CN102617937A - Rubber additive pre-dispersion, preparation method thereof and method for preparing rubber additives - Google Patents
Rubber additive pre-dispersion, preparation method thereof and method for preparing rubber additives Download PDFInfo
- Publication number
- CN102617937A CN102617937A CN2012100724771A CN201210072477A CN102617937A CN 102617937 A CN102617937 A CN 102617937A CN 2012100724771 A CN2012100724771 A CN 2012100724771A CN 201210072477 A CN201210072477 A CN 201210072477A CN 102617937 A CN102617937 A CN 102617937A
- Authority
- CN
- China
- Prior art keywords
- rubber
- predispersion
- rubber accelerator
- dispersion
- accelerator
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a rubber additive pre-dispersion which is high in compatibility with different kinds of rubber and of which the residual components do not influence the performance of rubber products and a simple method for preparing the rubber additive pre-dispersion conveniently. In addition, the invention also provides a method for preparing rubber additives containing the rubber additive pre-dispersion. The rubber additive pre-dispersion can be suitable for different rubber additives and is high in compatibility with different rubber products; components of the rubber additive pre-dispersion do not influence the vulcanization characteristics of ingredients and the physical properties of the products; and the rubber additive pre-dispersion and additive master batches can be granulated in an extruder by regulating a ratio of resin type chlorinated polyethylene (CPE) to a corresponding plasticizer and mixing in a banburying machine, and the master batches are blown into a collector through an air blower and are cooled transiently to obtain the pre-dispersion finish products of various additives. The rubber additive pre-dispersion can be widely applied to the field of production of the rubber additives.
Description
Technical field
The present invention relates to the preparation method of a kind of rubber accelerator predispersion and this rubber accelerator predispersion, and the preparation method who comprises the rubber accelerator of this rubber accelerator predispersion.
Background technology
Rubber accelerator (like vulcanization accelerator etc.) major part is a dry-powdered, and its volume density is less, is prone to fly upward, and particularly under wetting conditions, very easily adheres to the metallic surface, and under dryness, itself is difficult for being scattered in the rubber batching.Rubber dry-powdered additive is in producing and using; There is amounts of dust to fly upward; Cause the working space dust to exceed standard easily, having a strong impact on the healthy of staff (like Imidazolidinyl Urea, respiratory tract, influences reproduction and physiological well-being; Cause allergy, suck toxic dust etc.); And can pollute (harmful etc.) to ecotope as hydrobiont being had toxicity, environment, and receiving many-sided influences such as relevant laws and regulations and protection environment, existing a lot of rubber item manufacturer all requires to use granulated product.
Existing rubber accelerator such as vulcanization accelerator can be made masterbatch through dry powder is carried out granulation, and convenient the interpolation used, and can avoid problems such as above-mentioned various contact dust simultaneously.The dry powder master batch technologies such as granulation or wet bonding granulation of directly pressurizeing through dry powder are produced; Though these two kinds of method simple and fasts; The concentration of gained additive masterbatch is higher, but owing to applying pressure in the manufacturing processed is bigger, forms scleroma group in the powder developmental process easily; Be difficult for scattering after being added into the rubber batching, can cause the ununiformity of batching.Not scattered scleroma group can be deposited in the rubber unvulcanizate, is not easy to filter out, and the physical and mechanical properties of resulting product can reduce or cause the products appearance defective, influences the qualification rate of goods, finally causes production cost to rise.Therefore, terminal client needs manufacturers improving aspect the convenience of the easily disperse of dry powder master batch and batch mixes.
Summary of the invention
Technical problem to be solved by this invention is the deficiency that overcomes prior art, provides the strong and residual component of a kind of consistency to different rubber not influence the rubber accelerator predispersion of rubber product performance fully; And the method for a kind of ME this rubber accelerator predispersion of preparation easy, easy to make; In addition, the present invention also provides a kind of preparation to comprise the method for the rubber accelerator of said rubber accelerator predispersion.
The technical scheme that rubber accelerator predispersion of the present invention is adopted is, accounting is calculated by weight, and it comprises following composition:
EPDM 40%~90%, and CPE 5%~40%, Triple Pressed Stearic Acid 0.5%~10%.
The technical scheme that the preparation method adopted of rubber accelerator predispersion of the present invention is that this method may further comprise the steps:
(1), adds in the Banbury mixer with after the weighing by a certain percentage of EPDM, CPE and Triple Pressed Stearic Acid;
(2) opened mixer mixing 5~10 minutes, temperature is controlled between 65 ℃~110 ℃, soften into soft agglomerate to mixture after, stop mixingly, blanking is subsequent use, promptly obtains the rubber accelerator predispersion.
The technical scheme that the preparation method adopted that the present invention comprises the rubber accelerator of rubber accelerator predispersion is that this method may further comprise the steps:
A, accounting calculating by weight; Need carry out carrying out in pre-dispersed additives dry powder and 2%~10% RUBBER PROCESS OIL input Banbury mixer 8%~15% rubber accelerator predispersion, 50%~80% mixing; Wherein, Mixing time is 5~10 minutes, and melting temperature is controlled between 65 ℃~110 ℃;
B, be scattered in fully in the said rubber accelerator predispersion, and when in banburying chamber, forming softish rubber block, stop mixing when need carry out pre-dispersed additives dry powder;
C, carry out granulation to the rubber block, form the rubber accelerator particle at last.
