CN102493066A - 一种可拔染色纺纱线的加工方法 - Google Patents

一种可拔染色纺纱线的加工方法 Download PDF

Info

Publication number
CN102493066A
CN102493066A CN2011103786050A CN201110378605A CN102493066A CN 102493066 A CN102493066 A CN 102493066A CN 2011103786050 A CN2011103786050 A CN 2011103786050A CN 201110378605 A CN201110378605 A CN 201110378605A CN 102493066 A CN102493066 A CN 102493066A
Authority
CN
China
Prior art keywords
processing method
dyeing
spinning
sliver
dyed yarn
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2011103786050A
Other languages
English (en)
Inventor
朱国民
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuxi Natural Textile Industrial Co Ltd
Original Assignee
Wuxi Natural Textile Industrial Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuxi Natural Textile Industrial Co Ltd filed Critical Wuxi Natural Textile Industrial Co Ltd
Priority to CN2011103786050A priority Critical patent/CN102493066A/zh
Publication of CN102493066A publication Critical patent/CN102493066A/zh
Pending legal-status Critical Current

Abstract

本发明涉及纺织领域的一种可拔染色纺纱线的加工方法,按照以下步骤生产:a.棉条染色,选取一定质量的棉条,以中温活性染料染成需要的颜色;b.纺纱,按照色纺工艺根据需要将步骤a的染色棉条按比例与本色或其他染色棉条进行纺纱;c.按照生产要求对步骤b的色纺纱按烧毛、摇纱工艺进行烧毛、摇纱;和/或d.色纺纱二次染色或拔白;本发明加工方法采用了棉条进行染色代替了传统散纤维染色,缩短了色纺纱加工的流程,降低了纺纱的难度,并采用更加环保的酶精练技术,减少了对棉纤维的损伤,提高了棉纤维的可纺性,是一种全新的可拔染色纺纱加工方法。

