CN102875017B - A kind of Phosphorus Slag solution generates the method for lagging material - Google Patents
A kind of Phosphorus Slag solution generates the method for lagging material Download PDFInfo
- Publication number
- CN102875017B CN102875017B CN201110200173.4A CN201110200173A CN102875017B CN 102875017 B CN102875017 B CN 102875017B CN 201110200173 A CN201110200173 A CN 201110200173A CN 102875017 B CN102875017 B CN 102875017B
- Authority
- CN
- China
- Prior art keywords
- phosphorus slag
- stove
- slag solution
- zirconium
- heat
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a kind of method that Phosphorus Slag solution generates lagging material, the Phosphorus Slag solution that Phosphorus Slag mineralising fire grate is put is imported multi-functional accumulation of heat zirconium stove, after multi-functional accumulation of heat zirconium stove insulation or heating, enter Water Cooled Centrifugal Machine, be rotated into cotton by Water Cooled Centrifugal Machine and blown out by blower fan.In multi-functional accumulation of heat zirconium stove, first can also add high-al clay that weight is Phosphorus Slag solution 30 ~ 60% or add weight is Phosphorus Slag solution 40 ~ 60% sintered coal gangue, be heated to 1600 ~ 2000 DEG C of fusion and decomposition, then import Phosphorus Slag solution and discharge into cotton.The method can realize continuous free of discontinuities and produce, and can produce the lagging material of high temperature resistant (less than 1200 DEG C), and effective processing and utilizing carbon monoxide waste gas, there is economy and environment double benefit.
Description
Technical field
The present invention relates to the regeneration method of Phosphorus Slag, particularly relate to a kind of method that Phosphorus Slag solution generates lagging material.
Background technology
In the process of producing yellow phosphorus, a large amount of Phosphorus Slags and carbon monoxide can be discharged, difficult treatment, contaminate environment.Application number be 88105942.0 application for a patent for invention disclose a kind of generation method utilizing the direct fibroblast of Phosphorus Slag, utilize the high-temperature slag meeting fibre-forming condition smelted yellow phosphorus electric furnace and discharge, adopt pneumatics to blow cotton technique and be directly blow molded into ca silicate fibre cotton, air compressor machine blows cotton operating pressure 0.4 ~ 0.6MPa, adopt double V-shaped nozzle, be less than 1400 DEG C in material temperature and become cotton.But the unexposed concrete operation step of this application, lacks operability.The patent No. be 200710054726.3 patent of invention disclose a kind of Phosphorus Slag solution and produce the method for lagging material, at the slag notch of yellow phosphorus ore deposit smelting furnace, diversion trench is set, the Phosphorus Slag solution of discharge is caused above the thumb wheel of high-speed rotation, thumb wheel sense of rotation arranges recovery approach, arrange blower back to thumb wheel, Phosphorus Slag solution has got rid of and has drawn wire under the effect of blower by thumb wheel.This method give concrete operation step, workable, but though described diversion trench is made by lagging material, can be bad for high temperature Phosphorus Slag heat insulation effect in production practice, the yellow phosphorus mineralising stove production cycle is about 4 hours, the discharge yellow phosphorus quantity of slag is about ten tons, drain time is half an hour, if the Phosphorus Slag full scale production of about ten tons is not digested within the halfhour time, temperature then can be caused to decline and be difficult to continue to produce, if complete production within half an hour, then equipment investment is excessive, but also will have the damp production waiting for Phosphorus Slag for four hours; In addition, the lagging material that the method is produced does not add other raw materials owing to only utilizing Phosphorus Slag itself, makes the lagging material produced generally can only be used for the hot vessel insulation of less than 400 DEG C.The problem of all unresolved carbon monoxide off gas treatment of aforementioned two patent documentations.
Glass melter, refers to the Thermal Equipment for fusion cast glass admixtion in glass manufacture, by the grog (glass cullet) of the powder prepared by glass ingredient and admixture high temperature melting, clarification form the glass metal meeting forming requirements in kiln.(Baidupedia, glass melter, http: ∥ baike.baidu.com/view/1865782.html) therefore, glass melter is a kind of well Heat preservation equipment, but there is the problem of the structure utilizing glass melter and principle solution Phosphorus Slag solution production lagging material in prior art, in practice, do not find that Phosphorus Slag solution produces the example of lagging material.
Summary of the invention
Technical problem to be solved by this invention is to provide a kind of method that Phosphorus Slag solution generates lagging material, the method can realize continuous free of discontinuities and produce, the lagging material of high temperature resistant (less than 1200 DEG C) can be produced, and effective processing and utilizing carbon monoxide waste gas, there is economy and environment double benefit.
