CN102358689B - Redispersable latex powder phenolic foam incubation slurry - Google Patents
Redispersable latex powder phenolic foam incubation slurry Download PDFInfo
- Publication number
- CN102358689B CN102358689B CN 201110227941 CN201110227941A CN102358689B CN 102358689 B CN102358689 B CN 102358689B CN 201110227941 CN201110227941 CN 201110227941 CN 201110227941 A CN201110227941 A CN 201110227941A CN 102358689 B CN102358689 B CN 102358689B
- Authority
- CN
- China
- Prior art keywords
- redispersable latex
- latex powder
- kilograms
- phenolic foam
- incubation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention discloses a redispersable latex powder phenolic foam incubation slurry. The slurry comprises a redispersable latex powder incubation material and phenolic foam particles, wherein a weight ratio of the redispersable latex powder incubation material to the phenolic foam particles is 1:0.6-0.8. The redispersable latex powder incubation material comprises the following components: 13-15 kg of redispersible powder, 3-8 kg of cellulose ether, 0.5-1.5 kg of a water-proofing agent, 80-100 kg of fly ash, 0.5-2 kg of glass fiber, 420-450 kg of cement and 100-150 kg of quartz sand with a particle size more than 100 meshes. The redispersable latex powder phenolic foam incubation slurry of the present invention can be adopted as a building external wall insulation material, and has a good insulation effect. The thermal conductivity of the slurry is less than or equal to 0.045 W/m.K. The redispersable latex powder phenolic foam incubation slurry of the present invention has high fire-protection rating, and the fire performance is class A2.
Description
Technical field
The present invention relates to a kind of material of construction, particularly the high Redispersable latex powder phenolic foam incubation slurry of a kind of high insulating effect and fire-protection rating.
Background technology
In the prior art, the skin lagging material is generally organic materials (such as materials such as polystyrene foam plate, urethane), although high insulating effect, but fire-protection rating is low, the spark of the generations such as pyrotechnics firecracker, electric welding or the metal cutting skin lagging material that easily ignites, thereby presence of fire accident.
Summary of the invention
For the deficiencies in the prior art, the object of the present invention is to provide the high Redispersable latex powder phenolic foam incubation slurry of a kind of high insulating effect and fire-protection rating, reduce because of the skin lagging material presence of fire accident of igniting.
Technical scheme of the present invention is achieved in that Redispersable latex powder phenolic foam incubation slurry, comprise redispersable latex powder insulation material and phenol formaldehyde foam, the weight proportion of described redispersable latex powder insulation material and described phenol formaldehyde foam is: 1: 0.6～0.8; Described redispersable latex powder insulation material composed as follows: 13～15 kilograms of redispersable latex powders, 3～8 kilograms of ether of cellulose, 0.5～1.5 kilogram of water-resisting agent, flyash 80～double centner, 0.5～2 kilogram in glass fibre, 100～150 kilograms of 420～450 kilograms of cement and quartz sands.Described phenol formaldehyde foam preferably uses the particle of phenol formaldehyde foam.
Above-mentioned Redispersable latex powder phenolic foam incubation slurry, described quartz sand are more than or equal to 100 purpose quartz sands.
Above-mentioned Redispersable latex powder phenolic foam incubation slurry, the weight proportion of described redispersable latex powder insulation material and described phenol formaldehyde foam is: 1: 0.7.
Above-mentioned Redispersable latex powder phenolic foam incubation slurry, described redispersable latex powder insulation material composed as follows: 14 kilograms of redispersable latex powders, 5 kilograms of ether of cellulose, 1 kilogram of water-resisting agent, 90 kilograms in flyash, 1.5 kilograms in glass fibre, 125 kilograms of 435 kilograms of cement and quartz sands.
Above-mentioned Redispersable latex powder phenolic foam incubation slurry, described cement are 425 cement.
Above-mentioned vitrified micro-bubble phenolic foam thermal insulation size, described redispersable latex powder are Germany's watt gram rubber powder.
The invention has the beneficial effects as follows: Redispersable latex powder phenolic foam incubation slurry of the present invention is as the skin lagging material, its high insulating effect, and thermal conductivity is less than or equal to 0.045W/mK; Fire-protection rating is high, and fire resistance reaches A
2Level.
