CN102700274A - Method for acquiring colorized holographic pattern and colorized holographic pattern package paper structure - Google Patents
Method for acquiring colorized holographic pattern and colorized holographic pattern package paper structure Download PDFInfo
- Publication number
- CN102700274A CN102700274A CN2010101330157A CN201010133015A CN102700274A CN 102700274 A CN102700274 A CN 102700274A CN 2010101330157 A CN2010101330157 A CN 2010101330157A CN 201010133015 A CN201010133015 A CN 201010133015A CN 102700274 A CN102700274 A CN 102700274A
- Authority
- CN
- China
- Prior art keywords
- film
- mold pressing
- hologram pattern
- multicolor patterns
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a method for acquiring colorized holographic pattern and a colorized holographic pattern package paper structure. The method comprises the following steps of: supplying a thin film; printing a multi-color pattern on the surface of the thin film; coating a die-pressing agent on the thin film printed with the multi-color pattern; and performing sleeving die-pressing on the thin film coated with the die-pressing agent through die-pressing machinery with a holographic die-pressing plate, so that a holographic pattern is registered and matched with the multi-color pattern. According to the technical scheme, the holographic pattern and the printed pattern can be precisely matched, and the pattern effect is greatly enhanced.
Description
Technical field
The present invention relates generally to the pattern process field, is meant a kind of preparation method and color hologram pattern wrapping paper structure of color hologram pattern especially.
Background technology
Holographic technique is widely used, and the packaging material that contain hologram pattern are also using widely, and usually, hologram pattern can be divided into two kinds:
One, continuity pattern (wallpaper) means by less hologram pattern and is stitched together without interruption, forms as the same visual effect of wallpaper, and like the light beam figure of common indication, rainbow (Rainbow) figure etc.
Two, hologram (pegister image) independently means the graph-text content that can independently distinguish.
Hologram has unique optical effect, in packages printing under spot light; Hologram combines through following method with traditional printing color usually, like thermoprint, promptly on stock surface that traditional printing is accomplished through the method for thermoprint; Hologram " is inlayed " in printing figure message, carried out colored printing on the thermoprint surface then, this method is referred to as the first ironing and then printing method usually; The method that also has other, as printing the method for afterwards scalding earlier, it is former to be also roughly the same.
The inventor finds in realizing process of the present invention, has following shortcoming in the prior art at least: the technological process of its realization is complicated, and hologram pattern and the printed patterns realized can not mate sometimes, thereby influences pattern effect greatly.
Summary of the invention
The present invention proposes a kind of preparation method and color hologram pattern wrapping paper structure of color hologram pattern, and its technological process is simple, can accurately mate hologram pattern and printed patterns, has improved pattern effect greatly.
Technical scheme of the present invention is achieved in that
A kind of preparation method of color hologram pattern comprises:
One film is provided;
At said film surface printing multicolor patterns;
Coating mold pressing agent on the said film behind the printing multicolor patterns;
Mold pressing machinery through contour forging printing plate is housed overlaps a mold pressing to the said film that is coated with the mold pressing agent, makes hologram pattern and said multicolor patterns alignment coupling.
Preferably, said mold pressing machinery through contour forging printing plate is housed also comprises after the said film of coating mold pressing agent is overlapped a mold pressing step:
The mold pressing surface vacuum evaporated metal layer of the said film after cover position mold pressing.
Preferably, after the mold pressing surface vacuum evaporated metal layer step of said film, also comprise:
To the said film coated adhesive behind the vacuum evaporation metal level;
One base material is provided, with the said film and the said base material Compound Machining of coating adhesive.
Preferably, before said film surface printing multicolor patterns step, also comprise:
On said film, be coated with mould release; And
Also comprise after said said film and the said base material Compound Machining step with coating adhesive:
Said film is peeled off from said base material.
A kind of preparation method of color hologram pattern comprises:
One film is provided;
Surface printing multicolor patterns at said film;
Another surface coated mold pressing agent at said film;
Mold pressing machinery through contour forging printing plate is housed overlaps a mold pressing to the said film that is coated with the mold pressing agent, makes hologram pattern and said multicolor patterns alignment coupling.