Description

一种可拔染色纺纱线的加工方法
技术领域
本发明涉及纺织技术领域的一种新型色纺纱的加工方法,具体地说是一种采用全新的可拔染色纺纱的加工方法。
背景技术
色纺纱一般是由两种或两种以上的不同色泽纤维混合纺成的纱线,色纺纱制成的面料具有一种朦胧自然的风格效果,深受消费者欢迎。目前市场上的色纺纱多为棉散纤维染色,再经过梳棉、并条、粗条、细条等工序加工而来,染料以中温型活性染料为主,色泽鲜艳,色谱齐全,能形成多种风格,但这种加工方法流程长,生产周期长,棉纤维损伤较为严重,可纺性不高,所以造成色纺纱的风格多为白色棉花与有色棉花混棉纺纱形成色纺纱,风格比较固定。
发明内容
本发明针对现有技术的加工方法流程长、生产周期长、棉纤维损伤较为严重的问题,提供了一种新型可拔染色纺纱线的加工方法,减少了纺纱工序难度、周期及对棉纤维的损伤,增加了色纺纱的可纺性,提高了色纺纱的市场竞争力。
为了解决上述技术问题,本发明提供了如下的技术方案:
一种可拔染色纺纱线的加工方法,步骤如下:
a、棉条染色,选取一定质量的棉条,以中温活性染料染成需要的颜色;b、纺纱,按照色纺工艺根据需要将步骤a的染色棉条按比例与本色或其他染色棉条进行纺纱;c、按照生产要求对步骤b的色纺纱按烧毛、摇纱工艺进行烧毛、摇纱;和/或d、色纺纱二次染色或拔白处理。
以上步骤a、d所使用的中温活性染料在市场上有广泛生产和销售,如台湾永光KN型中温活性染料。      
本发明所述的新型可拔染色纺纱线的加工方法,所用棉纤维为棉条;色纺纱中染色纤维占纤维总量的15%~90%。
上述步骤a中染色工艺步骤有:酶前处理,水洗,活性染料染色,水洗,皂洗,水洗。其中酶前处理工艺为:精练酶2~3g/L、纯碱0.05~0.07g/L、温度为45~60℃,时间为25~45min。染色工艺为:染料浓度(owf)为0.01~9.0%、氯化钠用量10~80g/L、纯碱用量10~20g/L、温度为50~60℃,时间为30~75min。皂洗工艺为:时间10~25min、皂洗剂1~3g/L,温度为90~100℃。
二次染色工艺步骤如上,其中,酶前处理工艺为:精练酶1.5~2.5g/L、纯碱0.06~0.09g/L、温度为50~60℃,时间为30~40min。染色工艺为:染料浓度(owf)为0.01~1.5%、氯化钠用量10~30g/L、纯碱用量10~20g/L、温度为60℃、时间为30~45min。皂洗工艺为:时间10~20min、皂洗剂1~3g/L,温度为80~90℃。
本发明生产的可拔染色纺纱具有生产流程短,纺纱难度低,节能环保的优势,能广泛应用于针织和梭织加工中,扩大了色纺纱的范围和种类,提升了色纺纱的整体品质。
与现有的色纺纱加工技术相比,本发明的加工方法的优点在于:
1、采用棉条染色代替传统的散纤维染色,水电气节约30%以上,操作时间减少3~4小时/缸,同时减少了纺纱工序难度和周期,常规的色纺纱周期为2~3个月,而采用棉条染色只需要1个月左右时间,而且将常规的色纺纱从配棉开始的工序直接缩短为从并条开始做,缩短了时间和提高了工作效率;
2、采用经济环保的酶处理工艺代替传统的高温碱煮练工艺,减少了对棉纤维的损伤,增加了色纺纱的可纺性,降低了纺纱的损耗达0.5~1%,纺纱支数得到提升,能达到80S/和100S/1;
3、采用色纺纱二次染色技术增加了色纺纱的色彩内容,扩大了色纺纱的品种,按本发明的方法能增加色纺纱的种类20~30个。
具体实施方式
实施例1
一种原料配比为“50%黄色棉条+50%本色棉条”生产可拔染色纺纱线(60s/2)的加工方法:
1、棉条精练、染色:在棉条染色机上染黄色棉条。精练:精练酶2g/L、纯碱0.05g/L、温度为60℃,时间为25min。染色:活性黄3RS浓度为2.0%(owf),氯化钠20g/L,纯碱20g/L,染色温度为60℃,时间50min。皂洗: 时间15min、皂洗剂2g/L,温度为90℃;
2、纺纱:按照50:50的质量比例将黄色棉条、本色棉条按照纺纱工艺纺纱; 
3、烧毛、摇纱:纱线烧毛机将上述纱线进行烧毛,车速为850m/min,然后进行摇纱,绞重为550g;
4:水洗、烘干和倒筒。
实施例2
一种原料配比为“20%红色棉条+80%本色棉条”生产红蓝色纺纱线(70s/2)的加工方法,包括以下加工步骤:
1、棉条精练、染色:在棉条染色机上染红色棉条,精练:精练酶2.5g/L、纯碱0.06g/L、温度为50℃,时间为35min。染色:活性红3BSN浓度为4.8%(owf),加氯化钠60g/L,纯碱15g/L,染色温度为55℃,时间30min。皂洗:时间20min、皂洗剂2g/L,温度为100℃;
2、纺纱:按照20:80的重量比例将红色棉条、本色棉条按照色纺工艺纺纱;
3、烧毛、摇纱:纱线烧毛机将上述纱线进行烧毛,车速为950m/min,然后进行摇纱,绞重为250g;
4、二次染色:在绞纱染色机上将烧毛摇纱后的纱线进行二次酶精练和二次染色,使纱线中的本色纤维变成蓝色,进而得到红蓝色可拔色纺纱线。精练:精练酶1.5g/L、纯碱0.09g/L、温度为50℃,时间为30min。染色:活性蓝KN-B浓度为1.5%(owf),加氯化钠30g/L,纯碱15g/L,染色温度为60℃,时间30min。皂洗:时间15min、皂洗剂1g/L,温度为90℃;
5、水洗、烘干、倒筒。
实施例3
一种原料配比为“85%黑色棉条+15%本色棉条”生产深灰色色纺纱线(80s/2)的加工方法,包括以下加工步骤:
1、棉条精练、染色:在棉条染色机上染黑色棉条,精练酶3g/L、纯碱0.07g/L、温度为60℃,时间为45min。活性黑ED-H浓度为9%(owf),加入氯化钠80g/L,纯碱10g/L,温度为50℃,保温75min;
2、纺纱:按照85:15的质量比例将黑色棉条、本色棉条按照色纺工艺纺纱;
3、烧毛、摇纱:纱线烧毛机将上述纱线进行烧毛,车速为1000m/min,然后进行摇纱,绞重为550g;
4、水洗、烘干和倒筒;
5、按照工艺要求将上述色纺纱纱线进行织造;                    
6、拔白:拔白浆:雕白块25%,棉用增白剂4BK0.8%,10%尿素,甘油2%,白涂料10%,海藻酸钠糊20%,按照印花工艺进行拔白,102℃汽蒸10min,冷水洗,皂煮,水洗,烘干。
最后应说明的是:以上所述仅为本发明的优选实施例而已,并不用于限制本发明,尽管参照前述实施例对本发明进行了详细的说明,对于本领域的技术人员来说,其依然可以对前述各实施例所记载的技术方案进行修改,或者对其中部分技术特征进行等同替换。凡在本发明的精神和原则之内,所作的任何修改、等同替换、改进等,均应包含在本发明的保护范围之内。

