CN102268758A - Non-dyed anti-pilling color yarns and preparation method thereof - Google Patents

Non-dyed anti-pilling color yarns and preparation method thereof Download PDF

Info

Publication number
CN102268758A
CN102268758A CN2011101997146A CN201110199714A CN102268758A CN 102268758 A CN102268758 A CN 102268758A CN 2011101997146 A CN2011101997146 A CN 2011101997146A CN 201110199714 A CN201110199714 A CN 201110199714A CN 102268758 A CN102268758 A CN 102268758A
Authority
CN
China
Prior art keywords
bar
speed
spacing
color
cylinder
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2011101997146A
Other languages
Chinese (zh)
Other versions
CN102268758B (en
Inventor
单伟明
龚群策
陈占强
史世忠
董贯东
洪新强
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hangzhou Hongyu Textile Co Ltd
Original Assignee
Hangzhou Hongyu Textile Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hangzhou Hongyu Textile Co Ltd filed Critical Hangzhou Hongyu Textile Co Ltd
Priority to CN 201110199714 priority Critical patent/CN102268758B/en
Publication of CN102268758A publication Critical patent/CN102268758A/en
Application granted granted Critical
Publication of CN102268758B publication Critical patent/CN102268758B/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses a spinning process, and in particular relates to non-dyed anti-pilling color yarns and a preparation method thereof. The preparation method comprises the following steps of: mixing cotton; performing an opening and picking process; performing a cotton carding process; performing a drawing process; performing a blend drawing process; performing a vortex spinning process; and confirming a color. By the non-dyed anti-pilling color yarns and the preparation method thereof, the conventional technical resources are fully integrated; a brand-new yarn preparation method is provided; rich colors can be obtained without dyeing; energy conservation and emission reduction are achieved to the greatest extent, and the national policy of low carbon and environmental protection and the worldwide dominant political ideology at present are followed; the production cost is greatly reduced; and the added value of products is improved.

Description

A kind of non-ANTIPILLING dyed yarn and preparation method thereof that dyes
Technical field
The present invention is a kind of spinning process, particularly a kind of non-ANTIPILLING dyed yarn and preparation method thereof that dyes.
Background technology
Original liquid coloring technology of the prior art: raw material is to use the technology of online interpolation, original liquid coloring, is main body by the specific standard of fused mass directly spinning explained hereafter and coloured staple fibre of multiple primary color, and other material combination get.Fiber spin-dying technology is simple, the form and aspect high conformity, and the COLOR FASTNESS height can reduce cost, and reduces environmental pollution, is different from the colored fibre of conventional textile raw material dyeing.
The look spinning technique: look spins the technology that mode adopts " dyeing earlier, back spinning ", the reach of dyeing link, shortened the production procedure of back road processing enterprise, the dyeing ratio is little, and cost reduces significantly, uses the color color technology simultaneously, rationally adjust spinning process, product is Eco-Fashion, and color is abundant, adapts to wide.Appearance in succession along with national low-carbon (LC) policy, under this overall situation, the rise in price of dyeing such as dyestuff, auxiliary agent material, blowdown limits and needs the requirement of circular treatment, and the dyeing cost will significantly increase, the mode that adopts look to spin, the reach of dyeing link, reduce the ratio of ingrain significantly, spinning industry, look spins and will be a developing direction that country advocates.
The eddy current spinning technique: the air injection air vortex spinning machine is to grow up on the basis of Air-Jet Spinning, and air vortex spinning is open-end-spinning, belongs to true sth. made by twisting structure.The air-jet eddy-current spinning principle: the air-flow of spray orifice ejection forms negative pressuren zone at the nozzle entrance place, under suction function, is inhaled in the nozzle through the parallel fibers bundle of front roller drawing-off.The front end of fibre bundle around guid needle, be subjected to forming yarn tail end drawing and import in the doffing tube, its rear end is subjected to the effect of high-speed eddy axial thrust load, the part fiber is the umbrella lodging in the doffing tube porch, the fiber of lodging is exposed in the gyration airflow of spray orifice ejection, revolution with air-flow is twisted on the yarn tail, forms real short fibre yarn output of twisting with the fingers shape.Air vortex spinning line filoplume is few, any surface finish, and anti-pilling property is much better than the product of other spinning form; Good hygroscopicity.Fabric sheen is good, and softness has bony again, and DIMENSIONAL STABILITY is good, and is wear-resisting.