Preferably, said mold pressing machinery through contour forging printing plate is housed also comprises after the said film of coating mold pressing agent is overlapped a mold pressing step:
The mold pressing surface vacuum evaporated metal layer of the said film after cover position mold pressing.
A kind of preparation method of color hologram pattern comprises:
One film is provided;
Surface printing multicolor patterns at said film;
Another surface recombination moldable material at said film;
Mold pressing machinery through contour forging printing plate is housed overlaps a mold pressing to said moldable material, makes hologram pattern and said multicolor patterns alignment coupling.
Preferably, saidly also comprise after through the mold pressing machinery that contour forging printing plate is housed said moldable material being overlapped a mold pressing step:
The mold pressing surface vacuum evaporated metal layer of the said moldable material after cover position mold pressing.
A kind of preparation method of color hologram pattern comprises:
One film is provided;
Surface coated mold pressing agent at said film;
Mold pressing machinery through contour forging printing plate is housed carries out mold pressing to the said film that is coated with the mold pressing agent;
The mold pressing surface location printing multicolor patterns of the said film after mold pressing makes hologram pattern and said multicolor patterns alignment coupling.
Preferably, saidly after mold pressing surface location printing multicolor patterns step, also comprise:
Surface vacuum evaporated metal layer at said multicolor patterns.
A kind of color hologram pattern wrapping paper structure, said color hologram pattern wrapping paper structure is made according to the above each side's method.
Technical scheme according to the invention can mate hologram pattern and printed patterns more accurately than methods such as first ironing and then printing of the prior art, thereby improve pattern effect greatly, and technological process is simple, has reduced cost through location mold pressing or location printing.
Description of drawings
In order to be illustrated more clearly in the technical scheme in the embodiment of the invention; The accompanying drawing of required use is done to introduce simply in will describing embodiment below; Obviously, the accompanying drawing in describing below only is some embodiments of the present invention, for those of ordinary skills; Under the prerequisite of not paying creative work property, can also obtain other accompanying drawing according to these accompanying drawings.
Fig. 1 is the schematic flow sheet of preparation method first embodiment of a kind of color hologram pattern of the present invention;
Fig. 2 is the schematic flow sheet of preparation method second embodiment of a kind of color hologram pattern of the present invention;
Fig. 3 is the schematic flow sheet of preparation method the 3rd embodiment of a kind of color hologram pattern of the present invention;
Fig. 4 is the schematic flow sheet of preparation method the 4th embodiment of a kind of color hologram pattern of the present invention.
The specific embodiment
To combine the accompanying drawing in the embodiment of the invention below, the technical scheme in the embodiment of the invention is carried out clear, intactly description, obviously, described embodiment only is the present invention's part embodiment, rather than whole embodiment.Based on the embodiment among the present invention, those of ordinary skills are not making the every other embodiment that is obtained under the creative work prerequisite, all belong to the scope of the present invention's protection.
With reference to Fig. 1, show the schematic flow sheet of preparation method first embodiment of a kind of color hologram pattern of the present invention, comprise step:
Step S110, a film is provided.
Said film is preferably transparent polymeric film; Further; Said film be preferably PETG (Polyethylene terephthalate, PET) film, certainly; Said film also can or be suitable for the weblike material of contour forging for the thin-film material of other type, and the present invention does not limit this.
Step S120, at said film surface printing multicolor patterns.
At said film surface printing multicolor patterns, said multicolor patterns can be provided with according to actual needs through traditional printing process.
Step S130, coating mold pressing agent on the said film behind the printing multicolor patterns.
Behind printed patterns on the said film,,, form hologram pattern above that so that carry out mold pressing processing in the surface coated mold pressing agent of the printed layers of said film.
Step S140, the mold pressing machinery through contour forging printing plate is housed overlap a mold pressing to the said film of coating mold pressing agent.
Mold pressing machinery through contour forging printing plate is housed overlaps a mold pressing to the said film that is coated with the mold pressing agent; Make the hologram pattern on the said contour forging printing plate transfer to said film surface, and make said hologram pattern and said multicolor patterns alignment coupling through the parameters such as tension force of regulating mechanical rotating speed of said mold pressing or said film.