In above-mentioned steps a, in mixing process, open Banbury mixer once, make that the sizing material in the Banbury mixer freely rolls for several times.
The rubber accelerator particle diameter that in above-mentioned steps c, obtains is that 4~6mm, length are the regular cylindrical mobile property particle of 3~5mm.
Said RUBBER PROCESS OIL is the Rubber processing white mineral oil.
The invention has the beneficial effects as follows: because the present invention is with the tackiness agent of CPE (resin type chlorinatedpolyethylene) as said rubber accelerator predispersion; Cooperate said EPDM (terpolymer EP rubber) and Triple Pressed Stearic Acid; So strong and residual component does not influence the rubber product performance, the soft easy dispersion of gained predispersion particle to rubber accelerator predispersion of the present invention fully to the consistency of different rubber; Can reduce the time that material cooperates greatly, reduce the consumption of manpower, electric power; Simultaneously the homogeneity of rubber batching improves, and can not have not scattered scleroma group, avoids goods macroscopic irregularity to occur, defective situation such as rerum natura reduction.Because the dispersiveness of multiple additives all is improved, the rerum natura of gained rubber item can significantly promote.
In addition; The preparation method of rubber accelerator predispersion according to the invention and the said preparation method who includes the rubber accelerator of said rubber accelerator predispersion are ME making method easy, easy to make, can reduce staff's labour intensity widely.
Description of drawings
Fig. 1 is a process flow sheet of the present invention;
Fig. 2 is the chemical constitution table of predispersion among the embodiment one;
Fig. 3 is the chemical constitution table of predispersion among the embodiment two;
Fig. 4 is the data contrast table of experiment one;
Fig. 5 is the data contrast table of experiment two.
Embodiment
Like Fig. 1, shown in Figure 2; The present invention is directed to surface property like dry-powdered rubber accelerators such as vulcanization accelerators; The back is with the sticker of CPE (resin type chlorinatedpolyethylene) as its predispersion after deliberation, and collocation simultaneously comes to be made into particulate state to the preparation rubber accelerator as wetting agent with the good RUBBER PROCESS OIL of rubber batching intermiscibility power.Utilize the prepared rubber accelerator particle that includes the rubber accelerator predispersion of the inventive method, stronger to the rubber compatibility of opposed polarity, can adapt to rubber batching continuous and automatic process requirements.Simultaneously the homogeneity of rubber batching improves, and can not have not scattered scleroma group, avoids goods macroscopic irregularity to occur, defective situation such as rerum natura reduction.
Rubber accelerator predispersion of the present invention accounting by weight calculates, and it comprises following composition:
EPDM 40%~90%, and CPE 5%~40%, Triple Pressed Stearic Acid 0.5%~10%.
The preparation method of said rubber accelerator predispersion may further comprise the steps: (1) with EPDM (terpolymer EP rubber), CPE (resin type chlorinatedpolyethylene) and Triple Pressed Stearic Acid weighing by a certain percentage after, add in the Banbury mixer; (2) opened mixer mixing 5~10 minutes, soften into soft agglomerate to mixture after, stop mixingly, blanking is subsequent use, promptly obtains the rubber accelerator predispersion.
As shown in Figure 1; The preparation method of said rubber accelerator may further comprise the steps: a, accounting calculating by weight; 8%~15% rubber accelerator predispersion, 50%~80% need be carried out pre-dispersed additives dry powder and 2%~10% RUBBER PROCESS OIL drop into and carry out mixingly in the Banbury mixer, wherein, mixing time is 5~10 minutes; Melting temperature is controlled between 65 ℃~110 ℃; In mixing process, open Banbury mixer once, make that the sizing material in the Banbury mixer freely rolls for several times, said RUBBER PROCESS OIL is the Rubber processing white mineral oil; B, be scattered in fully in the said rubber accelerator predispersion, and when in banburying chamber, forming softish rubber block, stop mixing when need carry out pre-dispersed additives dry powder; C, carry out granulation to the rubber block, form the rubber accelerator particle at last, the rubber accelerator particle diameter is that 4~6mm, length are the regular cylindrical mobile property particle of 3~5mm.
Below, come the present invention is further described with two concrete embodiment.
Embodiment one:BTS is made into particulate product the dry-powdered accelerator M
As shown in Figure 1, take by weighing by the rubber accelerator predispersion 4.72KG for preparing in advance shown in the subordinate list among Fig. 21, drop in the Banbury mixer; Add and treat dispersive dry-powdered MBTS 36 KG; Open Banbury mixer, slowly add the Rubber processing white mineral oil after, put down and add ram and dw; Accomplish the banburying time of setting, about 5~8 minutes altogether.Open dw therebetween, rise and to add ram, make that sizing material freely rolls twice in the banburying storehouse, mixing fully even to guarantee.After treating that material is mixed to the more moistening block of formation softness fully in the banburying storehouse, can carry out pelletizing by blanking to forcing machine.Be about 5mm through promptly obtaining diameter after the cooling of air blast scoop, length is about the soft particle of cylindric mobile rubber of 3~5mm.