Summary of the invention
The present invention solves the deficiencies in the prior art, provide coloured chemical fibre of a kind of shades of colour and dyed yarn to carry out the layout of system with the application original liquid coloring, manufacture method with the dyed yarn of original liquid coloring chemical fibre and other textile raw material blending, adopt following technological process: system's layout, color matching, mixed cotton, blow room system, carding process, drawing process, the eddy current spinning process has solved the drawback that common coloured fibre can not continue to produce on the eddy current spinning equipment, overcome eddy current and spin the technical barrier that processing dyed yarn consumption of raw materials is big, yarn strength is low.
Above-mentioned technical problem of the present invention is mainly solved by following technical proposals:
A kind of non-ANTIPILLING dyed yarn that dyes, form by following prescription:
A bar: red coffee-like terylene 5%, golden yellow terylene 12%, white polyester 48%, white viscose glue 35%;
B bar: red coffee-like terylene 5%, golden yellow terylene 15%, white polyester 45%, white viscose glue 35%.
The non-ANTIPILLING dyed yarn that dyes can be made up of the bar of multiple different colours, and A bar and B bar are to lift row.
The non-ANTIPILLING dyed yarn that dyes, adopt the eddy current of original liquid coloring chemical fibre and other textile raw material blending to spin dyed yarn, it is wider that other textile raw material is contained face, comprises terylene, acrylic fibers, polyamide fibre, viscose glue, model, day silk, cotton etc., the raw material type number is not limit, and decides according to the needs of actual constituent and color.
A kind of non-preparation method who dyes the ANTIPILLING dyed yarn comprises following processing step:
(1), mixed cotton: A bar and B bar are carried out the mixed cotton processing respectively:
A bar and two kinds of raw materials of B bar are entered into griping cotton machine respectively fully mix, form the bale of cotton;
(2), blow room system: A bar and B bar are carried out blow room system respectively:
The mixed bale of cotton is sent in the opener, and hired roughneck's speed is 450~550r/min, and spacing between hired roughneck and the dirt rod in the opener, import is 10~14mm, and the centre is 11.5~15.5mm, and outlet is 14.5~18.5mm; Spacing between the dirt rod, import is 11~13mm, and the centre is 7~9mm, and outlet is 4~7mm, is made into lap, and lap is wrapped, and deposits 8~12 hours;
(3), carding process: A bar and B bar are carried out carding process respectively:
The lap of making is entered in the carding machine, the licker-in in the carding machine and the differential surface speed of cylinder are between 1.85~2.02, dwindle spacing of comb and parallel cotton fibers prior to spinning rear portion, leak the end import amplification of spacing, raise the mote knife relative position, and flat cutter is installed, implementing many combs lacks to fall, 5 that dwindle between cylinder and the cover plate space, and dwindle between cylinder and the doffer and space, and the cover plate velocity of rotation slows down, the speed of cylinder is 320~360r/min, the speed of licker-in is 750~850r/min, and the speed of cover plate is 85~121r/min, and 5 between cover plate and the cylinder space and are respectively 0.2mm, 0.18mm, 0.18mm, 0.18mm and 0.2mm, the height of mote knife is 3mm~5mm, angle is 90 degree~95 degree, and spacing of cylinder and doffer is 0.13~0.15mm, and weight of card sliver is 15~25g/5m;
(4), drawing process: A bar and B bar are carried out drawing process respectively:
The carded sliver that comb is good carries out drafting and forms ripe, and spacing of roller is 10*5*16mm during drafting, and the speed of shaping is 230~260m/min, ripe quantitatively be 18~25g/5m;
(5), merge drawing process: A bar and B bar are merged drawing process:
Ripe with step (4) merges drafting, and spacing of roller is that 10*5*16mm, the speed of shaping are 230~260m/min during drafting, ripe quantitatively be 18~25g/5m;
(6), eddy current spinning process:
Step (5) is circulated ripe that makes, enter into the air injection air vortex spinning machine, the pressure of nozzle is 0.5~0.6mPa, and blast is 1.6*10 4Pa~2.13*10 4Pa, the speed of a motor vehicle is 360~400m/min;
(7), color is confirmed: confirm as color, be carried out to bag and handle; Do not confirm as color, then enter color matching program(me), increase different vittas, the flow process before the circulation is carried out step (6) again, confirms up to color.
