Casting 2 wear-resistant white cast rice huller screen sheet press strip
Technical field
The present invention relates to a kind of casting cast iron products, especially cast 2 wear-resistant white cast rice huller screen sheet press strip.
Background technology
Rice huller screen sheet press strip is because of the bad part of changing often that weares and teares in the rice mill.Produce at present rice huller screen sheet press strip, what have uses machining production, on stripe shape iron plate jewel hole, insert bolt, the production process content is various and of poor qualityly cause husk rice to yield poorly; What have casts with grey cast-iron, and it is bad often to wear and tear, and causes the one of the main reasons of cracking rice in the rice milling process.
Summary of the invention
The present invention provides a kind of casting 2 wear-resistant white cast rice huller screen sheet press strip, and the castingin bolt engages firmly with rice huller screen sheet press strip, and white cast iron anti-wear is durable, has improved rice huller screen sheet press strip service life, has improved the husk rice quality.
The technical solution adopted for the present invention to solve the technical problems is: be made up of last greensand mold, sprue, cross gate, rice huller screen sheet press strip, first screw jack, first bolt lower end, following greensand mold, moulding board, first bolt upper end, second screw jack, second bolt lower end, second bolt upper end, case outside fix pin, detachable sandbox, ingate, clay-bonded sand greensand mold system sand.Rice huller screen sheet press strip, first screw jack, first bolt lower end, first bolt upper end, second screw jack, second bolt lower end, second bolt upper end, ingate, cross gate are located at down on the greensand mold; First bolt lower end is inserted in the first screw jack; Second bolt lower end is inserted in the second screw jack; Sprue is located on the greensand mold, and with detachable sandbox and the single sand shop sand molding of clay-bonded sand greensand mold, last greensand mold and following greensand mold are with case outside fix finger setting mould assembly; The electro-smelting furnace charge; 2 wear-resistant white cast rice huller screen sheet press strip molten iron advances people's sprue and advances people's cross gate and enter to be full of behind people's ingate rice huller screen sheet press strip die cavity and castingin first, second bolt upper end.
Clay-bonded sand greensand mold system sand is that casting uses the silica sand granularity to be 20-40 order clay-bonded sand greensand mold system sand.
The chemical composition of casting 2 wear-resistant white cast rice huller screen sheet press strip: C:3.5-3.8%, Si :≤0.6%, Mn:0.15-0.20%, P :≤0.3%, S:0.2-0.4%.
The metallographic structure of casting 2 wear-resistant white cast rice huller screen sheet press strip is: cementite+pearlite.
The invention has the beneficial effects as follows; Can enhance productivity to pick up than machining production with the production of casting 2 wear-resistant white cast rice huller screen sheet press strip and many times; And bolt engages firm, wear-resistant durablely with rice huller screen sheet press strip, and 2 wear-resistant white cast rice huller screen sheet press strip improves 4 times than grey cast-iron rice huller screen sheet press strip service life.
Description of drawings
Below in conjunction with accompanying drawing and embodiment the present invention is described further.
Accompanying drawing is the structure chart of casting 2 wear-resistant white cast rice huller screen sheet press strip.
Fig. 1 is the B-B cutaway view of Fig. 2.
Fig. 2 is the A-A cutaway view of Fig. 1.
Among the figure 1, go up greensand mold, 2, sprue, 3, cross gate, 4, rice huller screen sheet press strip; 5, first screw jack, 6, first bolt lower end, 7, greensand mold down, 8, moulding board; 9, first bolt upper end, 10, the second screw jack, 11, second bolt lower end, 12, second bolt upper end; 13, case outside fix pin, 14, detachable sandbox, 15, ingate, 16, clay-bonded sand greensand mold system sand.
The specific embodiment
Accompanying drawing is the structure chart of the casting 2 wear-resistant white cast rice huller screen sheet press strip of jet-air rice polisher NF-14 type.In Fig. 1,2; Type 4 casting method spring moulding with clay-bonded sand wet type system sand 17 and detachable sandbox 15; On moulding board 8, put earlier rice huller screen sheet press strip 4, the ingate 16 of 15 millimeters of length 200 mm wides 20 millimeters thick that are provided with first screw jack 5 and second screw jack 10, the apperance of cross gate 3 well; On moulding board 8, put the drag box of detachable sandbox 15 again well, make down greensand mold 7 with clay-bonded sand greensand mold system sand 17 spring sand; Make down greensand mold 7 from moulding board 8 upsets and afterwards and with 3 case outside fix pins, 13 location put the cope of detachable sandbox 15 well and spread down tap sand, after position of sound production sprue 2 apperances on cross gate 3 apperances, make greensand mold 1 with clay-bonded sand greensand mold system sand 17 spring sand; Trip out sprue 2 apperances; Open wide and go up greensand mold 1; Trip out the apperance of rice huller screen sheet press strip 4 on following greensand mold 7, ingate 16, cross gate 3; Be inserted in the first bolt lower end 6 of cup head M6 * 28 millimeter in the first screw jack 5 of 18 millimeters of Φ 4.8 millimeters deep; The second bolt lower end 11 of cup head M6 * 28 millimeter is inserted in the second screw jack 10 of 18 millimeters of Φ 4.8 millimeters deep, and first screw jack 5 is 160 ± 1 millimeters with the pitch of holes of second screw jack 10, and the bolt axis is to 20 millimeters of nearly broadside distances; Following greensand mold 7 is located mould assemblys with last greensand mold 14 with 3 case outside fix pins 13, takes off detachable sandbox 15 block sequenceses use but be placed on the cast place to the greensand mold of having made type behind the mould assembly.With 500kg electric induction furnace melting furnace charge; Charge composition is: steel-making is with three type 80% of one group of one-level of the pig iron; Foundry returns 20%; Pour into a mould when molten iron is reduced to 1400 ± 10 ℃ behind cast iron melting to 1500 ± 10 ℃, casting 2 wear-resistant white cast material molten iron gets into sprue 2 and gets into and be full of rice huller screen sheet press strip 4 die cavities and castingin first bolt upper end 9 and second bolt upper end 12 after cross gates 3 get into ingates 16.
Clay-bonded sand greensand mold system sand is that casting uses the silica sand granularity to be 20-40 order clay-bonded sand greensand mold system sand.
The chemistry of casting 2 wear-resistant white cast rice huller screen sheet press strip becomes: C:3.5-3.8%, and Si :≤0.6%, Mn:0.15-0.20%, P :≤0.3%, S:0.2-0.4%.
The metallographic structure of casting 2 wear-resistant white cast rice huller screen sheet press strip is: cementite+pearlite.