CN102909486A - 一种应用于低合金钢的药芯焊丝及其制备方法 - Google Patents

一种应用于低合金钢的药芯焊丝及其制备方法 Download PDF

Info

Publication number
CN102909486A
CN102909486A CN2012104171541A CN201210417154A CN102909486A CN 102909486 A CN102909486 A CN 102909486A CN 2012104171541 A CN2012104171541 A CN 2012104171541A CN 201210417154 A CN201210417154 A CN 201210417154A CN 102909486 A CN102909486 A CN 102909486A
Authority
CN
China
Prior art keywords
steel
flux
core wire
powder
wire
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012104171541A
Other languages
English (en)
Inventor
苏红菱
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HAIMEN WEILING WELDING MATERIAL MANUFACTURING CO LTD
Original Assignee
HAIMEN WEILING WELDING MATERIAL MANUFACTURING CO LTD
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HAIMEN WEILING WELDING MATERIAL MANUFACTURING CO LTD filed Critical HAIMEN WEILING WELDING MATERIAL MANUFACTURING CO LTD
Priority to CN2012104171541A priority Critical patent/CN102909486A/zh
Publication of CN102909486A publication Critical patent/CN102909486A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种应用于低合金钢的药芯焊丝,其特征在于:外皮采用低碳钢,焊芯按重量百分比包括如下成分:碳粉0.04-1%,钼粉0-6%,镍粉0-6%,钨粉0-10%,铌粉0-10%,钛粉0-1%,余量为铬粉。一种应用于低合金钢的药芯焊丝的制备方法,其特征在于包括如下步骤:将成品钢带裁剪成符合尺寸要求的钢带,将钢带清洗,烘干,控制烘干温度为100-200℃,在成型机将钢带压制出可以放置焊芯的槽,将上述比例制备的焊芯放入到焊芯的槽中,将放置焊芯后的钢带在合缝机中将钢带的边缘合缝即制得焊丝成品。本发明的优点是:采用本发明配比和方法制作的焊丝,可以对碳钢和低合金钢的零部件进行修复,也可以用作其他堆焊材料的过渡层,也可以用于轮齿、矿山车轮等的修复,耐压性强,使用效果好。

Description

一种应用于低合金钢的药芯焊丝及其制备方法
技术领域
[0001] 本发明涉及一种应用于低合金钢的药芯焊丝及其制备方法。
背景技术
[0002] 焊丝的使用越来越广泛。不同领域,不同场合所使用的焊丝是不同的。因此,焊丝内部的焊料的成分及其配比也应该是不同的。常规的焊丝采用的是常规的组分和制造方法制作完成的,不能满足不同领域的使用需求。因此,应该提供一种新的技术方案解决上述问题。
发明内容
[0003] 本发明的目的是:针对上述不足,提供一种应用于低合金钢的药芯焊丝及其制备方法。
[0004] 为实现上述目的,本发明采用的技术方案是:一种应用于低合金钢的药芯焊丝,夕卜皮采用低碳钢,焊芯按重量百分比包括如下成分:
碳粉 0.04-1%
钥粉 0-6%
镍粉 0-6%
钨粉 0-10%
铌粉 0-10%
钛粉 0-1%
铬粉余量。
[0005]
一种应用于低合金钢的药芯焊丝的制备方法,包括如下步骤:将成品钢带裁剪成符合尺寸要求的钢带,将钢带清洗,清洗完成后在干燥炉内进行烘干,控制烘干温度为100-20(TC,在成型机将钢带压制出可以放置焊芯的槽,将按照上述比例制备的焊芯放入到焊芯的槽中,将放置焊芯后的钢带在合缝机中将钢带的边缘合缝即制得焊丝成品。
[0006] 本发明的优点是:采用本发明配比和方法制作的焊丝,可以对碳钢和低合金钢的零部件进行修复,也可以用作其他堆焊材料的过渡层,也可以用于轮齿、矿山车轮等的修复,耐压性强,使用效果好。
具体实施方式
[0007] 下面结合具体实施方式对本发明作进一步详细叙述,以下实施方式仅是对本发明的举例说明,并不限制本发明的保护范围。
[0008] 实施例I
一种应用于低合金钢的药芯焊丝,外皮采用低碳钢,焊芯按重量百分比包括如下成分:碳粉O. 04%,钥粉1%,镍粉1%,钨粉2%,铌粉3%,钛粉O. 5%,余量为铬粉。一种应用于低合金钢的药芯焊丝的制备方法,包括如下步骤:将成品钢带裁剪成符合尺寸要求的钢带,将钢带清洗,清洗完成后在干燥炉内进行烘干,控制烘干温度为100°c,在成型机将钢带压制出可以放置焊芯的槽,将按照上述比例制备的焊芯放入到焊芯的槽中,将放置焊芯后的钢带在合缝机中将钢带的边缘合缝即制得焊丝成品。
[0009] 实施例2
一种应用于低合金钢的药芯焊丝,外皮采用低碳钢,焊芯按重量百分比包括如下成分:碳粉O. 06%,钥粉4%,镍粉3%,钨粉6%,铌粉6%,钛粉O. 6%,余量为铬粉。一种应用于低合金钢的药芯焊丝的制备方法,包括如下步骤:将成品钢带裁剪成符合尺寸要求的钢带,将钢带清洗,清洗完成后在干燥炉内进行烘干,控制烘干温度为150°C,在成型机将钢带压制出可以放置焊芯的槽,将按照上述比例制备的焊芯放入到焊芯的槽中,将放置焊芯后的钢带在合缝机中将钢带的边缘合缝即制得焊丝成品。
[0010] 实施例3 一种应用于低合金钢的药芯焊丝,外皮采用低碳钢,焊芯按重量百分比包括如下成分:碳粉1%,钥粉6%,镍粉6%,钨粉10%,铌粉10%,钛粉1%,余量为铬粉。一种应用于低合金钢的药芯焊丝的制备方法,包括如下步骤:将成品钢带裁剪成符合尺寸要求的钢带,将钢带清洗,清洗完成后在干燥炉内进行烘干,控制烘干温度为200°C,在成型机将钢带压制出可以放置焊芯的槽,将按照上述比例制备的焊芯放入到焊芯的槽中,将放置焊芯后的钢带在合缝机中将钢带的边缘合缝即制得焊丝成品。

Claims (2)

1. 一种应用于低合金钢的药芯焊丝,其特征在于:外皮采用低碳钢,焊芯按重量百分比包括如下成分:碳粉O. 04-1%;钥粉0-6% ;镍粉0-6% ;钨粉0-10%;铌粉 0-10% ;钛粉0-1%;铬粉余量。
2.如权利要求I所述一种应用于低合金钢的药芯焊丝的制备方法,其特征在于包括如下步骤:将成品钢带裁剪成符合尺寸要求的钢带,将钢带清洗,清洗完成后在干燥炉内进行烘干,控制烘干温度为100-200°C,在成型机将 钢带压制出可以放置焊芯的槽,将按照权利要求I所述比例制备的焊芯放入到焊芯的槽中,将放置焊芯后的钢带在合缝机中将钢带的边缘合缝即制得焊丝成品。
CN2012104171541A 2012-10-29 2012-10-29 一种应用于低合金钢的药芯焊丝及其制备方法 Pending CN102909486A (zh)