Hologram pattern on the said contour forging printing plate can be set according to the multicolor patterns or the user's request of printing.
In another embodiment of the present invention, can also comprise behind the said step S140:
Step S150, in the mold pressing surface vacuum evaporated metal layer of said film.
The mold pressing surface that it will be understood by those skilled in the art that the said film after the mold pressing of cover position also can the vapor deposition non-metallic layer except the vacuum evaporation metal level,
Evaporated metal layer or non-metallic layer are used to form protective layer, and can increase reflecting effect, thereby form better hologram pattern.
The metal level of vacuum evaporation can be aluminium lamination, copper layer, silver layer or other metal level, and the present invention is preferably aluminium lamination.
In another embodiment of the present invention, can also comprise behind the said step S150:
Step S160, on said film coating adhesive.
To the said film coated adhesive behind evaporated metal layer or the non-metallic layer.
Step S170, with the said film and the base material Compound Machining of coating adhesive.
One base material is provided, with the said film and the said base material Compound Machining of coating adhesive.
Said adhesive is mainly used in and film and base material is carried out compound, and said adhesive is preferably PUR.
Said base material can be paper or paperboard or film, can also be other material.
Certainly; Can not adopt adhesive yet and adopt other method (like pressing) to carry out said film and said base material compound; After said film and said base material Compound Machining, the pattern on the film is complete all to be transferred on the base material, thereby forms the packaging material with holographic effect.
In another embodiment of the present invention, can also comprise before the said step S120:
Step S111, on said film, be coated with mould release.
And behind said step S170, can also comprise:
Step S171, said film is peeled off from said base material.
On said film, be coated with mould release, thereby can the pattern on the film be separated from film in the transfer process afterwards.
Owing on said film, be coated with mould release among the step S111, so said film can strip down from said base material very easily.
Technical scheme according to the invention can mate hologram pattern and printed patterns more accurately than methods such as first ironing and then printing of the prior art, thereby improve pattern effect greatly, and technological process is simple, has reduced cost through location mold pressing or location printing.
With reference to Fig. 2, show the schematic flow sheet of preparation method second embodiment of a kind of color hologram pattern of the present invention, comprise step:
Step S210, a film is provided.
Said film is preferably transparent polymeric film; Further; Said film be preferably PETG (Polyethylene terephthalate, PET) film, certainly; Said film also can or be suitable for the weblike material of contour forging for the thin-film material of other type, and the present invention does not limit this.
Step S220, at a surface printing multicolor patterns of said film.
On a surface of said film, print multicolor patterns through traditional printing process, said multicolor patterns can be provided with according to actual needs.
Step S230, in another surface coated mold pressing agent of said film.
The mold pressing agent of coating and the multicolor patterns of printing lay respectively on two surfaces of said film, and the mold pressing agent of coating is used to carry out mold pressing processing, on the surface of film, to form hologram pattern.
Step S240, the mold pressing machinery through contour forging printing plate is housed overlap a mold pressing to the said film of coating mold pressing agent.
Mold pressing machinery through contour forging printing plate is housed overlaps a mold pressing to the surface of coating mold pressing agent on the said film; Make the hologram pattern on the said contour forging printing plate transfer to said film surface, and make said hologram pattern and said multicolor patterns alignment coupling through the parameters such as tension force of regulating mechanical rotating speed of said mold pressing or said film.
Hologram pattern on the said contour forging printing plate can be set according to the multicolor patterns or the user's request of printing.
In another embodiment of the present invention, can also comprise behind the said step S240:
Step S250, in the mold pressing surface vacuum evaporated metal layer of said film.
The mold pressing surface that it will be understood by those skilled in the art that the said film after the mold pressing of cover position also can the vapor deposition non-metallic layer except the vacuum evaporation metal level,
Evaporated metal layer or non-metallic layer are used to form protective layer, and can increase reflecting effect, thereby form better hologram pattern.
The metal level of vacuum evaporation can be aluminium lamination, copper layer, silver layer or other metal level, and the present invention is preferably aluminium lamination.
The both sides that multicolor patterns that present embodiment forms and hologram pattern lay respectively at film.
