CN103005978A - Antibacterial table cloth and preparation method thereof - Google Patents
Antibacterial table cloth and preparation method thereof Download PDFInfo
- Publication number
- CN103005978A CN103005978A CN2012105354855A CN201210535485A CN103005978A CN 103005978 A CN103005978 A CN 103005978A CN 2012105354855 A CN2012105354855 A CN 2012105354855A CN 201210535485 A CN201210535485 A CN 201210535485A CN 103005978 A CN103005978 A CN 103005978A
- Authority
- CN
- China
- Prior art keywords
- antibacterial
- percent
- tablecloth
- antibacterial agent
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to antibacterial table cloth and a preparation method thereof. The antibacterial table cloth comprises an organic antibacterial agent, wherein the organic antibacterial agent comprises the following components in percentage by weight: 0.1 percent to 0.5 percent of benzo thiazolinone and 0.05 percent to 1.0 percent of zinc pyrithione. The preparation method comprises the following steps of: (1) mixing 0.1 percent to 0.5 percent of benzo thiazolinone and 0.05 percent to 1.0 percent of zinc pyrithione for 5 to 6 minutes at normal temperature to obtain the organic antibacterial agent; and (2) carrying out high-speed mixing (the speed is 1,440 revolutions per minute), kneading, pelletizing and extrusion at a temperature of 150 DEG C and PET (polyethylene glycol terephthalate) cladding and wiredrawing on the organic antibacterial agent and a PVC (Poly Vinyl Chloride) ingredient, finally spinning and obtaining the antibacterial table cloth by sizing at a temperature of 130 to 150 DEG C and cutting. The antibacterial table cloth disclosed by the invention can be repeatedly used, is easy to wash and clean and has a durable antibacterial effect; and the preparation method is simple, is low in cost and has good application prospect.
Description
Technical field
The invention belongs to tablecloth and preparation field thereof, particularly a kind of antibacterial tablecloth and preparation method thereof.
Background technology
Tablecloth commonly used in the real life mainly contains:
The one, classify by production technology:
Plastic: the PVC tablecloth, the EVA tablecloth, the PEVA tablecloth, the bronze designs or patterns on fans, wooden furniture, etc. tablecloth, the cotton substrate PVC tablecloth, the PP tablecloth etc.;
Textile: terylen cotton knitting reticella tablecloth, textile mercerising tuscany lace tablecloth, wash a warp-knitting jacquard tablecloth, textile mercerising jacquard table cloth, polyester-cotton blend plain weave printed tablecloth, polyester-cotton blend plain weave embroidered table cloth, linen knitting reticella tablecloth, wash numb plain weave and applique the tablecloth;
The 2nd, classify by the scope of application: such as the circular tooth of the dining table limit tablecloth, the square flat limit of the dining table tablecloth, the circular edge of the tea table fringe tablecloth, bedroom bedside cupboard reticella tablecloth, the bedroom tea table rectangle decorations fringe tablecloth, bedroom bedside cupboard reticella tablecloth, the bedroom tea table rectangle decorations fringe tablecloth.Also has in addition the circular Disposable, nonwoven tablecloth of dining table etc.
But in actual applications, if washing totally can residual a lot of bacteriums after tablecloth repeatedly used, the people known from experience produce harm.
Nowadays, utilizing the capsule of nano technology to make textile have functional is one of the focus of future development.The application of microcapsules technology in weaving mainly is aspect the rear arrangement, various fabric post-finishing agents can be made the rear arrangement that is used for fabric behind the microcapsules, such as depilation, gas defence, antifog, anti-soil, wrinkle resistant, shrinkproof, deodorization, heat storing and heat preserving, softness, fragrance, fire-retardant, antibiotic, antiultraviolet etc.Most modes with co-blended spinning or coating put on fiber or the fabric, but co-blended spinning has relatively high expectations to equipment and technology content, also do not obtain large-scale production application, and cost are very high.
ZPT is used for the shampoo anti-dandruff, can suppress the growth of Gram-positive, negative bacteria and mould.Hair conditioning delays the aging of hair effectively, the generation of control white hair and alopecia.Also be used as in addition cosmetics preservative agent, finish, coating biocide; As the bactericide of the products such as coating and plastics, use also very extensive.
Summary of the invention
Technical problem to be solved by this invention provides a kind of antibacterial tablecloth and preparation method thereof, and this antibacterial tablecloth is reusable, easy cleaning, and cleaning, antibacterial effect continues; The preparation method is simple, and cost is low, has a good application prospect.
