CN103042158B - 一种高抗破碎性的型砂及其制备方法 - Google Patents

一种高抗破碎性的型砂及其制备方法 Download PDF

Info

Publication number
CN103042158B
CN103042158B CN201210569361.9A CN201210569361A CN103042158B CN 103042158 B CN103042158 B CN 103042158B CN 201210569361 A CN201210569361 A CN 201210569361A CN 103042158 B CN103042158 B CN 103042158B
Authority
CN
China
Prior art keywords
sand
parts
water
hour
mixing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201210569361.9A
Other languages
English (en)
Other versions
CN103042158A (zh
Inventor
张立安
魏明军
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
WANXIN CASTING CO Ltd MAANSHAN CITY
Original Assignee
WANXIN CASTING CO Ltd MAANSHAN CITY
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by WANXIN CASTING CO Ltd MAANSHAN CITY filed Critical WANXIN CASTING CO Ltd MAANSHAN CITY
Priority to CN201210569361.9A priority Critical patent/CN103042158B/zh
Publication of CN103042158A publication Critical patent/CN103042158A/zh
Application granted granted Critical
Publication of CN103042158B publication Critical patent/CN103042158B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种高抗破碎性的型砂,它是由下述重量份的原料组成的:石英砂84-94、混料18-25、陶土8-10、膨润土4-6、磷酸二氢铵2-4、水玻璃2-3、滑石粉1-2、石膏2-4、硬脂酸锌1-2、水3-10;采用该型砂生产的铸件发气量小、烘干时间短、透气性好、干拉强度高,并可改善砂型的脱模性,降低浇注时对水分的敏感性,同时对铸件的粘砂、夹砂、冲砂、气孔等缺陷有显著地改善,能使铸件进一步提高光洁度,在该型砂的生产过程中,通过预混合的方法,可以避免混料和膨润土遇水形成小粘团,无法均匀分散在型砂表面,在型砂的内部凝结成小团块,影响型砂性能。

Description

一种高抗破碎性的型砂及其制备方法
技术领域
[0001] 本发明主要涉及一种型砂,尤其涉及一种高抗破碎性的型砂及其制备方法。
背景技术
[0002] 在铸造中用来造型的材料。型砂一般由铸造用原砂、型砂粘结剂和辅加物等造型材料按一定的比例混合而成。型砂在铸造生产中的作用极为重要,因型砂的质量不好而造成的铸件废品约占铸件总废品的30〜50%。通常对型砂的要求是:1、具有较高的强度和热稳定性,以承受各种外力和高温的作用。2、良好的流动性,即型砂在外力或本身重力作用下砂粒间相互移动的能力。3、一定的可塑性,即型砂在外力作用下变形,当外力去除后能保持所给予的形状的能力。4、较好的透气性,即型砂孔隙透过气体的能力。5、高的溃散性,又称出砂性,即在铸件凝固后型砂是否容易破坏,是否容易从铸件上清除的性能。
发明内容
[0003] 本发明目的就是为了弥补已有技术的缺陷,提供一种高抗破碎性的型砂及其制备方法。
[0004] 本发明是通过以下技术方案实现的:
[0005] 一种高抗破碎性的型砂,它是由下述重量份的原料组成的:
[0006] 石英砂84-94、混料18-25、陶土 8-10、膨润土 4-6、磷酸二氢铵2-4、水玻璃2-3、滑石粉1-2、石膏2-4、硬脂酸锌1-2、水3-10 ;
[0007] 所述混料是由下述重量份的原料组成:
[0008] 高岭土 40-45、碳酸钙15-19、粉煤灰8-10、碳酸钠4-6、尿素2-4、硅酸钾2-3、草木灰0.6-0.8、石膏0.8-1、生石灰1-2 ;
[0009] 将上述重量份的粉煤灰、碳酸钙和高岭土混合研碎,过250-280目筛;
[0010] 然后与上述重量份的碳酸钠混合,在750-8001下煅烧30-40分钟;
[0011] 取出后研磨,过200-250目筛;
[0012] 将过筛后的粉末加入到粉末重量8-10倍的硫酸溶液中,混合搅拌0.5-1小时;
[0013] 将搅拌后的物料在温度为90-1001的水浴锅中加热1-2小时;
[0014] 将产物取出后,加水或者硫酸,调节至2-3 ;
[0015] 再放入恒温干燥箱,在100-1201下恒温干燥0.5-1小时;
[0016] 将上述重量份的草木灰用10-15%盐酸浸泡3-4小时,去离子水洗涤,再用10-12%氢氧化钠溶液浸泡3-4小时,再用去离子水洗涤至中性,烘干;
[0017] 将上述恒温干燥后的物料、烘干后的草木灰与剩余各原料混合研磨,过200-250目筛,即得所述混料;
[0018] 所述的硫酸的浓度为60-70%。
[0019] 一种高抗破碎性的型砂的制备方法,包括以下步骤:
[0020] (1)将上述重量份的陶土、石英砂混合研碎,过150-250目筛;
[0021] (2)在过筛后的地开石和石英砂中加入上述重量份60-70%的水,预混合40-508 ;
[0022] (3)再加入上述重量份的膨润土、磷酸二氢铵、水玻璃、滑石粉、石膏2-4、硬脂酸锌、混料混合搅拌20-308 ;
[0023] (4)最后再加入剩余的水,混合60-808,即得所述型砂。
[0024] 本发明的优点是:
[0025] 采用该型砂生产的铸件发气量小、烘干时间短、透气性好、干拉强度高,并可改善砂型的脱模性,降低浇注时对水分的敏感性,同时对铸件的粘砂、夹砂、冲砂、气孔等缺陷有显著地改善,能使铸件进一步提高光洁度,在该型砂的生产过程中,通过预混合的方法,可以避免混料和膨润土遇水形成小粘团,无法均匀分散在型砂表面,在型砂的内部凝结成小团块,影响型砂性能。
具体实施方式
[0026] 实施例1
[0027] —种高抗破碎性的型砂,它是由下述重量份(公斤)的原料组成的:
[0028] 石英砂94、混料25、陶土 10、膨润土 6、磷酸二氢铵4、水玻璃3、滑石粉1、石膏4、硬脂酸锌2、水6 ;
[0029] 所述混料是由下述重量份的原料组成:
[0030] 高岭土 45、碳酸钙19、粉煤灰10、碳酸钠6、尿素4、硅酸钾3、草木灰0.8、石膏0.8、生石灰2 ;
[0031] 将上述重量份的粉煤灰、碳酸钙和高岭土混合研碎,过280目筛;
[0032] 然后与上述重量份的碳酸钠混合,在8001下煅烧40分钟;
[0033] 取出后研磨,过250目筛;
[0034] 将过筛后的粉末加入到粉末重量10倍的硫酸溶液中,混合搅拌0.5小时;
[0035] 将搅拌后的物料在温度为1001的水浴锅中加热2小时;
[0036] 将产物取出后,加水或者硫酸,调节至3 ;
[0037] 再放入恒温干燥箱,在1201下恒温干燥0.5小时;
[0038] 将上述重量份的草木灰用15%盐酸浸泡4小时,去离子水洗涤,再用12%氢氧化钠溶液浸泡4小时,再用去离子水洗涤至中性,烘干;
[0039] 将上述恒温干燥后的物料、烘干后的草木灰与剩余各原料混合研磨,过250目筛,即得所述混料;
[0040] 所述的硫酸的浓度为70%。
[0041] 一种高抗破碎性的型砂的制备方法,包括以下步骤:
[0042] (1)将上述重量份的地开石、高岭石混合研碎,过250目筛;
[0043] (2)在过筛后的地开石和高岭石中加入上述重量份70%的水,预混合508 ;
[0044] (3)再加入上述重量份的膨润土、磷酸二氢铵、水玻璃、滑石粉、石膏4、硬脂酸锌、混料混合搅拌308 ;
[0045] (4)最后再加入剩余的水,混合808,即得所述型砂。
[0046] 性能测试:
[0047] 利用本发明方法生产的铸造型砂的工艺检测性能为:
[0048]湿压强度:0.10
[0049] 透气性93
[0050] 热湿拉强度(即幻:523
[0051] 破碎指数0):89%
[0052]紧实率 38%。

