CN102786243B - 一种改性再生骨料和再生骨料高性能混凝土 - Google Patents

一种改性再生骨料和再生骨料高性能混凝土 Download PDF

Info

Publication number
CN102786243B
CN102786243B CN201210261716.8A CN201210261716A CN102786243B CN 102786243 B CN102786243 B CN 102786243B CN 201210261716 A CN201210261716 A CN 201210261716A CN 102786243 B CN102786243 B CN 102786243B
Authority
CN
China
Prior art keywords
aggregate
concrete
recycled aggregate
regeneration aggregate
cement
Prior art date
Application number
CN201210261716.8A
Other languages
English (en)
Other versions
CN102786243A (zh
Inventor
邢锋
寇世聪
Original Assignee
深圳大学
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 深圳大学 filed Critical 深圳大学
Priority to CN201210261716.8A priority Critical patent/CN102786243B/zh
Publication of CN102786243A publication Critical patent/CN102786243A/zh
Application granted granted Critical
Publication of CN102786243B publication Critical patent/CN102786243B/zh

Abstract

本发明公开了一种改性再生骨料和再生骨料高性能混凝土。本发明的改性再生骨料是将再生骨料放入浓度为10-40wt %的纳米二氧化硅水胶体中浸泡处理,浸泡处理时间5天以上。将水泥、改性再生骨料、砂、碎石或细再生骨料及其他矿物添加剂按照一定的配合比搅拌即可得到再生骨料高性能混凝土。本发明根据再生骨料空隙率高导致的吸水率高的特点,基于现有再生骨料混凝土的制造方法,利用水胶体纳米二氧化硅改善再生骨料物理性质和力学性能,使混凝土的力学性能和耐久性大大改善。