As preferably, comprise following processing step:
(1), mixed cotton: A bar and B bar are carried out the mixed cotton processing respectively:
A bar and two kinds of raw materials of B bar are entered into griping cotton machine respectively fully mix, form the bale of cotton;
(2), blow room system: A bar and B bar are carried out blow room system respectively:
The mixed bale of cotton is sent in the opener, and hired roughneck's speed is 480~520r/min, and spacing between hired roughneck and the dirt rod in the opener, import is 10~12mm, and the centre is 11.5~14.5mm, and outlet is 14.5~16.5mm; Spacing between the dirt rod, import is 11~12mm, and the centre is 7~8mm, and outlet is 4~6mm, is made into lap, and lap is wrapped, and deposits 10~12 hours;
(3), carding process: A bar and B bar are carried out carding process respectively:
The lap of making is entered in the carding machine, the licker-in in the carding machine and the differential surface speed of cylinder are between 1.85~1.98, dwindle spacing of comb and parallel cotton fibers prior to spinning rear portion, leak the end import amplification of spacing, raise the mote knife relative position, and flat cutter is installed, implementing many combs lacks to fall, 5 that dwindle between cylinder and the cover plate space, and dwindle between cylinder and the doffer and space, and the cover plate velocity of rotation slows down, the speed of cylinder is 340~360r/min, the speed of licker-in is 780~850r/min, and the speed of cover plate is 95~121r/min, and 5 between cover plate and the cylinder space and are respectively 0.2mm, 0.18mm, 0.18mm, 0.18mm and 0.2mm, the height of mote knife is 3mm~5mm, angle is 92 degree~95 degree, and spacing of cylinder and doffer is 0.13~0.15mm, and weight of card sliver is 18~23g/5m;
(4), drawing process: A bar and B bar are carried out drawing process respectively:
The carded sliver that comb is good carries out drafting and forms ripe, and spacing of roller is 10*5*16mm during drafting, and the speed of shaping is 235~260m/min, ripe quantitatively be 18~23g/5m;
(5), merge drawing process: A bar and B bar are merged drawing process:
Ripe with step (4) merges drafting, and spacing of roller is that 10*5*16mm, the speed of shaping are 235~260m/min during drafting, ripe quantitatively be 18~23g/5m;
(6), eddy current spinning process:
Step (5) is circulated ripe that makes, enter into the air injection air vortex spinning machine, the pressure of nozzle is 0.52~0.58mPa, and blast is 1.8*10 4Pa~2.1*10 4Pa, the speed of a motor vehicle is 360~380m/min;
(7), color is confirmed: confirm as color, then advance as big production procedure; Do not confirm as color, then enter color matching program(me), increase different vittas, the flow process before the circulation is carried out step (6) again, confirms up to color, enters big production procedure again.
By the original liquid coloring technology, improve dyed yarn COLOR FASTNESS grade, reduce the eddy current that causes because of the COLOR FASTNESS problem and spin the drawback that operation can not continue to produce.The high corresponding minimizing of COLOR FASTNESS causes the injury to human body such as clothing dyestuff, inorganic residue, the non-ANTIPILLING dyed yarn health environment-friendly more that dyes because of dyeing.The original liquid coloring chemical fibre, reduces coloured fibre significantly and produces the problem that has some setbacks because of the raw material electrostatic problem causes much smaller than common dyeing same specification raw material than the resistance order of magnitude, enhances productivity.Original liquid coloring chemical fibre monofilament strength and same specification primary colors chemical fibre are quite powerful, but common coloured fibre monofilament strength is than same specification brown stock low 10%~20%, therefore the non-yarn of ANTIPILLING dyed yarn after that dye with respect to same specification base dyeing yarn, powerful advantage is arranged, overcome the monofilament strength loss that common dyed yarn causes because of stock-dye, thus the yarn strength that causes problem on the low side.Original liquid coloring chemical fibre colour stable is avoided loose stock dyeing color problem of unstable.
