CN102614871A - Method for preparing grapheme/silver nanoparticles composite material by using liquid phase method - Google Patents
Method for preparing grapheme/silver nanoparticles composite material by using liquid phase method Download PDFInfo
- Publication number
- CN102614871A CN102614871A CN2012100549522A CN201210054952A CN102614871A CN 102614871 A CN102614871 A CN 102614871A CN 2012100549522 A CN2012100549522 A CN 2012100549522A CN 201210054952 A CN201210054952 A CN 201210054952A CN 102614871 A CN102614871 A CN 102614871A
- Authority
- CN
- China
- Prior art keywords
- graphene
- grapheme
- solution
- liquid phase
- silver nanoparticles
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a method for preparing a grapheme/silver nanoparticles composite material by using a liquid phase method. N and N-dimethyl formamide (DMF) serve as a reducing agent, grapheme powder with purity as high as 99% serves as a carrier, and silver forms a core and grows on a grapheme layer under a soft reaction condition to obtain the grapheme/silver nanoparticles composite material. The preparation method has the advantages of being simple, convenient, rapid and high-efficient in process, the grapheme/silver nanoparticles composite material prepared by using the method is high in purity and less in impurity content, and silver nanoparticles generated on the surface layer of the grapheme are small in particle size, uniform in distribution and high in bond strength with the grapheme. The silver nanoparticles are closely absorbed on the grapheme layer, aggregation of the grapheme is effectively avoided, and application of the grapheme/silver nanoparticles composite material in the fields of electron, catalysis, antibiosis and the like can be enlarged.
Description
Technical field
The present invention relates to a kind of preparation method of nano composite material, relate in particular to the preparation method of a kind of Graphene-Nano silver grain composite.
Background technology
Graphene is that a kind of carbon atom is distributed in the monoatomic layer crystal on the two-dimentional honeycomb crystal lattice; Since the Graphene Graphene comes to light; Because its good physicochemical properties and wide application prospect, the research work relevant with Graphene become the current research focus of related discipline.
Graphene makes Graphene become a very desirable nanoparticulate carriers and prepares graphene-based composite owing to have two unique nanostructureds.Demonstrate the characteristic of many excellences and the excellent properties of Graphene inherence is also feasible based on the composite of Graphene, and received great concern.For example, Graphene is added in the SnAgCu solder, can obviously improve the intensity of solder; Utilizing Graphene is carrier loaded nano particle, can improve the application performance of these particles in fields such as energy storage, catalysis, sensor, photoelectricity.
The Ag nano particle makes it at catalysis, SERS, sensing, biomarker, aspect such as antibiotic important use arranged owing to have special electronic structure and huge specific area ratio.In the prior art, preparation and the application of some reports about Graphene-Nano silver grain composite arranged.For example; Germany " little " (Small; 2253 pages of 2009 20 phases) reported a kind of method of synthetic silver/graphite alkene composite, this method utilizes graphene oxide under alkali condition, to reduce silver nitrate, carries out hydrazine then and handles and make Graphene/argentum nano composite material; China " research in nanotechnology " (Nano Research; Volume was 339 pages in 2010 the 3rd) reported the preparation method of a kind of Graphene/silver; This method utilizes ethylene glycol and sodium borohydride as mixing reducing agent; Reduction silver nitrate and graphene oxide make Graphene-Yin mixture, and have analyzed its application aspect SERS and anti-biotic material; Britain's " chemical communication " (Chemical Communications, 2011 22 phase 6440 pages) has reported and has utilized polyvinylpyrrolidone (PVP) as reducing agent that reduction silver nitrate and graphene oxide prepare Graphene/argentum nano composite material.
Although the preparation method of Graphene/Nano silver grain composite has had some reports; But Graphene in the above-mentioned report/Nano silver grain composite material and preparation method thereof has mostly been used graphene oxide; And graphene oxide is compared with Graphene; Contain a lot of oxygen-containing functional groups on the surface of graphene oxide; These oxygen-containing functional groups and carbon atom combine through further reduction with the form of covalent bond, and part functional group still can not eliminate, thereby has had a strong impact on the serviceability of composite.