Description

一种改性再生骨料和再生骨料高性能混凝土技术领域
[0001] 本发明属于建筑材料领域混凝土类,涉及一种改性再生骨料和再生骨料高性能混凝土。
背景技术
[0002] 随着经济的高速发展,我国很多大城市中,建筑工业产生的废物已经变为公害。这些废物不仅对环境造成严重的破坏,而且正在和人类争夺生存的空间,严重影响国家的可持续发展。因此,开发减少、回收和利用建筑废物的新技术已迫在眉睫。
[0003] 建筑废物主要产生于旧建筑物的拆迁和新建筑物的建造过程中,因此,减少建筑物就必须在拆迁和建造工程中,采用先进的管理技术和拆迁建造技术。众所周知,建筑废物一般由混凝土碎块,粘土砖和瓷砖,砂和灰尘,木屑,塑料和废纸,废金属等组成。混凝土碎块通常是建筑废物的最大组成部分,经过破碎筛分的混凝土碎块可以被用来替代混凝土中的天然骨料或者被用来做道路的基础。这一类型回收材料就叫做循环再生骨料。循环再生骨料在一些欧美发达国家的建筑工业中已经成功应用,但是主要应用在非结构混凝土和道路的基础上,在结构混凝土中的应用有限,通常只有混凝土粗骨料的20%是循环再生骨料。这主要是由于循环再生骨料与天然的骨料相比强度低,多孔和有较高的吸水率。这就要求在配制混凝土时多加水来增加其流动度从而导致硬化混凝土的干缩率和蠕变增加。为了克服循环再生骨料再利用的这一困难,混凝土研究人员经过研究已经开发出了利用机压成型的方法制造混凝土隔墙砖和铺路砌块的专利技术。同时研究发现利用常压蒸气养护技术可以提高循环再生骨料在结构混凝土中的利用率。[0004] 再生骨料与天然石子骨料相比具有如下缺点:高空隙率、吸水率高,压碎指标低。因此,当再生骨料用来制造混凝土时,会带来混凝土的塌落度难以控制,强度低,弹性模量下降,干缩率和蠕变高以及耐久性下降等弱点,从而导致再生骨料在结构混凝土中的应用非常有限。
发明内容
[0005] 本发明要解决的技术问题是提供一种吸水率低、抗压强度高的再生骨料,以提高再生骨料在混凝土中的利用率。
[0006] 本发明要解决的技术问题是提供一种干缩率和蠕变低、耐久性好的再生骨料高性能混凝土。
[0007] 一种改性再生骨料,将再生骨料放入浓度为10_40wt %的纳米二氧化硅水胶体中浸泡处理,浸泡处理时间5天以上。
[0008] 以上所述的改性再生骨料,所述纳米二氧化硅的粒径范围为4-100纳米,比表面积≥ 700m2/g。
[0009] 以上所述的改性再生骨料,纳米二氧化硅水胶体的浓度为25_30wt %,再生骨料浸泡处理时间8-10天。[0010] 以上所述的改性再生骨料,再生骨料的粒径为5-30毫米,浸泡处理前的吸水率分别为 6%-8%,比重为 2300-2400 Kg/m3。
[0011] 一种再生骨料高性能混凝土的技术方案是,组分中含有上述的改性再生骨料。
[0012] 以上所述的再生骨料高性能混凝土,按重量百分比,改性再生骨料占粗骨料用量的 20%-100%。
[0013]以上所述的再生骨料高性能混凝土,胶凝材料用量为400_650Kg/m3,水灰比为
0.25-0.45,粗骨料用量为900-1100 Kg/m3,按重量百分比,改性再生骨料占粗骨料用量的50%-100%ο
[0014] 以上所述的再生骨料高性能混凝土,粉煤灰占胶凝材料用量0_30wt%,硅灰占胶凝材料用量0-10wt%,高岭粉占胶凝材料用量0-20wt%。
[0015] 以上所述的再生骨料高性能混凝土,胶凝材料用量为450_550Kg/m3,水灰比为
0.30-0.40,按重量百分比,改性再生骨料占粗骨料用量的50%-80% ;粉煤灰占胶凝材料用量25-30wt%,或硅灰占胶凝材料用量8-10wt%,或高岭粉占胶凝材料用量10-12wt%。
[0016] 以上所述的再生骨料高性能混凝土,对再生骨料进行改性的纳米二氧化硅水胶体的浓度为25-30wt %,再生骨料浸泡处理时间8-10天。
[0017] 本发明根据再生骨料空隙率高导致的吸水率高的特点,基于现有再生骨料混凝土的制造方法,利用水胶体纳米二氧化硅改善再生骨料物理性质和力学性能,使混凝土的力学性能和耐久性大大改善。
具体实施方式
[0018] 本发明根据再生骨料空隙率高导致的吸水率高的特点,基于现有再生骨料混凝土的制造方法,利用水胶体纳米二氧化硅改善再生骨料物理性质和力学性能,适用于高性能再生骨料混凝土。本发明首先将纳米二氧化硅按一定比例加入水中搅拌制造其水胶体,然后将再生骨料放入该水胶体中浸泡一定时间即可减低再生骨料的吸水率并增加其压碎指标。利用纳米二氧化硅水胶体处理过的再生骨料制造的混凝土其力学性能和耐久性大大改
口 ο
[0019] 本发明通过利用纳米二氧化硅水胶体浸泡处理再生骨料提高其性能的方法以提高再生骨料在高性能混凝土中的利用率。
[0020] 本发明高性能混凝土由水泥,骨料,掺合料,添加剂和水组成。其中水泥为混凝土技术中通常采用的任何水泥包括各类娃酸盐类水泥(Portland cement)、硫招酸盐水泥,或白水泥、或彩色水泥、或以上任何一种水泥加各种颜料。其中粗骨料包括:再生粗骨料,天然碎石,或卵石,或人造轻骨料,或以上骨料的混合物。细骨料包括河沙,或水洗海砂,或石英砂,或人工制造的各种细砂如玻璃砂和粉碎石砂;其中掺合料可包括:高岭粉(metakaolin),硅粉(silica fume)和填充细粉(如石灰石粉和钛白粉)。
[0021] 纳米二氧化硅为粒径范围为4-100纳米,比表面积> 700m2/g,且可以稳定地分散在水或其他液体中。