Color is to produce physiological influence by people's impression or association, and the effect of color matching is exactly by the level of comfort in change space and the requirement of the each side that ambiance satisfies the consumer.Dyed yarn color matching mainly be by color form and aspect, lightness, purity to recently controlling visual stimulus, reach the effect of color matching, simultaneously, pass on by psychological aspect sense organ, indirect ground changes color, thereby reaches the effect of color matching.
Dyed yarn color matching is set up on the color color matching theory, is model based on the colour solid of three primary colors theory, is different from the phenomenon that mixes fully of dyestuff color matching on the microcosmic, is different from macroscopical large scale solid arranging effect of matching colors again, between the colour mixture effect between the two.By system's layout, applied original liquid coloring chemical fibre and the yarn produced are planned, by the distinctive non-ANTIPILLING dyed yarn colour system of dying of theoretical arrangement one cover of color matching.
Air vortex spinning is a kind of novel spinning technique, because the eddy current spinning equipment not too adapts to, the equipment supplier does not recommend to produce the look spinning yet, in the actual production process, because it is the super draft spinning system that eddy current spins, the environmental requirement of spinning around it reaches color is very high, by main frame, the dolly of splicing, doffer etc. on the eddy current spinning equipment are transformed, the exploitation special part, raising equipment is to the susceptibility of color, carry out special workshop condition management, and formulate special spinning process, be implemented in eddy current spinning equipment smoothness and produce dyed yarn.Utilize the air-flow mixing principle of eddy current spinning equipment simultaneously, make product colour mixture effect uniform and smooth more, unique style.
Therefore, non-ANTIPILLING dyed yarn and preparation method thereof that dyes provided by the invention, fully integrate the prior art resource, a kind of brand-new yarn preparation method is provided, realize that dye-free also can obtain to enrich color, energy-saving and emission-reduction to greatest extent meet national policy and world's mainstream ideology of current low-carbon environment-friendly, reduce production costs significantly, improve added value of product.
 
The specific embodiment
Below by embodiment, technical scheme of the present invention is described in further detail.
A kind of non-ANTIPILLING dyed yarn that dyes, form by following prescription:
A bar: red coffee-like terylene 5%, golden yellow terylene 12%, white polyester 48%, white viscose glue 35%;
B bar: red coffee-like terylene 5%, golden yellow terylene 15%, white polyester 45%, white viscose glue 35%.
Embodiment 1:
A kind of non-preparation method who dyes the ANTIPILLING dyed yarn comprises following processing step:
(1), mixed cotton: A bar and B bar are carried out the mixed cotton processing respectively:
A bar and two kinds of raw materials of B bar are entered into griping cotton machine respectively fully mix, form the bale of cotton;
(2), blow room system: A bar and B bar are carried out blow room system respectively:
The mixed bale of cotton is sent in the opener, and hired roughneck's speed is 450r/min, and spacing between hired roughneck and the dirt rod in the opener, import is 10mm, and the centre is 11.5mm, exports to be 14.5mm; Spacing between the dirt rod, import is 11mm, and the centre is 7mm, exports to be 4mm, is made into lap, and lap is wrapped, and deposits 8 hours;
(3), carding process: A bar and B bar are carried out carding process respectively:
The lap of making is entered in the carding machine, the licker-in in the carding machine and the differential surface speed of cylinder are between 1.85, dwindle spacing of comb and parallel cotton fibers prior to spinning rear portion, leak the end import amplification of spacing, raise the mote knife relative position, and flat cutter is installed, implementing many combs lacks to fall, 5 that dwindle between cylinder and the cover plate space, and dwindle between cylinder and the doffer and space, and the cover plate velocity of rotation slows down, the speed of cylinder is 320r/min, the speed of licker-in is 750r/min, and the speed of cover plate is 85r/min, and 5 between cover plate and the cylinder space and are respectively 0.2mm, 0.18mm, 0.18mm, 0.18mm and 0.2mm, the height of mote knife is 3mm, angle is 90 degree, and spacing of cylinder and doffer is that 0.13mm, weight of card sliver are 15g/5m;
(4), drawing process: A bar and B bar are carried out drawing process respectively:
The carded sliver that comb is good carries out drafting and forms ripe, and spacing of roller is 10*5*16mm during drafting, and the speed of shaping is 230m/min, ripe be 18g/5m quantitatively;
(5), merge drawing process: A bar and B bar are merged drawing process:
Ripe with step (4) merges drafting, and spacing of roller is that 10*5*16mm, the speed of shaping are 230m/min during drafting, ripe be 18g/5m quantitatively;
(6), eddy current spinning process:
Step (5) is circulated ripe that makes, enter into the air injection air vortex spinning machine, the pressure of nozzle is 0.5mPa, and blast is 1.6*10 4Pa, the speed of a motor vehicle is 360m/min;
(8), color is confirmed: confirm as color, be carried out to bag and handle; Do not confirm as color, then enter color matching program(me), increase different vittas, the flow process before the circulation is carried out step (6) again, confirms up to color.
