CN102408794B - Vinyl acetate/acrylic emulsion waterproof paint - Google Patents
Vinyl acetate/acrylic emulsion waterproof paint Download PDFInfo
- Publication number
- CN102408794B CN102408794B CN201010290272.1A CN201010290272A CN102408794B CN 102408794 B CN102408794 B CN 102408794B CN 201010290272 A CN201010290272 A CN 201010290272A CN 102408794 B CN102408794 B CN 102408794B
- Authority
- CN
- China
- Prior art keywords
- parts
- vinyl acetate
- acrylic emulsion
- waterproof paint
- emulsion waterproof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a vinyl acetate/acrylic emulsion waterproof paint, which is prepared by the following raw materials according to weight ratio by stirring: 85 parts of vinyl acetate/acrylic emulsion , 20 parts of carboxymethyl cellulose, 25 parts of barium sulfate, 20 parts of benzoyl peroxide, 30 parts of amyl acetate, 15 parts of tourmalinite powder, 10 parts of carboxymethyl cellulose, 40 parts of magnesium silicate, 60 parts of water, 6 parts of binder, 6 parts of film forming auxiliary agent, 6 parts of dispersant and 5 parts of antifoaming agent. The product of the present invention has good application property, water resistance, insulation effect and high cost performance.
Description
Technical field
The present invention relates to a kind of vinyl acetate/acrylic emulsion waterproof paint.
Technical background
At present, people more and more focus on living environment now, so outdoor decoration is also more and more concerned.Exterior wall generally will be brushed heat insulation coating, but the water resistance of existing thermal insulation coatings is not so good, at its paint film after rain drop erosion, will integral body peel off, or because the difference of water ratio causes cracking or peels off, rainwater just infiltrates metope, and corrosion metope, seems very not attractive in appearance like this.
Summary of the invention
The present invention seeks to, in order to overcome the deficiencies in the prior art, provides the vinyl acetate/acrylic emulsion waterproof paint of a kind of water-repellancy and good heat preservation performance.
For addressing the above problem, technical scheme of the present invention is: a kind of vinyl acetate/acrylic emulsion waterproof paint stirs and makes according to weight proportion by following raw materials according: 85 parts of acrylate and vinyl acetate emulsions, 20 parts of carboxymethyl celluloses, 25 parts of barium sulfate, 20 parts of benzoyl peroxides, 30 parts of pentyl acetates, 15 parts of tourmaline powders, 10 parts of carboxymethyl celluloses, 40 parts of Magnesium Silicate q-agents, 60 parts of water, 6 parts of binding agents, 6 parts of film coalescence aid, 6 parts of dispersion agents, 5 parts of defoamers.
Beneficial effect of the present invention: there is good application property, water-repellancy, heat insulation effect, and cost performance is high.
Embodiment
Example of the present invention is can not limit the present invention to explanation of the present invention, in the implication suitable with the present invention and any change and the adjustment in scope, all should think within the scope of the invention.
Embodiment 1
Vinyl acetate/acrylic emulsion waterproof paint is stirred and is made by stirrer high speed dispersion according to weight proportion by following raw materials according: 85 parts of acrylate and vinyl acetate emulsions, 20 parts of carboxymethyl celluloses, 25 parts of barium sulfate, 20 parts of benzoyl peroxides, 30 parts of pentyl acetates, 15 parts of tourmaline powders, 10 parts of carboxymethyl celluloses, 40 parts of Magnesium Silicate q-agents, 60 parts of water, 6 parts of binding agents, 6 parts of film coalescence aid, 6 parts of dispersion agents, 5 parts of defoamers.
Claims (1)
1. a vinyl acetate/acrylic emulsion waterproof paint, is characterized in that it is to be stirred and make according to weight proportion by following raw materials according: 85 parts of acrylate and vinyl acetate emulsions, 30 parts of carboxymethyl celluloses, 25 parts of barium sulfate, 20 parts of benzoyl peroxides, 30 parts of pentyl acetates, 15 parts of tourmaline powders, 40 parts of Magnesium Silicate q-agents, 60 parts of water, 6 parts of binding agents, 6 parts of film coalescence aid, 6 parts of dispersion agents, 5 parts of defoamers.