CN103029307B - 一种复合材料盒型结构主梁的制作方法 - Google Patents

一种复合材料盒型结构主梁的制作方法 Download PDF

Info

Publication number
CN103029307B
CN103029307B CN201210532079.3A CN201210532079A CN103029307B CN 103029307 B CN103029307 B CN 103029307B CN 201210532079 A CN201210532079 A CN 201210532079A CN 103029307 B CN103029307 B CN 103029307B
Authority
CN
China
Prior art keywords
male mold
mold
type structures
case type
composite material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201210532079.3A
Other languages
English (en)
Other versions
CN103029307A (zh
Inventor
黄红初
吴平
马军
万建平
鄢和庚
李跃
殷俊
马闪红
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangxi Hongdu Aviation Industry Group Co Ltd
Original Assignee
Jiangxi Hongdu Aviation Industry Group Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangxi Hongdu Aviation Industry Group Co Ltd filed Critical Jiangxi Hongdu Aviation Industry Group Co Ltd
Priority to CN201210532079.3A priority Critical patent/CN103029307B/zh
Publication of CN103029307A publication Critical patent/CN103029307A/zh
Application granted granted Critical
Publication of CN103029307B publication Critical patent/CN103029307B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种复合材料盒型结构主梁的制作方法,所述方法包括如下步骤:A、制作阳模模具、阴模模具以及辅助工装均压板;B、将复合材料预浸料铺贴在阳模模具上,并在常温下进行抽真空预压实;C、将预压实的复合材料预浸料铺叠在阴模模具上;D、将辅助工装均压板、阳模模具、阴模模具由上而下组合,封装在真空袋内;E、将真空袋放入热压罐内抽真空并进行气密性检查;F、热压罐升温,保温,加压后保压升温,保温保压,降温,卸压并去除所述阳模模具、阴模模具、辅助工装均压板以及底板,最终得到所述复合材料盒型结构主梁。所述方法实现复合材料预浸料的每个型面区域都能在树脂凝胶时间段受到压力,防止压力偏小引起零件疏松。

