CN102916058A - 多晶硅太阳能电池用叠层减折射膜 - Google Patents
多晶硅太阳能电池用叠层减折射膜 Download PDFInfo
- Publication number
- CN102916058A CN102916058A CN2012104420012A CN201210442001A CN102916058A CN 102916058 A CN102916058 A CN 102916058A CN 2012104420012 A CN2012104420012 A CN 2012104420012A CN 201210442001 A CN201210442001 A CN 201210442001A CN 102916058 A CN102916058 A CN 102916058A
- Authority
- CN
- China
- Prior art keywords
- refraction
- solar cell
- film
- laminated
- polycrystalline silicon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种多晶硅太阳能电池用叠层减折射膜,该叠层减折射膜设置在太阳能电池多晶硅基体(3)的前表面,从内至外依次为二氧化硅层(2)和氮氧化硅层(1)。本发明采用二氧化硅空心球薄膜,其折射率为2.05,氮氧化硅薄膜的折射率为1.5~1.8,这种叠层膜与单层膜相比具有更好的光学匹配特性,不仅对在硅的主光谱响应的520nm的光有优异的减折射效果,而且对波长在300~1200nm范围内的光都有很好的件折射效果,从而提高多晶硅太阳能电池的转换效率,采用本结构后,我公司工业化生产的多晶硅太阳能电池的转换效率已超过19.5%,为当前世界最高水平。
Description
技术领域
本发明涉及一种太阳能电池的减折射膜结构,尤其是叠层减折射膜结构,具体地说是一种多晶硅太阳能电池用叠层减折射膜。
背景技术
单体太阳电池不能直接做电源使用。作电源必须将若干单体电池串、并联连接和严密封装成组件。太阳能电池组件(也叫太阳能电池组件)是太阳能发电系统中的核心部分,也是太阳能发电系统中最重要的部分。其作用是将太阳能转化为电能,太阳能电池片的转换效率一般定义为电池片的输出功率与入射到电池片表面的太阳光总功率之比。太阳光照射到电池片表面是会发生反射和折射,为提高电池片的转换效率,则要尽量减少折射损失和增加吸收。
随着太阳能技术的发展,通常在电池片表面镀上减折射膜减少折射损失和增加吸收。目前出现了多种减折射膜,通常采用单一层结构,难以获得理想的减折射效果。
发明内容
本发明的目的是针对目前单一层的减折射膜难以获得理想的减折射效果的问题,提出一种多晶硅太阳能电池用叠层减折射膜,是一种质量高、性能优良的折射膜结构。
本发明的技术方案是:
一种多晶硅太阳能电池用叠层减折射膜,该叠层减折射膜设置在太阳能电池多晶硅基体的前表面,从内至外依次为二氧化硅层和氮氧化硅层。
本发明的二氧化硅层为二氧化硅空心球薄膜。
本发明的二氧化硅空心球薄膜的厚度为18~20nm。
本发明的氮氧化硅层的厚度为36~40nm。
本发明的有益效果:
本发明采用二氧化硅空心球薄膜,其折射率为2.05,氮氧化硅薄膜的折射率为1.5~1.8,这种叠层膜与单层膜相比具有更好的光学匹配特性,不仅对在硅的主光谱响应的520nm的光有优异的减折射效果,而且对波长在300~1200nm范围内的光都有很好的件折射效果,从而提高多晶硅太阳能电池的转换效率,采用本结构后,我公司工业化生产的多晶硅太阳能电池的转换效率已超过19.5%,为当前世界最高水平。
附图说明
图1是本发明的结构示意图。
图中:1、氮氧化硅层;2、二氧化硅层;3、太阳能电池多晶硅基体。
具体实施方式
下面结合附图和实施例对本发明作进一步的说明。
如图1所示,一种多晶硅太阳能电池用叠层减折射膜,该叠层减折射膜设置在太阳能电池多晶硅基体3的前表面,从内至外依次为二氧化硅层2和氮氧化硅层1。
本发明的氮氧化硅层1的厚度为36~40nm。
本发明的二氧化硅层2为二氧化硅空心球薄膜;二氧化硅空心球薄膜的厚度为18~20nm。采用二氧化硅空心球薄膜,其折射率为2.05,氮氧化硅薄膜的折射率为1.5~1.8,这种叠层膜与单层膜相比具有更好的光学匹配特性,不仅对在硅的主光谱响应的520nm的光有优异的减折射效果,而且对波长在300~1200nm范围内的光都有很好的件折射效果,从而提高多晶硅太阳能电池的转换效率,采用本结构后,我公司工业化生产的多晶硅太阳能电池的转换效率已超过19.5%,为当前世界最高水平。
本发明未涉及部分均与现有技术相同或可采用现有技术加以实现。
Claims (4)
1.一种多晶硅太阳能电池用叠层减折射膜,其特征是该叠层减折射膜设置在太阳能电池多晶硅基体(3)的前表面,从内至外依次为二氧化硅层(2)和氮氧化硅层(1)。
2.根据权利要求1所述的多晶硅太阳能电池用叠层减折射膜,其特征是所述的二氧化硅层(2)为二氧化硅空心球薄膜。
3.根据权利要求2所述的多晶硅太阳能电池用叠层减折射膜,其特征是所述的二氧化硅空心球薄膜的厚度为18~20nm。
4.根据权利要求1所述的多晶硅太阳能电池用叠层减折射膜,其特征是所述的氮氧化硅层(1)的厚度为36~40nm。