CN102503569A - Transparent glaze as well as preparation method and using method thereof - Google Patents

Transparent glaze as well as preparation method and using method thereof Download PDF

Info

Publication number
CN102503569A
CN102503569A CN2011103080894A CN201110308089A CN102503569A CN 102503569 A CN102503569 A CN 102503569A CN 2011103080894 A CN2011103080894 A CN 2011103080894A CN 201110308089 A CN201110308089 A CN 201110308089A CN 102503569 A CN102503569 A CN 102503569A
Authority
CN
China
Prior art keywords
glaze
marzacotto
ceramic
transparent glaze
hole
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2011103080894A
Other languages
Chinese (zh)
Inventor
林海啸
蔡世山
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai Gaocheng Art Packaging Co Ltd
Original Assignee
Shanghai Gaocheng Art Packaging Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanghai Gaocheng Art Packaging Co Ltd filed Critical Shanghai Gaocheng Art Packaging Co Ltd
Priority to CN2011103080894A priority Critical patent/CN102503569A/en
Publication of CN102503569A publication Critical patent/CN102503569A/en
Pending legal-status Critical Current

Abstract

The invention provides a transparent glaze as well as a preparation method and a using method of the transparent glaze. The transparent glaze is characterized in that the transparent glaze is prepared from the following ingredients in parts by weight:100 parts of fritted glaze and 40-60 parts of water. The preparation method of the transparent glaze is characterized in that the method comprises the following step of: mixing the fritted glaze with the water according to a ratio to obtain the transparent glaze. The using method of the transparent glaze is characterized in that the method comprises the following steps of: baking a ceramic blank in a reduction atmosphere at a temperature in a range of 1280-1300 DEG C for 8-10 hours; carrying out abrasive blasting to form a through hole with a pre-set shape; mixing the transparent glaze with the water, wherein the weight concentration of the transparent glaze in the mixed solution is 60-65%; applying the mixed solution to the ceramic blank through a glaze spraying method and baking the ceramic blank at a temperature in a range of 980-1050 DEG C for 4-6 hours, so as to obtain a ceramic product with the through hole covered by the transparent glaze. The ceramic product provided by the invention is provided with a hole capable of being covered by the transparent glaze so that a special decoration effect is achieved.