Description

一种复合材料盒型结构主梁的制作方法
技术领域
本发明属于复合材料加工领域,具体地,涉及一种复合材料盒型结构主梁的制作方法。
背景技术
如图1所示,一种复合材料层压板盒型结构主梁为开口从端头向另一端头部位逐渐变窄、第一盖板(6)和第二盖板(7)为曲面的盒型结构件。其具体的结构为:所述第一盖板(6)和第二盖板(7)的结构为等腰梯形,第一盖板(6)和第二盖板(7)腰长尺寸为980mm,下底为160mm,上底为100mm,第一侧板(801)和第二侧板(802)由高54mm逐渐过渡到高25 mm的盒型结构。
 复合材料层压板盒型结构为中间空腹、薄壁结构盒型形式,对于这种复合材料结构件的成型方法通常采用阴阳模具组合成型,将零件组装在阴阳模具中按照规定的加温参数在热压机上加温固化成型;即利用阴阳模具材料本身热膨胀系数产生的挤压力,对零件施加压力加温成型,一种复合材料层压板盒型结构主梁成型方法原来就是使用该方法,即:先在阳模模具上进行预浸料的铺叠组合,然后在阴模模具中进行组装,再在热压机上进行加温成型。该成型方法易造成零件腹板区域大面积疏松,严重的影响产品质量,经分析:主要原因是由于该零件阴阳模具采用的材料均为45#钢,模具在加温的过程中其产生的热膨胀系数差异较小,零件在树脂凝胶时间段受到的压力偏小,不能达到层压板主梁在固化过程中所需要的成型压力。
目前像这种中间空腹、薄壁盒型结构的复合材料制件,通常采用热膨胀模塑法成型,其工作原理是采用不同系数的模具材料,利用其受热体积膨胀不同产生的挤压力,对产品施加压力,但是这种成型工艺对阳模(芯模)材料要求比较严格,主要时因为选用的模具材料要求其膨胀性能和复合材料制品的树脂凝胶时间相匹配,即在复合材料制品的树脂时间段能产生所需要的膨胀压力,该种材料的选择范围较小。
发明内容
为解决上述存在的问题,本发明的目的在于提供一种复合材料盒型结构主梁的制作方法,所述方法通过将复合材料预浸料分别铺贴在阳模模具上,并组合在一起进行抽真空预压实,然后组装在阴模模具和底板上,在底板上用密封材料件将零件和模具组装成密封状态,按照规定的加温参数进热压罐抽真空加温加压固化成型,实现复合材料预浸料的每个型面区域都能在树脂凝胶时间段受到压力,防止压力偏小引起零件疏松。
为解决上述存在的问题,本发明主要采用一种复合材料盒型结构主梁的制作方法,所述复合材料盒型结构主梁包括:第一盖板、第二盖板、第一侧板和第二侧板,所述第一盖板通过第一侧板和第二侧板与第二盖板连接,所述方法包括如下步骤:
A、根据所述复合材料盒型结构主梁的结构制作阳模模具、阴模模具以及辅助工装均压板;
B、将复合材料预浸料铺贴在阳模模具上,并在常温下进行抽真空预压实;
C、将预压实的复合材料预浸料铺叠在阴模模具上;
D、将辅助工装均压板、经步骤B处理后的阳模模具、经步骤C处理后的阴模模具由上而下组合,放置脱模材料、吸胶材料、隔离材料、透气材料后,组装在底板上,然后封装在真空袋内;
E、将真空袋放入热压罐内抽真空并进行气密性检查;
F、热压罐按照1℃~3℃/min的升温速率升温至135℃~145℃,保温30~40min,加压0.5MPa~0.6MPa的气压后保压升温至175℃~180℃,保温保压2~3小时后,以≤2℃/min的降温速率降温至40℃以下后,卸压并去除所述阳模模具、阴模模具、辅助工装均压板以及底板,最终得到所述复合材料盒型结构主梁。
根据本发明所提供的一种复合材料盒型结构主梁的制作方法,采用的是,所述阳模模具由第一阳模模具、第二阳模模具以及第三阳模模具组成;在步骤B中,将复合材料预浸料分别铺贴在第一阳模模具、第二阳模模具以及第三阳模模具上,然后组合成所述阳模模具。
根据本发明所提供的一种复合材料盒型结构主梁的制作方法,采用的是,在步骤B中,抽真空的时间为30~40min,抽真空后的真空度高于或者等于-0.096MPa。
本发明的有益效果在于:采用常温抽真空预压实和进热压罐加温加压固化时,复合材料预浸料的各个型面能在树脂凝胶时间段受到合适的压力,有利于复合材料预浸料内部挥发物和气泡排除,减少成型后的复合材料盒型结构主梁疏松的可能,提高了制件的质量,而且这种结构的阳模模具(芯模)不需要选用和树脂凝胶时间相匹配、热膨胀系数偏大的模具材料,阴阳模具选用同种的金属材料便可进行零件的制造。
附图说明
图1为本发明所提供的方法所要制作的复合材料盒型结构主梁的结构示意图。
图2为本发明所提供的方法中组装在底板上的结构示意图。
具体实施方式
下面结合附图对本发明所提供的一种复合材料盒型结构主梁的制作方法作进一步的解释说明。
本发明所提供的一种复合材料盒型结构主梁的制作方法的步骤如下:
A、根据所述复合材料盒型结构主梁的结构(如图1所示)制作阳模模具3、阴模模具4以及辅助工装均压板1。即辅助工装均压板1的下表面为第一盖板6的上表面的结构和曲面弧度。阳模模具3由第一阳模模具301、第二阳模模具302以及第三阳模模具303形成第一侧板801和第二侧板802的结构和布局。阴模模具4的上表面形成第二盖板7的下表面的结构和曲面弧度。
B、将复合材料预浸料2铺贴在阳模模具3上,并在常温下进行抽真空预压实。具体而言,将复合材料预浸料2分别铺贴在第一阳模模具301、第二阳模模具302以及第三阳模模具303上,然后组合成所述阳模模具3,并在常温下进行抽真空预压实。抽真空的时间为30~40min,抽真空后的真空度高于或者等于-0.096MPa。
C、将预压实的复合材料预浸料2铺叠在阴模模具4上。
D、将辅助工装均压板1、经步骤B处理后的阳模模具3、经步骤C处理后的阴模模具4由上而下组合,放置脱模材料、吸胶材料、隔离材料、透气材料后,组装在底板5上(如图2所示),然后封装在真空袋内。其中,所示脱模材料为脱模布,所示隔离材料为隔离膜,所示透气材料为透气毡。
E、将真空袋放入热压罐内抽真空并进行气密性检查,真空度应高于或者等于-0.096MPa。
F、热压罐按照1℃~3℃/min的升温速率升温至135℃~145℃,保温30~40min,加压0.5MPa~0.6MPa的气压后保压升温至175℃~180℃,保温保压2~3小时后,以≤2℃/min的降温速率降温至40℃以下后,卸压并去除所述阳模模具3、阴模模具4、辅助工装均压板1以及底板5,最终得到所述复合材料盒型结构主梁。

