CN102602095B - 冰箱彩塑覆膜饰条及其制备方法 - Google Patents
冰箱彩塑覆膜饰条及其制备方法 Download PDFInfo
- Publication number
- CN102602095B CN102602095B CN201210059264.5A CN201210059264A CN102602095B CN 102602095 B CN102602095 B CN 102602095B CN 201210059264 A CN201210059264 A CN 201210059264A CN 102602095 B CN102602095 B CN 102602095B
- Authority
- CN
- China
- Prior art keywords
- composite membrane
- overlay film
- plastic part
- refrigerator
- special plastic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及一种冰箱彩塑覆膜饰条,所述饰条(1)包括异形塑料件(1.1),其特征在于所述异形塑料件(1.1)的外表面覆有一层复合膜(1.2),所述复合膜(1.2)为塑料复合膜,其制备方法步骤包括:放卷、上胶、烘干、预热和覆膜。本发明一种冰箱彩塑覆膜饰条及其制备方法,由于异形塑料件的外表面覆有一层塑料复合膜,使得产品具有环保、易清洗、外观图案颜色灵活多样性,耐磨损性、表面抗裂性、抗酸碱性较好的优点。
Description
技术领域
本发明涉及一种冰箱彩塑覆膜饰条,特别涉及一种冰箱彩塑覆膜饰条及其制备方法,属于家用电器领域。
背景技术
传统的冰箱门边框用饰条表面采用喷涂的工艺进行表面处理,喷涂工艺具有以下几个缺点:1、由于喷漆环保性较差,使得喷涂之后的饰条整体环保性能较差;2、喷漆之后的饰条表面不易清理;3、普通的喷漆外观图案颜色的灵活多样性较差;4、饰条表面没有做过多的耐磨抗裂耐酸碱处理,使得边框的耐磨损性、表面抗裂性、抗酸碱性较差。
发明内容
本发明的目的在于克服上述不足,提供了一种环保、易清洗、外观图案颜色灵活多样性,耐磨损性、表面抗裂性、抗酸碱性较好的冰箱彩塑覆膜饰条及其制备方法。
本发明的目的是这样实现的:
一种冰箱彩塑覆膜饰条,所述饰条包括异形塑料件,所述异形塑料件的外表面覆有一层复合膜,所述复合膜为塑料复合膜。
所述异形塑料件由改性SMC塑料或者ABS塑料制成。
所述饰条制备方法工艺步骤如下:
步骤一、放卷
在放卷装置上进行复合膜放卷;
步骤二、上胶
步骤一放卷之后的复合膜背面在涂胶装置上涂覆胶水;
步骤三、烘干
步骤二上胶完成的复合膜进入加热装置进行加热烘干;
步骤四、预热
步骤三烘干完成后复合膜通过预热装置进行预热;
步骤五、覆膜
步骤四预热完成的复合膜与挤出成型的异形塑料件一起同时进入滚压装置进行异形塑料件表面覆膜,滚压装置采用多个压轮将复合膜压合于异形塑料件表面。
步骤一所述的放卷速度为1~10m/min,所述复合膜为VCM复合膜;
步骤二所述胶水由质量份数18~20份泰诺普公司生产的523胶水和质量份数为1~5份的固化剂混合制成;
步骤三所述的加热温度为20~100℃,加热时间为30~60s;
步骤四所述的预热温度为20~100℃;
步骤五所述的压合的压力为15~30MPa。
本发明的有益效果是:
本发明一种冰箱彩塑覆膜饰条及其制备方法,由于异形塑料件的外表面覆有一层塑料复合膜,使得产品具有环保、易清洗、外观图案颜色灵活多样性,耐磨损性、表面抗裂性、抗酸碱性较好的优点。
附图说明
图1为本发明一种冰箱彩塑覆膜饰条的实施例一结构示意图。
图2为本发明一种冰箱彩塑覆膜饰条的实施例二结构示意图。
图3为本发明一种冰箱彩塑覆膜饰条的制备方法流程图。
其中:
饰条1
异形塑料件1.1
塑料复合膜1.2
放卷装置2
涂胶装置3
加热装置4
预热装置5
滚压装置6。
具体实施方式
参见图1和图2,图1和图2分别为本发明涉及的一种冰箱彩塑覆膜饰条的实施例一盒实施例二结构示意图,本发明涉及的一种冰箱彩塑覆膜饰条,所述饰条1包括异形塑料件1.1,所述异形塑料件1.1最好由改性SMC塑料(片状模塑料)或者ABS塑料制成,所述异形塑料件1.1的外表面覆有一层复合膜1.2,所述复合膜1.2为塑料复合膜,所述复合膜1.2最好为VCM(氯乙烯)复合膜。
参见图3,本发明涉及的一种冰箱彩塑覆膜饰条,所述饰条1制备方法工艺步骤如下:
步骤一、放卷
在放卷装置2上进行复合膜放卷,放卷速度为1~10m/min,所述复合膜为塑料复合膜。
步骤二、上胶
步骤一放卷之后的复合膜背面在涂胶装置3上涂覆胶水,所述胶水由质量份数18~20份的双组份胶水和质量份数为1~5份的固化剂混合制成,所述双组份胶水最好为泰诺普公司生产的523胶水。
步骤三、烘干
步骤二上胶完成的复合膜进入加热装置4进行加热烘干,加热温度为20~100℃,加热时间为30~60s。
步骤四、预热
步骤三烘干完成后复合膜通过预热装置5进行预热,预热温度为20~100℃。
步骤五、覆膜
步骤四预热完成的复合膜与挤出成型的异形塑料件一起同时进入滚压装置6进行异形塑料件表面覆膜,滚压装置6采用多个压轮将复合膜压合于异形塑料件表面,压力为15~30MPa。
Claims (2)
1.一种冰箱彩塑覆膜饰条,所述饰条(1)包括异形塑料件(1.1),其特征在于所述异形塑料件(1.1)的外表面覆有一层复合膜(1.2),所述复合膜(1.2)为塑料复合膜,该冰箱彩塑覆膜饰条的制备方法的工艺步骤如下:
步骤一、放卷
在放卷装置(2)上进行复合膜放卷;
步骤二、上胶
步骤一放卷之后的复合膜背面在涂胶装置(3)上涂覆胶水;
步骤三、烘干
步骤二上胶完成的复合膜进入加热装置(4)进行加热烘干;
步骤四、预热
步骤三烘干完成后复合膜通过预热装置(5)进行预热;
步骤五、覆膜
步骤四预热完成的复合膜与挤出成型的异形塑料件一起同时进入滚压装置(6)进行异形塑料件表面覆膜,滚压装置(6)采用多个压轮将复合膜压合于异形塑料件表面;
其中步骤一所述的放卷速度为1~10m/min,所述复合膜为VCM复合膜;
步骤二所述胶水由质量份数18~20份泰诺普公司生产的523胶水和质量份数为1~5份的固化剂混合制成;
步骤三所述的加热温度为20~100℃,加热时间为30~60s;
步骤四所述的预热温度为20~100℃;
步骤五所述的压合的压力为15~30MPa。
2.根据权利要求1所述的一种冰箱彩塑覆膜饰条,其特征在于所述异形塑料件(1.1)由改性SMC塑料或者ABS塑料制成。