Technical scheme according to the invention can mate hologram pattern and printed patterns more accurately than methods such as first ironing and then printing of the prior art, thereby improve pattern effect greatly, and technological process is simple, has reduced cost through location mold pressing or location printing.
With reference to Fig. 3, show the schematic flow sheet of preparation method the 3rd embodiment of a kind of color hologram pattern of the present invention, comprise step:
Step S310, a film is provided.
Said film is preferably transparent polymeric film; Further; Said film be preferably PETG (Polyethylene terephthalate, PET) film, certainly; Said film also can or be suitable for the weblike material of contour forging for the thin-film material of other type, and the present invention does not limit this.
Step S320, at a surface printing multicolor patterns of said film.
On a surface of said film, print multicolor patterns through traditional printing process, said multicolor patterns can be provided with according to actual needs.
Step S330, at another surface recombination moldable material of said film.
Said moldable material can be oriented polypropylene (OPP) (Oriented Polypropylene Film, OPP) film of film, polyurethane plastics PUC film or other material.
Can adopt adhesive and adopt other method (like pressing) to carry out said film and said moldable material compound.
Step S340, said moldable material is overlapped a mold pressing through the mold pressing machinery that contour forging printing plate is housed.
Mold pressing machinery through contour forging printing plate is housed overlaps a mold pressing to said moldable material; Make the hologram pattern on the said contour forging printing plate transfer to said moldable material surface, and make said hologram pattern and said multicolor patterns alignment coupling through the parameters such as tension force of regulating mechanical rotating speed of said mold pressing or said film.
Hologram pattern on the said contour forging printing plate can be set according to the multicolor patterns or the user's request of printing.
In another embodiment of the present invention, can also comprise behind the said step S340:
Step S350, in the mold pressing surface vacuum evaporated metal layer of said moldable material.
It will be understood by those skilled in the art that on the mold pressing surface except the vacuum evaporation metal level, also can the vapor deposition non-metallic layer,
Evaporated metal layer or non-metallic layer are used to form protective layer, and can increase reflecting effect, thereby form better hologram pattern.
The metal level of vacuum evaporation can be aluminium lamination, copper layer, silver layer or other metal level, and the present invention is preferably aluminium lamination.
The both sides that multicolor patterns that present embodiment forms and hologram pattern lay respectively at film.
Technical scheme according to the invention can mate hologram pattern and printed patterns more accurately than methods such as first ironing and then printing of the prior art, thereby improve pattern effect greatly, and technological process is simple, has reduced cost through location mold pressing or location printing.
With reference to Fig. 4, show the schematic flow sheet of preparation method the 4th embodiment of a kind of color hologram pattern of the present invention, comprise step:
Step S410, a film is provided.
Said film is preferably transparent polymeric film; Further; Said film be preferably PETG (Polyethylene terephthalate, PET) film, certainly; Said film also can or be suitable for the weblike material of contour forging for the thin-film material of other type, and the present invention does not limit this.
Step S420, in the surface coated mold pressing agent of said film.
Step S430, the mold pressing machinery through contour forging printing plate is housed carry out mold pressing to the said film of coating mold pressing agent.
Mold pressing machinery through contour forging printing plate is housed carries out mold pressing to the said film that is coated with the mold pressing agent, makes the hologram pattern on the said contour forging printing plate transfer to said film surface.
Hologram pattern on the said contour forging printing plate can be set according to the multicolor patterns or the user's request of printing.
The mold pressing surface location printing multicolor patterns of step S440, the said film after mold pressing.
The mold pressing surface location printing multicolor patterns of the said film after mold pressing makes hologram pattern and said multicolor patterns alignment coupling.
Multicolor patterns was printed in the location after the difference of the present embodiment and first embodiment was first mold pressing.
In another embodiment of the present invention, can also comprise behind the said step S440:
Step S450, in the surface vacuum evaporated metal layer of said multicolor patterns.
It will be understood by those skilled in the art that surface at said multicolor patterns except the vacuum evaporation metal level, also can the vapor deposition non-metallic layer,
Evaporated metal layer or non-metallic layer are used to form protective layer, and can increase reflecting effect, thereby form better hologram pattern.