Therefore, directly on the Graphene surface, generate Nano silver grain, thereby preparation Graphene/argentum nano composite material has great importance.
Summary of the invention
To above-mentioned prior art, the present invention provides a kind of liquid phase method to prepare the method for Graphene/Nano silver grain composite.Adopt N, dinethylformamide (DMF) is as reducing agent, purity up to 99% graphene powder as carrier; Under the reaction condition of gentleness; Silver on graphene layer forming core, grow up, obtain Graphene/Nano silver grain composite, this preparation method's technology is simple; The Graphene of producing/silver composite material purity is high, and impurity content is few.Graphene-Nano silver grain the composite that is synthesized by preparation method of the present invention has potential extensive use at catalysis, photoelectric field, can enlarge the application of Graphene/argentum nano composite material in electronics, catalysis, field such as antibiotic.
In order to solve the problems of the technologies described above, a kind of liquid phase method of the present invention prepares the technical scheme that Graphene/method of Nano silver grain composite is achieved and is: this preparation method may further comprise the steps:
The N of step 1, preparation Graphene, dinethylformamide solution:
The ratio of Graphene with 0.1mg/mL~0.5mg/mL is scattered in the DMF solution; And adding surfactant lauryl sodium sulfate; Its quality is 0.1~0.5 times of Graphene quality; With above-mentioned solution at 40KHz, sonicated in the ultrasonic cleaner of 100W, the processing time is 60min~180min;
According to the mass ratio of Graphene and silver nitrate is to take by weighing silver nitrate in 1: 4~1: 12, the ratio of silver nitrate with 0.01mol/L~0.05mol/L is scattered in the deionized water vigorous stirring 5~10min under magnetic stirring apparatus;
Step 3, will mix by two kinds of solution with the step 2 preparation of above-mentioned steps one preparation; Ultrasonic concussion 30min~60min; Transfer to then in one or three mouthfuls of beakers, the pH value of this mixed solution is adjusted into 6~8, water-bath is heated to 60~70 ℃; And vigorous stirring, reaction 30min~90min;
Step 4, with the static 12h~24h of solution that above-mentioned steps three reaction is accomplished, obtain Graphene/silver composite deposition; Precipitated product is filtered, uses ethanol, acetone, washed with de-ionized water then successively, with product in air dry oven under room temperature dry 24h, obtain Graphene-Nano silver grain composite.
Wherein, the Graphene in the step 1 can prepare with physical method, and for example micromechanics is peeled off method, liquid phase or gas phase and directly peeled off method.
Wherein, be to be that 5% ammonia spirit carries out to the adjustment of the pH of mixed solution in the step 3 through 0.01mol/L salpeter solution or mass fraction.
In addition, can use condensing unit to prevent the evaporation of solvent in the step 3, its condensing unit is straight shape or spherical condensation tube.
Compared with prior art, the invention has the beneficial effects as follows:
(1) directly on graphene layer, generate silver nano-grain, the composite impurity content of preparation is low, applied range;
(2) the silver nano-grain particle diameter that give birth to generate on the Graphene top layer is little, be evenly distributed and the bond strength of Graphene high;
(3) Nano silver grain is adsorbed on the graphene layer closely, has effectively stoped the reunion of Graphene.
The present invention has that technology is simple, convenient, characteristics of high efficiency, and the synthetic Graphene-Nano silver grain composite of this method has potential extensive use at catalysis, photoelectric field.
Description of drawings
Fig. 1 is the Graphene/argentum nano composite material transmission electron microscope picture of embodiment 2 preparations;
Fig. 2 is the Graphene/argentum nano composite material EDX analysis result of embodiment 2 preparations;
Fig. 3 is the Graphene/argentum nano composite material X-ray diffraction analysis figure of embodiment 2 preparations;
Fig. 4 is the Graphene/Nano silver grain composite sem photograph of embodiment 2 preparations.
The specific embodiment
Elaborate in the face of embodiments of the invention down: each embodiment provided detailed embodiment and process, but protection scope of the present invention is not limited to following embodiment being to implement under the prerequisite with technical scheme of the present invention.
