CN102585622A - 一种掺杂纳米二氧化钛光触媒负离子涂料 - Google Patents
一种掺杂纳米二氧化钛光触媒负离子涂料 Download PDFInfo
- Publication number
- CN102585622A CN102585622A CN2012100364009A CN201210036400A CN102585622A CN 102585622 A CN102585622 A CN 102585622A CN 2012100364009 A CN2012100364009 A CN 2012100364009A CN 201210036400 A CN201210036400 A CN 201210036400A CN 102585622 A CN102585622 A CN 102585622A
- Authority
- CN
- China
- Prior art keywords
- percent
- titanium dioxide
- nano titanium
- doped nano
- negative ion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种掺杂纳米二氧化钛光触媒负离子涂料,其特征在于:涂料由下述重量百分含量的物料组成:聚羧酸胺盐0.6-1.2%,分散剂0.6-1.0%,表面活性剂0.1-0.2%,PH调节剂0.1-0.2%,消泡剂0.3-0.7%,乙二醇为2.5-4.5%,12醇脂为1.5-3.0%,钛白粉为15-25%,煅烧高岭土为6-12%,重钙为6-12%,硅酸铝为2-5%,苯丙乳液为30-45%,掺杂纳米二氧化钛为2-5%,聚氨脂增稠剂为0.6-1.2%,防霉剂为0.2-0.6%,防腐剂为0.1-0.2%,余量为水;本发明采用渗透性强、耐水性好、有弹性和具有抗碱性的微粒径苯丙乳液做主成膜物,采用掺杂纳米二氧化钛持久释放负离子,净化空气,采用纳米级超细硅酸铝提高耐候性和附着力,采用聚羧酸胺盐和聚氨脂增稠剂提高耐水性和稳定性,采用优质金红石型钛白粉,使墙面持久亮丽。
Description
技术领域
本发明涉及一种内墙用涂料,特别是一种不仅可通过太阳光、也可通过室内灯光全天候、具有可见光催化持久释放负离子、净化空气、覆盖细微裂纹、漆膜耐水、耐碱好、防霉防藻、抗污性等功能性与装饰性完美统一的环保涂料。
背景技术
人们向往自然的空气和环境,但家居装修生活中,甲醛限量超标、空气质量下降、墙面裂纹、发花、长霉、漏水、抗污等问题长期困扰人们家居生活,而这些均可通过涂刷墙面涂料而解决。目前许多墙面涂料均不能解决或不能完全解决这些问题,特别是空气质量问题,究其原因,主要是目前所使用的墙面漆不能净化空气或效果不好、净化效果不持久、不安全、不环保、耐水耐碱性不强,有的没有弹性,抗污性差,防霉防藻功能差,挥发性有机化合物(volatile organic compounds)含量高。
发明内容
为了克服现有技术的不足,本发明提供一种不仅可通过太阳光、也可通过室内灯光全天候光催化持久释放负离子、净化空气、覆盖细微裂纹、漆膜耐水、耐碱好、防霉防藻、抗污性等功能性与装饰性完美统一的环保墙面涂料。
本发明解决其技术问题所采用的技术方案是:
一种掺杂纳米二氧化钛光触媒负离子涂料,其特征在于:涂料由下述重量百分含量的物料组成:聚羧酸胺盐0.6-1.2%,分散剂0.6-1.0%,表面活性剂0.1-0.2%,PH调节剂0.1-0.2%,消泡剂0.3-0.7%,乙二醇为2.5-4.5%,12醇脂为1.5-3.0%,钛白粉为15-25%,煅烧高岭土为6-12%,重钙为6-12%,硅酸铝为2-5%,苯丙乳液为30-45%,掺杂纳米二氧化钛为2-5%,聚氨脂增稠剂为0.6-1.2%,防霉剂为0.2-0.6%,防腐剂为0.1-0.2%,余量为水。
本发明可采用辽宁龙清环保科技有限公司的掺杂纳米二氧化钛,型号为LLQTi-05A-w,其具有可见光催化持久释放负离子吸收甲醛,光解过程中产生的·OH、H2O2具有强氧化能力,可以抑制细菌生长。纳米TiO2具有非常高的化学活性,这是因为它具有奇异的表面结构。在TiO2纳米晶的表面,Ti原子缺少O氧原子的配位,这种严重的欠氧状态形成了大量的表面悬键,导致纳米粒子表面具有很高的活性。随着纳米TiO2粒径的下降,表面原子数、表面能和表面张力急剧增加,纳米TiO2的强度、韧性和超塑性与TiO2粗晶相比大大提高,纳米微粒的小尺寸效应、表面效应、量子尺寸效应及宏观量子隧道效应使得它们在电、磁、光、敏感性等方面表现出常规粒子不具备的特性。纳米TiO2的化学性质、光化学性质以及电化学性质就是这种高活性的表现。