[0022] 粒径范围在4-100纳米,比表面积可达到750m2/g的纳米二氧化娃(nano_Si02)可以稳定地分散在水或其他液体中。一般地,水泥水化产物中的毛细管孔在10-1000纳米,而在低水灰比条件下水化反应进行的较好的水泥浆体中其毛细管孔小于100纳米.水胶体纳米二氧化硅可以填充在毛细孔和水泥颗粒之间即发生“填充效应”且纳米二氧化硅可以与再生骨料中的氢氧化钙发生化学反应生成CSH凝胶从而改善混凝土的微观结构,降低空隙率,提高强度。
[0023] 本发明所述混凝土的各种成分配比可参考本领域的常规方案。
[0024] 优选地,本发明所述再生骨料高性能混凝土中,水灰比为0.25-0.45,胶凝材料(水泥+矿物添加剂)用量400-650Kg/m3,再生粗骨料可以取代天然石子骨料20%_100%,粉煤灰可以取代水泥量为0-30wt%,硅灰可以取代水泥量为5-10wt%,或高岭粉取代水泥量为0-20wt%。纳米二氧化硅水胶体的浓度为15%-35wt%,浸泡处理时间6-12天。
[0025] 更优选地,本发明所述再生骨料结构混凝土中,水灰比为0.30-0.40,胶凝材料(水泥+矿物添加剂)用量450-550Kg/m3,再生粗骨料可以取代天然石子骨料50%_80%,粉煤灰可以取代水泥量为25wt%,硅灰可以取代水泥量为8 wt%,或高岭粉取代水泥量为10wt%。纳米二氧化硅水胶体的浓度为30wt %,浸泡处理时间10天.[0026] 本发明上述再生骨料高性能混凝土的制备方法如下:
[0027] 首先将纳米二氧化硅按一定比例加入水中搅拌制造其水胶体,然后将再生骨料放入该水胶体中浸泡一定时间即可减低再生骨料的吸水率并增加其压碎指标。然后按照高性能混凝土的配合比设计将水泥,水,处理后的再生骨料,减水剂等原材料在搅拌机或搅拌车中混合搅拌均匀即可得到本发明制造的再生骨料高性能混凝土。
[0028] 下面,结合具 体实施例,对本发明作进一步详细说明。
[0029] 表1列出了粒径为20毫米和10毫米的再生骨料(处理前的吸水率分别为6.85%和7.92%,比重分别为2386公斤/立方米和2348公斤/立方米,利用不同浓度的二氧化硅在不同压力和不同养护时间条件下处理后按照标准方法测得的再生骨料的物理性质和力学性能。
[0030] 从表1所列的数据可以看出,随着nano_Si02浓度的增加和浸泡处理时间的延长,处理后的再生骨料的比重和压缩碎指标增加,吸水率下降。nano-Si02浓度达30%,浸泡处理时间10天时,骨料性能改善效果最佳。但是nano-Si02浓度超过30%,浸泡处理时间超过10天时骨料性能的改变已经变得不明显。
[0031] 表1:不同纳米二氧化硅浓度和不同浸泡时间处理过的再生骨料的性能表
[0032]
Figure CN102786243BD00061
[0033] 表2列出了利用浓度为30%纳米二氧化硅水胶体浸泡10天后的再生骨料制造混凝土的配比,而表3列出了按表2的配比制造的高性能混凝土的力学性能和耐久性能;其中,R0-50和R0-100采用未处理的再生骨料,分别为50%再生骨料取代天然骨料和100%再生骨料取代天然骨料;R_50和R-100是用浓度为30%纳米二氧化硅水胶体处理过的再生骨料,分别为50%再生骨料取代天然骨料和100%再生骨料取代天然骨料。
[0034] 从表3可以看出利用没有处理的再生骨料(R0-50和R0-100)混凝土力学性能和耐久性能较差。并且,混凝土的性能随着再生骨料的增加而下降。
[0035] 与未处理的再生骨料制造的混凝土相比,利用纳米二氧化硅水胶体处理过的再生骨料R-50和R-100制造的混凝土的28天抗压强度,劈裂强度和弹性模量都有较大的提高,112天干缩率下降,365天蠕变下降。50%再生骨料取代天然骨料制造的混凝土其28天抗压强度达到100兆帕。
[0036] 表2:不同再生骨料含量混凝土的配比表
[0037]
Figure CN102786243BD00071
[0038] 表3:不同再生骨料含量混凝土的性能表
[0039]
Figure CN102786243BD00072
[0040] 表4列出了利用浓度为30%纳米二氧化硅水胶体浸泡10天后的再生骨料在不同水泥含量,不同水灰比,不同矿物添加剂含量条件下的配比,而表5给出的是按表4的配比制造的混凝土的性能。由表5可以看出,水泥含量增加,水灰比降低,以及添加矿物添加剂高岭粉,或硅灰都可以大大改善再生骨料混凝土的力学性能和耐久性;添加粉煤灰则会降低混凝土 28天强度,但可以改善混凝土的耐久性。
[0041] 表4:不同水泥含量不同水灰比再生骨料混凝土的配比表
[0042]
Figure CN102786243BD00081
[0043] 表5:不同水泥含量不同水灰比再生骨料混凝土的性能表
[0044]
Figure CN102786243BD00082

Claims (1)

1.一种再生骨料高性能混凝土,其由水泥、骨料、掺合料、添加剂和水组成,所述骨料包括粗骨料和细骨料,其特征在于: 所述粗骨料中含有改性再生骨料,所述改性再生骨料的制备方法为,将再生骨料放入浓度为25-30wt%的纳米二氧化硅水胶体中浸泡处理,浸泡处理时间8-10天,所述纳米二氧化硅的粒径范围为4-100纳米,比表面积≥700m2/g,所述再生骨料的粒径为5_30毫米,浸泡处理前的吸水率分别为6%-8%,比重为2300-2400Kg/m3 ; 所述改性再生骨料占粗骨料用量的20%-100% (按重量百分比计),胶凝材料用量为.400-650Kg/m3,所述胶凝材料为水泥和矿物掺合料,所述矿物掺合料为粉煤灰或硅灰,所述粉煤灰占胶凝材料用量的25 — 30%,所述娃灰占胶凝材料用量的8 — 10%,水灰比为.0.25-0.45,粗骨料用 量为 900-1100Kg/m3。
CN201210261716.8A 2012-07-27 2012-07-27 一种改性再生骨料和再生骨料高性能混凝土 CN102786243B (zh)