CN102359194A - 一种芯材与无机发泡外层复合的保温型材 - Google Patents

一种芯材与无机发泡外层复合的保温型材 Download PDF

Info

Publication number
CN102359194A
CN102359194A CN2011101885403A CN201110188540A CN102359194A CN 102359194 A CN102359194 A CN 102359194A CN 2011101885403 A CN2011101885403 A CN 2011101885403A CN 201110188540 A CN201110188540 A CN 201110188540A CN 102359194 A CN102359194 A CN 102359194A
Authority
CN
China
Prior art keywords
heat
core
mixed
core material
foaming
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2011101885403A
Other languages
English (en)
Inventor
巢启
刘海锋
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN2011101885403A priority Critical patent/CN102359194A/zh
Publication of CN102359194A publication Critical patent/CN102359194A/zh
Pending legal-status Critical Current

Abstract

本发明公开的是一种芯材与无机发泡外层复合的保温型材。目前,在建筑行业里都希望建筑物外墙外保温材料达到既保温又阻燃,既有足够的强度容重又低的要求,但目前的技术都无法对这些问题有一个理想的解决方案。本发明选用高强度的无机材料以发泡的形态做芯材的外复合层,这种无机材料发泡后其体内结构会形成无数个细小的密闭泡孔,具有厚度大、强度高而重量轻的特点,并且阻隔外界高温对易燃芯材的能力强。通过本发明使建筑物外墙外保温材料既保温又有较强的阻燃性,既有较大的强度容重又低,能方便牢固地固定在建筑物外墙表面。

Description

一种芯材与无机发泡外层复合的保温型材
技术领域
本发明涉及的是一种芯材与无机发泡外层复合的保温型材,属于建筑技术领域。
背景技术
目前,建筑物外墙外保温材料的主流产品是泡沫保温贴面板,或由其它具有保温性能的材料做成的贴面板,这些材料的两个最大特点就是保温和易燃,既具有较好的保温性能又具有易燃性,这是一对矛盾,如何解决这对矛盾,是当前建筑行业里比较头痛的问题。在建筑行业里希望达到的效果就是既能保温又具有较强的阻燃性。为解决这对矛盾,人们采用了许多有效的措施,其中一种措施就是以保温贴面板作为芯材,然后在芯材的表面包裹其它无机阻燃材料,甚至包裹金属材料,目前市售的这种保温材料有聚苯板、挤塑板、酚醛发泡板。这种方法虽然解决了保温与阻燃的问题,但随之而来的就是容重与强度及阻燃性的矛盾,保温芯材的外复合层越厚,强度越强阻燃性越好,而容重就越大,越难固定在建筑物的外墙上,所以上述聚苯板、挤塑板、酚醛发泡板为了保证足够的强度,其容重都达到了15kg/平方米以上;而保温芯材的外包裹层越薄,虽然容重越小,易固定在建筑物外墙上,但强度就越弱阻燃性就越差。这是一对不可调和的矛盾,在目前的技术基础上,属于一个长期以来未能得到理想解决的技术难题。因此,寻找一种技术措施,解决这个技术难题,必定会使建筑外墙保温技术得到一次技术的进步。
发明内容
本发明的目的就是提供一种复合无机发泡外层的保温型材,使得所述保温型材,具有较大的强度及阻燃性,而容重又较小,能方便牢固地固定在建筑物外墙表面,克服现有保温型材容重与强度及阻燃性不能很好协调的问题。
为实现上述目的,本发明采用了下述技术方案:一种芯材与无机发泡外层复合的保温型材,是由下述方法制备的:
(1)取纤维素醚水溶液,铝粉膏,水泥发泡剂,工业用的表面活性剂,按照质量比200∶100∶2∶2-2.5的比例混合均匀,得到复合发泡剂备用;
(2)取动物性发泡剂,十二烷基本磺酸钠,十二烷基硫酸钠,水,按质量比30∶2.5-12.5∶1.25-6.25∶2000的比例混合均匀,得到发泡助剂。
(3)取细度为200-1000目的原料粉体、pp纤维、乳胶粉、钠水玻璃、及发泡助剂,按照质量比125∶1-3∶3-4∶80-90∶10-20的比例混合均匀,得到浆体备用;
(4)按照复合发泡剂与浆体的质量比为1∶26.7-160的比率混合均匀,得到发泡材料;
(5)所述发泡材料还可以是425#以上高标号水泥与乳胶粉以质量比95-98∶2-5的比例混合均匀而得到的浆体,按照动物性发泡剂发泡后与浆体的体积比为1-1.5∶1的比例混合均匀,得到发泡材料;
(6)取无机发泡复合聚苯乙烯发泡颗粒做成的保温型材、挤塑板、聚苯板、酚醛发泡板或聚氨酯发泡板作为保温芯材,在芯材的表面铺设一层与芯材相同尺寸的玻璃纤维网,然后用发泡材料将芯材包裹密闭,包裹层未发泡时的厚度是0.15-1厘米,让发泡材料在芯材外发泡定型即得。
采取上述措施的本发明,选用高强度的无机材料以发泡的形态作为芯材的外复合层,这种无机材料发泡后其体内结构会形成无数个细小的密闭泡孔,具有厚度大、强度高而重量轻的特点,并且阻隔外界高温对易燃芯材的能力强。B1级防火的有机芯材在复合了无机发泡层后,防火等级可升至A级,板材整体的抗拉拔和抗冲击强度也得到很大提高,板重反而降低至12kg/m2以下。
具体实施方式
实施例1
(1)取纤维素醚水溶液,铝粉膏,水泥发泡剂,工业用的表面活性剂,按照质量比200∶100∶2∶2的比例混合均匀,得到复合发泡剂备用;
(2)取动物性发泡剂,十二烷基本磺酸钠,十二烷基硫酸钠,水,按质量比0.3∶0.05∶0.025∶20比例混合均匀,得到发泡助剂。
(3)取细度为300目的矿渣、pp纤维、乳胶粉、钠水玻璃、及发泡助剂,按照质量比125∶1∶3∶80∶10的比例混合均匀,得到浆体备用;
(4)按照复合发泡剂与浆体的质量比为1∶26.7的比率混合均匀,得到发泡材料;
(5)取无机发泡复合聚苯乙烯发泡颗粒做成的保温型材作为保温芯材,在芯材的表面铺设一层与芯材相同尺寸的玻璃纤维网,用刮刀将搅拌均匀的发泡材料批刮到网格布面层上并刮平实,直到芯材的外表面完全被发泡材料覆盖,发泡材料的批刮厚度为0.5cm,待发泡过程完成即可得到3cm的无机发泡包裹层,在室温下静置1-3h,表面完全固化后,用相同的方法对保温芯材的剩下的几个外表面逐一批刮发泡材料,得到完全包裹无机发泡外层的保温型材。
实施例2
(1)取纤维素醚水溶液,铝粉膏,水泥发泡剂,工业用的表面活性剂,按照质量比200∶100∶2∶2.5的比例混合均匀,得到复合发泡剂备用;
(2)取动物性发泡剂,十二烷基本磺酸钠,十二烷基硫酸钠,水,按质量比3∶0.25∶0.125∶200的比例混合均匀,得到发泡助剂。
(3)取细度为500目的矿渣与粉煤灰混合粉体、pp纤维、乳胶粉、钠水玻璃、及发泡助剂,按照质量比125∶3∶4∶90∶20的比例混合均匀,得到浆体备用;
(4)按照复合发泡剂与浆体的质量比为1∶160的比率混合均匀,得到发泡材料;
(5)取挤塑板作为保温芯材,在芯材的表面铺设一层与芯材相同尺寸的玻璃纤维网,往喷枪内注入搅拌均匀的发泡材料,按下述喷涂条件喷涂:气压0.35-0.45MPa,工件与喷枪嘴距离保持适度,使外包裹层达到1~2mm的发泡材料喷涂厚度,待发泡过程完成时可得到4~6mm的外包裹层,将喷涂后的工件在室温下静置1-3h,表面发泡层完全固化后,用相同的方法对保温芯材的剩下的几个外表面逐一喷涂发泡浆料,最终得到完全包包裹无机发泡外层的保温型材。
实施例3
(1)取工业用动物性发泡剂和水,按照质量比1∶50-70的比例混合均匀,得到发泡剂水溶液;
(2)取标号425#以上的水泥、乳胶粉以及水,按照质量比97∶3∶60的比例混合均匀,得到浆体备用;
(3)将动物性发泡剂水溶液通过机械发泡机中按50倍比率发泡,然后与浆体按照体积比为1∶1的比率混合均匀,得到发泡材料;
(4)取酚醛发泡板或聚氨酯发泡板作为保温芯材,在芯材的表面铺设一层与芯材相同尺寸的玻璃纤维网。取大小为保温芯材的长宽厚尺寸加上2cm的发泡层厚度的模具,首先在模底满铺一层玻璃纤维网,再均匀平铺1.5-4mm发泡材料,接着将芯板按在发泡材料上,又在芯材面继续铺上1.5-4mm发泡材料,再铺一层玻璃纤维网,同时用发泡材料填满芯材四周,然后给模具加上盖子,待发泡材料充满模具时,发泡过程结束,在室温下静置1-3h,材料完全固化后从模具中取出,即得到完全复合无机发泡外层的保温型材。