Embodiment 2:
A kind of non-preparation method who dyes the ANTIPILLING dyed yarn comprises following processing step:
(1), mixed cotton: A bar and B bar are carried out the mixed cotton processing respectively:
A bar and two kinds of raw materials of B bar are entered into griping cotton machine respectively fully mix, form the bale of cotton;
(2), blow room system: A bar and B bar are carried out blow room system respectively:
The mixed bale of cotton is sent in the opener, and hired roughneck's speed is 500r/min, and spacing between hired roughneck and the dirt rod in the opener, import is 12mm, and the centre is 12.5mm, exports to be 16mm; Spacing between the dirt rod, import is 12mm, and the centre is 8mm, exports to be 5mm, is made into lap, and lap is wrapped, and deposits 10 hours;
(3), carding process: A bar and B bar are carried out carding process respectively:
The lap of making is entered in the carding machine, the licker-in in the carding machine and the differential surface speed of cylinder are between 1.95, dwindle spacing of comb and parallel cotton fibers prior to spinning rear portion, leak the end import amplification of spacing, raise the mote knife relative position, and flat cutter is installed, implementing many combs lacks to fall, 5 that dwindle between cylinder and the cover plate space, and dwindle between cylinder and the doffer and space, and the cover plate velocity of rotation slows down, the speed of cylinder is 340r/min, the speed of licker-in is 800r/min, and the speed of cover plate is 100r/min, and 5 between cover plate and the cylinder space and are respectively 0.2mm, 0.18mm, 0.18mm, 0.18mm and 0.2mm, the height of mote knife is 4mm, angle is 92 degree, and spacing of cylinder and doffer is that 0.14mm, weight of card sliver are 20g/5m;
(4), drawing process: A bar and B bar are carried out drawing process respectively:
The carded sliver that comb is good carries out drafting and forms ripe, and spacing of roller is 10*5*16mm during drafting, and the speed of shaping is 245m/min, ripe be 22g/5m quantitatively;
(5), merge drawing process: A bar and B bar are merged drawing process:
Ripe with step (4) merges drafting, and spacing of roller is that 10*5*16mm, the speed of shaping are 250m/min during drafting, ripe be 22g/5m quantitatively;
(6), eddy current spinning process:
Step (5) is circulated ripe that makes, enter into the air injection air vortex spinning machine, the pressure of nozzle is 0.55mPa, and blast is 2.0*10 4Pa, the speed of a motor vehicle is 380m/min;
(9), color is confirmed: confirm as color, be carried out to bag and handle; Do not confirm as color, then enter color matching program(me), increase different vittas, the flow process before the circulation is carried out step (6) again, confirms up to color.
