CN102304268A - 一种改性丙烯腈-丁二烯-苯乙烯共聚物及其制备工艺 - Google Patents

一种改性丙烯腈-丁二烯-苯乙烯共聚物及其制备工艺 Download PDF

Info

Publication number
CN102304268A
CN102304268A CN201110105894A CN201110105894A CN102304268A CN 102304268 A CN102304268 A CN 102304268A CN 201110105894 A CN201110105894 A CN 201110105894A CN 201110105894 A CN201110105894 A CN 201110105894A CN 102304268 A CN102304268 A CN 102304268A
Authority
CN
China
Prior art keywords
butadiene
styrene copolymer
calcium sulfate
acrylonitrile
parts
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201110105894A
Other languages
English (en)
Other versions
CN102304268B (zh
Inventor
刘珍如
刘立文
付桃梅
杨志强
宁勇
鲁纪鸣
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hunan Fu Xiang new type building material Co., Ltd.
Original Assignee
刘立文
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 刘立文 filed Critical 刘立文
Priority to CN2011101058947A priority Critical patent/CN102304268B/zh
Publication of CN102304268A publication Critical patent/CN102304268A/zh
Application granted granted Critical
Publication of CN102304268B publication Critical patent/CN102304268B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种改性丙烯腈-丁二烯-苯乙烯共聚物及其制备工艺,该改性丙烯腈-丁二烯-苯乙烯共聚物由以下重量份数的原料制成:丙烯腈-丁二烯-苯乙烯共聚物100份,硫酸钙晶须15~40份,主抗氧剂1680.1~0.4份,硬脂酸1~4份,硅烷偶联剂KH5500.1~0.5份。其制备方法是,将硫酸钙晶须与硅烷偶联剂KH550加入高速混合机中活化处理8~12min;将其余原料与改性硫酸钙晶须在高速混合机中,于75~85℃下混合6~9min,干燥;然后将所得混合物通过双螺杆挤出机熔融造粒。本发明之改性丙烯腈-丁二烯-苯乙烯共聚物,抗冲击强度高,韧性好,特别适于制作电视机外壳、精密仪器壳体、汽车内饰及仪表结构件等。

Description

一种改性丙烯腈-丁二烯-苯乙烯共聚物及其制备工艺
技术领域
[0001] 本发明涉及一种丙烯腈-丁二烯-苯乙烯共聚物及其制备工艺,尤其涉及一种硫酸钙晶须改性丙烯腈-丁二烯-苯乙烯共聚物及其制备工艺。
背景技术
[0002] 丙烯腈-丁二烯-苯乙烯共聚物,是一种强度高、韧性好、易于加工成型的热塑性高分子材料,适于制作一般机械零件、减磨耐磨零件、传动零件和电讯零件。但是,其抗冲击性能不是很好,限制了其进一步的运用。
发明内容
[0003] 本发明要解决的技术问题是,克服现有丙烯腈-丁二烯-苯乙烯共聚物材料的不足,提供一种抗冲击强度高,韧性好的硫酸钙晶须改性丙烯腈-丁二烯-苯乙烯共聚物及其制备工艺。
[0004] 本发明解决所述技术问题所采用的技术方案是:
本发明之改性丙烯腈-丁二烯-苯乙烯共聚物由以下重量份数的原料制成:丙烯腈-丁二烯-苯乙烯共聚物(ABS) 100份,硫酸钙晶须15 〜40份,主抗氧剂168 0. 1〜0. 4份,硬脂酸1〜4份,硅烷偶联剂KH550 0. 1〜0. 5 份。
[0005] 优选的重量配比为:丙烯腈-丁二烯-苯乙烯共聚物(ABS)IOO份,硫酸钙晶须30 份,主抗氧剂168 0.2份,硬脂酸3份,硅烷偶联剂KH550 0.3份。
[0006] 本发明之改性丙烯腈-丁二烯-苯乙烯共聚物的制备工艺,包括如下步骤:
(1)将硫酸钙晶须与硅烷偶联剂KH550,在高速混合机中活化处理8〜12 min (优选 10 min),得改性硫酸钙晶须;
(2)将所述丙烯腈-丁二烯-苯乙烯共聚物、主抗氧剂168、硬脂酸加入到高速混合机中,于75〜85°C (优选80°C )下混合6〜9min (优选Siiin),干燥,得丙烯腈-丁二烯-苯乙烯共聚物、主抗氧剂168、硬脂酸与改性硫酸钙晶须的混合物;
(3)将步骤(2)所得混合物通过双螺杆挤出机熔融造粒,机筒温度为180 2300C (优选210°C ),螺杆转速为100〜130转/分(优选120转/分)。
[0007] 硫酸钙晶须,又称石膏晶须,是一种硫酸钙的纤维状单晶体。研究表明,本发明使用之改性硫酸钙晶须长径比为10〜20,直径为0.5〜lym,其具有均勻的横截面,完整的内部结构,这一特征赋予其接近晶体理论值-原子间价键的强度。由于其具有极高的强度,细微的尺寸,易与ABS界面粘合,提高与基体的相容性和界面黏结力,当受外力强迫取向时,ABS中的残余应力能很好地传递给硫酸钙晶须,从而提高复合材料的强度,同时改善复合材料的韧性;由于硫酸钙晶须为无机物,在ABS基质中分散均勻,不易团聚,使复合材料性能稳定。
[0008] 本发明之改性丙烯腈-丁二烯-苯乙烯共聚物,抗冲击强度高,韧性好,特别适于制作电视机外壳、精密仪器壳体、汽车内饰及仪表结构件等。 具体实施方式
[0009] 以下结合实施例对本发明作进一步详细说明。
[0010] 实施例1 一 4改性丙烯腈-丁二烯-苯乙烯共聚物的原料重量配比见表1。
[0011] 各实施例改性丙烯腈-丁二烯-苯乙烯共聚物的制备方法:
(1)将硫酸钙晶须与硅烷偶联剂KH550,在高速混合机中活化处理10 min,得改性硫酸钙晶须;改性硫酸钙晶须长径比13,直径0. 7μπι ;
(2 )将所述丙烯腈-丁二烯-苯乙烯共聚物、主抗氧剂168、硬脂酸加入高速混合机中, 于80°C下混合8min,干燥,得丙烯腈-丁二烯-苯乙烯共聚物、主抗氧剂168、硬脂酸与改性硫酸钙晶须的混合物;
(3)将步骤(2)所得混合物通过双螺杆挤出机熔融造粒,机筒温度为210°C,螺杆转速为120转/分。
[0012] 实施例1 一 4产品性能测试按ATSM规定方法进行,结果见表2。