Claims (9)

1.一种可拔染色纺纱线的加工方法,其特征在于:包括如下步骤,
a. 棉条染色,选取一定质量的棉条,以中温型活性染料染成需要的颜色;
b. 纺纱,将步骤a的染色棉条按比例与本色或其他染色棉条进行纺纱;
c.对步骤b的色纺纱进行烧毛、摇纱;
和/或d. 对步骤c的色纺纱以中温型活性染料进行二次染色处理,或拔白处理。
2.根据权利要求1所述的可拔染色纺纱线的加工方法,其特征在于:所述步骤a、步骤d中染色工艺步骤包括酶前处理,活性染料染色和皂洗。
3.根据权利要求2所述的可拔染色纺纱线的加工方法,其特征在于:步骤a的酶前处理工艺为:精练酶2~3g/L、纯碱0.05~0.07g/L、温度为45~60℃,时间为25~45min。
4.根据权利要求2所述的可拔染色纺纱线的加工方法,其特征在于:步骤a的活性染料染色工艺为,染料浓度(owf)为0.1~9.0%、氯化钠用量10~80g/L、纯碱用量10~20g/L、温度为60℃,时间为30~75min。
5.根据权利要求2所述的可拔染色纺纱线的加工方法,其特征在于:步骤a的皂洗工艺为,时间10~25min、皂洗剂1~3g/L,温度为90~100℃。
6.根据权利要求2所述的可拔染色纺纱线的加工方法,其特征在于:步骤d的酶前处理工艺为,精练酶1.5~2.5g/L、纯碱0.06~0.09g/L、温度为50~60℃,时间为30~40min。
7.根据权利要求2所述的可拔染色纺纱线的加工方法,其特征在于:步骤d的活性染料染色工艺为,染料浓度(owf)为0.01~1.5%、氯化钠用量10~30g/L、纯碱用量10~20g/L、温度为60℃,时间为30~45min。
8.根据权利要求2所述的可拔染色纺纱线的加工方法,其特征在于:步骤d的皂洗工艺为,皂洗10~20min、皂洗剂1~2g/L,温度为80~90℃。
9.根据权利要求1所述的可拔染色纺纱线的加工方法,其特征在于:步骤b纺纱中染色棉条重量占棉条总重量的15%~90%。
CN2011103786050A 2011-11-24 2011-11-24 一种可拔染色纺纱线的加工方法 Pending CN102493066A (zh)