CN103101097B - 利用废旧木材制造实木复合门的方法 - Google Patents
利用废旧木材制造实木复合门的方法 Download PDFInfo
- Publication number
- CN103101097B CN103101097B CN201310038584.7A CN201310038584A CN103101097B CN 103101097 B CN103101097 B CN 103101097B CN 201310038584 A CN201310038584 A CN 201310038584A CN 103101097 B CN103101097 B CN 103101097B
- Authority
- CN
- China
- Prior art keywords
- door
- sheet material
- waste
- processing
- wood
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种利用废旧木材制造实木复合门的方法，包括以下步骤：S1：废旧木材的整理；S2：刨光处理；S3：锯成片状板材；S4：分级选板并进行翻新处理；S5：梳齿处理；S6：胶合形成指接条；S7：四面刨光后胶拼成指接拼板坯板；S8：通过木板冷压机对指接拼板坯板进行冷压处理；S9：锯边和砂光得到指接拼板；S10：采用指接拼板拼装门龙骨；S11：在所述门龙骨上贴门面板；S12：对贴在门龙骨上的门面板进行打磨或贴纸处理；S13；对步骤S12中经打磨或贴膜处理后的门进行喷漆处理，得到实木复合门成品。采用本发明所述的方法生产的实木复合门与实木门的性质相近，完全可以成为实木门的替代品，进而降低实木门的生产成本并有效地集约了林木资源。
Description
技术领域
本发明涉及一种废旧木材的再利用技术，尤其涉及利用废旧木材制造实木复合门的方法。
背景技术
现有技术中的实木门利用新砍伐的树木做成的木材为原料制成的，实木门的优点是自然环保、给人返朴归真的感觉；其缺点是价位高、受外界温度、湿度影响大易变形、开裂。因为实木门的选料均为天然木材，所以价格比较昂贵，无法满足低等消费水平消费者的消费需求。
另外，我国每年建筑和装修过程中会产生大量的木质建筑废弃物，合理的利用这些废弃木质建筑物，不仅可以节省大量处理费用，而且可以变废为宝，从而缓解我国木材的供需矛盾。如果能够利用废旧木材来替代新砍伐的木材制作出复合型实木门，不仅可以降低实木门的成本，而且变废为宝、集约了林木资源。
在利用废旧木材制门方面，现有的手段是先将废旧木材制成刨花板或纤维板，然后再以刨花板或纤维板为原料制门，这种门的品质与实木门相差很远。然而除此之外，尚无更好的技术手段能够利用废旧木材加工出实木门。
针对现有技术的不足，需研究一种利用废旧木材制作实木门的技术，以降低生产实木门的生产成本并解决木材资源的紧缺问题。
发明内容
有鉴于此，本发明提供一种利用废旧木材制造实木复合门的方法，本发明的方法步骤简单，废旧木材的利用率高，解决了现有实木门成本高和废旧木材无法有效利用的问题。
本发明通过以下技术手段解决上述技术问题：
本发明提供了一种利用废旧木材制造实木复合门的方法，包括以下步骤：
S1：废旧木材的整理，其内容包括剔除废旧木材上的金属物和建筑附属物、将所述废旧木材截成短木节；
S2：将经步骤S1处理后得到的短木节进行刨光处理；
S3：将刨光处理后的短木节锯成片状板材；
S4：对S3中的板材进行分级选板，从中选出轻度腐蚀板材和正常板材，并将所述轻度腐蚀板材进行翻新处理；