Description

A kind of marzacotto and preparation thereof and method of use
Technical field
The present invention relates to a kind of marzacotto and preparation thereof and method of use, belong to the ceramic technology field.
Background technology
Along with ceramic gets into huge numbers of families, ceramic glaze is the indispensable finishing material of ceramic, and existing ceramic glaze is can rough classification following according to classification and purposes: 1, lead glaze and leadless glaze; 2, raw glaze and fritted glaze; 3, once-firing or twice firing are used glaze; 4, ceramic tile, tableware, snitaryware and electroceramics are used glaze; 5, soak glaze, glaze spraying, water glaze by what enameling method was divided; 6, high melting glaze and low temperature glaze; 7, high expansion glaze and low bulk glaze; 8, firing atmosphere oxydizing flame, neutral flame and reducing flame; 9, coloured glaze and colourless glaze; 10, transparent and opaque glaze; 11, bright glaze, matt glaze, semi-mat glaze or figure glaze or the like.The stability of ceramic glaze, variety, glaze is decorated, pattern decoration has become the target that China pottery producer is pursued.
Summary of the invention
The purpose of this invention is to provide a kind of crystalline ceramics glaze and preparation and method of use.
In order to achieve the above object, the invention provides a kind of marzacotto, it is characterized in that, process by fritted glaze 100 weight parts and water 40~60 weight parts.
The present invention also provides the preparation method of above-mentioned marzacotto, it is characterized in that, comprising: with fritted glaze and water proportional mixing, obtain marzacotto.
The present invention also provides the method for use of above-mentioned marzacotto, it is characterized in that, comprising: ceramic body was fired in reducing atmosphere 8~10 hours at 1280~1300 ℃; Sandblast forms the through hole of predetermined shape; Marzacotto is mixed with water, and the weight concentration of marzacotto is 60~65% in the gained mixed solution, adopts the method for glaze spraying that mixed solution is applied on the ceramic body; Burnt till 4~6 hours at 980~1050 ℃, obtain the ceramic product that through hole is covered by marzacotto.
Preferably, the maximum distance of 2 of the edges of described through hole is not more than 1cm.
Advantage of the present invention is:
1, the present invention has adopted distinctive ceramic glaze prescription and manufacture craft, and the ceramic product of gained has the hole that is covered by marzacotto, has formed special decorative effect.
2, preparation and method of use are simple, and production cost is low.
Embodiment
Specify the present invention below in conjunction with embodiment.Ceramic body among the embodiment 1-3 is for to fire the biscuit that forms by commercially available ceramic base-material, and reducing atmosphere is a carbon monoxide atmosphere, and described fritted glaze is produced than inferior glaze ltd by Caro, and model is FKK-7012.
Embodiment 1
With fritted glaze 100 weight parts and water 40 weight part proportional mixing, obtain marzacotto.Ceramic body was fired in reducing atmosphere 8 hours at 1280 ℃; Sandblast forms a plurality of foliated lamellar through holes, and the maximum distance that the edge of foliated lamellar through hole is 2 is 1cm, and marzacotto is mixed with water; The weight concentration of marzacotto is 60% in the gained mixed solution; Adopt the method for glaze spraying that mixed solution is applied on the ceramic body, burnt till 4 hours, obtain the ceramic product that through hole is covered by marzacotto at 980 ℃; The said through hole printing opacity that is covered by marzacotto is waterproof, has special decorative effect.
Embodiment 2
With fritted glaze 100 weight parts and water 60 weight part proportional mixing, obtain marzacotto.Ceramic body was fired in reducing atmosphere 10 hours at 1300 ℃; Sandblast forms a plurality of foliated lamellar through holes, and the maximum distance that the edge of foliated lamellar through hole is 2 is 0.5cm, and marzacotto is mixed with water; The weight concentration of marzacotto is 65% in the gained mixed solution; Adopt the method for glaze spraying that mixed solution is applied on the ceramic body, burnt till 6 hours, obtain the ceramic product that through hole is covered by marzacotto at 1050 ℃; The said through hole printing opacity that is covered by marzacotto is waterproof, has special decorative effect.
Embodiment 3
With fritted glaze 100 weight parts and water 50 weight part proportional mixing, obtain marzacotto.Ceramic body was fired in reducing atmosphere 9 hours at 1290 ℃; Sandblast forms a plurality of foliated lamellar through holes, and the maximum distance that the edge of foliated lamellar through hole is 2 is 0.1cm, and marzacotto is mixed with water; The weight concentration of marzacotto is 63% in the gained mixed solution; Adopt the method for glaze spraying that mixed solution is applied on the ceramic body, burnt till 5 hours, obtain the ceramic product that through hole is covered by marzacotto at 1000 ℃; The said through hole printing opacity that is covered by marzacotto is waterproof, has special decorative effect.

Claims (4)

1. a marzacotto is characterized in that, is processed by fritted glaze 100 weight parts and water 40~60 weight parts.
2. the preparation method of the described marzacotto of claim 1 is characterized in that, comprising: with fritted glaze and water proportional mixing, obtain marzacotto.
3. the method for use of the described marzacotto of claim 1 is characterized in that, comprising: ceramic body was fired in reducing atmosphere 8~10 hours at 1280~1300 ℃; Sandblast forms the through hole of predetermined shape; Marzacotto is mixed with water, and the weight concentration of marzacotto is 60~65% in the gained mixed solution, adopts the method for glaze spraying that mixed solution is applied on the ceramic body; Burnt till 4~6 hours at 980~1050 ℃, obtain the ceramic product that through hole is covered by marzacotto.
4. the method for use of marzacotto as claimed in claim 3 is characterized in that, the maximum distance that the edge of described through hole is 2 is not more than 1cm.
CN2011103080894A 2011-10-12 2011-10-12 Transparent glaze as well as preparation method and using method thereof Pending CN102503569A (en)