Embodiment 1
The Graphene of getting 10mg is scattered among the DMF of 30mL; The lauryl sodium sulfate that adds 3mg then, at 40KHz, the 100W power ultrasonic is handled 100min; Thereby break the reunion of Graphene; Graphene film is dispersed in the DMF solution uniformly, makes the N of Graphene thus, dinethylformamide (DMF) solution; The silver nitrate that takes by weighing 40mg is dissolved in the deionized water of 15mL, and magnetic agitation 5 minutes is fully dissolved it and obtained silver nitrate aqueous solution; With the N of above-mentioned Graphene, dinethylformamide (DMF) solution and silver nitrate aqueous solution mix, ultrasonic oscillation 30min; Transfer to then in one or three mouthfuls of beakers; Adjustment pH value is 7, vigorous stirring reaction 30min in 60 ℃ water-bath, quiescent setting 24h after reaction is accomplished; To obtain the precipitated product filtration and use ethanol, acetone, washed with de-ionized water successively, drying at room temperature 24h promptly obtains product of the present invention in air dry oven: Graphene-Nano silver grain composite.
The Graphene of getting 10mg is scattered among the DMF of 30mL, adds the lauryl sodium sulfate of 3mg then, and at 40KHz, the 100W power ultrasonic is handled 60min, thereby the reunion of breaking Graphene is dispersed in the DMF solution graphene film uniformly; The silver nitrate that takes by weighing 80mg is dissolved in the deionized water of 15mL, and magnetic agitation 7 minutes is fully dissolved it; Above-mentioned two kinds of solution are mixed; Ultrasonic oscillation 60min transfers in three mouthfuls of beakers then, and using mass fraction is that 5% alkene ammoniacal liquor adjustment pH value is 8; Vigorous stirring reaction 60min in 65 ℃ water-bath; Quiescent setting 20h after reaction is accomplished also uses ethanol, acetone, washed with de-ionized water successively with the precipitated product filtration, and drying at room temperature 24h obtains Graphene/silver powder and is product of the present invention in air dry oven: Graphene-Nano silver grain composite.
We can find out from Fig. 1, and silver nano-grain is adsorbed on the surface of Graphene closely, and grain size is little, is evenly distributed.Fig. 2 is the analysis result of EDX, has shown that this composite is made up of Nano Silver and carbon structure.Fig. 3 is that the XRD analysis result shows: 4 diffraction maximums are the characteristic peak of Ag, have 4 crystal faces, and the corresponding indices of crystallographic plane are followed successively by (111) from inside to outside, and (200), (220) and (311) are face-centred cubic structure.Fig. 4 is that we can find out through sem photograph, the Graphene favorable dispersibility, and the silver nano-grain of Graphene top layer absorption has effectively stoped the reunion of Graphene.
Embodiment 3
The Graphene of getting 10mg is scattered among the DMF of 30mL, adds the lauryl sodium sulfate of 3mg then, at 40KHz; The 100W power ultrasonic is handled 120min, thereby the reunion of breaking Graphene is dispersed in the DMF solution graphene film uniformly; The silver nitrate that takes by weighing 120mg is dissolved in the deionized water of 15mL, and magnetic agitation 10min fully dissolves it; Above-mentioned two kinds of solution are mixed, and ultrasonic oscillation 50min transfers in one or three mouthfuls of beakers then; Using mass fraction is that 5% alkene ammoniacal liquor adjustment pH value is 8, vigorous stirring reaction 80min in 65 ℃ water-bath, quiescent setting 18h after the reaction completion; The precipitated product filtration is also used ethanol, acetone, washed with de-ionized water successively, drying at room temperature 24h in air dry oven, Graphene/silver powder that gained gets is product of the present invention: Graphene-Nano silver grain composite.