S5：对步骤S4中所述正常板材与经过翻新处理后得到的轻度腐蚀板材进行梳齿处理得到带有指接齿的板材；
S6：将上述带有指接齿的板材通过指接齿连接并胶合形成指接条；
S7：将上述指接条四面刨光后，在指接条的侧面涂胶将所述指接条胶拼成指接拼板坯板；
S8：通过木板冷压机对步骤S7中的指接拼板坯板进行冷压处理；
S9：对冷压处理过的指接拼板坯板进行锯边和砂光处理得到指接拼板；
S10：采用指接拼板拼装门龙骨；
S11：在所述门龙骨上贴门面板；
S12：对贴在门龙骨上的门面板进行打磨或贴膜处理；
进一步，在步骤S1中采用横截锯或单锯片圆锯机将所述废旧木材截成定长和定宽的短木节。
进一步，步骤S4中所述翻新处理，其具体步骤如下：
S41：采用喷枪将木材漂白剂均匀喷施于所述轻度腐蚀板材的表面，用以对轻度腐蚀板材进行漂色处理；
S42：将经过漂色处理的轻度腐蚀板材晾干后放入固体含量为50％-69％的异氰酸酯胶粘剂中常压下浸泡5-10min，然后取出沥干。
进一步，步骤S41中所述木材漂白剂由百分含量为20-30％过氧化氢、1-1.5％碳酸钠、0.3-0.5％氨和70-80％水组成。
进一步，步骤S5中所述梳齿处理是指在正常板材与经过翻新处理后得到的轻度腐蚀板材的宽度方向上锯出齿状结构。
进一步，步骤S1中所述废旧木材的整理还包括对废旧木材的烘干处理，经烘干处理后的废旧木材其含水率在8-12％之间。
本发明的有益效果：
1、本发明通过对废旧木材的特殊处理，使其能够生产出贴近实木的指接拼板，进而以该指接拼板为原料生产出实木复合门，该实木复合门与实木门的性质相近，完全可以成为实木门的替代品，进而降低实木门的生产成本并有效地集约了林木资源。
2、本发明提供的方法步骤简单，其只通过两次刷胶、一次冷压步骤即可生产出接近实木的指接拼板，从而降低了能源和辅料消耗成本。
附图说明
下面结合附图和实施例对本发明作进一步描述。
图1为本发明的方法流程示意图。
具体实施方式
本实施例详细查明了这种利用废旧木材制造实木复合门的方法，该方法具体包括以下步骤：
S1：废旧木材的整理，其步骤如下：a)剔除废旧木材上的金属物，如铁钉；b)将所述废旧木材截成短木节，采用横截锯或单锯片圆锯机将所述废旧木材截成定长和定宽的短木节，所形成的短木节宽度为50mm，长度一般在1m以下；c)通过超声振动将附着在木材表面的水泥等建筑附属物剔除；d)对短木节进行50烘干处理，将废旧木材的含水率控制在13％以下；
S2：将经步骤S1处理后得到的短木节进行刨光处理；
S3：通过多锯片圆锯机将刨光处理后的短木节锯成片状板材，其厚度统一为15mm；
S4：对S3中的板材进行分级选板，从中选出轻度腐蚀板材和正常板材，并将所述轻度腐蚀板材进行翻新处理，所述正常板材是指未经腐蚀的板材，所述对轻度腐蚀板材的翻新处理，其具体步骤如下：S41：采用喷枪将木材漂白剂均匀喷施于所述轻度腐蚀板材的表面，用以对轻度腐蚀板材进行漂色处理，所述木材漂白剂由百分含量为25％过氧化氢、1.2％碳酸钠、0.45％氨和75％水组成；S42：将经过漂色处理的轻度腐蚀板材晾干后放入固体含量为53％的异氰酸酯胶粘剂中常压下浸泡8min，然后取出沥干。异氰酸酯胶粘剂不含甲醛，具有粘结力强和环保效果；
S5：对步骤S4中所述正常板材与经过翻新处理后得到的轻度腐蚀板材进行梳齿处理得到带有指接齿的板材，所述梳齿处理是指在正常板材与经过翻新处理后得到的轻度腐蚀板材的宽度方向上锯出齿状结构；
S6：将上述带有指接齿的板材通过指接齿连接并胶合形成指接条；
S7：将上述指接条四面刨光后，通过木材涂胶机在指接条的侧面涂胶将所述指接条胶拼成指接拼板坯板；