Claims (2)

1.一种复合材料盒型结构主梁的制作方法,所述复合材料盒型结构主梁包括 :第一盖板(6)、第二盖板(7)、第一侧板(801)和第二侧板(802),所述第一盖板(6)通过第一侧板(801)和第二侧板(802)与第二盖板(7)连接,其特征在于,所述方法包括如下步骤 :
A、根据所述复合材料盒型结构主梁的结构制作阳模模具(3)、阴模模具(4)以及辅助工装均压板(1);
B、将复合材料预浸料(2)铺贴在阳模模具(3)上,并在常温下进行抽真空预压实 ;
C、将预压实的复合材料预浸料(2)铺叠在阴模模具(4)上 ;
D、将辅助工装均压板(1)、经步骤 B 处理后的阳模模具(3)、经步骤 C 处理后的阴模模具(4)由上而下组合,放置脱模材料、吸胶材料、隔离材料、透气材料后,组装在底板(5)上,然后封装在真空袋内 ;
E、将真空袋放入热压罐内抽真空并进行气密性检查 ;
F、热压罐按照 1℃ ~3℃ /min 的升温速率升温至 135℃ ~145℃,保温 30~40min,加压0.5MPa~0.6MPa 的气压后保压升温至 175℃ ~180℃,保温保压 2~3 小时后,以≤ 2℃ /min 的降温速率降温至 40℃以下后,卸压并去除所述阳模模具(3)、阴模模具(4)、辅助工装均压板(1)以及底板(5),最终得到所述复合材料盒型结构主梁;
所述阳模模具(3)由第一阳模模具(301)、第二阳模模具(302)以及第三阳模模具(303)组成 ;在步骤 B 中,将复合材料预浸料(2)分别铺贴在第一阳模模具(301)、第二阳模模具(302)以及第三阳模模具(303)上,然后组合成所述阳模模具(3)。
2.根据权利要求 1 所述的一种复合材料盒型结构主梁的制作方法,其特征在于,在步骤 B 中,抽真空的时间为 30~40min, 抽真空后的真空度高于或者等于 -0.096MPa。
3. 根据权利要求 1 所述的一种复合材料盒型结构主梁的制作方法,其特征在于,在步骤 E 中,真空袋抽真空后的真空度高于或者等于 -0.096MPa。
CN201210532079.3A 2012-12-12 2012-12-12 一种复合材料盒型结构主梁的制作方法 Active CN103029307B (zh)