Embodiment 4
The Graphene of getting 10mg is scattered among the DMF of 30mL, adds the lauryl sodium sulfate of 3mg then, at 40KHz; The 100W power ultrasonic is handled 180min, thereby the reunion of breaking Graphene is dispersed in the DMF solution graphene film uniformly; The silver nitrate that takes by weighing 80mg is dissolved in the deionized water of 15mL, and magnetic agitation 10min fully dissolves it; Above-mentioned two kinds of solution are mixed, and ultrasonic oscillation 40min transfers in one or three mouthfuls of beakers then; Using the salpeter solution adjustment pH value of 0.01mol/L is 6, vigorous stirring reaction 90min in 60 ℃ water-bath, quiescent setting 12h after reaction is accomplished; The precipitated product filtration is also used ethanol, acetone, washed with de-ionized water successively, and drying at room temperature 24h promptly gets product of the present invention in air dry oven: Graphene-Nano silver grain composite.
Embodiment 5
The Graphene of getting 10mg is scattered among the DMF of 30mL, adds the lauryl sodium sulfate of 3mg then, at 40KHz; The 100W power ultrasonic is handled 80min, and the silver nitrate that takes by weighing 80mg is dissolved in the deionized water of 15mL magnetic agitation 6min; It is fully dissolved, above-mentioned two kinds of solution are mixed ultrasonic oscillation 40min; Transfer in one or three mouthfuls of beakers; Using mass fraction is that 5% alkene ammoniacal liquor adjustment pH value is 8, vigorous stirring reaction 40min in 62 ℃ water-bath, quiescent setting 12h after the reaction completion; Sediment is used ethanol, acetone, washed with de-ionized water successively, and drying at room temperature 24h obtains product of the present invention in drying box: Graphene-Nano silver grain composite.
Although invention has been described for top combination figure; But the present invention is not limited to the above-mentioned specific embodiment, and the above-mentioned specific embodiment only is schematically, rather than restrictive; Those of ordinary skill in the art is under enlightenment of the present invention; Under the situation that does not break away from aim of the present invention, can also make a lot of distortion, these all belong within the protection of the present invention.
Claims (4)
1. a liquid phase method prepares the method for Graphene/Nano silver grain composite, it is characterized in that, may further comprise the steps:
The N of step 1, preparation Graphene, dinethylformamide solution:
Graphene is scattered in N with the ratio of 0.1mg/mL~0.5mg/mL; In the dinethylformamide solution; And add the surfactant lauryl sodium sulfate, its quality is 0.1~0.5 times of Graphene quality, with above-mentioned solution at 40KHz; Sonicated in the ultrasonic cleaner of 100W, the processing time is 60min~180min;
Step 2, preparation silver nitrate aqueous solution:
According to the mass ratio of Graphene and silver nitrate is to take by weighing silver nitrate in 1: 4~1: 12, the ratio of silver nitrate with 0.01mol/L~0.05mol/L is scattered in the deionized water vigorous stirring 5~10min under magnetic stirring apparatus;
Step 3, will mix by two kinds of solution with the step 2 preparation of above-mentioned steps one preparation; Ultrasonic concussion 30min~60min; Transfer to then in one or three mouthfuls of beakers, the pH value of this mixed solution is adjusted into 6~8, water-bath is heated to 60~70 ℃; And vigorous stirring, reaction 30min~90min;
Step 4, with the static 12h~24h of solution that above-mentioned steps three reaction is accomplished, obtain Graphene/silver composite deposition; Precipitated product is filtered, uses ethanol, acetone, washed with de-ionized water then successively, with product in air dry oven under room temperature dry 24h, obtain Graphene-Nano silver grain composite.
2. liquid phase method according to claim 1 prepares the method for Graphene/Nano silver grain composite, and wherein, the Graphene in the step 1 is made by physical method.
3. liquid phase method according to claim 2 prepares the method for Graphene/Nano silver grain composite, and wherein, said Graphene is peeled off method, liquid phase or gas phase by micromechanics and directly peeled off method and make.
4. liquid phase method according to claim 1 prepares the method for Graphene/Nano silver grain composite, wherein, is to be that 5% ammonia spirit carries out through 0.01mol/L salpeter solution or mass fraction to the adjustment of the pH of mixed solution in the step 3.