium blending grey cloth after washing is immersed in water, and bath raio is 1:15, and to add mass percentage concentration be 35% neutral scouring agent solution, and addition is every premium on currency 10g, processes 1 hour, and concise temperature is 70 ℃;
(4) dyeing: the cuprammonium blending grey cloth after concise is put into dyeing machine, and bath of dye liquor is than being 1:13, and every premium on currency adds 2g softener and 3g levelling agent, is warming up to 90 ℃, is incubated 15 minutes; Be warming up to again 120 ℃, be incubated 15 minutes; Be warming up to again 130 ℃, be incubated 45 minutes; Cool to room temperature, discharge dye liquor; Described programming rate is 2 ℃/minute; (5) rinsing, oven dry obtain described cuprammonium blended yarn woven fabric.
Embodiment three: a kind of production technology of cuprammonium blended yarn woven fabric comprises following processing step:
(1) copper ammonia fibre, carbon fiber and cotton fiber blending are obtained cuprammonium blending grey cloth, the mass ratio of copper ammonia fibre, carbon fiber and cotton fiber is 50:2:50;
(2) washing: cuprammonium blending grey cloth is cleaned in rinsing machine, and bath raio is 1:40, and adds mild detergent, and the consumption of cleaning agent is every premium on currency 4g, and water temperature is 62 ℃, and washing time is 0.6 hour;
(3) concise: the cuprammonium blending grey cloth after washing is immersed in water, and bath raio is 1:12, and to add mass percentage concentration be 32% neutral scouring agent solution, and addition is every premium on currency 8g, processes 0.6 hour, and concise temperature is 66 ℃;
(4) dyeing: the cuprammonium blending grey cloth after concise is put into dyeing machine, and bath of dye liquor is than being 1:12, and every premium on currency adds 1.5g softener and 2g levelling agent, is warming up to 80 ℃, is incubated 12 minutes; Be warming up to again 115 ℃, be incubated 12 minutes; Be warming up to again 125 ℃, be incubated 40 minutes; Cool to room temperature, discharge dye liquor; Described programming rate is 1.5 ℃/minute; (5) rinsing, oven dry obtain described cuprammonium blended yarn woven fabric.
Claims (2)
1. the production technology of a cuprammonium blended yarn woven fabric, is characterized in that, comprises following processing step:
(1) copper ammonia fibre, carbon fiber and cotton fiber blending are obtained cuprammonium blending grey cloth, the mass ratio of copper ammonia fibre, carbon fiber and cotton fiber is 40 ~ 60:1.5 ~ 3:37 ~ 58.5;
(2) washing: cuprammonium blending grey cloth is cleaned in rinsing machine, and bath raio is 1:30 ~ 50, and adds mild detergent, and the consumption of cleaning agent is every premium on currency 3 ~ 5g, and water temperature is 60 ~ 65 ℃, and washing time is 0.5 ~ 1 hour;
(3) concise: the cuprammonium blending grey cloth after washing is immersed in water, and bath raio is 1:10 ~ 15, and to add mass percentage concentration be 30 ~ 35% neutral scouring agent solution, and addition is every premium on currency 5 ~ 10g, processes 0.5 ~ 1 hour, and concise temperature is 65 ~ 70 ℃;
(4) dyeing: the cuprammonium blending grey cloth after concise is put into dyeing machine, and bath of dye liquor is than being 1:10 ~ 13, and every premium on currency adds 1 ~ 2g softener and 1 ~ 3g levelling agent, is warming up to 70 ~ 90 ℃, is incubated 10 ~ 15 minutes; Be warming up to again 110 ~ 120 ℃, be incubated 10 ~ 15 minutes; Be warming up to again 120 ~ 130 ℃, be incubated 30 ~ 45 minutes; Cool to room temperature, discharge dye liquor;
(5) rinsing, oven dry obtain described cuprammonium blended yarn woven fabric.
2. the production technology of antibiotic cuprammonium blended yarn woven fabric as claimed in claim 1, it is characterized in that: the programming rate in step (4) is 1 ~ 2 ℃/minute.