Embodiment two:S is prepared into granular product dry-powdered vulcanizer sulphur
As shown in Figure 1, take by weighing by the rubber accelerator predispersion 4.95KG for preparing in advance shown in the subordinate list among Fig. 32, drop in the Banbury mixer, add and treat dispersive dry powder sulphur S44KG; Open Banbury mixer, slowly add the Rubber processing white mineral oil after, put down and add ram and dw; Accomplish the banburying time of setting, about 5~8 minutes altogether, open dw therebetween; Rise adds ram, makes that sizing material freely stands up twice in the banburying storehouse, with guarantee mixing fully evenly.After treating that material is mixed to the more moistening block of formation softness fully in the banburying storehouse, can carry out pelletizing by blanking to forcing machine.Be about 5mm through promptly obtaining diameter after the cooling of air blast scoop, length is about the soft particle of cylindric mobile rubber of 3~5mm.
The product of the present invention after for cooling drying carried out mixing application test.
Experiment one: the contrast test of MBTS-80CPE carrier
In the mixing experimentation of standard glue, the rubber accelerator particle that includes the rubber accelerator predispersion and the mix of rubber raw material on open mixing roll that detect by an unaided eye and prepare by the inventive method.The situation of in mixing process, not observing when adding powder additive to take place seriously to fly upward; Because the particle of producing is the soft rubber particle, its additive is scattered in advance, its required mixing time with obviously reduce as contrast material powder additive product.The standard mixing time of this experiment is 15 minutes.Mixing time behind the use predispersion is 8~10 minutes.The otch degree of uniformity that detects by an unaided eye finds to exist not dispersive scleroma group.Its test correlation data is as shown in Figure 4.Wherein, SBR1712 137.5phr, Triple Pressed Stearic Acid 1phr, zinc oxide 5phr, carbon black HAF N330 75phr, perfume oil 12.5phr, processing aid WB212 1phr.
Experiment two: the contrast test of sulphur S-80CPE carrier
Carried out the control cure test to the powder additive powder with by the particulate additives product that the present invention prepares, under the standard cure condition, vulcanized, the comparative experiments of physical and mechanical properties is carried out in test piece to gained rubber then.Experiment shows that the predispersion particle that uses CPE to produce as sticker can't have influence on the physical and mechanical properties of rubber unvulcanizate.Its test correlation data is as shown in Figure 5.Wherein, the test basic components is: SBR1712 137.5phr, Triple Pressed Stearic Acid 1phr, zinc oxide 5phr, carbon black HAF N330 75phr, perfume oil 12.5phr, processing aid WB212 1phr.
The present invention can be widely used in the rubber accelerator production field.
Claims (6)
1. a rubber accelerator predispersion is characterized in that, accounting is calculated by weight, and it comprises following composition:
EPDM 40%~90%, and CPE 5%~40%, Triple Pressed Stearic Acid 0.5%~10%.
2. a method for preparing rubber accelerator predispersion as claimed in claim 1 is characterized in that, this method may further comprise the steps:
(1), adds in the Banbury mixer with after the weighing by a certain percentage of EPDM, CPE and Triple Pressed Stearic Acid;
(2) opened mixer mixing 5~10 minutes, temperature is controlled between 65 ℃~110 ℃, soften into soft agglomerate to mixture after, stop mixingly, blanking is subsequent use, promptly obtains the rubber accelerator predispersion.
3. a preparation method who comprises the rubber accelerator of rubber accelerator predispersion as claimed in claim 1 is characterized in that, this method may further comprise the steps:
A, accounting calculating by weight; Need carry out carrying out in pre-dispersed additives dry powder and 2%~10% RUBBER PROCESS OIL input Banbury mixer 8%~15% rubber accelerator predispersion, 50%~80% mixing; Mixing time is 5~10 minutes, and melting temperature is controlled between 65 ℃~110 ℃;
B, be scattered in fully in the said rubber accelerator predispersion, and when in banburying chamber, forming softish rubber block, stop mixing when need carry out pre-dispersed additives dry powder;
C, carry out granulation to the rubber block, form the rubber accelerator particle at last.
4. the preparation method of rubber accelerator according to claim 3 is characterized in that, in said step a, in mixing process, opens Banbury mixer once, makes that the sizing material in the Banbury mixer freely rolls for several times.
5. the preparation method of rubber accelerator according to claim 3, it is characterized in that: the rubber accelerator particle diameter that in said step c, obtains is that 4~6mm, length are the regular cylindrical mobile property particle of 3~5mm.
6. the preparation method of rubber accelerator according to claim 3, it is characterized in that: said RUBBER PROCESS OIL is the Rubber processing white mineral oil.