CN102351977B - 一种聚对苯二甲酸丁二醇酯增韧改性用丙烯酸酯共聚物乳液的制备方法 - Google Patents
一种聚对苯二甲酸丁二醇酯增韧改性用丙烯酸酯共聚物乳液的制备方法 Download PDFInfo
- Publication number
- CN102351977B CN102351977B CN2011101978501A CN201110197850A CN102351977B CN 102351977 B CN102351977 B CN 102351977B CN 2011101978501 A CN2011101978501 A CN 2011101978501A CN 201110197850 A CN201110197850 A CN 201110197850A CN 102351977 B CN102351977 B CN 102351977B
- Authority
- CN
- China
- Prior art keywords
- emulsion
- aqueous solution
- shell
- reductive agent
- seed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
Description
Claims (1)