Claims (2)

1.一种芯材与无机发泡外层复合的保温型材,其特征是所述保温型材是由下述方法制备的:
(1)取纤维素醚水溶液,铝粉膏,水泥发泡剂,工业用的表面活性剂,按照质量比200∶100∶2∶2-2.5的比例混合均匀,得到复合发泡剂备用;
(2)取动物性发泡剂,十二烷基本磺酸钠,十二烷基硫酸钠,水,按质量比30∶2.5-12.5∶1.25-6.25∶2000的比例混合均匀,得到发泡助剂;
(3)取细度为200-1000目的原料粉体、pp纤维、乳胶粉、钠水玻璃、及发泡助剂,按照质量比125∶1-3∶3-4∶80-90∶10-20的比例混合均匀,得到浆体备用;
(4)按照复合发泡剂与浆体的质量比为1∶26.7-160的比率混合均匀,得到发泡材料;
(5)取无机发泡复合聚苯乙烯发泡颗粒做成的保温型材、挤塑板、聚苯板、酚醛发泡板或聚氨酯发泡板作为保温芯材,在芯材的表面铺设一层与芯材相同尺寸的玻璃纤维网,然后用发泡材料将芯材包裹密闭,包裹层未发泡时的厚度是0.15-1厘米,让发泡材料在芯材外发泡定型即得。
2.根椐权利要求1所述的保温型材,其特征是所述发泡材料是425#以上高标号水泥与乳胶粉以质量比95-98∶2-5的比例混合均匀而得到的浆体,按照动物性发泡剂发泡后与浆体的体积比为1-1.5∶1的比例混合均匀所得。
CN2011101885403A 2011-07-05 2011-07-05 一种芯材与无机发泡外层复合的保温型材 Pending CN102359194A (zh)