CN103070729B - A kind of device and method promoting resin infiltration tooth structure inside - Google Patents
A kind of device and method promoting resin infiltration tooth structure inside Download PDFInfo
- Publication number
- CN103070729B CN103070729B CN201210579855.5A CN201210579855A CN103070729B CN 103070729 B CN103070729 B CN 103070729B CN 201210579855 A CN201210579855 A CN 201210579855A CN 103070729 B CN103070729 B CN 103070729B
- Authority
- CN
- China
- Prior art keywords
- resinoid bond
- tooth structure
- structure inside
- memory
- gases
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of device and method that resin infiltrates tooth structure inside that promotes, comprise resinoid bond memory, storage has resinoid bond pre-polymerization granule or resinoid bond colloid; Gas pressurized injection unit, produce gases at high pressure through resinoid bond memory, spray from nozzle; When gases at high pressure spray from nozzle, carry the resinoid bond pre-polymerization granule in resinoid bond memory or resinoid bond colloid, be ejected into around tooth structure to be repaired.The present invention is aided with certain external force when bonding agent permeates to tooth structure, impel bonding agent be seeped into tooth structure more deep layer, be combined with tooth structure tightr, effectively prevent the generation of interface seepage, the effective measures improving adhesive effect, more effectively can close dentin surface, become effective treatment tools such as hemodia.
Description
Technical field
The invention belongs to Dental Erosion technical field, relate to a kind of device and method that resin infiltrates tooth structure inside that promotes.
Background technology
Vertex-gluing graph in stomatology is after tooth defect or disappearance, the dummy of various material is fixed to dental surface structure or other repair materials by adhesives and gets on to reach the technology of reparation or therapeutic effect.The performance of bonding force mainly relies on macromolecule organic bonding material (resin bonding material) and various adhesive technology.
The important success factor of vertex-gluing graph is adhesive strength and the endurance life of dummy design and resin bonding material.The composition of resin bonding system mainly comprises: tooth erosion agent (Acidetching), bonding agent (Bonding, adhesive) or from acid corroding pretreatment agent (Self-echingprimer) and bonding agent, metal conditioner (metalprimer), ceramic surface treatment agent (silane coupler silanecoupling, oxide-based porcelain surface special handling agent), resin bonding cement (resincement, resin-basedlutingcement) etc.
The physical treatment on tooth surface and dummy surface comprises: cleaning, acid etching, is then coated with thin layer of adhesive at tooth surface.Current tooth bonding process adopts nature paint-on technique, bonding agent small brushes is applied to dental surface, allows bonding agent infiltrate tooth structure inside voluntarily, after solidification and tooth structure combine.This method greatest problem is bonding agent limited penetration depth, bonding agent and tooth structure are in conjunction with defective tightness, bonding rear interface exists seepage (micron order or nanoscale), and finally affect adhesive effect, cause recurrent caries, postoperative sensitivity and the bonding bad complication such as to come off.
Summary of the invention
The problem that the present invention solves is to provide a kind of device and method that resin infiltrates tooth structure inside that promotes, certain external force is aided with when bonding agent permeates to tooth structure, it is inadequate that solution resin material gos deep into the degree of depth in tooth structure, in conjunction with defective tightness, cause the difficult problem that resin bonding repairing effect is undesirable.
The present invention is achieved through the following technical solutions:
Promote that resin infiltrates a device for tooth structure inside, comprising:
Resinoid bond memory, storage has resinoid bond pre-polymerization granule or resinoid bond colloid;
Gas pressurized injection unit, produce gases at high pressure through resinoid bond memory, spray from nozzle;
When gases at high pressure spray from nozzle, carry the resinoid bond pre-polymerization granule in resinoid bond memory or resinoid bond colloid, be ejected on tooth structure to be repaired.
Described spraying high-pressure gas is 0.5Mpa ~ 5.0Mpa to the pressure on tooth structure, and injecting time is 5 ~ 30s.
The gases at high pressure of described injection and the angle of tooth structure are 30 ~ 90 degree.
Promote that resin infiltrates a method for tooth structure inside, comprise following operation:
To the bonding agent inject high pressure gas being coated in dental surface;
Or will the spraying high-pressure gas of resinoid bond pre-polymerization granule or resinoid bond colloid be carried to dental surface;
Described spraying high-pressure gas is to the pressure applying 0.5Mpa ~ 5.0Mpa during dental surface, and injecting time is 5 ~ 30s.
Described gases at high pressure and dental surface are 30 ~ 90 degree.
Described resinoid bond pre-polymerization granule comprises the fine particle utilizing the dentistry high molecular polymer of all existing Clinical practice to make, its diameter in nanometer to micron order.
Described resinoid bond colloid comprises all dentistry polymeric adhesives of existing Clinical practice.
Compared with prior art, the present invention has following useful technique effect:
Promotion resin provided by the invention infiltrates the device and method of tooth structure inside, certain external force is aided with when bonding agent permeates to tooth structure, impel bonding agent be seeped into tooth structure more deep layer, be combined with tooth structure tightr, effectively prevent the generation of interface seepage, the effective measures improving adhesive effect, more effectively can close dentin surface, become effective treatment tools such as hemodia.
Scanning electron microscope shows, and by gases at high pressure or macromolecule pre-polymerization particle jetting in adhesive surface, significantly can promote that bonding agent gos deep into degree in tooth structure inside, the resin formed dash forward length and form longer compared with traditional method, fuller.
