CN102610328A - Manufacturing method of polyvinyl acetal enameled NbTi/Cu superconducting wire - Google Patents
Manufacturing method of polyvinyl acetal enameled NbTi/Cu superconducting wire Download PDFInfo
- Publication number
- CN102610328A CN102610328A CN201210046388XA CN201210046388A CN102610328A CN 102610328 A CN102610328 A CN 102610328A CN 201210046388X A CN201210046388X A CN 201210046388XA CN 201210046388 A CN201210046388 A CN 201210046388A CN 102610328 A CN102610328 A CN 102610328A
- Authority
- CN
- China
- Prior art keywords
- nbti
- polyvinyl acetal
- cover
- enamel
- pioloform
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a manufacturing method of a polyvinyl acetal enameled NbTi/Cu superconducting wire. The superconducting wire takes a polyvinyl acetal paint as a paint for enameling, and a NbTi/Cu superconducting wire as a wire core. The method comprises an enameling process at a softening furnace temperature of 220-400 DEG C and a baking furnace temperature of 250-430 DEG C. The inventive method employs a polyvinyl acetal paint as an insulating paint, to ensure no cracking or pulverization of the enameled film at 269 DEG C below zero, and guarantee the insulation property of the enameled film, so as to ensure normal use of NbTi/Cu superconducting enameled wire at 269 DEG C below zero and realize superconducting performance.
Description
Technical field
The present invention relates to a kind of Pioloform, polyvinyl acetal enamel-cover NbTi/Cu superconducting line preparation method.
Background technology
Enamelled wire is a principal item of winding wire, is made up of conductor and paint film insulating barrier two parts, and bare wire forms through repeatedly painting, curing behind annealing softening again.But producing is the conformance with standard requirement, satisfies the product of customer requirement again and is not easy, and it receives raw material quality; Technological parameter, production equipment, factor affecting such as environment; Therefore, the mass property of various enamelled wires has nothing in common with each other, but all possesses mechanical performance; Chemical property, electrical insulation properties, hot property four big performances.
The classification of enamelled wire has by the insulating material branch: acetal paint envelope curve, polyester enamelled wire, polyurethane enamelled wire, modified poly ester enamelled wire, polyester-imide enamelled wire, polyester-imide/polyamide acid imide enamelled wire, polyimide enameled wire or the like.
Purposes by enamelled wire can be divided:
1, general purpose enamelled wire (ordinary lines) is mainly used in general motor, electrical equipment, instrument.The winding wire of workplaces such as transformer, as: polyester enamelled wire, modified poly ester enamelled wire.
2, heat-resistant enamelled wire; Be mainly used in the motor of 180 ℃ and above temperature environment work, electrical equipment, instrument, the winding wire of workplaces such as transformer, as: polyester-imide enamelled wire, polyimide enameled wire, polyester-imide/polyamidoimide composite enameled wire etc.
3, the enamelled wire of special purpose; Be meant to have the enamelled wire that certain mass property requires, be used for the winding wire of specific occasions, as: polyurethane enamelled wire (directly weldering property), self-binding enamel wire etc.
Press the conductor material branch: copper cash, aluminum steel, alloy wire.
Press the material shape branch: circle line, lenticular wire, tubular wire.
Press the insulation thickness branch: thin paint film line, paste paint film line and thickening paint film line.
NbTi/Cu superconduction enamelled wire is a kind of alloy wire, under ultralow temperature (subzero 269 ℃) environment, use, and could realize superconductivity, and under subzero 269 ℃ of environment, paint film loses insulation property because of the embrittlement easy of crack.
Summary of the invention
The technical issues that need to address of the present invention just are to overcome the defective of prior art; A kind of Pioloform, polyvinyl acetal enamel-cover NbTi/Cu superconducting line preparation method is provided; It utilizes the Pioloform, polyvinyl acetal lacquer as insulating varnish, has guaranteed that paint film embrittlement cracking, powdered etc. can not take place under the subzero 269 ℃ of environment of ultralow temperature, has guaranteed the insulation property of paint film; Guarantee the normal use of NbTi/Cu superconduction enamelled wire under the subzero 269 ℃ of environment of ultralow temperature, realized superconductivity.
For addressing the above problem, the present invention adopts following technical scheme:
The invention provides a kind of Pioloform, polyvinyl acetal enamel-cover NbTi/Cu superconducting line preparation method, said Pioloform, polyvinyl acetal enamel-cover NbTi/Cu superconducting line is used lacquer with the Pioloform, polyvinyl acetal lacquer as enamel-cover, and said preparation method comprises the enamel-cover process, and the furnace temperature of enamel-cover process is:
Softening furnace temperature: 220 ℃ ~ 400 ℃;
Oven drying temperature: 250 ℃ ~ 430 ℃.
Said Pioloform, polyvinyl acetal enamel-cover NbTi/Cu superconducting line dimensional accuracy is controlled at ± 0.005mm.