In order to solve the problems of the technologies described above, the present invention takes following technical scheme:
A kind of Phosphorus Slag solution generates the method for lagging material, it is characterized in that: the Phosphorus Slag solution that Phosphorus Slag mineralising fire grate is put is imported multi-functional accumulation of heat zirconium stove, after multi-functional accumulation of heat zirconium stove insulation or heating, enter Water Cooled Centrifugal Machine, be rotated into cotton by Water Cooled Centrifugal Machine and blown out by blower fan.
Or, in multi-functional accumulation of heat zirconium stove, adding the high-al clay that weight is Phosphorus Slag solution 30 ~ 60% or adding weight is Phosphorus Slag solution 40 ~ 60% sintered coal gangue, be heated to 1600 ~ 2000 DEG C of fusion and decomposition, import Phosphorus Slag solution again and discharge, be rotated into cotton by Water Cooled Centrifugal Machine and blown out by blower fan.
The fuel used carbon monoxide put for Phosphorus Slag mineralising fire grate of multi-functional accumulation of heat zirconium stove, is provided with infrared thermometer above multi-functional accumulation of heat zirconium stove.
Multi-functional accumulation of heat zirconium stove, adopts the basic structure of cell furnace and principle to make, adopts the zirconia block of high-temperature heat-resistance, can be heated to 1600 ~ 2000 DEG C with Phosphorus Slag solution contact position.
The invention has the beneficial effects as follows, owing to have employed multi-functional accumulation of heat zirconium stove, both the Phosphorus Slag solution in stove can be kept original temperature thus carried out free of discontinuities production, can add again containing aluminium ore material, heating makes it decompose, thus produce high-temperature-resistant thermal-insulation material, can for less than 1200 DEG C hot vessel; Carbon monoxide is used for fuel, there is economy and environment double benefit.
Accompanying drawing explanation
Fig. 1 multi-functional accumulation of heat zirconium furnace structure schematic diagram;
Fig. 2 the method for the invention device layout schematic diagram.
1, flue 2, regenerator 3, charging opening 4, melting end 5, port 6, dog-hole 7, lattice wall 8, cooling end 9, checker brick
Embodiment
Embodiment one:
The Phosphorus Slag solution that Phosphorus Slag mineralising stove 11 is released imports multi-functional accumulation of heat zirconium stove 13 through diversion trench, the CO (carbon monoxide converter) gas of discharging by the road 12 incendiary pencils entering multi-functional accumulation of heat zirconium stove 13 carries out combustion heating, the temperature of multi-functional accumulation of heat zirconium stove 13 can be monitored by infrared thermometer mounted thereto, Phosphorus Slag solution enters Water Cooled Centrifugal Machine 15 after insulation, Water Cooled Centrifugal Machine high speed rotating, Phosphorus Slag is pulled into thread, blown out into cotton by blower fan 14 and enter recovery approach 16 and reclaim.
The present embodiment becomes cotton with Phosphorus Slag merely, does not add other auxiliary materials, but owing to there being the insulation effect of multi-functional accumulation of heat zirconium stove, can realizing lasting free of discontinuities and produce.
Embodiment two:
In multi-functional accumulation of heat zirconium stove 13, first heat the high-al clay in 3 villages (or 4 tons or 5 tons), more than 90% is reached containing aluminium sesquioxide, or add the sintered coal gangue of 4 tons (or 5 tons or 6 tons), more than 70 are reached containing aluminium sesquioxide, be heated to 1600 ~ 2000 DEG C, enter the Phosphorus Slag solution of 10 tons after melting, continue heating, then enter in Water Cooled Centrifugal Machine 15 and carry out into cotton recovery.Insulating cotton can resistance to less than 1200 DEG C high temperature.
Claims (2)
1. the method for a Phosphorus Slag solution generation lagging material, it is characterized in that: the Phosphorus Slag solution put by Phosphorus Slag mineralising fire grate imports multi-functional accumulation of heat zirconium stove through diversion trench, the incendiary pencil that the CO (carbon monoxide converter) gas of discharging enters multi-functional accumulation of heat zirconium stove by the road carries out combustion heating, Water Cooled Centrifugal Machine is entered after multi-functional accumulation of heat zirconium stove insulation, by Water Cooled Centrifugal Machine high speed rotating, Phosphorus Slag is pulled into thread, blown out into cotton by blower fan and enter recovery approach and reclaim; Wherein, in multi-functional accumulation of heat zirconium stove, add the high-al clay that weight is Phosphorus Slag solution 30 ~ 60% or add the sintered coal gangue that weight is Phosphorus Slag solution 40 ~ 60%, be heated to 1600 ~ 2000 DEG C of fusion and decomposition, import Phosphorus Slag solution again and discharge, be rotated into cotton by Water Cooled Centrifugal Machine and blown out by blower fan.
2. Phosphorus Slag solution as claimed in claim 1 generates the method for lagging material, it is characterized in that: above multi-functional accumulation of heat zirconium stove, be provided with infrared thermometer.