Embodiment
The present invention is described further by reference to the accompanying drawings:
Embodiment 1
The Redispersable latex powder phenolic foam incubation slurry of the present embodiment comprises redispersable latex powder insulation material and phenol formaldehyde foam, and the weight proportion of described redispersable latex powder insulation material and described phenol formaldehyde foam is: 1: 0.7; Described redispersable latex powder insulation material composed as follows: 14 kilograms of redispersable latex powders, 5 kilograms of ether of cellulose, 1 kilogram of water-resisting agent, 90 kilograms in flyash, 1.5 kilograms in glass fibre, 125 kilograms of 435 kilograms of 425 cement and 100 order quartz sands.
Utilize the present embodiment Redispersable latex powder phenolic foam incubation slurry as the skin lagging material, its high insulating effect, thermal conductivity is 0.038W/mK; Fire resistance reaches A
2Level.
Embodiment 2
The Redispersable latex powder phenolic foam incubation slurry of the present embodiment comprises redispersable latex powder insulation material and phenol formaldehyde foam, and the weight proportion of described redispersable latex powder insulation material and described phenol formaldehyde foam is: 1: 0.6; Described redispersable latex powder insulation material composed as follows: 13 kilograms of redispersable latex powders, 3 kilograms of ether of cellulose, 0.5 kilogram of water-resisting agent, 80 kilograms in flyash, 0.5 kilogram in glass fibre, 420 kilograms of 425 cement and 150 order quartz sand double centners.
Utilize the present embodiment Redispersable latex powder phenolic foam incubation slurry as the skin lagging material, its high insulating effect, thermal conductivity is 0.042W/mK; Fire resistance reaches A
2Level.
Embodiment 3
The Redispersable latex powder phenolic foam incubation slurry of the present embodiment comprises redispersable latex powder insulation material and phenol formaldehyde foam, and the weight proportion of described redispersable latex powder insulation material and described phenol formaldehyde foam is: 1: 0.8; Described redispersable latex powder insulation material composed as follows: 15 kilograms of redispersable latex powders, 8 kilograms of ether of cellulose, 1.5 kilograms of water-resisting agents, flyash double centner, 2 kilograms in glass fibre, 150 kilograms of 450 kilograms of 425 cement and 200 order quartz sands.
Utilize the present embodiment Redispersable latex powder phenolic foam incubation slurry as the skin lagging material, its high insulating effect, thermal conductivity is 0.035W/mK; Fire resistance reaches A
2Level.
Claims (5)
1. Redispersable latex powder phenolic foam incubation slurry is characterized in that, comprises redispersable latex powder insulation material and phenol formaldehyde foam, and the weight proportion of described redispersable latex powder insulation material and described phenol formaldehyde foam is: 1: 0.6～0.8; Described redispersable latex powder insulation material composed as follows: 13～15 kilograms of redispersable latex powders, 3～8 kilograms of ether of cellulose, 0.5～1.5 kilogram of water-resisting agent, flyash 80～double centner, 0.5～2 kilogram in glass fibre, 100～150 kilograms of 420～450 kilograms of cement and quartz sands, described redispersable latex powder are Germany's watt gram rubber powder.
2. Redispersable latex powder phenolic foam incubation slurry according to claim 1 is characterized in that, described quartz sand is more than or equal to 100 purpose quartz sands.
3. Redispersable latex powder phenolic foam incubation slurry according to claim 2 is characterized in that, the weight proportion of described redispersable latex powder insulation material and described phenol formaldehyde foam is: 1: 0.7.
4. Redispersable latex powder phenolic foam incubation slurry according to claim 3, it is characterized in that, described redispersable latex powder insulation material composed as follows: 14 kilograms of redispersable latex powders, 5 kilograms of ether of cellulose, 1 kilogram of water-resisting agent, 90 kilograms in flyash, 1.5 kilograms in glass fibre, 125 kilograms of 435 kilograms of cement and quartz sands.
5. arbitrary described Redispersable latex powder phenolic foam incubation slurry is characterized in that according to claim 1-4, and described cement is 425 cement.