The dimensional accuracy control method is:
A is to transmission pipe road overcoat insulating tube, makes insulating varnish and the extraneous interlayer that forms, and controls the viscosity and the temperature of insulating varnish, the insulating barrier uniformity of coating through the temperature of control interlayer;
B carries out contactless japanning between painted tool and the conductor in the japanning process, avoid conductor to change and form adding up of dimensional discrepancy, and influence the overall dimension of final superconductor;
C measures per pass japanning amount meticulously by in the road japanning process, whether forms deviation with calculated value, avoids number too much to make the deviation accumulation overrun, and japanning road number is augmented or deleted in final decision.
The present invention utilizes the Pioloform, polyvinyl acetal lacquer as insulating varnish; Guaranteed that paint film embrittlement cracking, powdered etc. can not take place under the subzero 269 ℃ of environment of ultralow temperature; The insulation property of paint film have been guaranteed; Guarantee the normal use of NbTi/Cu superconduction enamelled wire under the subzero 269 ℃ of environment of ultralow temperature, realized superconductivity.
The present invention can be applied to Medical Devices, environmental protection equipment, preparation equipment, analytical test instruments/equipment, submarine propeller, aircraft carrier catapult etc.
Embodiment
The invention provides a kind of Pioloform, polyvinyl acetal enamel-cover NbTi/Cu superconducting line preparation method, said Pioloform, polyvinyl acetal enamel-cover NbTi/Cu superconducting line is used lacquer with the Pioloform, polyvinyl acetal lacquer as enamel-cover, and said preparation method comprises the enamel-cover process, and the furnace temperature of enamel-cover process is:
Softening furnace temperature: 220 ℃ ~ 400 ℃;
Oven drying temperature: 250 ℃ ~ 430 ℃.
Said Pioloform, polyvinyl acetal enamel-cover NbTi/Cu superconducting line dimensional accuracy is controlled at ± 0.005mm.
The dimensional accuracy control method is:
A is to transmission pipe road overcoat insulating tube, makes insulating varnish and the extraneous interlayer that forms, and controls the viscosity and the temperature of insulating varnish, the insulating barrier uniformity of coating through the temperature of control interlayer;
B carries out contactless japanning between painted tool and the conductor in the japanning process, avoid conductor to change and form adding up of dimensional discrepancy, and influence the overall dimension of final superconductor;
C measures per pass japanning amount meticulously by in the road japanning process, whether forms deviation with calculated value, avoids number too much to make the deviation accumulation overrun, and japanning road number is augmented or deleted in final decision.
The present invention utilizes the Pioloform, polyvinyl acetal lacquer as insulating varnish; Guaranteed that paint film embrittlement cracking, powdered etc. can not take place under the subzero 269 ℃ of environment of ultralow temperature; The insulation property of paint film have been guaranteed; Guarantee the normal use of NbTi/Cu superconduction enamelled wire under the subzero 269 ℃ of environment of ultralow temperature, realized superconductivity.
The present invention can be applied to Medical Devices, environmental protection equipment, preparation equipment, analytical test instruments/equipment, submarine propeller, aircraft carrier catapult etc.
What should explain at last is: obviously, the foregoing description only be for clearly the present invention is described and is done for example, and be not qualification to execution mode.For the those of ordinary skill in affiliated field, on the basis of above-mentioned explanation, can also make other multi-form variation or change.Here need not also can't give exhaustive to all execution modes.And conspicuous variation of being amplified out thus or change still are among protection scope of the present invention.
Claims (3)
1. Pioloform, polyvinyl acetal enamel-cover NbTi/Cu superconducting line preparation method; It is characterized in that; Said Pioloform, polyvinyl acetal enamel-cover NbTi/Cu superconducting line is used lacquer with the Pioloform, polyvinyl acetal lacquer as enamel-cover; With the NbTi/Cu superconducting line is core, and said preparation method comprises the enamel-cover process, and the furnace temperature of enamel-cover process is:
Softening furnace temperature: 220 ℃ ~ 400 ℃;
Oven drying temperature: 250 ℃ ~ 430 ℃.
2. Pioloform, polyvinyl acetal enamel-cover NbTi/Cu superconducting line preparation method as claimed in claim 1 is characterized in that: said Pioloform, polyvinyl acetal enamel-cover NbTi/Cu superconducting line dimensional accuracy is controlled at ± 0.005mm.
3. Pioloform, polyvinyl acetal enamel-cover NbTi/Cu superconducting line preparation method as claimed in claim 2 is characterized in that the dimensional accuracy control method is:
A is to transmission pipe road overcoat insulating tube, makes insulating varnish and the extraneous interlayer that forms, and controls the viscosity and the temperature of insulating varnish, the insulating barrier uniformity of coating through the temperature of control interlayer;
B carries out contactless japanning between painted tool and the conductor in the japanning process, avoid conductor to change and form adding up of dimensional discrepancy, and influence the overall dimension of final superconductor;
C measures per pass japanning amount meticulously by in the road japanning process, whether forms deviation with calculated value, avoids number too much to make the deviation accumulation overrun, and japanning road number is augmented or deleted in final decision.