Accompanying drawing explanation
Fig. 1 is structural representation of the present invention;
Fig. 2 is the resin microscopical view that traditional method is formed;
Fig. 3 is the resin microscopical view that spraying high-pressure gas is formed.
Wherein, 1 is gas pressurized injection unit, and 2 is resinoid bond memory, and 3 is screen cloth, and 4 is nozzle.
Detailed description of the invention
Below in conjunction with specific embodiment, the present invention is described in further detail, and the explanation of the invention is not limited.
Promote that resin infiltrates a device for tooth structure inside, comprising:
Resinoid bond memory, storage has resinoid bond pre-polymerization granule or resinoid bond colloid;
Gas pressurized injection unit, produce gases at high pressure through resinoid bond memory, spray from nozzle;
When gases at high pressure spray from nozzle, carry the resinoid bond pre-polymerization granule in resinoid bond memory or resinoid bond colloid, be ejected into around tooth structure to be repaired.
Specifically as shown in Figure 1; resinoid bond memory 2 internal memory contain resinoid bond pre-polymerization granule or resinoid bond colloid; the outlet of resinoid bond memory 2 is provided with through hole or the screen cloth 3 of considering hole; when the gases at high pressure of gas pressurized injection unit 1 generation are through resinoid bond memory 2; gases at high pressure carry resinoid bond pre-polymerization granule in resinoid bond memory or resinoid bond colloid; when being ejected into tooth structure to be repaired from nozzle 4, certain pressure will be applied.Be aided with certain external force when bonding agent permeates to tooth structure like this, impel bonding agent be seeped into tooth structure more deep layer, be combined with tooth structure tightr.
Utilize the promotion resin of this device to infiltrate the method for tooth structure inside, comprise following operation:
To the bonding agent inject high pressure gas being coated in dental surface;
Or will the spraying high-pressure gas of resinoid bond pre-polymerization granule or resinoid bond colloid be carried to dental surface;
Described spraying high-pressure gas is to the pressure applying 0.5Mpa ~ 5.0Mpa during dental surface, and injecting time is 5 ~ 30s.
Further, described gases at high pressure and dental surface are 30 ~ 90 degree.
Concrete, described resinoid bond pre-polymerization granule comprises the fine particle utilizing the dentistry high molecular polymer of all existing Clinical practice to make, its diameter in nanometer to micron order.
Described resinoid bond colloid comprises all dentistry polymeric adhesives of existing Clinical practice.
To the bonding agent inject high pressure gas being coated in dental surface, or use this equipment that the pre-polymerization microgranule of one family macromolecule material is sprayed to adhesive surface, promote bonding agent infiltration further; And then carry out follow-up sticky integrate.
With existing bonding as a comparison, the effect after spraying high-pressure gas is applied as shown in Figure 2 and Figure 3:
Fig. 2 is the resin that traditional method is formed, and Fig. 3 is the resin microscopical view that spraying high-pressure gas is formed; Result shows: traditional method formed prominent bent at its tip, obviously attenuate, curling; And the resin that spraying high-pressure gas technology is formed is prominent obviously long and form is even, without attenuating phenomenon.Thus make bonding agent be seeped into tooth structure more deep layer, to be combined tightr with tooth structure, effectively prevent the generation of interface seepage, be the effective measures improving adhesive effect, more can effectively close dentin surface, become effective treatment tools such as hemodia.
Claims (6)
1. promote that resin infiltrates a device for tooth structure inside, it is characterized in that, comprising:
Resinoid bond memory, storage has resinoid bond pre-polymerization granule or resinoid bond colloid, and the outlet of resinoid bond memory is provided with the screen cloth with through hole or filter opening;
Gas pressurized injection unit, the gases at high pressure of generation, through resinoid bond memory, spray from nozzle;
When gases at high pressure spray from nozzle, carry the resinoid bond pre-polymerization granule in resinoid bond memory or resinoid bond colloid, be ejected into around tooth structure to be repaired.
2. the device promoting resin infiltration tooth structure inside as claimed in claim 1, it is characterized in that, spraying high-pressure gas is 0.5Mpa ~ 5.0Mpa to the pressure on tooth structure, and injecting time is 5 ~ 30s.
3. the device promoting resin infiltration tooth structure inside as claimed in claim 1, it is characterized in that, the gases at high pressure of described injection and the angle of tooth structure are 30 ~ 90 degree.
4. utilize the promotion resin of the non-treatment object of device as claimed in claim 1 to infiltrate a method for tooth structure inside, it is characterized in that, comprise following operation:
To the spraying high-pressure gas of resinoid bond pre-polymerization granule or resinoid bond colloid be carried to dental surface;
Described spraying high-pressure gas is to the pressure applying 0.5Mpa ~ 5.0Mpa during dental surface, and injecting time is 5 ~ 30s; The gases at high pressure sprayed and dental surface are 30 ~ 90 degree.
5. as claimed in claim 4 promote the method that resin infiltrates tooth structure inside, it is characterized in that, described resinoid bond pre-polymerization granule is the fine particle utilizing the dentistry high molecular polymer of Clinical practice to make, its diameter in nanometer to micron order.
6. the method promoting resin infiltration tooth structure inside as claimed in claim 4, it is characterized in that, described resinoid bond colloid comprises the dentistry polymeric adhesive of Clinical practice.