S8：通过木板冷压机对步骤S7中的指接拼板坯板进行冷压处理，冷压处理节约能耗，免除了煤炭费以及和锅炉相关的费用，另外，冷压会减少木材压缩率(等于增加木制品的厚度)，以及木材内部的应力，防止变型；
S9：对冷压处理过的指接拼板坯板进行锯边和砂光处理得到指接拼板。
S10：采用指接拼板拼装门龙骨：根据木门的结构，将所述指接拼板进行开榫和打卯，用经过开榫和打卯后的指接拼板榫卯组合成为门龙骨；
S11：在所述门龙骨上贴门面板，所述门面板优选经过雕花处理的三聚氰胺饰面板；
S12：对贴在门龙骨上的门面板进行打磨或贴膜处理，所述贴膜处理具体是指将三聚氰胺浸胶纸在高温高压下贴在门面板上，其所形成的门面具有美观、环保、耐磨、耐高温、耐腐蚀等优点；
S13；对步骤S12中经打磨或贴膜处理后的门进行喷漆处理，得到实木复合门成品，通过对得到的实木复合门进行性能测试，其各项指标符合国家标准。
通过本发明所述的方法制造得到的实木复合门具有很好的抗变形和抗冲击性能，而且具有耐磨、耐高温、耐腐蚀、防水等优点。
本发明充分利用废旧木材生产出高品质的实木复合门，解决了现有实木门成本高和废旧木材无法有效利用的问题。
最后说明的是，以上实施例仅用以说明本发明的技术方案而非限制，尽管参照较佳实施例对本发明进行了详细说明，本领域的普通技术人员应当理解，可以对本发明的技术方案进行修改或者等同替换，而不脱离本发明技术方案的宗旨和范围，其均应涵盖在本发明的权利要求范围当中。
Claims (5)
1.一种利用废旧木材制造实木复合门的方法，其特征在于，包括以下步骤：
S1：废旧木材的整理，其内容包括剔除废旧木材上的金属物和建筑附属物、将所述废旧木材截成短木节；
S2：将经步骤S1处理后得到的短木节进行刨光处理；
S3：将刨光处理后的短木节锯成片状板材；
S4：对S3中的板材进行分级选板，从中选出轻度腐蚀板材和正常板材，并将所述轻度腐蚀板材进行翻新处理；所述翻新处理，其具体步骤如下：
S41：采用喷枪将木材漂白剂均匀喷施于所述轻度腐蚀板材的表面，用以对轻度腐蚀板材进行漂色处理；
S42：将经过漂色处理的轻度腐蚀板材晾干后放入固体含量为50％-69％的异氰酸酯胶粘剂中常压下浸泡5-10min，然后取出沥干；
S5：对步骤S4中所述正常板材与经过翻新处理后得到的轻度腐蚀板材的进行梳齿处理得到带有指接齿的板材；
S6：将上述带有指接齿的板材通过指接齿连接并胶合形成指接条；
S7：在将上述指接条四面刨光后，在指接条的侧面涂胶将所述指接条胶拼成指接拼板坯板；
S8：通过木板冷压机对步骤S7中的指接拼板坯板进行冷压处理；
S9：对冷压处理过的指接拼板坯板进行锯边和砂光处理得到指接拼板；
S10：采用指接拼板拼装门龙骨；
S11：在所述门龙骨上贴门面板；
S12：对贴在门龙骨上的门面板进行打磨或贴膜处理；
S13；对步骤S12中经打磨或贴膜处理后的门进行喷漆处理，得到实木复合门成品。
2.根据权利要求1所述的利用废旧木材制造实木复合门的方法，其特征在于，在步骤S1中采用横截锯或单锯片圆锯机将所述废旧木材截成定长和定宽的短木节。
3.根据权利要求1所述的利用废旧木材制造实木复合门的方法，其特征在于，步骤S41中所述木材漂白剂由百分含量为20-25％过氧化氢、1-1.5％碳酸钠、0.3-0.5％氨和70-80％水组成，上述各组分含量之和为100％。
4.根据权利要求3所述的利用废旧木材制造实木复合门的方法，其特征在于，步骤S5中所述梳齿处理是指在正常板材与经过翻新处理后得到的轻度腐蚀板材的宽度方向上锯出齿状结构。
5.根据权利要求4所述的利用废旧木材制造实木复合门的方法，其特征在于，步骤S1中所述废旧木材的整理还包括对废旧木材的烘干处理，经烘干处理后的废旧木材其含水率在8-12％之间。