CN102477527B - 壳体的制作方法及由该方法制得的壳体 - Google Patents
壳体的制作方法及由该方法制得的壳体 Download PDFInfo
- Publication number
- CN102477527B CN102477527B CN201010555189.2A CN201010555189A CN102477527B CN 102477527 B CN102477527 B CN 102477527B CN 201010555189 A CN201010555189 A CN 201010555189A CN 102477527 B CN102477527 B CN 102477527B
- Authority
- CN
- China
- Prior art keywords
- target
- layer
- housing
- matrix
- making method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
壳体 | 10 |
基体 | 11 |
色彩层 | 13 |
图案层 | 15 |
防护层 | 17 |
Claims (9)