CN102560466B - 一种延长镀锌三价铬钝化液寿命的方法 - Google Patents

一种延长镀锌三价铬钝化液寿命的方法 Download PDF

Info

Publication number
CN102560466B
CN102560466B CN201210028324.7A CN201210028324A CN102560466B CN 102560466 B CN102560466 B CN 102560466B CN 201210028324 A CN201210028324 A CN 201210028324A CN 102560466 B CN102560466 B CN 102560466B
Authority
CN
China
Prior art keywords
passivating solution
trivalent chromium
old
value
zinc
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201210028324.7A
Other languages
English (en)
Other versions
CN102560466A (zh
Inventor
叶金堆
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Acer Is (fujian) Chemical Co Ltd
Original Assignee
Acer Is (fujian) Chemical Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Acer Is (fujian) Chemical Co Ltd filed Critical Acer Is (fujian) Chemical Co Ltd
Priority to CN201210028324.7A priority Critical patent/CN102560466B/zh
Publication of CN102560466A publication Critical patent/CN102560466A/zh
Application granted granted Critical
Publication of CN102560466B publication Critical patent/CN102560466B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明所述一种延长镀锌三价铬钝化液寿命的方法,其特征是:在镀锌三价铬老钝化液中加入氨基羧酸类络合剂,同时调高镀锌三价铬老钝化液的pH值。本发明所述氨基羧酸类络合剂以乙二胺四乙酸(EDTA)或氮基三乙酸(NTA)为最佳,其用量为0.2-5g/L,最佳用量为0.5-2g/L;所述pH值取决于镀锌三价铬老钝化液中锌离子的浓度,与新钝化液相比,锌离子每增加1g/L,pH值调高0.05—0.1。本发明能延长钝化液使用时间,工件所获得的钝化膜的各项性能与新开缸相当,由于延长钝化液的寿命,可减少废液的排放,起到环境保护的效果。

