CN102397902A - Production technology of novel aluminum section for radiator - Google Patents
Production technology of novel aluminum section for radiator Download PDFInfo
- Publication number
- CN102397902A CN102397902A CN2010102763818A CN201010276381A CN102397902A CN 102397902 A CN102397902 A CN 102397902A CN 2010102763818 A CN2010102763818 A CN 2010102763818A CN 201010276381 A CN201010276381 A CN 201010276381A CN 102397902 A CN102397902 A CN 102397902A
- Authority
- CN
- China
- Prior art keywords
- production technology
- substrate
- section bar
- aluminium section
- aluminum section
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a production technology of a novel aluminum section for a radiator. The aluminum section comprises a substrate, the upper surface of the substrate is integratedly provided with a strip-shaped radiation plate which is perpendicular to the substrate, one side of the substrate is integratedly provided with a mounting plate, and the mounting plate is in parallel with the strip-shaped radiation plate. The production technology comprises the following steps: 1, heating an extrusion die and an A6060 aluminum bar to 480-500DEG C; 2, putting the heated aluminum bar in the extrusion die, and carrying out extrusion molding by an extruder according to an extrusion speed of 20-22m/min; 3, cooling extruded workpieces to room temperature, and straightening the cooled workpieces; and 4, keeping the temperature of the straightened workpieces at 195-205DEG C for 3.5-4.5h to age the workpieces. By adopting the production technology of the novel aluminum section for the radiator to produce the aluminum section, the aluminum section has the advantages of good quality, high qualification rate, and low production cost, so economic benefits of enterprises are effectively improved.
Description
Technical field
The present invention relates to a kind of new radiator and use the aluminium section bar production technology, belong to shape extruding manufacture technology field.
Background technology
At present, be more and more widely in the use of commercial production and daily life medium section, particularly shape (for example aluminium section bar), for example door-window section bar, shaped material of radiator and frame section bar etc. all adopt aluminium alloy extrusions mostly.Along with the progressively increase of section bar use amount, people have higher requirement to the structure and the quality of section bar, in order to produce the section bar of different structure and different qualities, must adopt pointed production technology to produce corresponding section bar.
Summary of the invention
The purpose of this invention is to provide a kind of new radiator and used the aluminium section bar production technology.
For realizing above-mentioned purpose; The invention provides following technical scheme: a kind of new radiator is used the aluminium section bar production technology; Aluminium section bar comprises substrate, and integrated setting has the strip heat sink vertical with substrate on the upper surface of substrate, and a side integrated setting of said substrate has installing plate; This installing plate and strip heat sink laterally arrange, and its production craft step is following:
At first, be that the aluminium bar of A6060 is heated between 480 ℃-500 ℃ with extrusion die and material;
Then, the aluminium bar after the heating is positioned in the extrusion die, adopts extruder to carry out extrusion modling, extrusion speed is controlled between the per minute 20m-22m;
Afterwards, with carrying out straightening processing behind the work-piece cools that squeezes out to the normal temperature;
The workpiece that subsequently, will pass through straightening processing is incubated 3.5 hours-4.5 hours and handles to carry out actual effect under 195 ℃-205 ℃ environment.
Said actual effect treatment temperature is 200 ℃.
The time that said actual effect is handled is 4 hours.
Adopt blower fan to force cooling during the said work-piece cools that squeezes out.
Adopt new radiator of the present invention to carry out the production of aluminium section bar with the aluminium section bar production technology, the quality better of its product, qualification rate are high, production cost is lower, effectively raise economic benefit of enterprises.
Description of drawings
Fig. 1 is the structural representation of new radiator with aluminium section bar.
The specific embodiment
The invention discloses a kind of new radiator and use the aluminium section bar production technology; Wherein, aluminium section bar is as shown in Figure 1, comprises substrate 1; Integrated setting has the strip heat sink 3 vertical with substrate on the upper surface of substrate 1; One side integrated setting of said substrate has installing plate 2, and this installing plate and strip heat sink laterally arrange, and the production of this aluminium section bar specifically comprises following processing step:
At first, be that the aluminium bar of A6060 (A6060 is aluminium commonly used, and the technical staff in the industry all knows this aluminium, therefore its constituent is not given unnecessary details here) is heated between 480 ℃-500 ℃ with extrusion die and material;
Then, the aluminium bar after the heating is positioned in the extrusion die, adopts extruder to carry out extrusion modling, extruder adopts the 800T extruder, and extrusion speed is controlled between the per minute 20m-22m, adopts flow quantity control instrument to control extrusion speed;
Afterwards; With carrying out straightening processing behind the work-piece cools that squeezes out to the normal temperature; Adopt blower fan to force cooling to the mode of the workpiece blowing that squeezes out during cooling, when straightening processing, adopt seven-roll Abramsen machine to carry out tension straingtening, wherein tractive force is between 1 to 150 ton;
The workpiece that subsequently, will pass through straightening processing is incubated 3.5 hours-4.5 hours and handles to carry out actual effect under 195 ℃-205 ℃ environment.The actual effect treatment temperature is preferably 200 ℃ in the present embodiment, and the preferred time that actual effect is handled is 4 hours.After actual effect was handled, the case hardness of aluminium section bar reached webster hardness 8HW-13HW.
What should explain at last is: the above is merely the preferred embodiments of the present invention; Be not limited to the present invention; Although the present invention has been carried out detailed explanation with reference to previous embodiment; For a person skilled in the art, it still can be made amendment to the technical scheme that aforementioned each embodiment put down in writing, and perhaps part technical characterictic wherein is equal to replacement.All within spirit of the present invention and principle, any modification of being done, be equal to replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (4)
1. a new radiator is used the aluminium section bar production technology; It is characterized in that: aluminium section bar comprises substrate; Integrated setting has the strip heat sink vertical with substrate on the upper surface of substrate; One side integrated setting of said substrate has installing plate, and this installing plate and strip heat sink laterally arrange, and its production craft step is following:
At first, be that the aluminium bar of A6060 is heated between 480 ℃-500 ℃ with extrusion die and material;
Then, the aluminium bar after the heating is positioned in the extrusion die, adopts extruder to carry out extrusion modling, extrusion speed is controlled between the per minute 20m-22m;
Afterwards, with carrying out straightening processing behind the work-piece cools that squeezes out to the normal temperature;
The workpiece that subsequently, will pass through straightening processing is incubated 3.5 hours-4.5 hours and handles to carry out actual effect under 195 ℃-205 ℃ environment.
2. new radiator according to claim 1 is used the aluminium section bar production technology, it is characterized in that: said actual effect treatment temperature is 200 ℃.
3. new radiator according to claim 1 and 2 is used the aluminium section bar production technology, it is characterized in that: the time that said actual effect is handled is 4 hours.
4. new radiator according to claim 3 is used the aluminium section bar production technology, it is characterized in that: adopt blower fan to force cooling during the said work-piece cools that squeezes out.