本发明的分散剂可采用DOW 公司聚羧酸胺盐,型号为731A的产品。
本发明的表面活性剂可采用美国联合化学公司的UC-Glfwet1200,主要成分为烷氧基化醇。
本发明的防霉剂可采用为先创公司的AF2130,主要成分为胺基甲酸-1-氯-苯并咪唑-2-甲基酸和N-(3,4二氯苯基)-N.N-二甲基脲的混合物。
本发明的防腐剂可采用先创公司的GT2060,主要成分为异噻唑啉酮。
本发明的苯丙乳液可采用BASF公司的苯乙烯与丙烯酸脂合成乳液,型号为296DS。
本发明的消泡剂可采用为吉雅德公司的有机硅和矿物油混合物,型号为7120。
本发明的聚氨脂增稠剂可采用中昶公司的NLS300。
PH值调节剂可根据配料的酸碱情况采用如氢氧化钙等碱性物质或酸性物质调节,如DOW公司生产的型号为AMP-95的物质。
本发明按常规工艺即可生产,如按顺序投料,每种料搅拌均匀后再投下一种料,边投料边搅拌,待分散均匀后检测粘度即可。
本发明的有益效果是:本发明采用渗透性强、耐水性好、有弹性和具有抗碱性的微粒径苯丙乳液做主成膜物,采用掺杂纳米二氧化钛持久释放负离子,净化空气,采用纳米级超细硅酸铝提高耐候性和附着力,采用聚羧酸胺盐和聚氨脂增稠剂提高耐水性和稳定性,采用优质金红石型钛白粉,使墙面持久亮丽。
下面结合实施例对本发明进一步说明。
具体实施方式
实施例1
首先配料,称取洁净自来水14㎏,分散剂1㎏,表面活性剂0.1㎏,PH调节剂0.1㎏,消泡剂0.3㎏,乙二醇为2.5㎏,12醇脂为1.8㎏,钛白粉为18㎏、煅烧高岭土为8㎏,重钙为8㎏,硅酸铝为2㎏,苯丙乳液为38㎏,掺杂纳米二氧化钛为2㎏,聚氨脂增稠剂为0.8㎏,防霉剂为0.2㎏,防腐剂为0.2㎏,按常规制漆工艺顺序投料,每种料搅拌均匀后再投下一种料,边投料边搅拌,待分散均匀后检测粘度即可制得本发明的掺杂纳米二氧化钛光触媒负离子涂料。
实施例2
首先配料,称取洁净自来水15㎏,分散剂0.8㎏,表面活性剂0.15㎏,PH调节剂0.1㎏,消泡剂0.4㎏,乙二醇为3㎏,12醇脂为2㎏,钛白粉为20㎏,煅烧高岭土为10㎏,重钙为6㎏,硅酸铝为2㎏,苯丙乳液为35㎏,掺杂纳米二氧化钛3㎏,聚氨脂增稠剂为0.7㎏,防霉剂为0.3㎏,防腐剂为0.2㎏,按常规制漆工艺顺序投料,每种料搅拌均匀后再投下一种料,边投料边搅拌,待分散均匀后检测粘度即可制得本发明的掺杂纳米二氧化钛光触媒负离子涂料。
实施例3
首先配料,称取洁净自来水16㎏,分散剂0.6㎏,表面活性剂0.1㎏,PH调节剂0.1㎏,消泡剂0.3㎏,乙二醇为2.5㎏,12醇脂为2.2㎏,钛白粉为22㎏,煅烧高岭土为8㎏,重钙为10㎏,硅酸铝为4㎏,苯丙乳液为40㎏,掺杂纳米二氧化钛为4㎏,聚氨脂增稠剂为0.9㎏,防霉剂为0.5㎏,防腐剂为0.2㎏,按常规制漆工艺顺序投料,每种料搅拌均匀后再投下一种料,边投料边搅拌,待分散均匀后检测粘度即可制得本发明的掺杂纳米二氧化钛光触媒负离子涂料。
本发明采用的原料易得,便于施工,能有效净化空气、耐水、耐碱好、覆盖细微裂纹、防霉防藻、抗污性强、色泽持久亮丽。
Claims (5)
1.一种掺杂纳米二氧化钛光触媒负离子涂料,其特征在于:涂料由下述重量百分含量的物料组成:聚羧酸胺盐0.6-1.2%,分散剂0.6-1.0%,表面活性剂0.1-0.2%,PH调节剂0.1-0.2%,消泡剂0.3-0.7%,乙二醇为2.5-4.5%,12醇脂为1.5-3.0%,钛白粉为15-25%,煅烧高岭土为6-12%,重钙为6-12%,硅酸铝为2-5%,苯丙乳液为30-45%,掺杂纳米二氧化钛为2-5%,聚氨脂增稠剂为0.6-1.2%,防霉剂为0.2-0.6%,防腐剂为0.1-0.2%,余量为水。
2.根据权利要求1所述的一种掺杂纳米二氧化钛光触媒负离子涂料,其特征在于:防腐剂为异噻唑啉酮。
3.根据权利要求1所述的一种掺杂纳米二氧化钛光触媒负离子涂料,其特征在于:消泡剂为有机硅和矿物油混合物。
4.根据权利要求1所述的一种掺杂纳米二氧化钛光触媒负离子涂料,其特征在于:表面活性剂为烷氧基化醇。
5.根据权利要求1所述的一种掺杂纳米二氧化钛光触媒负离子涂料,其特征在于:防霉剂为胺基甲酸-1-氯-苯并咪唑-2-甲基酸和N-(3,4二氯苯基)-N.N-二甲基脲的混合物。