Description

一种延长镀锌三价铬钝化液寿命的方法
技术领域
[0001] 本发明涉及一种延长镀锌三价铬钝化液寿命的方法。
背景技术
[0002] 在电镀工艺中,国际上明令淘汰六价铬钝化工艺,普遍采用三价铬钝化工艺,但传统的三价铬钝化液寿命较短,一般在锌离子含量达到约5g/L时就无法得到合格钝化膜,必须交换甚至倒掉钝化液,给污水处理带来较大负担,无法做到清洁生产、节能减排。
发明内容
[0003] 本发明的目的,是要提供一种延长镀锌三价铬钝化液寿命的方法,用它来处理老化的钝化液,使其性能恢复至新开缸水平,可以延长钝化液一倍以上使用时间,减少废液的排放,有利环境保护。
[0004] 本发明是这样实现的,所述一种延长镀锌三价铬钝化液寿命的方法,其特征是:在镀锌三价铬老钝化液中加入氨基羧酸类络合剂,同时调高镀锌三价铬老钝化液的PH值。
[0005] 本发明所述氨基羧酸类络合剂以乙二胺四乙酸(EDTA)或氮基三乙酸(NTA)为最佳,其用量为0.2-5g/L,最佳用量为0.5-2g/L ;所述pH值取决于镀锌三价铬老钝化液中锌离子的浓度,与新钝化液相比,锌离子每增加lg/L,pH值调高0.05—0.1。
[0006] 本发明的有益效果是,它能延长钝化液使用寿命,工件所获得的钝化膜的各项性能与新开缸相当,由于延长钝化液的寿命,可减少废液的排放,起到环境保护的效果。
具体实施方式
[0007] 本发明所述一种延长 镀锌三价铬钝化液寿命的方法,通过下列七个实施例做进一步说明。
[0008] 实施例1
[0009] EKEM-261三价铬蓝白新钝化液配制,50ml/L(Cr3+含量1.lg/L),调整pH值为1.8。钢铁镀锌后,进入该新钝化液钝化10秒,结果镀件外观蓝色均匀,耐中性盐雾实验(NSS)72—96小时。保持钝化液中Cr3+含量不变(1.lg/L)、pH值1.8,经过工作15天后,钝化液中Zn2+浓度自然升高至5g/L,钢铁镀锌后,进入该老钝化液钝化10秒,结果边角、孔位等处发黄,颜色不均匀,耐NSS降至48-72小时。在老钝化液中加入乙二胺四乙酸(EDTA) 0.5g/L,pH调为2.3进行再生,钢铁镀锌后,进入该再生钝化液钝化10秒,钝化膜外观蓝色均匀,耐NSS 72-96小时,恢复开缸水平。
[0010] 实施例2
[0011] 用氮基三乙酸(NTA)0.5g/L替代实施例1中的EDTA0.5g/L,pH值调为2.3进行再生,钢铁镀锌后,进入该再生钝化液钝化10秒,钝化膜外观蓝色均匀,耐NSS 72-96小时,恢复开缸水平。
[0012] 实施例3[0013] 实施例1的EKEM-261三价铬蓝白再生钝化液工作20天(累计工作35天)后,继续保持钝化液中Cr3+含量不变(1.lg/L),钝化液中Zn2+浓度自然升高至8g/L,在钝化液中加入EDTA 0.2g/L (累计加入0.7g/L),pH调为2.5,钢铁镀锌后,进入该再生钝化液钝化10秒,钝化膜外观蓝色均匀,耐NSS 72-96小时,恢复开缸水平。钝化液寿命延长I倍多。
[0014] 实施例4
[0015] 实施例3的再生钝化液继续工作25天(累计工作50天),钝化液中Zn2+浓度自然升高至12g/L,在钝化液中加入EDTA 0.2g/L (累计加入0.9g/L),pH调为2.7,钢铁镀锌后,进入该再生钝化液钝化10秒,钝化膜外观蓝色均匀,耐NSS 72-96小时,恢复开缸水平。钝化液寿命延长2倍多。
[0016] 实施例5
[0017] 实施例1中在老钝化液中加入EDTA 0.5g/L,但pH值保持开缸1.8不变进行再生,钢铁镀锌后,进入该再生钝化液钝化10秒,钝化膜未能恢复至开缸水平,外观不蓝,耐NSS 48-72 小时。
[0018] 实施例6
[0019] 实施例1中在老钝化液中不加EDTA,只将pH值提高至2.3进行再生,钢铁镀锌后,进入该再生钝化液钝化10秒,钝化膜未能恢复至开缸水平,外观蓝色发紫不均匀,耐NSS 48-72 小时。
[0020] 实施例7
[0021] 三价铬蓝白钝化液:三氯化铬:5 g/L (Cr3+含量1.0g/L),氟化钠:4 g/L,氯化钴:1.8 g/L,硝酸钠:10g/L,用65%硝酸调整pH值为1.7。钢铁镀锌后,进入该新钝化液钝化8秒,结果镀件外观蓝色均匀,耐NSS24-48小时。保持钝化液中Cr3+含量不变(1.0g/L)、pH值1.7,该钝化液经过工作7天后,Zn2+浓度自然升高至8g/L,钢铁镀锌后,进入该老钝化液钝化8秒,结果边角、孔位等处发黄,颜色不均匀,耐NSS降至24小时以下。在老钝化液中加入EDTA 0.5g/L, pH调为2.3进行再生,钢铁镀锌后,进入该再生钝化液钝化8秒,钝化膜外观蓝色均匀,耐NSS 24-48小时,恢复开缸水平。
[0022] 上述仅为本发明的具体实施方式,但发明的设计构思并不局限于此,凡利用此构思对本发明进行非实质性的改动,均应属于侵犯本发明保护范围的行为。

Claims (2)

1.一种延长镀锌三价铬钝化液寿命的方法,其特征是:在镀锌三价铬老钝化液中,保持三价铬含量不变,加入氨基羧酸类络合剂,同时调高镀锌三价铬老钝化液的PH值;所述的氨基羧酸类络合剂为乙二胺四乙酸(EDTA)或氮基三乙酸(NTA)。
2.根据权利要求1所述一种延长镀锌三价铬钝化液寿命的方法,其特征是:所述乙二胺四乙酸(EDTA)或氮基三乙酸(NTA)用量为0.2-5g/L ;所述pH值取决于镀锌三价铬老钝化液中锌离子的浓度,与新·钝化液相比,锌离子每增加lg/L,pH值调高0.05—0.1。
CN201210028324.7A 2012-02-09 2012-02-09 一种延长镀锌三价铬钝化液寿命的方法 Active CN102560466B (zh)