CN102408619A - Modified high-temperature-resistance polyvinyl chloride (PVC) cable material and preparation method thereof - Google Patents
Modified high-temperature-resistance polyvinyl chloride (PVC) cable material and preparation method thereof Download PDFInfo
- Publication number
- CN102408619A CN102408619A CN2011102821023A CN201110282102A CN102408619A CN 102408619 A CN102408619 A CN 102408619A CN 2011102821023 A CN2011102821023 A CN 2011102821023A CN 201110282102 A CN201110282102 A CN 201110282102A CN 102408619 A CN102408619 A CN 102408619A
- Authority
- CN
- China
- Prior art keywords
- polyvinyl chloride
- cable material
- preparation
- compound
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a modified high-temperature-resistance polyvinyl chloride (PVC) cable material and a preparation method thereof. The modified high-temperature-resistance polyvinyl chloride cable material is prepared by the step of mixing raw materials in certain parts by weight, wherein the raw materials comprise a ethylene-vinyl acetate copolymer EVA, PVC resins, kaolin, ammonium polyphosphate, calcined zeolite powder, carbon black, straw ashes, attapulgite, a silane coupling agent, titanate, 6-tert-butyl-3-methyl phenol, paraffin and acrylic rubber. The preparation method is simple and convenient to operate, the formula of raw materials is reasonable, and the prepared cable material has the advantages of high mechanical property, high temperature resistance and high flame retardant property and is low-smoke and non-toxic when being burnt.
Description
Technical field
The present invention relates to a kind of modified, high temperature resistant polyvinyl chloride cable material and preparation method thereof, belong to field of cables.
Background technology
Along with rapid economic development, electric wire all is widely used in industry-by-industry, field.Along with the frequent generation of electrical fire accident, the fire-retardant problem of electric wire causes the attention of countries in the world gradually.Discharge a large amount of smog during cable fire and deleterious, corrosive gas is Hazard Factor in the fire, in fire, hindered people's safe escape and fire-fighting work, make lives and properties suffer heavy losses.While is along with the development of communication career, automotive industry and computer industry; Particularly many occasions such as aviation lead, line for cars, high temperature instrument cable, oil drilling platform cable more and more need be used low smoke no-halogen wire cable high temperature resistant, weather.
Summary of the invention
The purpose of this invention is to provide a kind of modified, high temperature resistant polyvinyl chloride cable material and preparation method thereof, CABLE MATERIALS of the present invention have the mechanical property height, high temperature resistant, flame retardant properties is high, LSZH during burning.
For realizing the following technical scheme of above-mentioned purpose employing of the present invention:
The modified, high temperature resistant polyvinyl chloride cable material is characterized in that the weight part of its constitutive material is:
The preparation method of described modified, high temperature resistant polyvinyl chloride cable material is characterized in that may further comprise the steps:
(1) weight part by constitutive material takes by weighing each raw material, and ethylene-vinyl acetate copolymer EVA, PVC RESINS, attapulgite, kaolin, roasting zeolite powder and carbon black are mixed, and obtains compound A;
(2) add ammonium polyphosphate, stalk ashes, silane coupling agent, titanic acid ester, the 6-tertiary butyl-3-methylphenol, paraffin and acrylic rubber among the compound A in above-mentioned steps (1) by weight; Under the normal temperature stirring at low speed 1-2 minute; Make to mix, obtain compound B;
(3) the compound B that above-mentioned steps (2) is obtained adds mill and Banbury mixer or twin screw extruder is mixing, granulation, controlled temperature 140-170 ℃, obtains finished product.
Beneficial effect of the present invention:
Preparing method of the present invention is simple, and is easy to operate, and the constitutive material prescription is reasonable, the CABLE MATERIALS that makes have the mechanical property height, high temperature resistant, flame retardant properties is high, LSZH during burning.
Embodiment
Embodiment 1: the modified, high temperature resistant polyvinyl chloride cable material, and the weight part of its constitutive material is:
The preparation method of described modified, high temperature resistant polyvinyl chloride cable material may further comprise the steps:
(1) weight part by constitutive material takes by weighing each raw material, and ethylene-vinyl acetate copolymer EVA, PVC RESINS, attapulgite, kaolin, roasting zeolite powder and carbon black are mixed, and obtains compound A;
(2) add ammonium polyphosphate, stalk ashes, silane coupling agent, titanic acid ester, the 6-tertiary butyl-3-methylphenol, paraffin and acrylic rubber among the compound A in above-mentioned steps (1) by weight; Under the normal temperature stirring at low speed 1-2 minute; Make to mix, obtain compound B;
(3) the compound B that above-mentioned steps (2) is obtained adds mill and Banbury mixer or twin screw extruder is mixing, granulation, controlled temperature 140-170 ℃, obtains finished product.
Embodiment 2: CABLE MATERIALS of the present invention and existing CABLE MATERIALS general property compare:
Embodiment 3: test correlated results relatively like following table after above-mentioned materials is vulcanized film-making:
Claims (2)
1. modified, high temperature resistant polyvinyl chloride cable material is characterized in that the weight part of its constitutive material is:
Ethylene-vinyl acetate copolymer EVA 65-75 part
PVC RESINS 20-30 part
Kaolin 15-25 part
Ammonium polyphosphate 10-20 part
Roasting zeolite powder 10-15 part
Carbon black 20-25 part
Stalk ashes 3-8 part
Attapulgite 15-25 part
Silane coupling agent 1-2 part
Titanic acid ester 1-2 part
The 6-tertiary butyl-3-methylphenol 1-1.5 part
Paraffin 0.5-1 part
Acrylic rubber 4-5 part.
2. the preparation method of a modified, high temperature resistant polyvinyl chloride cable material as claimed in claim 1 is characterized in that may further comprise the steps:
(1) weight part by constitutive material takes by weighing each raw material, and ethylene-vinyl acetate copolymer EVA, PVC RESINS, attapulgite, kaolin, roasting zeolite powder and carbon black are mixed, and obtains compound A;
(2) add ammonium polyphosphate, stalk ashes, silane coupling agent, titanic acid ester, the 6-tertiary butyl-3-methylphenol, paraffin and acrylic rubber among the compound A in above-mentioned steps (1) by weight; Under the normal temperature stirring at low speed 1-2 minute; Make to mix, obtain compound B;
(3) the compound B that above-mentioned steps (2) is obtained adds mill and Banbury mixer or twin screw extruder is mixing, granulation, controlled temperature 140-170 ℃, obtains finished product.