A kind of antibacterial tablecloth of the present invention, described antibacterial tablecloth contains organic antibacterial agent; Wherein, the consisting of of organic antibacterial agent: by weight percentage, 0.1% ~ 0.5% benzothiazolinone (Arch chemical Vanquish-100) and 0.05% ~ 1.0% ZPT (ZPT).Two kinds of organic antibacterial agents have extraordinary synergy, and two chlorine substituents of benzothiazolinone play chelation with the zinc-base of ZPT system, the antibacterial activity that more promotes, thus improve antibacterial effect.The antibacterial activity of one group of antibiotic sample that Fig. 1 represents, the test microbes that adopts in this agar plate test is staphylococcus aureus ATCC 6538.As can be seen from the figure, #5, #6, #7 sample sample disc has formed the protection zone of a very large circle bacteria growing inhibiting on every side, and the sample #8 that does not contain antiseptic then is full of bacterium.
Consisting of of described organic antibacterial agent: by weight percentage, 0.1% benzothiazolinone and 0.05% ZPT.
Consisting of of described organic antibacterial agent: by weight percentage, 0.5% benzothiazolinone and 1.0% ZPT.
The preparation method of a kind of antibacterial tablecloth of the present invention comprises:
(1) by weight percentage, the benzothiazolinone with 0.1% ~ 0.5% and 0.05% ~ 1.0% ZPT normal temperature mixed 5 ~ 6 minutes, obtained organic antibacterial agent;
(2) above-mentioned organic antibacterial agent and PVC batching are extruded, coated wire drawing with PET through mixed at high speed (speed is 1440 rev/mins), kneading, 150 ℃ of granulations, be formed by weaving at last, namely get antibacterial tablecloth through 130-150 ℃ of typing, cutting.
Beneficial effect
Antibacterial tablecloth of the present invention is reusable, easy cleaning, and cleaning, antibacterial effect continues; The preparation method is simple, and cost is low, has a good application prospect.
Description of drawings
Fig. 1 is the agar plate resolution chart; Wherein 5,6,7,8 is four kinds of samples.
The specific embodiment
Below in conjunction with specific embodiment, further set forth the present invention.Should be understood that these embodiment only to be used for explanation the present invention and be not used in and limit the scope of the invention.Should be understood that in addition those skilled in the art can make various changes or modifications the present invention after the content of having read the present invention's instruction, these equivalent form of values fall within the application's appended claims limited range equally.
Embodiment 1
(1) by weight percentage, the benzothiazolinone with 0.1% and 0.05% ZPT normal temperature mixed 5 minutes, obtained organic antibacterial agent;
(2) above-mentioned organic antibacterial agent and PVC batching are extruded, coated wire drawing with PET through mixed at high speed (speed is 1440 rev/mins), kneading, 150 ℃ of granulations, be formed by weaving at last, namely get antibacterial tablecloth through 130 ℃ of typings, cuttings.
Embodiment 2
(1) by weight percentage, the benzothiazolinone with 0.5% and 1.0% ZPT normal temperature mixed 6 minutes, obtained organic antibacterial agent;
(2) above-mentioned organic antibacterial agent and PVC batching are extruded, coated wire drawing with PET through mixed at high speed (speed is 1440 rev/mins), kneading, 150 ℃ of granulations, be formed by weaving at last, namely get antibacterial tablecloth through 150 ℃ of typings, cuttings.
Claims (4)
1. antibacterial tablecloth, it is characterized in that: described antibacterial tablecloth contains organic antibacterial agent; Wherein, the consisting of of organic antibacterial agent: by weight percentage, 0.1% ~ 0.5% benzothiazolinone and 0.05% ~ 1.0% ZPT.
2. a kind of antibacterial tablecloth according to claim 1 is characterized in that: the consisting of of described organic antibacterial agent: by weight percentage, and 0.1% benzothiazolinone and 0.05% ZPT.
3. a kind of antibacterial tablecloth according to claim 1 is characterized in that: the consisting of of described organic antibacterial agent: by weight percentage, and 0.5% benzothiazolinone and 1.0% ZPT.
4. the preparation method of an antibacterial tablecloth comprises:
(1) by weight percentage, the benzothiazolinone with 0.1% ~ 0.5% and 0.05% ~ 1.0% ZPT normal temperature mixed 5 ~ 6 minutes, obtained organic antibacterial agent;
(2) above-mentioned organic antibacterial agent and PVC batching are extruded, coated wire drawing with PET through mixed at high speed, kneading, 150 ℃ of granulations, be formed by weaving at last, namely get antibacterial tablecloth through 130-150 ℃ of typing, cutting.