Claims (4)

1. 一种改性丙烯腈-丁二烯-苯乙烯共聚物,其特征在于,由以下重量份数的原料制成:丙烯腈-丁二烯-苯乙烯共聚物100份,硫酸钙晶须15 〜40份,主抗氧剂168 0. 1〜0. 4份,硬脂酸1〜4份,硅烷偶联剂KH550 0. 1〜0. 5份。
2.根据权利要求1所述的改性丙烯腈-丁二烯-苯乙烯共聚物,其特征在于,由以下重量份数的原料制成:丙烯腈-丁二烯-苯乙烯共聚物100份,硫酸钙晶须30份,主抗氧剂 168 0. 2份,硬脂酸3份,硅烷偶联剂KH550 0. 3份。
3. —种如权利要求1或2所述的改性丙烯腈-丁二烯-苯乙烯共聚物的制备工艺,其特征在于,包括以下步骤:(1)将硫酸钙晶须与硅烷偶联剂KH550,在高速混合机中活化处理8 、12 min,得改性硫酸钙晶须;(2)将所述丙烯腈-丁二烯-苯乙烯共聚物、主抗氧剂168、硬脂酸加入到高速混合机中,于75〜85°C下混合6〜9min,干燥,得丙烯腈-丁二烯-苯乙烯共聚物、主抗氧剂168、 硬脂酸与改性硫酸钙晶须的混合物;(3)将步骤(2)所得混合物通过双螺杆挤出机熔融造粒,机筒温度为180〜230°C,螺杆转速为100 130转/分。
4. 一种如权利要求3所述的改性丙烯腈-丁二烯-苯乙烯共聚物的制备工艺,其特征在于,包括以下步骤:(1)将硫酸钙晶须与硅烷偶联剂KH550,在高速混合机中活化处理10 min,得改性硫酸钙晶须;(2)将所述丙烯腈-丁二烯-苯乙烯共聚物、主抗氧剂168、硬脂酸加入到高速混合机中,于80°C下混合Smin,干燥,得丙烯腈-丁二烯_苯乙烯共聚物、主抗氧剂168、硬脂酸与改性硫酸钙晶须的混合物;(3)将步骤(2)所得混合物通过双螺杆挤出机熔融造粒,机筒温度为210°C,螺杆转速为120转/分。
CN2011101058947A 2011-04-27 2011-04-27 一种改性丙烯腈-丁二烯-苯乙烯共聚物及其制备工艺 Active CN102304268B (zh)