Claims (2)

1.一种高抗破碎性的型砂,其特征在于它是由下述重量份的原料组成的: 石英砂84-94、混料18-25、陶土 8_10、膨润土 4_6、磷酸二氢铵2_4、水玻璃2_3、滑石粉1-2、石膏2-4、硬脂酸锌1-2、水3-10 ; 所述混料是由下述重量份的原料制成: 高岭土 40-45、碳酸钙15-19、粉煤灰8-10、碳酸钠4_6、尿素2_4、硅酸钾2_3、草木灰0.6-0.8、石膏 0.8-1、生石灰 1-2 ; 该混料的制备方法为:将上述重量份的粉煤灰、碳酸钙和高岭土混合研碎,过250-280目筛; 然后与上述重量份的碳酸钠混合,在750-800°C下煅烧30-40分钟; 取出后研磨,过200-250目筛; 将过筛后的粉末加入到粉末重量8-10倍的硫酸溶液中,混合搅拌0.5-1小时; 将搅拌后的物料在温度为90-100°C的水浴锅中加热1-2小时; 将产物取出后,加水或者硫酸,调节PH至2-3 ; 再放入恒温干燥箱,在100-120°C下恒温干燥0.5-1小时; 将上述重量份的草木灰用10-15%盐酸浸泡3-4小时,去离子水洗漆,再用10-12%氢氧化钠溶液浸泡3-4小时,再用去离子水洗涤至中性,烘干; 将上述恒温干燥后的物料、烘干后的草木灰与剩余各原料混合研磨,过200-250目筛,即得; 所述的硫酸的浓度为60-70%。
2.一种如权利要求1所述的高抗破碎性的型砂的制备方法,其特征在于包括以下步骤: (1)将上述重量份的陶土、石英砂混合研碎,过150-250目筛; (2)在过筛后的陶土和石英砂中加入上述重量份60-70%的水,预混合40-50s ; (3)再加入上述重量份的膨润土、磷酸二氢铵、水玻璃、滑石粉、石膏2-4、硬脂酸锌、混料混合搅拌20-30s ; (4)最后再加入剩余的水,混合60-80s,即得所述型砂。
CN201210569361.9A 2012-12-25 2012-12-25 一种高抗破碎性的型砂及其制备方法 Active CN103042158B (zh)