The metal level of vacuum evaporation can be aluminium lamination, copper layer, silver layer or other metal level, and the present invention is preferably aluminium lamination.
Technical scheme according to the invention can mate hologram pattern and printed patterns more accurately than methods such as first ironing and then printing of the prior art, thereby improve pattern effect greatly, and technological process is simple, has reduced cost through location mold pressing or location printing.
The invention also discloses a kind of color hologram pattern wrapping paper structure, said color hologram pattern wrapping paper structure is made according to above each method embodiment.
One of ordinary skill in the art will appreciate that; In each method embodiment of the present invention; The sequence number of said each step can not be used to limit the sequencing of each step; For those of ordinary skills, under the prerequisite of not paying creative work property, the priority of each step is changed also within protection scope of the present invention.
The above is merely preferred embodiment of the present invention, and is in order to restriction the present invention, not all within spirit of the present invention and principle, any modification of being done, is equal to replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (11)
1. the preparation method of a color hologram pattern is characterized in that, comprising:
One film is provided;
At said film surface printing multicolor patterns;
Coating mold pressing agent on the said film behind the printing multicolor patterns;
Mold pressing machinery through contour forging printing plate is housed overlaps a mold pressing to the said film that is coated with the mold pressing agent, makes hologram pattern and said multicolor patterns alignment coupling.
2. the preparation method of color hologram pattern according to claim 1 is characterized in that, said mold pressing machinery through contour forging printing plate is housed also comprises after the said film of coating mold pressing agent is overlapped a mold pressing step:
The mold pressing surface vacuum evaporated metal layer of the said film after cover position mold pressing.
3. the preparation method of color hologram pattern according to claim 2 is characterized in that, after the mold pressing surface vacuum evaporated metal layer step of said film, also comprises:
To the said film coated adhesive behind the vacuum evaporation metal level;
One base material is provided, with the said film and the said base material Compound Machining of coating adhesive.
4. the preparation method of color hologram pattern according to claim 3 is characterized in that, before said film surface printing multicolor patterns step, also comprises:
On said film, be coated with mould release; And
Also comprise after said said film and the said base material Compound Machining step with coating adhesive:
Said film is peeled off from said base material.
5. the preparation method of a color hologram pattern is characterized in that, comprising:
One film is provided;
Surface printing multicolor patterns at said film;
Another surface coated mold pressing agent at said film;
Mold pressing machinery through contour forging printing plate is housed overlaps a mold pressing to the said film that is coated with the mold pressing agent, makes hologram pattern and said multicolor patterns alignment coupling.
6. the preparation method of color hologram pattern according to claim 5 is characterized in that, said mold pressing machinery through contour forging printing plate is housed also comprises after the said film of coating mold pressing agent is overlapped a mold pressing step:
The mold pressing surface vacuum evaporated metal layer of the said film after cover position mold pressing.
7. the preparation method of a color hologram pattern is characterized in that, comprising:
One film is provided;
Surface printing multicolor patterns at said film;
Another surface recombination moldable material at said film;
Mold pressing machinery through contour forging printing plate is housed overlaps a mold pressing to said moldable material, makes hologram pattern and said multicolor patterns alignment coupling.
8. the preparation method of color hologram pattern according to claim 7 is characterized in that, saidly also comprises after through the mold pressing machinery that contour forging printing plate is housed said moldable material being overlapped a mold pressing step:
The mold pressing surface vacuum evaporated metal layer of the said moldable material after cover position mold pressing.
9. the preparation method of a color hologram pattern is characterized in that, comprising:
One film is provided;
Surface coated mold pressing agent at said film;
Mold pressing machinery through contour forging printing plate is housed carries out mold pressing to the said film that is coated with the mold pressing agent;
The mold pressing surface location printing multicolor patterns of the said film after mold pressing makes hologram pattern and said multicolor patterns alignment coupling.
10. the preparation method of color hologram pattern according to claim 9 is characterized in that, saidly after mold pressing surface location printing multicolor patterns step, also comprises:
Surface vacuum evaporated metal layer at said multicolor patterns.
11. a color hologram pattern wrapping paper structure is characterized in that, said color hologram pattern wrapping paper structure is made according to each said method of claim 1 to 10.