Embodiment 3:
A kind of non-preparation method who dyes the ANTIPILLING dyed yarn comprises following processing step:
(1), mixed cotton: A bar and B bar are carried out the mixed cotton processing respectively:
A bar and two kinds of raw materials of B bar are entered into griping cotton machine respectively fully mix, form the bale of cotton;
(2), blow room system: A bar and B bar are carried out blow room system respectively:
The mixed bale of cotton is sent in the opener, and hired roughneck's speed is 550r/min, and spacing between hired roughneck and the dirt rod in the opener, import is 14mm, and the centre is 15.5mm, exports to be 18.5mm; Spacing between the dirt rod, import is 13mm, and the centre is 9mm, exports to be 7mm, is made into lap, and lap is wrapped, and deposits 12 hours;
(3), carding process: A bar and B bar are carried out carding process respectively:
The lap of making is entered in the carding machine, the licker-in in the carding machine and the differential surface speed of cylinder are between 2.02, dwindle spacing of comb and parallel cotton fibers prior to spinning rear portion, leak the end import amplification of spacing, raise the mote knife relative position, and flat cutter is installed, implementing many combs lacks to fall, 5 that dwindle between cylinder and the cover plate space, and dwindle between cylinder and the doffer and space, and the cover plate velocity of rotation slows down, the speed of cylinder is 360r/min, the speed of licker-in is 850r/min, and the speed of cover plate is 121r/min, and 5 between cover plate and the cylinder space and are respectively 0.2mm, 0.18mm, 0.18mm, 0.18mm and 0.2mm, the height of mote knife is 5mm, angle is 95 degree, and spacing of cylinder and doffer is that 0.15mm, weight of card sliver are 25g/5m;
(4), drawing process: A bar and B bar are carried out drawing process respectively:
The carded sliver that comb is good carries out drafting and forms ripe, and spacing of roller is 10*5*16mm during drafting, and the speed of shaping is 260m/min, ripe be 25g/5m quantitatively;
(5), merge drawing process: A bar and B bar are merged drawing process:
Ripe with step (4) merges drafting, and spacing of roller is that 10*5*16mm, the speed of shaping are 260m/min during drafting, ripe be 25g/5m quantitatively;
(6), eddy current spinning process:
Step (5) is circulated ripe that makes, enter into the air injection air vortex spinning machine, the pressure of nozzle is 0.6mPa, and blast is 2.13*10 4Pa, the speed of a motor vehicle is 400m/min;
(10), color is confirmed: confirm as color, be carried out to bag and handle; Do not confirm as color, then enter color matching program(me), increase different vittas, the flow process before the circulation is carried out step (6) again, confirms up to color.
Embodiment 1 to embodiment 3: the non-ANTIPILLING dyed yarn anti-fluffing and anti-pilling grade of dying reaches more than 3.5 grades, and washing fastness reaches more than 4 grades.Soft, good luster.

Claims (3)

1. non-ANTIPILLING dyed yarn that dyes is characterized in that being made up of following prescription:
A bar: red coffee-like terylene 5%, golden yellow terylene 12%, white polyester 48%, white viscose glue 35%;
B bar: red coffee-like terylene 5%, golden yellow terylene 15%, white polyester 45%, white viscose glue 35%.
2. a non-preparation method who dyes the ANTIPILLING dyed yarn is characterized in that, comprises following processing step:
(1), mixed cotton: A bar and B bar are carried out the mixed cotton processing respectively:
A bar and two kinds of raw materials of B bar are entered into griping cotton machine respectively fully mix, form the bale of cotton;
(2), blow room system: A bar and B bar are carried out blow room system respectively:
The mixed bale of cotton is sent in the opener, and hired roughneck's speed is 450~550r/min, and spacing between hired roughneck and the dirt rod in the opener, import is 10~14mm, and the centre is 11.5~15.5mm, and outlet is 14.5~18.5mm; Spacing between the dirt rod, import is 11~13mm, and the centre is 7~9mm, and outlet is 4~7mm, is made into lap, and lap is wrapped, and deposits 8~12 hours;
(3), carding process: A bar and B bar are carried out carding process respectively:
The lap of making is entered in the carding machine, the licker-in in the carding machine and the differential surface speed of cylinder are between 1.85~2.02, dwindle spacing of comb and parallel cotton fibers prior to spinning rear portion, leak the end import amplification of spacing, raise the mote knife relative position, and flat cutter is installed, implementing many combs lacks to fall, 5 that dwindle between cylinder and the cover plate space, and dwindle between cylinder and the doffer and space, and the cover plate velocity of rotation slows down, the speed of cylinder is 320~360r/min, the speed of licker-in is 750~850r/min, and the speed of cover plate is 85~121r/min, and 5 between cover plate and the cylinder space and are respectively 0.2mm, 0.18mm, 0.18mm, 0.18mm and 0.2mm, the height of mote knife is 3mm~5mm, angle is 90 degree~95 degree, and spacing of cylinder and doffer is 0.13~0.15mm, and weight of card sliver is 15~25g/5m;
(4), drawing process: A bar and B bar are carried out drawing process respectively:
The carded sliver that comb is good carries out drafting and forms ripe, and spacing of roller is 10*5*16mm during drafting, and the speed of shaping is 230~260m/min, ripe quantitatively be 18~25g/5m;
(5), merge drawing process: A bar and B bar are merged drawing process:
Ripe with step (4) merges drafting, and spacing of roller is that 10*5*16mm, the speed of shaping are 230~260m/min during drafting, ripe quantitatively be 18~25g/5m;
(6), eddy current spinning process:
Step (5) is circulated ripe that makes, enter into the air injection air vortex spinning machine, the pressure of nozzle is 0.5~0.6mPa, and blast is 1.6*10 4Pa~2.13*10 4Pa, the speed of a motor vehicle is 360~400m/min;
(7), color is confirmed: confirm as color, be carried out to bag and handle; Do not confirm as color, then enter color matching program(me), increase different vittas, the flow process before the circulation is carried out step (6) again, confirms up to color.
3. a kind of non-preparation method who dyes the ANTIPILLING dyed yarn according to claim 2 is characterized in that, comprises following processing step:
(1), mixed cotton: A bar and B bar are carried out the mixed cotton processing respectively:
A bar and two kinds of raw materials of B bar are entered into griping cotton machine respectively fully mix, form the bale of cotton;
(2), blow room system: A bar and B bar are carried out blow room system respectively:
The mixed bale of cotton is sent in the opener, and hired roughneck's speed is 480~520r/min, and spacing between hired roughneck and the dirt rod in the opener, import is 10~12mm, and the centre is 11.5~14.5mm, and outlet is 14.5~16.5mm; Spacing between the dirt rod, import is 11~12mm, and the centre is 7~8mm, and outlet is 4~6mm, is made into lap, and lap is wrapped, and deposits 10~12 hours;
(3), carding process: A bar and B bar are carried out carding process respectively:
The lap of making is entered in the carding machine, the licker-in in the carding machine and the differential surface speed of cylinder are between 1.85~1.98, dwindle spacing of comb and parallel cotton fibers prior to spinning rear portion, leak the end import amplification of spacing, raise the mote knife relative position, and flat cutter is installed, implementing many combs lacks to fall, 5 that dwindle between cylinder and the cover plate space, and dwindle between cylinder and the doffer and space, and the cover plate velocity of rotation slows down, the speed of cylinder is 340~360r/min, the speed of licker-in is 780~850r/min, and the speed of cover plate is 95~121r/min, and 5 between cover plate and the cylinder space and are respectively 0.2mm, 0.18mm, 0.18mm, 0.18mm and 0.2mm, the height of mote knife is 3mm~5mm, angle is 92 degree~95 degree, and spacing of cylinder and doffer is 0.13~0.15mm, and weight of card sliver is 18~23g/5m;
(4), drawing process: A bar and B bar are carried out drawing process respectively:
The carded sliver that comb is good carries out drafting and forms ripe, and spacing of roller is 10*5*16mm during drafting, and the speed of shaping is 235~260m/min, ripe quantitatively be 18~23g/5m;
(5), merge drawing process: A bar and B bar are merged drawing process:
Ripe with step (4) merges drafting, and spacing of roller is that 10*5*16mm, the speed of shaping are 235~260m/min during drafting, ripe quantitatively be 18~23g/5m;
(6), eddy current spinning process:
Step (5) is circulated ripe that makes, enter into the air injection air vortex spinning machine, the pressure of nozzle is 0.52~0.58mPa, and blast is 1.8*10 4Pa~2.1*10 4Pa, the speed of a motor vehicle is 360~380m/min;
(7), color is confirmed: confirm as color, then advance as big production procedure; Do not confirm as color, then enter color matching program(me), increase different vittas, the flow process before the circulation is carried out step (6) again, confirms up to color, enters big production procedure again.
CN 201110199714 2011-07-18 2011-07-18 Non-dyed anti-pilling color yarns and preparation method thereof Expired - Fee Related CN102268758B (en)